• Corrosion Science and Technology
• /
• v.22 no.3
• /
• pp.193-200
• /
• 2023

Titanium alloy (grade-4) is commonly used in industrial and medical applications. To improve its corrosion resistance and biocompatibility for medical use, it is necessary to form a titanium oxide film. In this study, the morphology of the oxide film formed by anodizing Ti-grade 4 using different electrolytes was analyzed. Wetting properties before and after surface modification with SAM coating were also observed. Electrolytes used were categorized as A, B, and C. Electrolyte A consisted of 0.3 M oxalic acid and ethylene glycol. Electrolyte B consisted of 0.1 M NH₄F and 0.1 M H₂O in ethylene glycol. Electrolyte C consisted of 0.07 M NH₄F and 1 M H₂O in ethylene glycol. Samples B and C exhibited a porous structure, while sample A formed a thickest oxide film with a droplet-like structure. AFM analysis and contact angle measurements showed that sample A with the highest roughness exhibited the best hydrophilicity. After surface modification with SAM coating, it displayed superior hydrophobicity. Despite having the thickest oxide film, sample A showed the lowest insulation resistance due to its irregular structure. On the other hand, sample C with a thick and regular porous oxide film demonstrated the highest insulation resistance.

• Applied Microscopy
• /
• v.52
• /
• pp.3.1-3.8
• /
• 2022

Our purpose in this study is to analyze the microstructural characteristics and constituent elements of inorganic substances added to the yellow ink and red ink pigments used in permanent makeup. We observed the microstructural properties of inorganic pigments added to the ink using a scanning electron microscopy (SEM) and analyzed the constituent elements of the inorganic pigment particles using an energy dispersive X-ray spectroscopy (EDX). In red wine-colored ink, cubic titanium dioxide with a diameter of 110 to 200 nm was the major component, and rod-shaped iron oxide was rarely observed. Most of the ingredients of taupe yellow ink were rod-shaped yellow iron oxide, and a small amount of cubic titanium dioxide was observed. Red wine-colored ink and taupe yellow ink contained lumps composed of titanium dioxide particles. In red wine-colored ink, lumps were formed by agglomeration. However, we observed that the surface of the lump composed of titanium dioxide in the taupe yellow ink had a smooth surface caused by external physical compression. The titanium dioxide particle mass which found in taupe yellow ink in this study is an artificial product. When this mass accumulates in the dermis, it may cause a color mismatch. Therefore, permanent makeup using fine pigments should be free of foreign substances that may cause trouble in the skin. In addition, there is a need to improve the quality of the ink so that the required color can be safe and long lasting in the dermis.

• Korean Journal of Materials Research
• /
• v.11 no.10
• /
• pp.851-858
• /
• 2001

One of the important phase of black titanium oxide is $Ti_4O_7$ which has the excellent properties such as the greatest electrical conductivity among the titanium oxides, chemical resistance against acidic and alkalic conditions and electro-wave absorption etc., so it has been considered as a promising material to be used widely all over the parts of industries. In this study, $Ti_4O_7$ phase was successfully synthesized by the reaction of TiO$_2$/ Mg system. With the change of the mole of TiO$_2$to Mg, the most excellent blackness was appeared in the 3.5 mole which was the smaller amount than the stoichiometric 4.0 mole. In addition, we found that the blackness decreased as the mole ratio of reactent increased. With decreasing particle size of magnesium, blackness of titanium oxide increased. The reaction property was changed with the compaction pressure, and optimum pressure was found to be 10 MPa. At 55$0^{\circ}C$ of reduction temperature, the blackness increased as the reaction time increased. The blackness of synthesized black titanium oxide was 14 to 18, and the average particle size was 0.2 $\mu\textrm{m}$.

• Journal of Biosystems Engineering
• /
• v.35 no.6
• /
• pp.420-425
• /
• 2010

We produced a basic system of sterilization of nutrient solution based on the characteristics of coated filter with the visible light-reactive titanium oxide photocatalyst according to the findings of the first stage. We developed a model system with a proper number and arrangement of filter elements, the visible light-reactive titanium oxide photocatalyst according to findings from the basic performance test. Main results of this study were as followers; The ceramic filters showed the best performance of sterilization of nutrient solution. The visible light-reactive titanium oxide photocatalyst sterilized more effectively the nutrient solution under the sunlight than UV light. The sterilization performance by passing repeatedly through a few filter was more efficient than that by treating simultaneously with a large number of filters. The filter with 15ppi in pore size, 20 mm in thickness, and 3 layers in titanium oxide coating was desirable in the intensity and sterilization performance.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.372-372
• /
• 2007

Titanium oxide nanotube arrays were fabricated by the anodization of pure titanium thin film deposited at $500^{\circ}C$ on silicon substrates. The titania nanotubes were grown by anodization in nonaqueous-base electrolytes at different potentials between 5 V and 30 V. $TiO_2$ nanotube array with a small pore diameter of 40 nm and long titanium oxide layer of $4\;{\mu}m$ was obtained. The $TiO_2$ nanotube array was used as a porous electrode for quartz crystal microbalance (QCM). Nanoporous morphology of electrode will increase the sensitivity of microbalance.

