• Journal of Industrial Technology
• /
• v.23 no.A
• /
• pp.187-191
• /
• 2003

A hollow-fiber type polysulfone UF membrane was surface-coated with hydroxyethylmethacrylate (HEMA). The effect of various coating parameters on permeation flux, such as concentration ratio of AIBN/HEMA, solvent(water or methanol), and UV irradiation time, was investigated. The water permeation flux of oil-emulsion increased with concentration ratio of AIBN/HEMA, and increased with UV irradiation time. The flux of the membrane coated in solution using methanol as a solvent was greater than that of the membrane coated in solution using water as a solvent. The flux of both the coated and the uncoated membrane declined with the operation. The flux decline means that the membrane fouling by oil-emulsion occurs. However, the fouling of the coated membrane was much less than that of the uncoated membrane.

• Journal of Electrochemical Science and Technology
• /
• v.9 no.3
• /
• pp.212-219
• /
• 2018

Perovskite type ceramic membranes which exhibit dual ion conduction (proton and oxygen ion conduction) can permeate water and can aid solving operational problems such as temperature gradient and carbon deposition associated with a working solid oxide fuel cell. From this point of view, it is crucial to reveal water transport mechanism and especially the nature of the surface sites that is necessary for water incorporation and evolution. $BaCe_{0.8}Y_{0.2}O_{3-{\alpha}}$ (BCY20) was used as a model proton and oxygen ion conducting membrane in this work. Four different catalytically modified membrane configurations were used for the investigations and water flux was measured as a function of temperature. In addition, CO was introduced to the permeate side in order to test the stability of membrane against water and $CO/CO_2$ and post operation analysis of used membranes were carried out. The results revealed that water incorporation occurs on any exposed electrolyte surface. However, the magnitude of water permeation changes depending on which membrane surface is catalytically modified. The platinum increases the water flux on the feed side whilst it decreases the flux on the permeate side. Water flux measurements suggest that platinum can block water permeation on the permeate side by reducing the access to the lattice oxygen in the surface layer.

• Korean Membrane Journal
• /
• v.7 no.1
• /
• pp.19-27
• /
• 2005

PP hollow fiber membrane was hydrophilized by EVOH dip coating followed by low temperature plasma treatment and UV irradiation. EVOH coating attained high water flux without any prewetting but its stability did not guaranteed at high water permeation rate. At high water permeation rate, water flux declined gradually due to swelling and delamination of the EVOH coating layer causing pore blocking effect. However, plasma treatment reduces the swelling, which suppress delamination of the EVOH coating layer from PP support result in relieving the flux decline. Also, UV irradiation helped the crosslinking of the EVOH coating layer to enhance the performance at low water permeation rate. FT-IR and ESCA analyses reveal that EVOH dip coating performed homogeneously through not only membrane surface but also matrix. Thermogram of EVOH film modified plasma treatment and W irradiation show that crosslinking density of EVOH layer increased. Chemical modification by plasma treatment and UV irradiation stabilized the hydrophilic coating layer to increase the critical flux of the submerged membrane.

• Clean Technology
• /
• v.5 no.2
• /
• pp.69-78
• /
• 1999

Separation characteristics of cutting oil-in-water emulsions were studied experimentally by using various kinds of flat-type microfiltration and ultrafiltration membranes. For ultrafiltration membranes the permeation behavior of cutting oil emulsions obeys the film model, whereas a significant deviation from the model was observed for ASYPOR microfiltration membranes. The experimental data obtained for all the membranes showed that the effect of operating pressure on the permeation flux of oil-in-water emulsions is not very significant. At low transmembrane pressures the permeation flux decreased gradually with increasing filtration time, whereas the permeation flux at high transmembrane pressures decreased steeply for early filtration time. However, every flux eventually reached a constant value that depends only on the applied transmembrane pressure. For the hydrophobic polycarbonate microfiltration membrane the permeation flux increased with the filtration time. The critical permeation pressures were also determined from the data obtained from unstirred cell experiments.

• Membrane Journal
• /
• v.10 no.3
• /
• pp.121-129
• /
• 2000

The membrane requires both high in selectivity and flux. However, the permselective membrane has low flux. In this study, the porous alumina membrane was coated with silane coupling agent in order to enhance the flux with proper selectivity. The contact angle of water to the surface-modified alumina membrane was greater than 90$^{\circ}$, which indicated the high hydrophobicity. The modified membrane was tested in vapor permeation for the concentration of aqueous ethanol, isopropanol, and n-butanol. With the increase of ethanol, isopropanol, butanol concentration in the feed, permeation flux increased due to the greater affinity of ethanol, isopropanol, butanol with surface-modified alumina membrane than that of water. The experimental results showed that the permeation tate of surface-modified alumina membrane was 20~1000 times greater than that of a polymer membranes.

