• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.36 no.6
• /
• pp.1109-1116
• /
• 2016

There are various test methods for evaluating the reflective cracking resistance of asphalt concrete pavement. Repeated direct tensile test is cheap and simple compared to the other traditional experimental methods. Determination of failure criteria is needed to apply a repeated direct tensile test. Various methods were used to determine the number of failure of repeated direct tensile test. The number of failure was defined as the time to reach 10% of the initial load, this method can be satisfied with specified tolerance of 10%. When the thickness of specimen is increased to 50 mm from 30 mm, the failure number is increased by 13.6 times. Thus, this result shows that the thickness of pavement is a big influence on the reflective cracking resistance. Reflective cracking resistance of asphalt concrete is decreased according to the increase in opening displacement. The repeated direct tensile test can be used as a reflective cracking resistance factor in pavement design, because it can evaluate the reflective cracking resistance according to the pavement thickness, opening displacement, material properties etc.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.35 no.10
• /
• pp.207-215
• /
• 2019

The aim of the research is analyzing the simple adiabatic temperature rising properties and the heat of hydration based on different placing timing of the mass concrete depending on various replacing ratios of blast furnace slag to comparative analyze the thermal cracking index and cracking possibility. As a result from the experiment, a suggested adiabatic temperature rising equation based on various blast furnace slag replacing ratios can be provide favorable correlation with over 0.99 of $R^2$ value by applying the initial induction period. With this relationship, more accurate prediction of the amount of the hydration heat rising and heating timing, and it is known that there is an approximately $13.1^{\circ}C$ of gap between plain concrete without blast furnace slag and concrete with 80 % of replacing blast furnace slag. To control the setting time and heat rising gap, the mix designs between top and bottom concrete casts were changed 15 cases, and D, E, H, I, and L models of controlling the heat of hydration showed 41.23 to $46.88^{\circ}C$ of core temperature and 0.98 to 1.27 of thermal cracking index. Therefore the cracking possibility was 15 to 52 % of favorable results of possibly controlling both the cracking due to the internal and external retainment and concrete temperature at early age.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.1
• /
• pp.57-67
• /
• 2007

The service life of concrete structure is to a great extent influenced by crack developed at early ages of concrete material. Especially, hydration heat is a main cause of thermal cracking at mass concrete structures. The thermal cracking of massive structure is analyzed of the thermal cracking index which was presented Concrete Standard Specifications. The thesis analyzed the thermal cracking index which considered various variable (cement type, height of casting, curing condition, concrete mixing temperature, the unit cement content) at internal restricted mass concrete. The analysis result is denoted increase and decrease rate of thermal cracking index whenever the variables change. The results is helped to understand thermal cracking every time structures is designed and constructed. And I think that it is useful economic and stable design of mass concrete structures.

• Journal of Bio-Environment Control
• /
• v.17 no.2
• /
• pp.143-149
• /
• 2008

The effects of fruit bagging time, bag kinds, and plant oil treatment on fruit cracking, pathogenic decay, and quality in grapevines were studied. The occurrence of cracking fruit was not affect by bag kinds in 'Campbell Early'. But, bitter rot occurrence in 'Campbell Early' and occurrence of cracking fruit and bitter rot in 'Wase Campbell Early' decreased effectively compared the ones of conventional bag, window bag, calcium coated bag to non-bagging. The cracking fruit occurrence of and 'Kyoho' decreased significantly by bagging to each before July 5 of 'Campbell Early' and before June 29 and July 5 of 'Kyoho' grapevines. The cracking fruit and bitter rot occurrence by plant oil treatment decreased significantly in 'Wase Campbell Early', and increased calcium of fruit skin in 'Campbell Early'. The soluble solids in fruits were much reduced by window bag and the Hunter b value in fruit skin was reduced by calcium coated bag. Accordingly, treatment of Ca-coated bag and plant oil was become judgment to reduction effect of cracking fruit.

• Horticultural Science & Technology
• /
• v.33 no.4
• /
• pp.479-485
• /
• 2015

This study was conducted to study the factors inducing micro-cracking and determine proper practices to reduce its occurrence in 'Mansoo' pear fruits. Micro-cracking was observed on ripe fruits. Occurrence of micro-cracking was closely related to sun duration time in August. Micro-cracking occurred severely with shorter sun duration, but weakly with longer sun duration and continuous sunlight. Micro-cracking fruits occurred more frequently in trees with a pergola training system than in those with Y-trellis, but there was no difference between the irrigated and non-irrigated groups. While no micro-cracking was observed without fruit bagging, micro-cracking occurred in fruits with black and yellow outer paper bagging at rates of 62.2 and 17.3%, respectively. Our results suggest that the light condition was the most important cause of micro-cracking because the occurrence of micro-cracking in 'Mansoo' fruits was affected by factors including sun duration, trellis system and fruit bag color. We suggested that micro-cracking could be reduced in 'Mansoo' fruit by optimizing the light conditions with the proper trellis system, bagging color and summer pruning.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.3
• /
• pp.48-54
• /
• 2022

