• Journal of Biomedical Engineering Research
• /
• v.25 no.2
• /
• pp.157-163
• /
• 2004

Nitrogen ion implantation and ion plating techniques were applied for improvement of the wear resistance of metallic implant materials. In this work, the wear dissolution behaviour of a nitrogen ion implanted super stainless steel (S.S.S, 22Cr-20Ni-6Mo-0.25N) was compared with those of S.S.S, 316L SS and TiN coated 316L SS. The amounts of Cr and Ni ions worn-out from the specimens were Investigated using an electrothermal atomic absorption spectrometry. Furthermore, the Ti(Grade 2) disks were coated with TiN, ZrN and TiCN by use of low temperature arc vapor deposition and the wear resistance of the coating layers was compared with that of titanium. The chemical compositions of the nitrogen ion implanted and nitride coated layers were examined with a scanting auger electron spectroscopy. It wat observed that the metal ions released from the nitrogen ion implanted S.S.S surface were significantly reduced. From the results obtained, it was shown that the nitrogen ion implanted zone obtained with 100 KeV ion energy was easily removed within 200,000 revolutions from a wear dissolution testing under a similar load condition when applied to artificial hip joint. The remarkable improvement in wear resistance weir confirmed by the nitrides coated Ti materials and the wear properties differ greatly according to the chemical composition of the coating layers. for specimens with the same coating thickness of about 3$\mu\textrm{m}$, TiCN coated Ti showed the highest wear resistance. However, after removing the coating layers, the wear rates of all nitrides coated Ti reverted to their normal rates of below 10,000 revolutions from Ti-disk-on-disk wear testing under the same load condition. From the results obtained, it is suggested that the insufficient depth of the 100 Kel N$\^$＋/ ion implanted zone and of the nitrides coated layers of 3$\mu\textrm{m}$ are subject to restriction when used as frictional parts of load bearing implants.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.134-135
• /
• 2011

