• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.111-114
• /
• 2007

We have investigated the effect of different heat treatment processes on electrical and magnetic properties of Bi2212/Ag ROSAT wire. The ROSAT wire was fabricated by stacking and arranging 12 filaments Bi2212/Ag tapes in triple rotation symmetry in a Ag tube. ROSAT wires have been prepared using a partial melting method with changing $T_{max}$ and $T_a$ in oxygen atmosphere. The highest critical current density($J_c$) at 65 K under 0 T was $21,158\;A/cm^2$ for wire prepared $890\;^{\circ}C(T_{max})$ and $840\;^{\circ}C(T_a)$, respectively. SEM results indicated that the wire prepared at $890\;^{\circ}C(T_{max})$ and $840\;^{\circ}C(T_a)$ showed better directional phases than the other samples. However the result of magnetic susceptibility measurement indicates that the wire prepared $890\;^{\circ}C(T_{max})$ and $835\;^{\circ}C(T_a)$ had better superconducting phases than the other samples. It was revealed that heat treatment temperature was important factor for superconducting properties of the ROSAT wire.

• Proceedings of the KIEE Conference
• /
• 1998.07a
• /
• pp.125-127
• /
• 1998

Superconducting tape is being developed for electrical equipment such as superconducting transformers and generators. AC loss reduction is primary concern in the development of such high-efficiency equipment. AC losses in Bi-2223 silver-sheathed tapes, both single and multi-filamentary, were investigated by means of AC magnetization techniques. The results were compared with the hysteresis loss equation based on Bean model and the eddy current loss equation. The AC loss, of the mono-filamentary tape was the hysteresis. On the contrary, the AC loss of the multi-filamentary tape was substantially dominated by the eddy current loss in the Ag matrix.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.593-596
• /
• 2003

A proposed way to prepare $YBa_2Cu_3O_y$ wires or tapes is that Ag is used as substrate and melting point of $YBa_2Cu_3O_y$ is decreased to lower than the melting point of silver ($961\;^{\circ}C$). Therefore after the deposition of $YBa_2Cu_3O_y$ film on Ag substrate, the heat treatment can be carried out below the Ag melting point. Silver (Ag) and Lead oxide(PbO) were selected to be additives for $YBa_2Cu_3O_y$. Different Ag and PbO contents were added in $YBa_2Cu_3O_y$, the melting points of which were measured by DTA. In order to guarantee that the superconductivity of $YBa_2Cu_3O_y$ was not reduced after Ag and PbO added into $YBa_2Cu_3O_y$, their superconductivities were measured. It is proved that as additives, both Ag and PbO can reduce the melting point of $YBa_2Cu_3O_y$. For Ag doped $YBa_2Cu_3O_y$, $T_c$ is about 93K and ${\Delta}Tc$ is $2{\sim}3K$. For PbO doped $YBa_2Cu_3O_y$, $T_c$ is $88K{\sim}92K$ and ${\Delta}T_c$ is $11{\sim}12K$. When 10 wt% of Ag and 10 wt% PbO were added in $YBa_2Cu_3O_y$, the melting point of the mixture of $YBa_2Cu_3O_y$ (80 wt%), Ag (10 wt%) and PbO (l0 wt%) is $943^{\circ}C$. The transition temperatures ($T_c$) of the sample is 91.8 K.