This research describes a quantitative procedure used to estimate the effect of concrete cracking on stiffness degradation of concrete shear walls and provides analytical references for the seismic design of concrete shear walls. As preliminary research on the seismic response of concrete shear walls, nonlinear transient analysis was performed with commercial FE software. The study presents the nonlinear time history analysis results in terms of concrete damage and cracking behavior induced by seismic input motions. By varying the input motions, concrete strength and shear wall thickness, the seismic responses of a shear wall were examined with nonlinear time history analysis, and the progressive cracking behavior and corresponding hysteresis loop were described. Based on the analysis results, frequency and stiffness degradation of the shear wall from progressive concrete damage and cracking were captured with respect to the seismic levels. The results of this study suggest that stiffness degradation from concrete cracking should be appropriately considered when determining the seismic capacity of RC shear wall structures.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2005.04a
• /
• pp.448-455
• /
• 2005

In this paper, an analytical model for estimation of the time at which the concrete surface begins to dry is introduced to predict whether or not plastic shrinkage cracks occur. First of all, the validity of a consolidation model for bleeding of cement paste proposed by Tan et al. is verified by comparing the analytical results with the experimental results, and used to evaluate the rate and amount of bleed water of concrete. Also an analytical model for evaporation of bleed water which considers the effect of the temperature variation of concrete surface due to hydration heat on the evaporation rate is proposed, and the experimental and analytical results are then compared to verify the validity of the introduced model. In advance, the time at which the concrete surface begins to dry is estimated using above two analytical models, and compared with the experimental results about the time at which plastic shrinkage cracks occur. From the comparison, it is verified that the proposed model can predict the occurrence of plastic shrinkage cracking with comparative precision.

• Corrosion Science and Technology
• /
• v.7 no.5
• /
• pp.243-251
• /
• 2008

Magnesium alloys become popular research topic in last decade due to its light weight and relatively high strength-to-weight ratio in the energy aspiration age. Almost all structure materials are supposed to suspend stress. Magnesium is quite sensitive to corrosive environment, and also sensitive to environmental assisted cracking. However, so far we have the limited knowledge about the environmental sensitive cracking of magnesium alloys. The corrosion fatigue (CF) test was conducted. Many factors' effects, like grain size, texture, heat treatment, loading frequency, stress ratio, strain rate, chemical composition of environment, pH value, relative humidity were investigated. The results showed that all these factors had obvious influence on the crack initiation and propagation. Especially the dependence of CF life on pH value and frequency is quite different to the other traditional structural metallic materials. In order to interpret the results, the electrochemistry tests by polarization dynamic curve and electrochemical impedance spectroscopy were conducted with and without stress. The corrosion of magnesium alloys was also studied by in-situ observation in environmental scanning electron microscopy (ESEM). The corrosion rate changed with the wetting time during the initial corrosion process. The pre-charging of hydrogen caused crack initiated at $\beta$ phase, and with the increase of wetting time the crack propagated, implying that hydrogen produced by corrosion reaction participated in the process.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.715-722
• /
• 2001

The main purpose of this study is to evaluate early age thermal stresses and to estimate the risk of thermal cracking in the footings of Hyungsan bridge. In this study, stress analyses are performed for several construction stages using the computation of temperature distributions. The stress analysis results show that, not using the embedded pipe cooling, placing the concrete at once for each footings may cause sever thermal cracking. So, the structures should be constructed with one horizontal construction joint. Then the height of each lifts were determined to be 1.50 meters. Using various time intervals between lifts, temperature and stress.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.693-698
• /
• 2003

Corrosion of reinforcement and deterioration of concrete short the lifetime of reinforced concrete structure and affect the safety of the structure. In particular, the corrosion of reinforcement causing the inner pressure of the interface between the concrete and reinforcement is known to significantly contribute to the premature deterioration of concrete structure. Several attempts have been made to predict the cracking time of the concrete structure. However, problems such as the lack of reproducibility of concrete tests and non-uniformity of materials have hampered thess kinds of studies. Thus, the mechanism of the concrete cracking due to reinforcement corrosion is in the way. This studymeasured the mechanical properties of corrosion products using the nano-indentation test method. Likewise, the critical thickness of corrosion products for the cracking of concrete cover was investigated using the finite element and experimental methods.