• Carbon letters
• /
• v.15 no.1
• /
• pp.71-76
• /
• 2014

Activated carbon nanofibers (ACNF) were prepared from polyacrylonitrile (PAN)-based nanofibers using $CO_2$ activation methods with varying activation process times. The surface and structural characteristics of the ACNF were observed by scanning electron microscopy and X-ray diffraction, respectively. $N_2$ adsorption isotherm characteristics at 77 K were confirmed by Brunauer-Emmett-Teller and Dubinin-Radushkevich equations. As experimental results, many holes or cavernous structures were found on the fiber surfaces after the $CO_2$ activation as confirmed by scanning electron microscopy analysis. Specific surface areas and pore volumes of the prepared ACNFs were enhanced within a range of 10 to 30 min of activation times. Performance of the porous PAN-based nanofibers as an electrode for electrical double layer capacitors was evaluated in terms of the activation conditions.

• Journal of the Korean Society of Industry Convergence
• /
• v.26 no.6_3
• /
• pp.1333-1339
• /
• 2023

To produce activated carbon fibers, the process is carried out through either physical activation method or chemical activation method. In this study, we present the results regarding the characteristics of activated carbon fibers manufactured under various conditions through the quantitative control of steam. The yield after activation indicates a decreasing trend with the increase in steam quantity and activation time. Additionally, specific surface area characteristics exhibit variations based on activation time and steam flow rate. The SEM analysis results reveal that higher steam flow rates lead to the presence of both mesopores and macropores on the surface of activated carbon fibers (ACF).

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.213-214
• /
• 2009

A thin film hydroxyapatite (HA) films was deposited on anodized titanium by RF sputtering method. The anodized titanium enhanced the biocompatibility of the Ti and the bioactivity was improved further by the HA deposited on the anodized Ti. $TiO_2$ layer with $0.2{\sim}0.5{\mu}$ diameter pore size was formed on the Ti surface by anodization. Anodized $TiO_2$ layer analysis HA film deposited, oxide pore size and number decreased compared with non-HA deposited surface. The corrosion resistance of HA deposited/anodized Ti was higher than that of the non-treatment Ti alloy in Hank's solution, indicating better protective effect. From the results of cell culture using MTT assays, the best cell proliferation showed in HA deposited surface after anodization of Ti surfaces compared with another surface treatment.

• Korean Journal of Materials Research
• /
• v.22 no.6
• /
• pp.321-327
• /
• 2012

The production of functional activated carbon materials starting from inexpensive natural precursors using environmentally friendly and economically effective processes has attracted much attention in the areas of material science and technology. In particular, the use of plant biomass to produce functional carbonaceous materials has attracted a great deal of attention in various aspects. In this study the preparation of activated carbon has been attempted from rice husks via a chemical activation-assisted microwave system. The rice husks were milled via attrition milling with aluminum balls, and then carbonized under purified $N_2$. The operational parameters including the activation agents, chemical impregnation weight ratio of the calcined rice husk to KOH (1:1, 1:2 and 1:4), microwave power heating within irradiation time (3-5 min), and the second activation process on the adsorption capability were investigated. Experimental results were investigated using XRD, FT-IR, and SEM. It was found that the BET surface area of activated carbons irrespective of the activation agent resulted in surface area. The activated carbons prepared by microwave heating with an activation process have higher surface area and larger average pore size than those prepared by activation without microwave heating when the ratio with KOH solution was the same. The activation time using microwave heating and the chemical impregnation ratio with KOH solution were varied to determine the optimal method for obtaining high surface area activated carbon (1505 $m^2$/g).

• Journal of Korean society of Dental Hygiene
• /
• v.14 no.4
• /
• pp.585-591
• /
• 2014

Objectives : The purpose of this study was to investigate of the color change, tooth surface and intra-pulpal temperature of tooth bleaching by light activation Methods : Forty-eight extracted bovine teeth were immersed into a tea solution for 24 hours. The specimens were randomly divided into four groups(n=15):(G1) 15% HP + without light activation, (G2) 15% HP + light activation, (G3) 25% HP + without light activation, (G4) 25% HP + light activation. All specimens were bleached for 15 minutes three times. The spectrophotometer (CM-2600d, Konica Minolta, Osaka, Japan) was used including before bleaching, immediately after bleaching, 1 week, 1 and 3 months after the end of bleaching. The temperature rise were measured in the pulpal chamber and tooth surface with a digital thermocouple thermometer(Termopar Digital Multimeter, Tektronix DMM916, USA). Between the tested time points, the specimens were stored in distilled water. The data were analyzed by ANOVA, t-test and Tukey's post hoc test set at 0.05. Results : There was no significant color change by the use of light after the bleaching treatment(p>0.05). The dental bleaching treatments of teeth with 15% HP and 25% HP did not seem to be more effective when light source was used. There was no difference in color stability between groups within three month(p>0.05). There was an increase in tooth surface and pulp temperature, but it was not sufficient to cause damage to the pulp. Conclusions :The use of light activation has no obvious effective impact on the tooth bleaching effect.

