• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.06a
• /
• pp.99-102
• /
• 2006

In the present study, the blow forming characteristics of AZ31 sheet was investigated to test the feasibility of the practical application of wrought Mg alloys. Mg alloys have drawn a huge attention in the field of transportation and consumer electronics industries since it is the lightest alloy which could be industrially applicable. Most Mg alloy components have been fabricated by casting method. However, there have been a lot of research activities on the wrought alloys and their plastic forming process recently. Shallow cups for the small electronics cases have been stamped with warm die system. However, some technical issues will challenge Mg forming when large parts are considered with warm die system over $200^{\circ}C$. Most of all, thermal expansion of die system will deteriorate a die accuracy. On the other hand, blow forming does not have a problem with inaccuracy with die system. In this study, tensile tests were followed by blow forming at various temperature and pressure. AZ31 sheet showed a superplastic deformation behavior with extensive grain boundary sliding at the temperature above $300^{\circ}C$. However, the deformation behavior was likely to differ depending on stress condition.

• Transactions of Materials Processing
• /
• v.18 no.4
• /
• pp.317-322
• /
• 2009

Superplastic deformation behavior of a Zn-0.3 wt.% Al was investigated. Grain sizes of $1{\mu}m$ and $10{\mu}m$ were obtained by a thermomechanical treatment. A series of load relaxation and tensile tests were conducted at various temperatures ranging from RT ($24^{\circ}C$) to $200^{\circ}C$. A large elongation of 1400% was obtained at room temperature in the specimens with the grain size of $1{\mu}m$. In the case of specimens with the grain size of $10{\mu}m$, relatively lower elongation at room temperature was obtained and, as the temperature increases above $100^{\circ}C$, a high elongation of about 400 % has been obtained at $200^{\circ}C$ under the strain rate of $2{\times}10^{-4}/s$. Dynamic materials model (DMM) has been employed to explain the contribution from GBS of Zn-Al alloy. Power dissipation efficiency for GBS was evaluated as above 0.4 and found to be very close to the unity as strain rate decreased and temperature increased, suggesting that GBS could be regarded as Newtonian viscous flow.

• Journal of the Korean Society for Heat Treatment
• /
• v.10 no.2
• /
• pp.81-92
• /
• 1997

The effect of alloying elements, precipitate size, its distribution, and dislocation substructure resulted from warm rolling or cold rolling in the superplastic Al-Mg alloy system was investigated. One of the major requirements for fine structure superplasticity is that the grain size should be very small. Fine grain structure is controlled by the dislocation substructure and the dynamic recrystallization during hot or warm working. The recovery of Al-Mg base alloys was constrained resulting in relatively high dislocation density when the alloys were warm rolled. In particular, Al-Mg-Zr alloy exhibited the smallest sub-grain size among Al-Mg alloys containing Mn, Cu, Zr as a third element. The Al-Mg-Mn alloy cold rolled 80% after hot rolling showed the maximun strain rate sensitivity exponent, m, of 0.75 under strain rate of $7.1{\times}10^{-4}/s$ at $500^{\circ}C$. The elongation of the alloys was limited in spite of high m values due to large dispersoids containing appreciable amount of Fe impurities.

• Journal of the Korean Society for Precision Engineering
• /
• v.26 no.10
• /
• pp.89-96
• /
• 2009

In recent years, there has been a considerable interest in the application of super plastic forming in the aircraft and automotive industries. This requires a detailed design of the technological process in order to exploit its peculiar potentialities better. Nowadays, the finite element method is used to plan the sheet metal forming processes whose simulation requires determination of material constants for super plastic materials. The present work is aimed to show a simple method to characterize super plastic materials duplex stainless steel which was formed by a constant gaspressure to hemispheres with and without back pressure. The forming operation was performed using an in-house designed and built biaxial forming apparatus. The temporal change of dome heights of hemispheres were measured for applying the pressures. The flow stresses and strain rates developed at the top of the dome during the forming step were shown to follow closely the flow stress - strain rate relationship obtained from the strain rate change tests performed at the same temperature.

• Korean Journal of Materials Research
• /
• v.5 no.3
• /
• pp.371-378
• /
• 1995

YBCO 산화물 초전도체의 초소성 변형에 대한 최적 변형조건을 파악하고자 80$0^{\circ}C$~93$0^{\circ}C$의 온도범위에서 1.0 $\times$ $10^{-3}$s^{-1}$!1.0 $\times$ $10^{-7}$s^{-1}$의 초기변형속도로 압축시험을 수행하였다. 변형속도 민감지수는 m=0.50 $\pm$ 0.1로 나타났다. 이는 결정립계 미끄러지\ulcornerㄹ 주 변형기구로 하는 초소성임을 의미한다. 결정립크기에 따른 유동응력과의 관계는 $\sigma$\propto$d^{1.8 $\pm$ 0.3}$의 지수함수식을 이루고 있으며 Nabarro-Hering 크\ulcorner과 상응하는 격자확산이 확산경로임을 보였다. 초소성 변형에 대한 활성화에너지는 Q=571 $\pm$ 30 kJ/mole이었다. 본 실험온도 구간에서 압축 변형시 변형속도, 변형응력 및 결정립크기에 따른 고온 변형거동 관계식은 $\varepsilon$=A$\sigma$^{2.00 $\pm$ 0.04 - 1.8 $\pm$ 0.3}$ exp(-571 $\pm$ 30kJ/RT)와 같이 유도 되었다. 본 실험조건에서 최적 초소성 변형조건은 86$0^{\circ}C$ 부금, 초기변형속도 ~1.0 $\times$ $10^{-4}$S^{-1}$이었다.

