• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.05a
• /
• pp.232-233
• /
• 2014

Recently, water treatment facility is usually eastablished in underground, and waterproofing and anti-corrosion materials for concrete structures applied water treatment tank is developing in various ways. However, as the limit of research focused on durability improvement of top coating material, it is insufficient to study on the adhesion strength between the concrete surface and primer. Therefore, there is to confirm the adhesion of between concrete surface and the three primers used as anti-corrosion waterproofing materials, and to investigate the properties of adhesion strength according to the condition such as wet codition and water pressure condition of the concrete surface in this study.

• Corrosion Science and Technology
• /
• v.20 no.5
• /
• pp.242-248
• /
• 2021

Unforeseen failures of boilers in power plants may affect the continuation of electricity generation. Main failures in boilers are influenced by the tube material, tube position, boiler service temperature and pressure, and chemical composition of the feed water and coal. This investigation was intended to find answers on the causes and mechanism of failure of the fire-side boiler water-wall tubes, due to perforation and corrosion. The tube conformed to the material requirements in terms of its chemical composition and hardness. Microscopic examination showed ferrite and pearlite indicating no changes in its microstructure due to the temperature variation. SEM test showed a single layer and homogenous film density particularly on the area far from perforation. However, layers of corrosion product were formed on the nearby perforation area. EDX showed that there were Na, Ca, S, and O elements on the failed surface. XRD indicated the presence of Fe₂O₃ oxide. The failure mechanism was identified as a result of significant localized wall thinning of the boiler water wall-tube due to oxidation.

• Tribology and Lubricants
• /
• v.20 no.2
• /
• pp.97-101
• /
• 2004

This paper reports the studies on the wear-corrosion behavior of Al-Mg alloy in various pH environments. In various pH of sea water, corrosion and wear-corrosion loss of Al-Mg alloy were investigated. Also, the polarization test of Al-Mg alloy using potentiostat/galvanostat was carried out. And the rubbed surface of Al-Mg alloy using scanning electron micrographs after wear-corrosion test was examined in various pH values of sea water. The main results are as following : The polarization resistance of Al-Mg alloy in pH 4 solution is higer than that in pH 6.7 solution, and the corrosion current density in pH 4 is controlled than in pH 6.7 solution. The wear-corrosion loss of Al-Mg alloy with lowering pH becomes sensitive. As the oxide product of Al-Mg alloy appears granular structure and exholiation phenomenon, wear-corrosion loss of Al-Mg alloy increases.

• Corrosion Science and Technology
• /
• v.18 no.4
• /
• pp.138-147
• /
• 2019

Pipes and components of the secondary system in the pressurized water reactor (PWR) are mainly comprised of manufactured carbon steel. Thus, the generated carbon steel corrosion products are transported into the steam generator and deposited, thereby deteriorating the integrity of the steam generator. Environmental condition in the secondary system of the PWRs differs across different locations. So, the corrosion rate and types of corrosion products depend on specific locations in the secondary system. In this study, the quantity and chemical compositions of corrosion products generated in various locations that vary in different temperatures and chemistry conditions were investigated. As a result of evaluating the PWR "Unit A" that is in current operation, the amount of corrosion products generated in the section of high temperature feedwater system was identified as the largest source in the secondary system. Major components of corrosion products were iron oxides such as magnetite, hematite, and lepidocrocite.

• Corrosion Science and Technology
• /
• v.23 no.3
• /
• pp.203-214
• /
• 2024

A heat exchanger is a device designed to transfer heat between two or more fluids. In a vehicle's thermal management system, Al heat exchangers play a critical role in controlling and managing heat for efficient and safe operation of the engine and other components. The fluid used to prevent heat exchangers from overheating the engine is mostly tap water. Heat exchange performance can be maintained at sub-zero temperatures using a solution mixed with antifreeze. Although the fluid flowing through the heat exchanger can reduce the temperature inside the engine, it also has various problems such as cavitation corrosion. Cavitation corrosion characteristics in tap water and corrosion characteristics were evaluated in this study when antifreeze was added for test specimens where AA4045 was cladded on the inner surface of AA3003 tubes of a fin-type heat exchanger. The cavitation corrosion resistance of AA3003 was found to be superior to that of AA4045 regardless of the test solution due to higher corrosion resistance and hardness of AA3003 than those of AA4045. The cavitation corrosion rate of Al alloys increased with the addition of antifreeze.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.31 no.4
• /
• pp.413-422
• /
• 1995

