• 소성∙가공
• /
• 제25권2호
• /
• pp.96-101
• /
• 2016

The current study was conducted to elucidate the effect of cementite morphology and matrix-ferrite microstructure on sliding wear behavior in spheroidized high carbon (1wt. % C) steel. The high carbon steel was initially heat treated to obtain a full pearlite or a martensite microstructure before the spheroidization. The spheroidizing heat treatment was performed on the full pearlitic steel for 100 hours at 700℃ and tempering was performed on the martensitic steel for 3 hours at 650℃. A spheroidized cementite phase in a ferrite matrix was obtained for both the full pearlite and the martensite microstructures. Sliding wear tests were conducted using a pin-on-disk wear tester with the heat treated steel as the disk specimen. An alumina(Al₂O₃) ball was used as the pin counterpart during the test. After the spheroidizing heat treatment and the tempering, both pearlite and martensite exhibited similar microstructures of spheroidized cementite in a ferrite matrix. The spheroidized pearlite specimens had lower hardness than the tempered martensite; however, the wear resistance of the spheroidized pearlite was superior to that of the tempered martensite.

• 대한금속재료학회지
• /
• 제47권7호
• /
• pp.406-415
• /
• 2009

A study was conducted on the effects of carbon, tungsten, and vanadium on the wear properties and surface roughness of four High Speed Steel (HSS) rolls manufactured by the centrifugal casting method. Hot-rolling simulation tests were carried out using a high-temperature wear tester capable of controlling speed, load, and temperature. HSS rolls contained a large amount (up to 25 vol.%) of carbides such as MC, $M_{2}C$, $M_{7}C_{3}$, and $M_{6}C$ carbides formed in the tempered martensite matrix. The matrix consisted mainly of lath tempered martensite when the carbon content in the matrix was small, and contained a considerable amount of plate tempered martensite when the carbon content increased. The high-temperature wear test results indicated that the wear properties and surface roughness of the rolls improved when the amount of hard MC carbides formed inside solidification cells increased. The rolls distribution was also homogeneous. The best wear properties and surface roughness were obtained from a roll where a large amount of MC carbides was homogeneously distributed in the lath tempered martensite matrix. The proper contents of carbon equivalent, tungsten equivalent, and vanadium were 2.0~2.3%, 9~10%, and 5~6%, respectively.

• 한국재료학회지
• /
• 제25권11호
• /
• pp.607-611
• /
• 2015

The microstructural evolution of Grade 91 tempered martensite ferritic steels heat treated at $760{\sim}1000^{\circ}C$ for two hours was investigated using scanning electron microscopy(SEM), energy disperse spectroscopy(EDS), electron backscattered diffraction (EBSD), and transmission electron microscopy(TEM); a microhardness tester was also employed, with a focus on the grain and precipitate evolution process as well as on the main hardening element. It was found that an evolution of tempered martensite to ferrite($760{\sim}850^{\circ}C$), and to fresh martensite($900{\sim}1000^{\circ}C$), occurred with the increase of temperature. Simultaneously, the parabolic evolution characteristics of the low angle grain boundary(LAGB) increased with the increase of the heating temperature(highest fraction of LAGB at $925^{\circ}C$), indicating grain recovery upon intercritical heating. The main precipitate, $M_{23}C_6$, was found to be coarsened slightly at $760{\sim}850^{\circ}C$; it then dissolved at $850{\sim}1000^{\circ}C$. Besides this, $M_3C$ cementite was formed at $900{\sim}1000^{\circ}C$. Finally, the experimental results show that the hardness of the steel depended largely on the matrix structure, rather than on the precipitates, with the fresh martensite showing the highest hardness value.

