• Magazine of the Korea Concrete Institute
• /
• v.7 no.6
• /
• pp.233-241
• /
• 1995

In this thesis, the fatigue tests were performed on a series of R /C beams repaired with co& crete-lmlyrner composites to investigate the fatigue bahavior. The three point loading system is used in the fatigue tests. In these tests, relations between the repeated loading cycles and mid-span deflections, number of repeated loading cycles when repaired beams were fractured, the bonding performance of repair materials were observed. On this basis, the mid-span deflections, the crack growth and failure mode of repaired R /C beams were studied. A S-N curve was drawn to present the fatigue strength of repaired beams. From the test results, it was shown that behavior of R /C beams repaired with polymer-cement series were very sirnillar to control beam about bonding performance, mid-span deflections and fatigue strength according to S-N curve drawn by the regression anlysis on the fatigue test results.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.32 no.6
• /
• pp.359-366
• /
• 2019

Experimental and analytical studies on the behavioral characteristics of a pre-stressed (PS) steel girder are conducted to investigate the effects of deviators on the non-linear inelastic properties of the PS system. In this regard, 4 test specimens consisting of a steel H-beam, a straight cable with eccentricity, anchorages, and deviators are built and failure tests are performed under two-point loading. In addition, in-plane elastic deformation theories for the PS system without a deviator, and with three deviators at regular intervals are analytically formulated and solved using a symbolic calculation technique. To verify the validity of the experimental and the proposed analytical theories, the results obtained using FEM models composed of beam elements, rigid beam elements, and truss cable elements, are compared to the experimental results and the analytical solutions. As a result, it is determined that externally installed un-bonded deviators inhibit flexural deformation of the deformed beam to such an extent that their elastic stiffness, and failure strength are significantly improved compared to those of the PS system without deviators.

• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.3
• /
• pp.191-196
• /
• 2011

Purpose: In this study, we evaluated the bond-strength between a few metal ceramic-alloys and veneered-porcelain and found if the bond strength of metal-ceramic alloy with lower gold content than the presently used gold alloy was high enough. Materials and methods: For this study, after plasticizing porcelain only for gold alloy, metal specimen was fabricated using Ni-Cr alloy and gold alloy with different gold content. Three point flexural test were performed to measure their bond-strength. Results: The bonding strength of Group 1 to porcelain was $40.62{\pm}3.32$ MPa, which was the highest (P<.05). In sequence of decreasing value, Group 2 (75%) was $37.47{\pm}1.57$ MPa, Group 3 (52%) $35.85{\pm}1.48$ MPa, Group 4 (51.5%) $35.04{\pm}1.34$ MPa, Group 5 (32%) $33.17{\pm}1.62$ MPa, Group 6 (10%) $30.75{\pm}1.21$ MPa. Bonding strength of Group 3 and Group 4 to porcelain did not show statistically significant difference with comparison to that of Group 5 (Duncan's test, P>.05), while there was a significant difference between that of Group 2, Group 3 and Group 4 and that of Group 6 (Duncan's test, P<.05). The bonding strength between gold alloy and porcelain increased according to the content of gold. In all experimental groups showed higher value than 25 MPa, which is the least value recommended by ISO 9693. Conclusion: In all groups, bonding strength was higher than 25 MPa, which is the least value of ISO9693. Therefore, it is considered that metal gold alloy with low gold content is clinically usable.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.33 no.2
• /
• pp.71-79
• /
• 2017

Purpose: Ni-Cr alloy does not contain Beryllium, causing the metal compound to form oxides in the furnace but by using Titanium as a chemical catalyst the forming of the oxides can be controlled, and by controlling the impurities formed on the metal surface, the possibility of the Ni-Cr alloy bond strength being increased can be analysed. Materials and Methods: Titanium was used as a chemical catalyst in the porcelain for the oxidation of beryllium-free metal (Ni-Cr) alloy. The T1 group, which does not use Titanium power as a chemical catalyst is a reference model for comparison. The T2 group and T3 group used 10 g and 20 g of Titanium power, respectively. They are fabricated to observe the shear bond strength and surface properties. There was no significance when One-way ANOVA analysis/Tukey Honestly Significant Difference Test was conducted for statistical analysis among groups (P > 0.05). Results: Results of measuring the three-point flexural bond strength of the Ni-Cr alloy and thickness of the oxide film. Experiment T3 using 20 g Titanium chemical catalyst: $39.22{\pm}3.41MPa$ and $6.66{\mu}m$, having the highest bond strength and thinness of oxide film. Experiment T2 using 10 g Titanium chemical catalyst: $34.65{\pm}1.39MPa$ and $13.22{\mu}m$. Experiment T1 using no Titanium chemical catalyst: $32.37{\pm}1.91MPa$ and $22.22{\mu}m$. Conclusion: The T2 and T3 experiments using Titanium chemical catalyst showed higher bond strength for the Ni-Cr alloy and lower thickness of oxide film than experiment T1, and the titanium catalyst being able to increase bond strength was observed.