Fabrication and Pore Properties of SUS316L Membrane with Double-Layered Pore Structures by Wet Powder Spraying

  • Min-Jeong Lee;Hyeon-Ju Kim;Manho Park;Jung-Yeul Yun
    • Archives of Metallurgy and Materials
    • /
    • 제67권4호
    • /
    • pp.1531-1534
    • /
    • 2022
  • In this study, a SUS316L membrane having double layered pore structures was fabricated, and the pore characteristics were analyzed after coating with a spherical powder and a flake-shaped powder on a disk-shaped SUS316L support using a wet powder spraying process. The thickness of the coated layer was checked using an optical microscope, and air permeability was measured using a capillary flow porometer. When the coating amount was similar, the fine porous layer prepared using flake powder was thicker and showed higher porosity. In the case of a similar thickness, the case of using flake powder was half of the amount of spherical powder used. Therefore, it was confirmed that it is possible to manufacture a metal membrane having a high filter efficiency even with a small coating amount when using the flake powder.

다공성 Ni 금속 지지체를 사용한 Pd-Ni 합금 수소 분리막 연구 (A Study on the Pd-Ni Alloy Hydrogen Membrane using the Porous Nickel Metal Support)

  • 김동원;엄기연;김상호;박종수
    • 한국표면공학회지
    • /
    • 제37권5호
    • /
    • pp.289-295
    • /
    • 2004
  • A dense palladium-nikel (Pd-Ni) alloy composite membrane has been fabricated on microporous nickel support mixed with submicron/micron nickel powder instead of mesoporous stainless steel support. Plasma treatment process is introduced as pre-treatment process instead of HCI activation. Pd-Ni alloy composite membrane prepared by electro plating was fairly a uniform and dense surface morphology. The membrane was characterized by permeation experiments with hydrogen and nitrogen gases at temperature 773 K and pressure 2.2 psi. The results showed that hydrogen ($H_2$) permeance was 27 ml/$\textrm{cm}^2$ㆍatmㆍmin and hydrogen/ nitrogen ($_H2$$N_2$) selectivity was 8 at 773 K.

Microstructure and Pore Characteristics of a SUS316L Gas Filter Fabricated by Wet Powder Spraying

  • Min-Jeong Lee;Yu-Jeong Yi;Hyeon-Ju Kim;Manho Park;Jungwoo Lee;Jung-Yeul Yun
    • Archives of Metallurgy and Materials
    • /
    • 제67권4호
    • /
    • pp.1547-1550
    • /
    • 2022
  • In this study, a flake-shaped metal powder was coated on a tube shaped pre-sintered 316L stainless steel support using a wet powder spraying process to fabricate a double pore structure, and the pore characteristics were analyzed according to coating time and tube rotation speed. The thickness of the coated layer was checked via optical microscopy, and porosity was measured using image analysis software. Air permeability was measured using a capillary flow porometer. As a result of the experiment, the optimal rotation speed of the support tube was established as 200 rpm. When the rotation speed was fixed, the coating thickness and the coating amount of the double pore structure increased as the coating time increased. The porosity of the double pore structure was increased due to the irregular arrangement of the flake-shaped powder. The air permeability of the double pore structure decreased with increasing fine pore layer thickness.

실리카-지르코니아 분리막 성능에 대한 다공성 지지체와 중간층의 영향 (The Effect of Porous Support and Intermediate Layer on the Silica-zirconia Membranes for Gas Permeation Performance)

  • 이혜련;서봉국
    • 멤브레인
    • /
    • 제25권1호
    • /
    • pp.15-26
    • /
    • 2015
  • 본 연구에서는 기공의 크기가 큰 다공성 지지체를 $3{\sim}4{\mu}m$, 150 nm의 크기를 갖는 ${\alpha}$-알루미나 입자를 물과 실리카-지르코니아 용액에 각각 분산시키는 방법으로 표면 개질을 하였다. $3{\sim}4{\mu}m$ 크기의 알루미나 입자가 분산된 용액을 이용하여 금속 지지체 및 알루미나 지지체에 코팅하였을 때, 코팅횟수가 증가할수록 지지체의 표면의 큰 기공이 감소하였고, 여기에 150 nm 크기의 알루미나 입자가 분산된 용액으로 추가 코팅을 하면 작은 크기의 알루미나 입자가 기공 사이사이에 들어가면서 지지체를 좀 더 매끄럽게 개질하는 역할을 하는 것을 확인하였다. 특히 실리카-지르코니아 용액을 분산매로 하여 표면 개질을 한 경우, 알루미나 입자가 실리카-지르코니아 층에 촘촘하게 박힌 모양으로 고정이 되어 지지체 개질에 효과적임을 확인하였다. 이러한 방법으로 제조된 실리카-지르코니아 분리막의 기체투과도는 상온에서 각각 $1.8-8.4{\times}10^{-4}mol{\cdot}m^{-2}{\cdot}s^{-1}{\cdot}Pa^{-1}$, $3.3-5.0{\times}10^{-5}mol{\cdot}m^{-2}{\cdot}s^{-1}{\cdot}Pa^{-1}$이며 수소/질소 선택도는 Knudsen 분포를 보였다. 표면 개질된 지지체에 다양한 분리층을 형성하는 방법으로 무기 분리막 응용에 이용할 수 있을 것으로 예상된다.