• Journal of Korea Foundry Society
• /
• v.17 no.3
• /
• pp.252-257
• /
• 1997

The 8 mm dia: Sn-38%Pb eutectic alloy rods were produced by use of the horizontal continuous casting process with the heated mold and chill cast process. The cast rods were rolled into 2.0${\sim}$0.5 mm thick plates and structural and mechanical properties were examined. The results revealed that the plates produced by the continuous casting process with the heated mold show much higher superplasticity at ambient temperature (1550% elongation at 0.5mm thick plate and 0.5mm/min strain rate) than the plates procuced by chill cast process (630% elongation). Such a high superplasticity of the continuous cast plates is due to the high-quality plates free from any inside and surface defects with fine and uniform distribution of eutectic phases.

• Korean Journal of Materials Research
• /
• v.30 no.2
• /
• pp.57-60
• /
• 2020

Titanium aluminides have attracted special interest as light-weight/high-temperature materials for structural applications. The major problem limiting practical use of these compounds is their poor ductility and formability. The powder metallurgy processing route has been an attractive alternative for such materials. A mixture of Ti and Al elemental powders was fabricated to a mechanical alloying process. The processed powder was hot pressed in a vacuum, and a fully densified compact with ultra-fine grain structure consisting of Ti₃Al intermetallic compound was obtained. During the compressive deformation of the compact at 1173 K, typical dynamic recrystallization (DR), which introduces a certain extent of grain refinement, was observed. The compact had high density and consisted of an ultra-fine equiaxial grain structure. Average grain diameter was 1.5 ㎛. Typical TEM micrographs depicting the internal structure of the specimen deformed to 0.09 true strain are provided, in which it can be seen that many small recrystallized grains having no apparent dislocation structure are generated at grain boundaries where well-developed dislocations with high density are observed in the neighboring grains. The compact showed a large m-value such as 0.44 at 1173 K. Moreover, the grain structure remained equiaxed during deformation at this temperature. Therefore, the compressive deformation of the compact was presumed to progress by superplastic flow, primarily controlled by DR.

• Transactions of Materials Processing
• /
• v.19 no.6
• /
• pp.352-356
• /
• 2010

This paper was designed to fabricate the micro-spur gear by the LIGA and hybrid powder extrusion process. It is important to manufacture a micro-die with a high aspect ratio and determine appropriate extrusion conditions for a microforming. Ni has been used to fabricate micro-dies. LIGA process was capable to produce micro-extrusion dies with close tolerance, longer bearing length and adequate surface quality. Superplastic Al-78Zn powders have the great advantage in achieving deformation under low stresses and exhibiting good micro-formability with average strain rate raging from $10^{-3}$ to $10^{-2} s^{-1}$ and constant temperature ranging from 503 to 563K. Al-78Zn powders were compacted into a cylindrical shape ($\Phi3\times$h10mm) under compressive force of 10kN and, subsequently, the compacted powders were extruded by the hybrid powder extrusion process controlling of the temperature holing time for a improvement on formability of Al-22Zn powder. Micro-extrusion has succeeded in forming micro-gear shafts.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.05a
• /
• pp.172-175
• /
• 2001

The high temperature deformation behavior of two-phase gamma TiAl alloy has been investigated with the variation of temperature and ${\gamma}/{\alpha}_2$ volume fraction. For this purpose, a series of load relaxation tests and tensile tests have been conducted at temperature ranging from 800 to $1050^{\circ}C$. In the early stage of the deformation as in the load relaxation test experimental flow curves of the fine-grained TiAl alloy are well fitted with the combined curves of two processes (grain matrix deformation and dislocation climb) in the inelastic deformation theory. The evidence of grain boundary sliding has not been observed at this stage. However, when the amount of deformation is large (${\epsilon}{\approx}$ 0.8), flow curves significantly changes its shape indicating that grain boundary sliding also operates at this stage, which has been attributed to the occurrence of dynamic recrystallization during the deformation. With the increase in the volume fraction of ${\alpha}_2$-phase, the flow stress for grain matrix deformation increases since ${\alpha}_2$-Phase is considered as hard phase acting as barrier for dislocation movement. It is considered that cavity initiation is more probable to occur at ${\alpha}_2/{\gamma}$ interface rather than at ${\gamma}/{\gamma}$ interface.

• Journal of Korea Technology Innovation Society
• /
• v.8 no.3
• /
• pp.1027-1059
• /
• 2005

The purpose of this paper is to analyze the dynamic characteristics of innovation sources such as scientific knowledges, processing technologies and user's needs in advanced metals technology. The journal articles data of four advanced materials are analyzed; amorphous metals, superplastic materials, shape memory alloys and aluminum-lithium alloy. Some regularities are found from the analysis of the four materials. The innovation proceeds through close interactions among the innovation sources. As the innovation proceeds, the relative importance of each source changes: scientific knowledge initiates the innovation and becomes the most important source in the first phase, then the processing technologies increase importance in the second phase, and then scientific knowledge, again, becomes the leading factor of innovation. Scientific knowledge and processing technology take turns leading the innovation. The impacts of users' needs to the innovation increase more and more as innovation proceeds. The results of analysis imply to the policy makers that emphasis of policy, and therefore the allocation of sources for innovation, should vary along the phases in the life cycle of advanced metals technology.