• Applied Chemistry for Engineering
• /
• v.10 no.6
• /
• pp.954-959
• /
• 1999

Radiation-induced grafting of 2-hydroxyethyl methacrylate(HEMA), acrylic acid(AAc) and methacrylic acid(MAAc) onto polypropylene microfiltration membrane has been studied. The effect of grafting conditions such as solvent composition(MeOH and $H_2O$) and monomer concentration on the grafting yield in investigated. The highest degree of grafting is obtained at a solvent composition of 25% $H_2O$:75% MeOH for HEMA, pure water for AAc and 50% $H_2O$:50% MeOH for MAAc. Modification of the PP membranes with hydrophilic monomers is shown to cause an increase in the water permeation flux of the membranes. It is found that HEMA is the best monomer to increase the water permeation flux and the highest water permeation flux is obtained at 99% degree of grafting. The water permeation flux of AAc-grafted PP membrane and MAAc-grafted PP membrane is very sensitive to environmental pH and $Cu^{2+}$ ion, but the water permeation flux of HEMA-grafted PP membrane scarcely depends on pH and $Cu^{2+}$ ion.

• Journal of Environmental Science International
• /
• v.25 no.2
• /
• pp.231-238
• /
• 2016

In this study, we have investigated to find optimal pre-treatment flocculation condition by analyzing the floc growth rate with mixing conditions and the membrane permeation flux for pre-treatment step of the membrane process. The higher mixing intensity showed a constant floc size index (FSI) values, and lower mixing intensity increased the degree of dispersion of the FSI values. Results of comparing the distribution characteristics of the FSI value and the permeation flux were more effective in increasing flux when the FSI values were 0.2 or higher. The degree of dispersion of FSI was relatively large in 40 rpm mixing condition compared to 120 rpm. In 40 rpm mixing condition, it decreased the permeation flux compared to 120 rpm because various sizes of flocs were distributed. Coagulation-UF membrane process enhanced 30%~40% of the flux rate compare to UF alone process, and the coagulation-MF process increased up to 5% of the flux rate compare to MF alone process. Pre-treatment, that is, coagulation process, has been found to be less effects on relatively larger pore size for MF membrane. For UF membrane, the flux was a little bit same when applying only the rapid mixing process or rapid mixing with slow mixing processes together. In case of MF membrane, the flux was improved when rapid mixing process applied with slow mixing process together.

• Membrane Journal
• /
• v.8 no.2
• /
• pp.102-108
• /
• 1998

Permeation behavior of the semiconductor rinsing wastewater containing Si particles was examined by ultrafiltration using the polysulfone plate membrane. The permeation flux was gradually decreased with time. It was due to the growth of cake deposited on the membrane surface and the pore plugging by Si particles. Permeation flux of cross flow type was 1.4 times higher than that of the dead end flow type. Nitrogen back flushing which is the removing method of membrane fouling was superior to the water sweeping. With nitrogen back flushing, the decrease of permeation flux due to the fouling was recovered about 85 % to the initial flux in the flat plate membrane system. The rejection rate of Si particles was about 90 % and the size of Si particle in the permeate was about 70 nm.

• Korean Membrane Journal
• /
• v.3 no.1
• /
• pp.24-31
• /
• 2001

Ultrafiltration membranes base on copoly(amide-imide) derivatives were prepared by the phase inversion method and the factors determining the permeation characteristics of membrane were investigated. The permeation behavior was observed by the relative ratio of permeate flux (J$\_$t/)/pure water flux (J$\_$o/). The characteristics through membrane were measured using aqueous solution of poly(ethyleneglycol) (MW 2.0$\times$10$\^$4/) over a temperature range of 10∼90$\^{C}$. With increasing the operating temperature, the relative ratio of flux became high. All the membranes had good chemical stability. Copoly(amide-imide) membranes having various Permeation properties could be obtained. Further, it was proved that the membrane performances could be determined from the preparation conditions as well as various operating conditions.

• Archives of Pharmacal Research
• /
• v.27 no.11
• /
• pp.1177-1182
• /
• 2004

The effect of poly[2-methacryloyloxyethyl phosphorylcholine] (pMPC) on the skin permeation property was investigated by performing in vitro skin permeation study of a model drug, nicotinic acid (NA). Effect of pMPC polymer in donor solution on skin permeation rates was evaluated using side-by-side diffusion cells. Also, the structural alterations in the stratum corneum (SC), inter-lamellar bilayer (ILB) and dermis layers in pMPC-treated and -untreated skin sections were investigated with transmission electron microscopy (TEM). The permeation profile of NA without pMPC in donor solution showed biphasic mode: initial $1^{st} phase and 2^{nd}$ hydration phase. The sudden, more than 10-fold increase in flux from the initial steady state (43.5 $\mu g/cm^2$/hr) to the $2^{nd}$ hydration phase (457.3 $\mu g/cm^2$/hr) suggests the disruption of skin barrier function due to extensive hydration. The permeation profile of NA with 3% pMPC in the donor solution showed monophasic pattern: the steady state flux (10.9 $\mu g/cm^2$/hr) without abrupt increase of the flux. The degree of NA permeation rate decreased in a concentration-dependent manner of pMPC. TEM of skin equilibrated with water or 2% pMPC for 12 h showed that corneocytes are still cohesive and epidermis is tightly bound to dermis in 2% pMPC-treated skin, while wider separation between corneocytes and focal dilations in inter-cellular spaces were observed in water-treated skin. This result suggests that pMPC could protect the barrier property of the stratum corneum by preventing the disruption of ILB structure caused by extensive skin hydration during skin permeation study.