• 한국재료학회지
• /
• 제10권6호
• /
• pp.409-414
• /
• 2000

3%C-10%Cr-5%Mo-5%W, 3%C-10%V-5%Mo-5%W 및 3%C-17%Cr-3%V의 3종류 고합금백주철에 있어서 열처리후의 기지조직의 변태거동을 연구하였다. 15kg 용량의 고주파 유도용해로에 선철, 고철, Fe-Cr, Fe-V, Fe-Mo 및 Fe-W 등을 장입시켜 용해시킨 후 슬래그를 제거시키고 $1550^{\circ}C$에서 Y-block의 펩 주형에 주입시켰다. 적당한 크기로 절단한 시편을 진공분위기하에$950^{\circ}C$에서 5시간동안 우선 균질화처리를 실시하였다. 그 후 다시 이 시편을 $1050^{\circ}C$에서 2시간동안 오스테나이징시킨 후 강제공냉을 행하였다. 강제공냉된 시편을 $300^{\circ}C$에서 3시간 유지시킨 후 템퍼링을 실시하였다. 주방상태에서의 기지조직은 3합금 공히 퍼얼라이트이었으며 강제공냉후에는 마르텐사이트 및 오스테나이트로 변태하였다. 또한 기지조직내에 무수히 많은 이차탄화물 입자들의 석출되었다. 템프링 후 일부 오스테나이트 및 마르텐사이트는 템퍼드마르텐사이트로 변태하였다. 변태하였다.

• Journal of Welding and Joining
• /
• 제17권3호
• /
• pp.55-65
• /
• 1999

Metallurgical factors influencing toughness of the Intercritically Reheated Coarse-Grained Heat Affected Zone (ICCG HAZ) of multiple welded SA508-cl.3 Reactor Pressure Vessel Steel were evaluated. The recrystallized austenite formed along the prior austenite grain boundaries and late interfaced on heating to the intercritical range was transformed to bainite and/or martensite during cooling. The newly formed martensite always included some retained austenite(M-A constituents). The characteristics(amount, hardness, density, and size) of M-A constituents were found to be strongly associated with both peak temperature and cooling time(△t8/5(2)) of last pass. Toughness in the ICCG HAZ was deteriorated with increasing amount of M-A constituents which was increased with increasing the last peak temperature within the intercritical temperature range. Meanwhile, for the same intercritical peak temperature, toughness was decreased with increasing cooling time. When cooling time was short, the dominant factor influencing toughness of the ICCG HAZ was amount of M-A constituents. However, when cooling time was lengthened, the hardness difference between M-A constituents and softened matrix(tempered martensite) was found to be the dominant factor.

• 한국표면공학회지
• /
• 제17권1호
• /
• pp.7-13
• /
• 1984

Carburizing of a 12%Cr steel containing 0.6%Si was performed at 950$^{\circ}C$ for various times, and the microstructure, hardness and the water characteristics of the carburized chromium steel were examined. The results obtained in this study are as follows: 1. Carbide-dispersed layer (CD layer) with fine dispersion of $Cr_7C_3$ in martensite matrix was formed by carburizing. The radius and amount of the carbides in the surface region of CD layer were about 0.3${\mu}m$ and 35% by volume, respectively. 2. Chromium steel carburized and quench-tempered showed better wear resistance and hardness than ordinary high chromium tool steel. It is concluded from these results that fine dispered carbides are very effective in improving wear resistance and hardness.

