• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.2
• /
• pp.160-167
• /
• 2017

The purpose of this study is to identify the possibility of developing the 100% Recycled-resources Absorbent-Pervious Alkali-activated Blocks using both the alkalli-binder and the recycled aggregate. In addition, It established a test method such as Void ratio, compressive strength, coefficient permeability, absorption, and evaporation. As a result, an alkali-activated using recycled aggregate block was able to manufacture an 24 MPa class absorbent-pervious blocks with a liquid type sodium silicate and early high temperature curing. In this case, water-holding capacity, absorption and relative absorption were more effective than the natural aggregates. In conclusion, Absorbent-pervious alkali-activated Block Using recycled aggregate has a surface temperature reducing effect of approximately 10 % compared to ordinary concrete block.

• Journal of the Korea Concrete Institute
• /
• v.14 no.2
• /
• pp.249-256
• /
• 2002

High performance concrete is prone to large autogenous shrinkage due to its low water to binder ratio (W/B). The autogenous shrinkage of concrete is caused by self-desiccation as a result of water consumption by the hydration of cement. In this study, the autogenous shrinkage of high performance concrete with and without fly ash was Investigated. The properties of fresh concrete, slump loss, air content, and flowability as well as the mechanical properties, compressive strength and modulus of elasticity, were also measured. Test results was shown that the autogenous shrinkage of concrete increased as the W/B decreased. For the same W/B, the autogenous shrinkage of high strength concrete with fly ash was considerably reduced although the development of its compressive strength was delayed at early ages. Furthermore, the autogenous shrinkage and compressive strength of high strength concrete were more rapidly developed than those of normal strength concrete. It was concluded that fly ash could improve the quality of high strength concrete with respect to the workability and autogenous shrinkage.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.9 no.2
• /
• pp.1-9
• /
• 2009

Water binder ratio combine high-performance concrete shrinkage of less than 0.4 to determine the transformation to a total shrinkage of water to move outside and internal consumption of moisture due to drying shrinkage and autogenous shrinkage, and then, the relative humidity changes and strain to be approached by surface physics describe the relationship between self-desiccation and autogenous shrinkage was set. To verify the self-desiccation in the humidity shrinkage and humidity measurements performed, and the research model, Tazawa, CEB-FIP model than to let the measure and the most similar results in this study based on self-desiccation model, autogenous shrinkage didn't represent the linear shrinkage by the drying shrinkage of the external moving but exponential relationships, unlike with the nature and rapid in the early age properly describes the attributes in shrinkage could see. After this research to move moisture and to reflect the shrinkage model, temperature, moisture transfer, strain analysis by multi-physics model is very similar to the results of mock-up specimen measurements performed for this research, the value measured by the internal consumption of moisture, therefore self-desiccation and a multi-physics model considering autogenous shrinkage might be relevant.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.211-218
• /
• 2018

This study examined the reliability and revision necessity of concrete standard specifications based on the comparisons with test data obtained by using domestic artificial lightweight aggregates and the contents specified in different foreign specifications including ACI 211.2, ACI 213, ACI 301, JASS 5 and CEB-FIP. To achieve the continuous particle distribution of domestic fine lightweight aggregates, the partial addition of natural sand with the maximum size of 2.5mm was required. To control the segregation and excessive bleeding in the fresh lightweight concrete, the current limitations on the water-to-binder ratio and unit water content need to be modified using lower values. In particular, a rational mixture proportion approach of lightweight concrete needs to be established for the targeted requirements of initial slump, 28-day compressive strength, air content and dry unit weight. Ultimately, significant revision of the concrete standard specifications is required considering the characteristics of domestic artificial lightweight aggregates.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.4
• /
• pp.59-67
• /
• 2016

Concrete is a very useful construction material for the sealing disposal of hazardous substances. In general, mass concrete is applied to these structures. And, the mineral admixtures are recommended for the long term performance. Calcium leaching could be happened due to the contact with pure water in underground structures. Thus, it is needed to evaluate the resistance of calcium leaching for concrete mixed with mineral admixtures. From the test results, the mineral admixtures are effective to the improvement of long term compressive strength and chloride diffusion coefficient in concrete members. When calcium leaching is happened, however, the reduction of compressive strength and chloride penetration resistance is severe than OPC case, the micro pore distribution is adversely affected. Consequently, when the mineral admixtures are applied to underground structures which is exposed to calcium leaching environment, it is desirable to reduce water-to-binder ratio, to expose after the sufficient pozolanic reaction, and to use BFS than FA.

