In order to fabricate adhesiveless 2-layer flexible copper clad laminate (FCCL) used for COF (chip on film) with high peel strength, polyimide (PI; Kapton-EN, $38\;{\mu}m$) surface was modified by reactive $O_2^+$ and $N_2O^+$ ion beam irradiation. 300 mm-long linear electron-Hall drift ion source was used for ion irradiation with ion current density (J) higher than $0.5\;mA/cm^2$ and energy lower than 200 eV. By vacuum web coating process, PI surface was modified by linear ion source and then 10-20 nm thick Ni-Cr and 200 nm thick Cu film were in-situ sputtered as a tie layer and seed layer, respectively. Above this sputtered layer, another $8-9{\mu}m$ thick Cu layer was grown by electroplating and subsequently acid and base resistance and thermal stability were tested for examining the change of peel strength. Peel strength for the FCCLs treated by both $O_2^+$ and $N_2O^+$ ion irradiation showed similar magnitudes and increased as the thickness of tie layer increased. FCCL with Cu (200 nm)/Ni-Cr (20 nm)/PI structure irradiated with $N_2O^+$ at $1{\times}10^{16}/cm^2$ ion fluence was proved to have a strong peel strength of 0.73 kgf/cm for as-received and 0.34 kgf/cm after thermal test.

• Korean Chemical Engineering Research
• /
• v.51 no.2
• /
• pp.214-220
• /
• 2013

Hydrophobic coating on a silicate-based yellow phosphor ($Sr_2SiO_4:Eu^{2+}$) was carried out by using hexamethyldisiloxane (HMDSO) precursor in an atmospheric pressure dielectric barrier discharge plasma reactor, eventually to improve the long-term stability and reliability of the phosphor. The phosphor powder samples were characterized by a scanning electron microscope (SEM), a transmission electron microscope (TEM), a fluorescence spectrophotometer and a contact angle analyzer. After the coating was prepared, the contact angle of the phosphor powder increased to $133.0^{\circ}$ for water and to $140.5^{\circ}$ for glycerol, indicating that a hydrophobic layer was formed on its surface. The phosphor coated with HMDSO exhibited photoluminescence enhancement up to 7.8%. The SEM and TEM images of the phosphor powder revealed that the plasma coating led to a morphological change from grain-like structure to smooth surface with 31~46 nm thick hydrophobic layer. The light emitting diode (3528 1 chip LED) fabricated with the coated phosphor showed a substantial enhancement in the reliability under a special test condition at $85^{\circ}C$ and 85% relative humidity for 1,000 h (85/85 testing). The plasma-mediated method proposed in this work may be applicable to the formation of 3-dimensional coating layer on irregular-shaped phosphor powder, thereby improving the reliability.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.1
• /
• pp.39-49
• /
• 1999

Monolayer thick fluorocarbon films were characterized by the contact angle measurements. The contact angles of three different liquids, water, formamide and diiodomethane were measured on spun coated, vapor phased deposited films and Teflon surface. The highest contact angle over $130^{\circ}$was observed on fluorocarbon films deposited on Al substrates while the lowest angles below $70^{\circ}$deposited on oxide. The surface energies were calculated based on Lewis acid /base theory. The surface energies of Teflon and spin coated FC films were calculated to have 18 and 8.4 dynes /cm, respectively. Higher energies of 31 to .35 dynes /cm were calculated on vapor phase deposited films on silicon and oxide. However vapor phase deposited films on aluminum only showed a large Lewis base energy term. It might be explained by the surface roughness and heterogeneity as observed by dynamic contact angles and AFM measurements.

• Journal of the Semiconductor & Display Technology
• /
• v.14 no.1
• /
• pp.61-65
• /
• 2015

We have fabricated poly(3,4-ethylenedioxythiophene) : poly(4-styrenesulfonate) (PEDOT : PSS) thin films using a slotdie coater for the applications of OLED lightings. It is demonstrated that the properties of slot-die coated PEDOT : PSS films are comparable with those of spin-coated ones. Namely, the average and peak-to-peak roughness of the slot-die coated 50-nm-thick PEDOT : PSS film are measured to be as low as 0.247 nm and 1.3 nm, respectively. Moreover, we have obtained excellent thickness uniformity (~1.91%). With the slot-die coated PEDOT : PSS films, we have fabricated green phosphorescent OLED devices. For comparison, we have also fabricated OLED devices with spin-coated PEDOT : PSS films. Both show almost no discrepancy in device performance. The power efficiency (25.4 lm/W) and emission uniformity (77%) of OLEDs with slot-die coated PEDOT : PSS films are shown to be slightly lower than those (27.3 lm/W, 80%) of OLEDs with spin-coated PEDOT : PSS films at the luminance of 1,000nit, increasing the feasibility of using a slot-die coating process for the fabrication of large-area OLED lighting sources at a competitive price.

• Journal of the Korean Electrochemical Society
• /
• v.20 no.2
• /
• pp.41-48
• /
• 2017

Herein, we have fabricated an ultrathin aluminum oxide ($Al_2O_3$) coated PP separator by using a RF sputter deposition process. Approximately 20 nm thickness coating layer on the bare PP separator was formed at the power of 55 W for 2 minutes without thermal damage. Whereas only permeability of the coated separator was degraded slightly, other properties such as thermal stability, uptake amount of liquid electrolyte, and ionic conductivity were improved comparing to the bare PP separator. As a result, an only 20-nm-thick $Al_2O_3$ coating layer could improve the rate capability compared with a bare PP separator under a high current density.