양자점은 전자와 양공을 3차원으로 속박 시키므로 기존의 bulk나 양자우물보다 양자점을 이용한 레이저 다이오드의 경우 낮은 문턱 전류, 높은 미분이득 및 온도 안전성의 장점이 있을 거라 기대되고 있다. 그러나, 양자점은 낮은 areal coverage 때문에 높은 속박효율을 얻지 못하고 있다. 이러한 양자점의 문제점을 해결하기 위해 양자점을 양자우물 안에 성장시켜 운반자들의 포획을 향상시키는 방법들이 연구되고 있다. 양자우물 안에 양자점을 넣으면 양자우물이 운반자들의 포획을 증가 시키고, 열적 방출도 억제하여 온도 안정성이 향상 되는 것으로 알려져 있다. 광통신 대역의 1.3 ${\mu}m$ 경우, GaAs계를 이용하여 InAs 양자점을 strained InGaAs 박막을 우물층으로 한 dot-in-a-well 구조의 연구는 몇몇 보고된 바 있다. 그러나 InP계를 사용하는 1.55 ${\mu}m$ 대역에서 dot-in-a-well구조의 연구는 아직 미미하다. 본 연구에서는 유기 금속 화학 증착법(metal organic chemical vapor deposition)을 이용하여 InP 기판 위에 InAs 양자점을 자발성장법으로 성장하였으며 dot-in-a-well 구조에서 우물층으로 1.35 ${\mu}m$ 파장의 $In_{0.69}Ga_{0.31}As_{0.67}P_{0.33}$ (1.35Q)를, 장벽층으로는 1.1 ${\mu}m$ 파장의 $In_{0.85}Ga_{0.15}As_{0.32}P_{0.68}$(1.1Q)를 사용하였다. 양자우물층과 장벽층은 모두 InP 기판과 격자가 일치하는 조건으로 성장하였다. III족 원료로는 trimethylindium (TMI)와 trimethylgalium (TMGa)을 사용하였으며 V족 원료 가스로는 $PH_3$ 100%, $AsH_3$ 100%를, carrier gas로는 $H_2$를 사용하였다. InP buffer층의 성장 온도는 640$^{\circ}C$이며 양자점 성장 온도는 520$^{\circ}C$이다. 양자점 형성은 원자력간 현미경(Atomic force microscopy)를 이용하여 확인하였으며, 박막의 결정성은 쌍결정 회절분석(Double crystal x-ray deffractometry)를 이용하여 확인하였다. 확인된 성장 조건을 이용하여 양자점 시료를 성장하였으며 광여기분광법(Photoluminescence)을 이용하여 광특성을 분석하였다. Fig. 1은 dot in a barrier 와 dot-in-a-well 시료의 성장구조이다. Fig. 1(a)는 일반적인 dot-in-a-barrier 구조로 InP buffer층을 성장하고 1.1Q를 100 nm 성장한 후 양자점을 성장하였다. 그 후 1.1Q 100 nm와 InP 100 nm로 capping하였다. Fig. 1(b)는 dot-in-a-well 구조로 InP buffer층을 성장하고 1.1Q를 100 nm 성장 후 1.35Q 우물층을 4 nm 성장하였다. 그 위에 InAs 양자점을 성장하였다. 그 후에 1.35Q 우물층을 4 nm 성장하고 1.1Q 100 nm와 InP 100 nm로 capping하였다. Fig. 2는 dot-in-a-barrier 시료와 dot-in-a-well 시료의 상온 PL data이다. Dot-in-a-barrier 시료의 PL 파장은 1544 nm이며 반치폭은 79.70 meV이다. Dot-in-a-well 시료의 파장은 1546 nm이며 반치폭은 70.80 meV이다. 두 시료의 PL 파장 변화는 없으며, 반치폭은 dot-in-a-well 시료가 8.9 meV 감소하였다. Dot-in-a-well 시료의 PL peak 강도는 57% 증가하였으며 적분강도(integration intensity)는 45%가 증가하였다. PL 데이터에서 높은 에너지의 반치폭 변화는 없으며 낮은 에너지의 반치폭은 8 meV 감소하였다. 적분강도 증가에서 dot-in-a-well 구조가 dot-in-a-barrier 구조보다 전자-양공의 재결합이 증가한다는 것을 알 수 있으며, 반치폭 변화로부터 특히 높은 에너지를 갖는 작은 양자점에서의 재결합이 증가 된 것을 알 수 있다. 이는 양자우물이 장벽보다 전자-양공의 구속력을 증가시키기 때문에 양자점에 전자와 양공의 공급을 증가시키기 때문이다. 따라서 낮은 에너지를 가지는 양자점을 모두 채우고 높은 에너지를 가지는 양자점까지 채우게 되므로, 높은 에너지를 가지는 양자점에서의 전자-양공 재결합이 증가되었기 때문이다. 뿐만 아니라 파장 변화 없이 PL peak 강도와 적분강도가 증가하고 낮은 에너지 쪽의 반치폭이 감소한 것으로부터 에너지가 낮은 양자점보다는 에너지가 높은 양자점에서의 전자-양공 재결합율이 급증하였음을 알 수 있다. 우리는 이와 같은 연구에서 InP계를 이용해 1.55 ${\mu}m$에서도 dot in a well구조를 성장 하여 더 좋은 특성을 낼 수 있으며 앞으로 많은 연구가 필요할 것이라 생각한다.

• Journal of the Korean Magnetics Society
• /
• v.19 no.3
• /
• pp.89-93
• /
• 2009

Amorphous $Ge_{1-x}Mn_x$ semiconductor thin films grown by low temperature vapor deposition were annealed, and their electrical and magnetic properties have been studied. The amorphous thin films were $1,000{\sim}5,000\;{\AA}$ thick. Amorphous $Ge_{1-x}Mn_x$ thin films were annealed at $300^{\circ}C$, $400^{\circ}C$, $500^{\circ}C$, $600^{\circ}C$ and $700^{\circ}C$ for 3 minutes in high vacuum chamber. X-ray diffraction analysis reveals that as-grown $Ge_{1-x}Mn_x$ semiconductor thin films are amorphous and are crystallized by annealing. Crystallization temperature of amorphous $Ge_{1-x}Mn_x$ semiconductor thin films varies with Mn concentration. Amorphous $Ge_{1-x}Mn_x$ thin films have p-type carriers and the carrier type is not changed during annealing, but the electrical resistivity increases with annealing temperature. Magnetization characteristics show that the as-grown amorphous $Ge_{1-x}Mn_x$ thin films are ferromagnetic and the Curie temperatures are around 130 K. Curie temperature and saturation magnetization of annealed $Ge_{1-x}Mn_x$ thin films increase with annealing temperature. Magnetization behavior and X-ray analysis implies that formation of ferromagnetic $Ge_3Mn_5$ phase causes the change of magnetic and electrical properties of annealed $Ge_{1-x}Mn_x$ thin films.