Cavitation erosion-corrosion implies damage to materials due to the shock pressure or shock wave that results when bubbles form and collapse at a metal surface within a liquid. If the liquid is corrosive to the material, a condition typically encountered in industry, the component materials may suffer serious damage by a combination of mechanical and electrochemical attack. In this study, the mild steel(SS41) was tested by using the piezoelectric vibrator with 20kHz, 24$\mu$m to cavity generation apparatus. The damage behaviour of vibration cavitation erosion-corrosion and the environment characteristics were investigated in various solutions which are seawater, tap water and distilled water. The main results obtained are as follows; 1) The cavitation erosion-corrosion damage behaviour in the seawater increases to occur at the equal degree on the middle portion and the outside portion of specimen. The distilled water specimen, on other hand, occurs beginning on the outside portion across to the middle portion of specimen. 2) The cavitation erosion-corrosion damage in the tap water of low specific resistance more increases than that in the distilled water of high specific resistance at the initial testing time and more decreases than that in it by the CaCO sub(3) film with testing time. 3) Cavitation erosion-corrosion damage characteristic divides into four regions; incubation region, acceleration region, deceleration region and steady state region.

• Journal of environmental and Sanitary engineering
• /
• v.17 no.1
• /
• pp.57-62
• /
• 2002

Carbon cast iron and Zinc coated steel were the most widely used portable water of supply and distribution Pipeline system. The leaching of red water in portable water could produce sericus environmental sanitary problems. Due to the red water was the most alternative to inner scale of metal pipeline. So this study was conducted the impact of red water on scale products, and was evaluated by the corrosive metal contaminants of 20 fears over. Surface tests, metal surface composition measurements of samples XRF, XRD, and SEM(EDS), analysis were used to investigate the corrosion characteristies of carbon cast iron and Zinc coated steel. As the contaminants of Fe increased the red water of carbon castiron pipe increased due to the scale products amount of $Fe_2O_3$ (Hemite).

• Nuclear Engineering and Technology
• /
• v.54 no.12
• /
• pp.4481-4490
• /
• 2022

In this study, a new rupture disk corrosion test (RDCT) method was developed for real-time detection of stress corrosion cracking (SCC) initiation of Alloy 600 in a primary water environment of pressurized water reactors. In the RDCT method, one side of a disk specimen was exposed to a simulated primary water at high temperature and pressure while the other side was maintained at ambient pressure, inducing a dome-shaped deformation and tensile stress on the specimen. When SCC occurs in the primary water environment, it leads to the specimen rupture or water leakage through the specimen, which can be detected in real-time using a pressure gauge. The tensile stress applied to the disk specimen was calculated using a finite element analysis. The tensile stress was calculated to increase as the specimen thickness decreased. The SCC initiation time of the specimen was evaluated by the RDCT method, from which result it was found that the crack initiation time decreased with the decrease of specimen thickness owing to the increase of applied stress. After the SCC initiation test, many cracks were observed on the specimen surface in an intergranular fracture mode, which is a typical characteristic of SCC in the primary water environment.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.5 s.57
• /
• pp.160-168
• /
• 2009

After steel bar was corroded it removes concrete contaminated, it does steel bar corrosion protection, repairing method and corrosion inhibitor spreading method are difficult to secure corrosion protection performance. Accordingly, in this research before Research and Development to penetrate corrosion inhibitor to high pressure by steel bar position, it measures penetration depth through corrosion inhibitor high pressure penetration experiment and amount of nitrite by position and then it predicts penetration depth in accordance with water-cement ratio, pressure, pressure time and it computed water-cement ratio, pressure, pressure time to be more than 0.6 mol ratio of chloride ion and nitrite to have outstanding corrosion protection performance. As a result of experiment, water-cement ratio gives the biggest influence to penetration of corrosion inhibitor and also the more depth of specimen becomes deep, concentration of penetrated corrosion inhibitor does not equal and becomes low.

• Corrosion Science and Technology
• /
• v.23 no.4
• /
• pp.315-323
• /
• 2024

This work examined pitting corrosion failure of a copper heat-return pipe used in a district heating system. The copper pipe was corroded with a 48% reduction in thickness due to localized corrosion on the inner surface exposed to heating water of 20 ~ 40 ℃. Fe and Si elements as corrosion products were found around pits. Cl element was also observed, which accelerated oxidation of copper inside pits. Cu₂O deposits on the pit's bottom surface decreased the pH inside the pit. X-ray diffraction analysis revealed hematite, cuprite, malachite and brochantite as corrosion products. Chemical analysis demonstrated that Fe and Si elements did not exist in the copper, supply water, or heating water, indicating that Fe and Si species might have entered into the pipe from the exterior. These results indicated that pits were initiated due to ion concentration gradient near Fe and Si species. Moreover, the interior of pits had lower pH due to Cl^- concentration and Cu₂O reactions, which accelerated the pit's growth and led to formation of pinholes. Additionally, we confirmed that the type of pitting corrosion was a complex combination of types I and II based on the HCO₃^-/SO₄^2- ratio, pH, temperature, and corrosion products.