• Korean Journal of Applied Biomechanics
• /
• v.15 no.1
• /
• pp.63-74
• /
• 2005

J. R. PARK. The Analysis of Electrimyography and Kinematic of Kumdo Player's Head Hitting. Korean Journal of Sport Biomechanics, Vol. 15, No. 1, pp. 63-74, 2005. The purpose of this study were to describe and compare the selected electromyographical muscle activities of arm and kinematic data of kumdo player's head hitting. Using surface electrode electromyography, we evaluated muscle activity in 6 male players during head hitting motion. Surface electrodes were used to record the level of muscle activity in the carpi radialis, deltoid, triceps, biceps muscles during the player's head hitting. These signals were compared with %RVC(Reference voluntary contraction) which was normalized by IEMG(Integrated EMG). The kumdo head hitting motion was divided into two phases: back swing, down swing. we observed patterns of arm muscle activity throughout two phases of the kumdo head hiting The results can be summarized as follows: right elbow angle had decreased and left deltoid muscle's activation had higher than right deltoid muscle's activation, right carpi radialis muscle's activation had higher than left carpi radialis muscle's activation in back swing phase, knee angle had decreased and left triceps muscle's activation had higher than right triceps muscle's activation, right deltoid muscle's activation had higher than left deltoid muscle's activation, right carpi radialis muscle's activation had higher than left carpi radialis muscle's activation in down swing phase

• Carbon letters
• /
• v.8 no.1
• /
• pp.37-42
• /
• 2007

Carbon nanofiber (CNF) grown catalytically was chemically activated with KOH to attain structural change of CNF. The structural changes of CNF through KOH activation were investigated by using BET and SEM. From the results of BET, it was found that KOH activation was effective to develop particular sizes of pores on the CNF surface, increasing the surface area of CNF. Activated CNF was applied as an anode catalyst support of fuel cell. The effects of different activation conditions including the activation temperature and the activation time on the specific surface area of the CNF activated with KOH were investigated to obtain appropriate structure as a catalyst support. The 60 wt% Pt-Ru catalyst prepared was observed by using TEM and XRD.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.3
• /
• pp.132-141
• /
• 2010

NiTi alloy has been used for orthodontic wire due to good mechanical properties, such as elastic strength and frictional resistance, combined with a high resistance to corrosion. Recently, these wire were coated by polymer and ceramic materials for aesthetics. The purpose of this study was to investigate surface characteristics of polymer coated NiTi alloy wire for orthodontics using various instruments. Wires (round type and rectangular type) were used, respectively, for experiment. Polymer coating was carried out for wire. Specimen was investigated with field emission scanning electron microscopy(FE-SEM), energy dispersive x-ray spectroscopy(EDS) and atomic force microscopy(AFM). The phase transformation of non-coated NiTi wire from martensite to austenite occurred at the range of $14{\sim}15^{\circ}C$, in the case of coated wire, it occurred at the range of $16{\sim}18^{\circ}C$. Polymer coating on NiTi wire surface decreased the surface defects such as scratch which was formed at severe machined surface. From the AFM results, the average surface roughness of non-coated and coated NiTi wire was 13.1 nm, and 224.5 nm, respectively. From convetional surface roughness test, the average surface roughness of non-coated and coated NiTi wire was $0.046{\mu}m$, and $0.718{\mu}m$, respectively.

• Journal of the Korean Wood Science and Technology
• /
• v.16 no.3
• /
• pp.5-16
• /
• 1988

This experiment was executed to investigate the effect of activation of veneer surface by oxidizing agents, hydrogen peroxide and nitric acid, on bonding characteristics of Malas(Homalium foetidum Benth) plywood, in which the effects of these oxidizing agents amount, pretreatment time, and pressing time and temperatue on shear strength of the plywood were examined and discussed. In this research the activation of veneer surface by oxidants was effective in raising shear strength but the difference in shear strength was not observed between hydrogen peroxide and nitric acid treatment. Hydrogen peroxide treatment, however, seemed to be more profitable to industrial application because of its lower concentration and easier handling than nitric acid. The bonding method by lignin-phenol adhesive through surface activation revealed inferior shear strength to phenol- and urea-formaldehyde adhesive but superior water resistance to urea-formaldehyde adhesive and this bonding method, in addition, have the advantage of lower cost compared with phenol-formaldehyde adhesive, Therefore, this bonding method by lignin-phenol adhesive through surface activation seemed to economical in manufacturing of water-resistant wood panel materials in future.

• Journal of the Korean Ceramic Society
• /
• v.36 no.6
• /
• pp.577-582
• /
• 1999

Activated carbon fibers were prepared from stabilized PAN fibers by chemical activation using hydroxide. The variations in specific surface area amount of iodine adsorption micro-structure and pore size distribution in the activated carbon fibers after the activation process were discussed. In the chemical activation using potassium hydroxide specific surface area of about 2545m2/g and amount of iodine adsorption of 2049 mg/g were obtained at the condition of KOH/fiber ratio of 1 and 800$^{\circ}C$ Nitrogen adsorption isotherms for PAN based activated carbon fibers showed the type I in the Brunauer-Deming-Deming-Teller classification indicating the micro-pores consisting the activated fibers.