• Journal of Technologic Dentistry
• /
• v.32 no.4
• /
• pp.297-305
• /
• 2010

Purpose: The purpose of this study was to observe the change of metal-mold reaction and surface roughness in titanium casting specimens for phosphate-silica alumina bonded investment with mold temperatures. Methods: The metal-phosphate silica alumina bonded mold interface reaction and surface roughness of titanium casting specimens according to mold temperatures were investigated. The Specimens were analysed by scanning electron microscopy and surface roughness tester. Results: The oxidation behavior indicated by the growth of oxide thickness. The titanium-oxide layer were consisted two layer of a porous external and a dense internal one. The reaction layer and surface roughness increased with increasing investment material temperature. Conclusion: In this work, The most suitable mold temperature in casting of pure titanium was $200^{\circ}C$.

• Journal of Electrical Engineering and Technology
• /
• v.6 no.5
• /
• pp.684-687
• /
• 2011

In this study, we investigate the photovoltaic performance of transparent conductive indium tin oxide (ITO), titanium-doped indium oxide (ITiO), and fluorine-doped tin oxide (FTO) films. ITO and ITiO films are prepared by radio frequency magnetron sputtering on soda-lime glass substrate at $300^{\circ}C$, and the FTO film used is a commercial product. We measure the X-ray diffraction patterns, AFM micrographs, transmittance, sheet resistances after heat treatment, and transparent conductive characteristics of each film. The value of electrical resistivity and optical transmittance of the ITiO films was $4.15{\times}10^{-4}\;{\Omega}-cm$. The near-infrared ray transmittance of ITiO is the highest for wavelengths over 1,000 nm, which can increase dye sensitization compared to ITO and FTO. The photoconversion efficiency (${\eta}$) of the dye-sensitized solar cell (DSC) sample using ITiO was 5.64%, whereas it was 2.73% and 6.47% for DSC samples with ITO and FTO, respectively, both at 100 mW/$cm^2$ light intensity.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.5
• /
• pp.325-329
• /
• 2002

We investigated the oxide thickness and color evolution with the oxidation temperatures between $370^{\circ}C$ and $950^{\circ}C$ for 30 minutes in an electric furnace. Oxide thickness and color index were determined by cross sectional field emission scanning electron microscopy (FESEM) images and digital camera images, respectively. We confirmed that thermal oxidation was suitable for the mass production of color-titanium products, while coloring process window was narrow compared with anodizing oxidation process.

• Journal of the Korean Solar Energy Society
• /
• v.26 no.4
• /
• pp.55-61
• /
• 2006

Titanium oxide ($TiO_2$) films are deposited on the indium tin oxide (ITO) substrate in an $Ar/O_2$ atmosphere by using reactive RF (Radio Frequency) magnetron sputtering technique, and Electrochromic properties and durability of $TiO_2$ films deposited at different preparation conditions are investigated by using UV-VIS spectrophotometer and cyclic voltammetry Li+ interalation/deintercalation in $TiO_2$ films shows that the electrochromic properties and durability of as-deposited films strongly depend on gas pressure $TiO_2$ films formed in our sputtering conditions are found to remain transparent, irrespective of their Li+ ion contents. The optimum sputtering conditions for film as passive counter electrode in electrochromic devices are working pressure of $1.0\;{\times}\;10^{-2}\;torr$ and oxygen flow raes of $10{\sim}15\;sccm$, respectively.

• Journal of Power System Engineering
• /
• v.11 no.2
• /
• pp.44-50
• /
• 2007

The oxidation behavior of commercial pure titanium is investigated in the temperature range of $727^{\circ}C{\sim}950^{\circ}C$ in mixed gases. The weight change is measured by TGA during oxidation in mixed gases. The oxidation behavior indicated by weight gain or the growth of oxide layer is based on the linear rate law at high temperatures. The structure of the oxide scale formed during oxidation is analysed by optical microscopy, electron probe microanalyzer, scanning electron microscope and x-ray diffraction. Oxide scales have a $TiO_2$ structure, and are constituted with multi-layered or two layered porous external one and a dense internal one. Ti-O solid solution region is formed at the interface of metal and scale layer. The formation of oxide scale is influenced by the oxidation temperature, time, crystal structure and the condition of atmosphere.