• Elastomers and Composites
• /
• v.51 no.1
• /
• pp.31-37
• /
• 2016

In this study, we studied the photocatalytic functionality such as deodorant, antibacterial, antistatic of polyester fabrics treated with visible-light responsive photocatalyst. According to UV/visible spectrometry result, the UV-visible peak of visible-light responsive photocatalyst was found to be red shift at 420 nm sensitive in the visible light region. Also, the deodorizing and antimicrobial performance were shown to be retained more than 99% both before washing and even after 25 times washing. According to washing durability of polyester fabrics treated with visible-light responsive photocatalyst, the reduction effects for gas such as ammonia, trimethylamine, formaldehyde and toluene after 25 times washing appeared to be retained as much as before washing. At both before washing and after 25 times washing, antistatic property showed frictional voltage of approximately 250V.

• Elastomers and Composites
• /
• v.49 no.1
• /
• pp.53-58
• /
• 2014

In this study, characteristics of visible-light responsive photocatalyst Weltouch, especially VOCs reduction of visible-light responsive photocatalyst coated nylon/polyester composite fiber for vehicle interior parts and materials were evaluated. Visible-light responsive photocatalyst Weltouch was observed for both anatase phase and rutile phase. It is activated by light longer than 420nm. VOCs and formaldehyde generated from visible-light responsive photocatalyst treated nylon/polyester composite fiber were reduced confirmly. Visible-light responsive photocatalyst was firmly attached to the surface of nylon/polyester composite fiber without elimination even after 25 times repeated washing. And washing durability of nylon/polyester composite fiber confirmed the excellence that reduction effects of VOCs after repeated washing has appeared as much as before washing.

• Elastomers and Composites
• /
• v.48 no.3
• /
• pp.209-215
• /
• 2013

On this study, visible-light responsive photocatalyst prepared by sol-gel method was evaluated the effect of the reduction of volatile organic compounds (VOCs) occurred in vehicle interior and its property was examined. According to UV/visible result, visible-light responsive photocatalyst was found that the UV-visible peak is red shift at 420nm, is sensitive in the visible light region. With vehicle interior parts and materials coated visible-light responsive photocatalyst, VOCs was measured by GC/MS. Measuring the VOCs generated from vehicle interior parts and materials, the reduction of VOCs was confirmed.

• Elastomers and Composites
• /
• v.48 no.3
• /
• pp.221-224
• /
• 2013

In this study, VOC analysis method of vehicle interior materials and parts treated to visible-light responsive photocatalyst was tested by sample bag filled with air instead of nitrogen. As a result, when analyzed VOC of vehicle interior materials and parts, sample bag filled with the nitrogen was not confirmed of effect reducing VOCs and formaldehyde. However, VOCs and formaldehyde of sample bag that was filled with air instead of nitrogen, decreased significantly. Reaction effect for visible light-responsive photocatalyst was confirmed that sample bag of vehicle interior materials and parts should be filled with air instead of nitrogen.

• Elastomers and Composites
• /
• v.51 no.3
• /
• pp.226-232
• /
• 2016

We studied the photocatalytic functionality such as deodorant, antibacterial, fine dust collection efficiency of polyester-based non-woven fabric filter treated with self-actuated photocatalyst. According to UV/visible result, the UV-visible peak of visible-light responsive photocatalyst was found to be red shift at 420 nm sensitive in the visible light region. The deodorizing performance was shown to be reduced more than 80% even without dark conditions. Fine dust particles collection efficiency was shown to be excellent at the size of not only $2.5{\mu}m{\sim}10.0{\mu}m$ but also less than $2.5{\mu}m$. Also antimicrobial and antifungus was shown to be reduced more than 99.9%.

• Korean Journal of Materials Research
• /
• v.30 no.12
• /
• pp.641-649
• /
• 2020

A facile microwave assisted solvothermal process is designed for fabricating SnS nanoparticles decorated on graphene nanosheet, which used as visible light driven photocatalyst. Some typical characterization techniques such as XRD, FT-IR, SEM with EDX analysis, and TEM and BET analysis are used to analyse the physical characteristics of as-prepared samples. Spherical SnS nanoparticles are uniformly dispersed on the surface of graphene nanosheet due to ammonia, which can prevent the aggregation of graphene oxide. Meanwhile, microwave radiation provides fast energy that promotes the formation of spherical SnS nanoparticles within a short time. The visible light photocatalytic activity of as-prepared SnS-GR nanocomposites is analysed through photodegradation efficiency of methylene blue with high concentration. According to the higher photocatalytic property, the as-prepared SnS-GR nanocomposites can be expected to be an efficient visible light driven photocatalyst. After five cycles for decolorization, the rate decreases from 87 % to 78 % (about 9 %). It is obvious that the photocatalytic activity of SnS-GR nanocomposite has good repeatability.