• Journal of the Korean Vacuum Society
• /
• v.17 no.6
• /
• pp.528-537
• /
• 2008

60 nm and 20 nm thick hydrogenated amorphous silicon(a-Si:H) layers were deposited on 200 nm $SiO_2$/single-Si substrates by inductively coupled plasma chemical vapor deposition(ICP-CVD). Subsequently, 30 nm-Ni layers were deposited by an e-beam evaporator. Finally, 30 nm-Ni/(60 nm and 20 nm) a-Si:H/200 nm-$SiO_2$/single-Si structures were prepared. The prepared samples were annealed by rapid thermal annealing(RTA) from $200^{\circ}C$ to $500^{\circ}C$ in $50^{\circ}C$ increments for 40 sec. A four-point tester, high resolution X-ray diffraction(HRXRD), field emission scanning electron microscopy(FE-SEM), transmission electron microscopy(TEM), and scanning probe microscopy(SPM) were used to examine the sheet resistance, phase transformation, in-plane microstructure, cross-sectional microstructure, and surface roughness, respectively. The nickel silicide from the 60 nm a-Si:H substrate showed low sheet resistance from $400^{\circ}C$ which is compatible for low temperature processing. The nickel silicide from 20 nm a-Si:H substrate showed low resistance from $300^{\circ}C$. Through HRXRD analysis, the phase transformation occurred with silicidation temperature without a-Si:H layer thickness dependence. With the result of FE-SEM and TEM, the nickel silicides from 60 nm a-Si:H substrate showed the microstructure of 60 nm-thick silicide layers with the residual silicon regime, while the ones from 20 nm a-Si:H formed 20 nm-thick uniform silicide layers. In case of SPM, the RMS value of nickel silicide layers increased as the silicidation temperature increased. Especially, the nickel silicide from 20 nm a-Si:H substrate showed the lowest RMS value of 0.75 at $300^{\circ}C$.

• Economic and Environmental Geology
• /
• v.54 no.1
• /
• pp.49-60
• /
• 2021

The Geumhwa Au-Ag deposit is located within the Cretaceous Gyeongsang basin. Mineral paragenesis can be divided into two stages (stage I and II) by major tectonic fracturing. Stage II is economically barren. Stage I, at which the precipitation of major ore minerals occurred, is further divided into three substages(early, middle and late) with paragenetic time based on minor fractures and discernible mineral assemblages: early substage, marked by deposition of pyrite with minor wolframite; middle substage, characterized by introduction of electrum and base-metal sulfides with Cu-As and/or Cu-Sb sulfosalts; late substage, marked by hematite and Bi-sulfosalts with secondary minerals. Changes in vein mineralogy reflect decreases in temperature and sulfur fugacity with a concomitant increase in oxygen fugacity. Fluid inclusion data indicate progressive decreases in temperature and salinity within each substage with increasing paragenetic time. During the early portion of stage I, high-temperature (≥410℃), high-salinity fluids (up to ≈44 equiv. wt. % NaCl) formed by condensation during decompression of a magmatic vapor phase. During waning of early substage, high-temperature, high-salinity fluids gave way to progressively cooler, more dilute fluids associated with main Au-Ag mineralization (middle) and finally to ≈180℃ and ≥0.7 equiv. wt. % NaCl fluids associated with hematite and sulfosalts (± secondary) mineralization (late substage). These trends are interpreted to indicate progressive mixing of high- and medium to low-salinity hydrothermal fluids with cooler, more dilute, oxidizing meteoric waters. The Geumhwa Au-Ag deposit may represent a vein-type system transitional between porphyry-type and epithermal-type.