• Advances in concrete construction
• /
• v.3 no.3
• /
• pp.203-221
• /
• 2015

This paper presents the results of a study undertaken to investigate the enhancement of concrete strength using Silpozz and Rice Husk Ash (RHA). The total percentage of supplementary cementitious material (SCM) substituted in this study was 20%. Six different concrete mixes were prepared such as without replacement of cement with silpozz and RHA (0% silpozz and 0% RHA) is treated as conventional concrete, whereas in other five concrete mixes cement was replaced by 20% of silpozz and RHA as (0% silpozz and 20% RHA), (5% silpozz and 15% RHA), (10% silpozz and 10% RHA), (15% silpozz and 5% RHA) and (20% silpozz and 0% RHA) with decreasing water-binder (w/b) ratio i.e. 0.375, 0.325 and 0.275 and increasing super plasticiser dose. New generation polycarboxylate base water reducing admixture i.e., Cera Hyperplast XR-W40 was used in this study. The results of this research indicate that as w/b decreases, super plasticiser dose need to be increased so as to increase the workability of concrete. The effects of replacing cement by silpozz and RHA on the compressive strength, split tensile strength and flexural strength were evaluated. The concrete mixture with different combination of silpozz and RHA gives higher strength as compared to control specimen for all w/b ratios and also observed that the early age strength of concrete is more as compared to the later age strength. It is also observed that the strength enhancement of concrete mixture prepared with the combination of cement, silpozz and RHA is higher as compared to the concrete mixture prepared with cement and silpozz or cement and RHA.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.35 no.7
• /
• pp.179-186
• /
• 2019

Air lime is a traditional building material of Korea. It had been used in roofs, walls, floors and masonry joints of traditional buildings until the advent of Portland cement. However, due to its low strength and durability, the lime is currently avoided as a repair or restoration material for the preservation of architectural heritage. Furthermore, due to the current practice of using hydraulic materials such as Portland cement, understanding of the material characteristics of air lime is very poor in practice. In this context, this study intended to improve the mechanical properties of the air lime mortar by reducing water contents, and also the carbonation reaction of the mortar was quantitatively evaluated to clearly understand the characteristics of this material. Accordingly, air lime mortar with a water-to-binder ratio of 0.4 was manufactured using polycarboxylate-type superplasticizer. During the 7 days of sealed curing period, the mortar did not harden at all. In other words, there was no reaction required for hardening since it could not absorb carbon dioxide from the atmosphere. However, once exposed to the air, the compressive strength of the mortar began to rapidly increase due to the carbonation reaction, and the strength increased steadily until the 28th day; after then, the strength development was significantly slowed down. On the 28th day, the mortar exhibit a compressive strength of about 5 MPa, which is equivalent to the European standard regarding strength of hydraulic lime used for preservation of architectural heritage.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.1
• /
• pp.1-12
• /
• 2021

The present study proposes the modified-stoichiometric model for describing hydration of sodium silicate-based alkaliactivated slag(AAS), and compares the results with the thermodynamic modelling-based calculations. The proposed model is based on Chen and Brouwers(2007a) model with updated database as reported in recent studies. In addition, the calculated results for AAS are compared to those for hydrated portland cement. The maximum difference between the proposed model and the thermodynamic calculation for AAS was at most 20%, and the effects of water-to-binder ratio and activator dosages were identically described by both approaches. In particular, the amount of non-evaporable water was within 10% difference, and was in excellent agreement with the experimental results. Nevertheless, notable deviation was observed for the chemical shrinkage, which is largely dependent on the volume of hydrates and pores.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.3
• /
• pp.103-110
• /
• 2019

Damage to the pavement system due to various causes will be required rapid repair work for reopening the vehicle traffic. The magnesium oxide phosphate composite(MPC) has a short curing time and is capable of early compressive strength development, is suitable for rapid repair materials. The aim of this study was to evaluate the hardening and compressive strength characteristics of MPC according to the water-binder (W / B) ratio and magnesium-phosphate(M / P) ratio in order to develop repair materials consisted with light burned magnesia and potassium dihydrogen phosphate. In order to ensure the workability in the field application, the difference of mechanical properties according to standard sand and ordinary sand and performance of retards were evaluated. The mix proportion with W/B ratio was about 35% and the M/P ratio was about 1.0 ~ 1.2 has a superior perfomance with strength and hardening condition. Especially, the strength of composite at only 1 day curing with W/B ratio of 0.35 and the M/P ratio of 1.2 was shown the higher than 25.0 MPa. Boric acid as a retarder was found to be suitable for ensuring the working time, and the purity of magnesium oxide was about 90 ~ 95%, which is effective for ensuring curing time and strength.

• Applied Chemistry for Engineering
• /
• v.21 no.2
• /
• pp.217-223
• /
• 2010

In general, fiber-reinforced plastics (FRP) wastes are simply buried or burned. Landfill brings about a permanent contamination of soil due to the inability of FRP to decompose and incineration causes an issue of generating toxic gases and dusts. There have been several ways to treat the FRP wastes such as landfill, incineration, chemical recycling, material recycling and the utilization of energy from combustion. Most methods excluding material recycling are known to have critical limitations in economic, technical and environmental manners. However it is known that material recycling is most desirable among the methods handling FRP wastes. In this study, to investigate the purpose of feasibility of material recycling, various bulk molding compound (BMC) specimens were prepared with the various contents of unsaturated polyester resin binder (25, 30, 35 wt%) and the various replacement ratios of FRP wastes powder (0, 25, 50, 75, 100 wt%) substituted for filler. To evaluate the physical properties BMC specimens, various tests such as tensile strength, flexural strength, impact strength, hot water resistance and SEM imaging were conducted. As a results, mechanical strengths decreased with an increase of replacement ratio of FRP waste powder and physical properties of BMC specimens were deteriorated in the hot water resistance. The fluidity of BMC with more than 50 wt% of the replacement ratio of FRP wastes powder decreased remarkably, causing a problem in the BMC composite.