• Particle and aerosol research
• /
• v.6 no.4
• /
• pp.165-172
• /
• 2010

Titania is widely used as an effective photocatalyst for the photodegradation of environmental pollutants in air. In this study, novel N-doped $ZrO_2/TiO_2$ photocatalysts were synthesized via sol-gel method and characterized by UV-Vis spectrophotometer, transmission electron microscope, and X-ray diffractometer. N-doped $ZrO_2/TiO_2$ photocatalysts were nano-sized with an average particle size of about 20 nm. The XRD pattern of N-doped $ZrO_2/TiO_2$ photocatalysts showed both anatase and rutile phases. The photocatalytic activity of N-doped $ZrO_2/TiO_2$ photocatalysts was evaluated by degradation of NO under UV and visible light irradiation at various parameters such as amount of photocatalyst, concentration of NO, and intensity of light. The photocatalytic activity of N-doped $ZrO_2/TiO_2$ photocatalysts was effective for the enhancement of the degradation of NO and higher than that of $TiO_2$ photocatlysts under UV and visible light irradiation.

• Journal of the Korean Chemical Society
• /
• v.61 no.4
• /
• pp.168-178
• /
• 2017

$La/TiO_2$ - graphene composites were synthesized in this study, and applied to the photocatalytic degradation of Rhodamine B (RhB) under UV-visible light irradiation. X-ray diffraction (XRD), surface analysis, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM), and Transmission electron microscopy (TEM) analysis demonstrated that $La/TiO_2$ nanoparticles were well distributed on the surface of graphene, and formed the heterostructure of $La/TiO_2$-graphene. Compared to the pure $TiO_2$, $La/TiO_2$-graphene composites displayed much higher photocatalytic activities in RhB degradation under UV-visible light irradiation. The photocatalytic data of $La/TiO_2$-graphene composites exhibit extended light absorption in the visible light region, and possess better charge separation capability than that of pure $TiO_2$. The high photocatalytic activity was attributed to the composite's high adsorptivity, extended light absorption, and increased charge separation efficiency, due to the excellent electrical properties of graphene, and the large surface contact between graphene and $La/TiO_2$ nanoparticles.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.130.1-130.1
• /
• 2013

We made attempts to improve photocatalytic activity of $TiO_2$ nanoparticles under visible light exposure by combining two additional treatments. N-doping of $TiO_2$ by ammonia gas treatment at $600^{\circ}C$ increased absorbance of visible light. By coating thin film of polydimethylsiloxane (PDMS), and subsequent vacuum-annealing at $800^{\circ}C$, $TiO_2$, became more hydrophilic, thereby enhancing photocatalytic activity of $TiO_2$. Four types of $TiO_2$ samples were prepared, bare-$TiO_2$, hydrophilic-modified $TiO_2$ ($h-PDMS/TiO_2$), N-doped $TiO_2$ ($N/TiO_2$) and hydrophilic-modified and N-doped $TiO_2$ ($h-PDMS/N/TiO_2$). Adsorption capability was evaluated under dark condition and photocatalytic activity of $TiO_2$ was evaluated by photodegradation of MB under blue LED (400 nm< ${\lambda}$) irradiation. N-doping on $TiO_2$ was characterized using XPS and hydrophilic modification of $TiO_2$ surface was analyzed by FT-IR spectrometer. It was found that N-doping and hydrophilic modification both had positive effect on enhancing adsorption capability and photocatalytic activity of $TiO_2$ at the same time. Particularly, N-doping enhanced visible light absorption of $TiO_2$, whereas hydrophilic surface modification increased MB adsorption capacity. By combining these two strategies, photocatalytic acitivity under visible light irradiation became the sum of individual effects of N-doping and hydrophilic modification.

• Applied Chemistry for Engineering
• /
• v.19 no.1
• /
• pp.1-16
• /
• 2008

Titanium dioxide ($TiO_2$) is one of the most researched semiconductor oxides that has revolutionised technologies in the field of environmental purification and energy generation. It has found extensive applications in heterogenous photocatalysis for removing organic pollutants from air and water and also in hydrogen production from photocatalytic water-splitting. Its use is popular because of its low cost, low toxicity, high chemical and thermal stability. But one of the critical limitations of $TiO_2$ as photocatalyst is its poor response to visible light. Several attempts have been made to modify the surface and electronic structures of $TiO_2$ to enhance its activity in the visible light region such as noble metal deposition, metal ion loading, cationic and anionic doping and sensitisation. Most of the results improved photocatalytic performance under visible light irradiation. This paper attempts to review and update some of the information on the $TiO_2$ photocatalytic technology and its accomplishment towards visible light region.