• Korean Journal of Materials Research
• /
• v.23 no.4
• /
• pp.211-214
• /
• 2013

The effects of a Ni coating on the sensing properties of nano ZnO:Ni based gas sensors were studied for $CH_4$ and $CH_3CH_2CH_3$ gases. Nano ZnO sensing materials were prepared by the hydrothermal reaction method. The Ni coatings on the nano ZnO surface were deposited by the hydrolysis of zinc chloride with $NH_4OH$. The weight % of Ni coating on the ZnO surface ranged from 0 to 10 %. The nano ZnO:Ni gas sensors were fabricated by a screen printing method on alumina substrates. The structural and morphological properties of the nano ZnO : Ni sensing materials were investigated by XRD, EDS, and SEM. The XRD patterns showed that nano ZnO : Ni powders with a wurtzite structure were grown with (1 0 0), (0 0 2), and (1 0 1) dominant peaks. The particle size of nano ZnO powders was about 250 nm. The sensitivity of nano ZnO:Ni based sensors for 5 ppm $CH_4$ gas and $CH_3CH_2CH_3$ gas was measured at room temperature by comparing the resistance in air with that in target gases. The highest sensitivity of the ZnO:Ni sensor to $CH_4$ gas and $CH_3CH_2CH_3$ gas was observed at Ni 4 wt%. The response and recovery times of 4 wt% Ni coated ZnO:Ni gas sensors were 14 s and 15 s, respectively.

• Journal of Electrochemical Science and Technology
• /
• v.7 no.2
• /
• pp.132-138
• /
• 2016

In this study, we report the fabrication of functional complex fibers, which have been studied widely globally for numerous applications. Here, we fabricated conductive complex fibers with antibacterial properties by coating metal ions on the surface of plastic (polypropylene) fibers using the electroless and electrochemical deposition. First, we polished the polypropylene melt-blown fiber surface and obtained an absorbing Pd seed layer on its surface. Subsequently, we substituted the Pd with Cu. Bis-3-sulfopropyl-disulfide disodium salt (SPS), polyethylene glycol (PEG), and ethylene thiourea (ETU) were used as the brightener, carrier, and leveler, respectively for the electroplating. We focused on most achieving the stable plating condition to remove dendrites, which are normally during electroplating metals so that smooth layer is formed on the fiber surface. The higher the amount of SPS, the higher was the extent of irregular plate-like growth. Many irregularities in the form of round spheres were observed with increase in the amount of PEG and ETU. Hence, when the additives were used separately, a uniform coating could not be obtained. A stable coating was obtained when the three additives were combined and a uniform 5-9 μm thick copper layer with a stable morphology could be obtained around the fiber. We believe that our results can be applied widely to obtain conductive fibers with antibacterial properties and are useful in aiding research on conductive lightweight composite fibers for application in information technology and robotics.

• Journal of Powder Materials
• /
• v.20 no.6
• /
• pp.445-452
• /
• 2013

Yttria-stabilized zirconia (YSZ) coatings are fabricated via suspension plasma spray (SPS) for thermal barrier applications. Three different suspension sets are prepared by using a planetary mill as well as ball mill in order to examine the effect of starting suspension on the phase evolution and the microstructure of SPS prepared coatings. In the case of planetary-milled commercial YSZ powder, a deposited thick coating turns out to have a dense, vertically-cracked microstructure. In addition, a dense YSZ coating with fully developed phase can be obtained via suspension plasma spray with suspension from planetary-milled mixture of $Y_2O_3$ and $ZrO_2$.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.6
• /
• pp.434-443
• /
• 2014

PURPOSE. The purpose of this study was to evaluate and compare the effects of different surface pretreatment techniques on the surface roughness and shear bond strength of a new self-adhering flowable composite resin for use with lithium disilicate-reinforced CAD/CAM ceramic material. MATERIALS AND METHODS. A total of one hundred thirty lithium disilicate CAD/CAM ceramic plates with dimensions of $6mm{\times}4mm$ and 3 mm thick were prepared. Specimens were then assigned into five groups (n=26) as follows: untreated control, coating with $30{\mu}m$ silica oxide particles ($Cojet^{TM}$ Sand), 9.6% hydrofluoric acid etching, Er:YAG laser irradiation, and grinding with a high-speed fine diamond bur. A self-adhering flowable composite resin (Vertise Flow) was applied onto the pre-treated ceramic plates using the Ultradent shear bond Teflon mold system. Surface roughness was measured by atomic force microscopy. Shear bond strength test were performed using a universal testing machine at a crosshead speed of 1 mm/min. Surface roughness data were analyzed by one-way ANOVA and the Tukey HSD tests. Shear bond strength test values were analyzed by Kruskal-Wallis and Mann-Whitney U tests at ${\alpha}=.05$. RESULTS. Hydrofluoric acid etching and grinding with high-speed fine diamond bur produced significantly higher surface roughness than the other pretreatment groups (P<.05). Hydrofluoric acid etching and silica coating yielded the highest shear bond strength values (P<.001). CONCLUSION. Self-adhering flowable composite resin used as repair composite resin exhibited very low bond strength irrespective of the surface pretreatments used.

• Journal of the Korean Ceramic Society
• /
• v.39 no.12
• /
• pp.1153-1157
• /
• 2002

The fabrication of a three-layered asymmetric ceramic membrane was performed by slip casting of the porous alumina support and dip coating of the alumina intermediate layer using high purity ${\alpha}-Al_2O_3$ powders that have different particle size, followed by screen printing-pyrolysis of the $Tio_2$ layer as an ultrafilteration membrane using Ti-naphthenate solution. The bending strength, porosity and mean pore size of the alumina support were 231 kg/$cm^2$s, 30.26% and 0.19 ${mu}m$, respectively. The thickness of the intermediate layer was 30 ${mu}m$ and the mean pore size of that was 0.063 ${mu}m$. Also, the top layer was 0.5 ${mu}m$ thick and micropores with about 20 nm size were formed uniformly.