• 한국주조공학회지
• /
• 제20권2호
• /
• pp.104-109
• /
• 2000

Three different white cast irons alloyed with Cr, V, Mo and W were prepared in order to study their abrasion wear behavior in as-cast and heat-treated conditions. The specimens were produced using a 15㎏-capacity high frequency induction furnace. Melts were super-heated to $1600^{\circ}C$, and poured at $1550^{\circ}C$ into Y-block pepset molds. Three combinations of the alloying elements were selected so as to obtain the different types of carbides : 3%C-10%Cr-5%Mo-5%W(alloy No. 1: $M_7C_3$ and $M_6C$), 3%C -10%V-5%Mo-5%W(alloy No. 2: MC and $M_2C$) and 3%C-17%Cr-3%V(alloy No. 3: $M_7C_3$ only). A scratching type abrasion test was carried out in the states of as-cast(AS), homogenizing(AH), air-hardening(AHF) and tempering(AHFT). First of all, the as-cast specimens were homogenized at $950^{\circ}C$ for 5h under the vacuum atmosphere. Then, they were austenitized at $1050^{\circ}C$ for 2h and followed by air-hardening in air. The air-hardened specimens were tempered at $300^{\circ}C$ for 3h. 1 ㎏ load was applied in order to contact the specimen with abrading wheel which was wound by 120 mesh SiC paper. The wear loss of the test piece(dimension: $50{\times}50{\times}5$ mm) was measured after one cycle of wear test and this procedure was repeated up to 8 cycles. In all the specimens, the abrasion wear loss was found to decrease in the order of AH, AS, AHFT and AHF states. Abrasion wear loss was lowest in the alloy No.2 and highest in the alloy No.1 except for the as-cast and homogenized condition in which the alloy No.3 showed the highest abrasion wear loss. The lowest abrasion wear loss of the alloy No.2 could be attributed to the fact that it contained primary and eutectic MC carbides, and eutectic $M_2C$ carbide with extremely high hardness. The matrix of each specimen was fully pearlitic in the as-cast state but it was transformed to martensite, tempered martensite and austenite depending upon the type of heat-treatment. From these results, it becomes clear that MC carbide is a significant phase to improve the abrasion wear resistance.

• 열처리공학회지
• /
• 제22권5호
• /
• pp.282-289
• /
• 2009

The effects of the high temperature gas nitriding (HTGN), tempering and subzero treatment of STD11 steel have been investigated. HTGN treatment was carried out at $1050^{\circ}C$, $1100^{\circ}C$ and $1150^{\circ}C$ for 1 hr. in an atmosphere of $1\;kg/cm^2$ nitrogen gas. Tempering and double-tempering were performed at $550^{\circ}C$ for 1 hr. The surface layer of HTGN-treated steel appeared the precipitates of $M_2N$, $M_7C_3$ and $M_{23}C_6$ in the matrix of austenite. However, the interior region exhibited martensite with the precipitation of carbides. The nitrogen content of the surface layer appeared ~1.35 wt.%, ~0.83 wt.% and ~0.56 wt.% at the HTGN treatment temperature of $1050^{\circ}C$, $1100^{\circ}C$ and $1150^{\circ}C$, respectively. The surface hardness of double-tempered and subzero-treated steel measured the maximum value of 828 Hv, 960 Hv, 750 HV after HTGN treatment at the $1050^{\circ}C$, $1100^{\circ}C$ and $1150^{\circ}C$, respectively. These hardness value increased above 230~420 Hv compared with the HTGN-treated steel due to the decrease in retained austenite and existence of fine precipitates.

• 대한금속재료학회지
• /
• 제48권11호
• /
• pp.974-980
• /
• 2010

Various types of steel, namely, 0.35C, 0.2C-Cr, and 0.2C-Cr-Mo steels, were quenched and tempered by high-frequency induction heat treatment. The type, size, and spheroidization of the carbides varied depending on the tempering temperatures ($450{\sim}720^{\circ}C$). During the tempering process, the carbide was precipitated in the martensite matrix. The 0.35C, 0.2C-Cr, and 0.2C-Cr-Mo steels contained carbides that were smaller than 120 nm. The carbide was spheroidized as the tempering temperature increased. Owing to the fine microstructure and spheroidization of the carbides, all three steels had a high tensile strength as well as yield ratio and reduction of area. In the case of the 0.2C-Cr steel, the use of Cr as an alloying element facilitated the precipitation of alloyed carbides with an extremely small particle and resulted in an increase in the spheroidization rate of the carbides. As a result, a large reduction of area was achieved (>70%). The 0.2C-Cr-Mo steel had the highest tensile strength because of the high hardenability that can be attributed to the presence of alloying elements (Cr and Mo). Quenching and tempering steels by induction heat treatment resulted in a high strength of over 1 GPa and a large reduction of area (>70%) because of the rapid heating and cooling rates.