• 한국초전도학회:학술대회논문집
• /
• v.13
• /
• pp.30-30
• /
• 2003

• 한국초전도학회:학술대회논문집
• /
• 2008.08a
• /
• pp.61-61
• /
• 2008

• Journal of Powder Materials
• /
• v.15 no.3
• /
• pp.182-187
• /
• 2008

Carbon was known to be one of effective additives which can improve the flux pinning of $MgB_2$ at high magnetic fields. In this study, glycerin $(C_3H_8O_3)$ was selected as a chemical carbon source for the improvement of critical current density of $MgB_2$. In order to replace some of boron atoms by carbon atoms, the boron powder was heat-treated with liquid glycerin. The glycerin-treated boron powder was mixed with an appropriate amount of magnesium powder to $MgB_2$ composition and the powder pallets were heat treated at $650^{\circ}C\;and\;900^{\circ}C$ for 30 min in a flowing argon gas. It was found that the superconducting transition temperature $(T_c)$ of $Mg(B_{1-x}C_x)_2$ prepared using glycerin-treated boron powder was 36.6 K, which is slightly smaller than $T_c$(37.1 K) of undoped $MgB_2$. The critical current density $(J_c)$ of $Mg(B_{1-x}C_x)_2$ was higher than that of undoped $MgB_2$ and the $T_c$ improvement effect was more remarkable at higher magnetic fields. The $T_c$, decrease and $J_c$ increase associated with the glycerin treatment for boron powder was explained in terms of the carbon substitution to boron site.

• Progress in Superconductivity and Cryogenics
• /
• v.14 no.3
• /
• pp.53-59
• /
• 2012

Adiabatic demagnetization refrigerator (ADR) for hydrogen re-liquefaction operating between 24 K and 20 K has been designed. $Dy_{0.9}Gd_{0.1}Ni_2$, whose Curie temperature is 24 K, is selected as a magnetic refrigerant. The magnetic refrigerant powder is sintered with oxygen-free high purity copper (OFHC) powder to enhance its effective thermal conductivity as well as to achieve relatively high frequency. A perforated plate heat exchanger (PPHE) operated with forced convection is utilized as a heat switch. The forced convection heat switch is expected to have fast response relative to a conventional gas-gap heat switch. A conduction-cooled high Tc superconducting (HTS) magnet is employed to apply external magnetic field variation on a magnetic refrigerant. $2^{nd}$ generation GdBCO coated conductor HTS tape with Kapton$^{(R)}$ insulation (SUNAM Inc.) will be utilized for the HTS magnet. The magnetization and demagnetization processes are to be achieved by the AC operation of the HTS magnet. The designed magnetic field and target ramp rate of the HTS magnet are over 4 T with 180 A and 0.4 T/s, respectively. AC loss distribution on HTS magnet is theoretically estimated.

• Progress in Superconductivity and Cryogenics
• /
• v.22 no.4
• /
• pp.20-23
• /
• 2020

Among many variables in processing the high performance MgB2 bulk superconductors, simple and important approach is to optimize the size dependence of the Mg & B raw powders. The present study is dedicated towards the variation in superconducting properties of MgB2 depending upon the various combination of Mg & B powders with the two different particle sizes respectively. From morphological investigation of the MgB2 samples, narrow and long pores are observed when the larger Mg powders are used, whereas it is rather like the oval shapes with the smaller Mg powders. Also, it can be seen that the connectivity of the MgB2 samples is much enhanced with the smaller size of the B powders. Jc-H properties of the MgB2 samples also indicate that the highest Jc can be obtained when using the smaller size of the B powder with the combination of the smaller Mg powders than that of the larger Mg powders. If the cases with the larger B powers, it is more favorable to select the larger Mg powders with the better Jc-H properties considering shorter diffusion length of Mg and more homogeneous mixture between the Mg & B powders.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.3
• /
• pp.13-17
• /
• 2006

The effect of the addition of the nano size $Y_2O_3$ powder on the microstructurte and superconducting properties of YBCO thin film deposited on LAO single crystalline substrate by TFA-MOD method was studied. Nano size $Y_2O_3$ powder was added to the stoichiometric precursor solution with a cation ratio of Y : Ba . Cu = 1 : 2 : 3 prepared using TFA as chelating agent. Precursor solutions with and without $Y_2O_3$ addition were coated on $LaAlO_3(100)$ single crystalline substrates by dip coating method. Calcination and conversion heat treatments were performed in controlled atmosphere containing moisture Current carrying capacity(Jc) of YBCO film was enhanced about 50% by $Y_2O_3$ doping and it is thought to be due to the better connectivity of YBCO grains and/or the flux pinning by the $Y_2O_3$ particles embedded in YBCO grains.

• Progress in Superconductivity and Cryogenics
• /
• v.19 no.1
• /
• pp.42-46
• /
• 2017

The effects of the heat treatment temperature ($600^{\circ}C-1050^{\circ}C$) on the formation of $MgB_2$ and the superconducting properties have been examined. The self-synthesized $MgB_4$ and commercial Mg powders were used as raw materials for the formation of $MgB_2$. The superconducting critical temperatures ($T_cs$) of $MgB_2$ bulk superconductors prepared at $600^{\circ}C-850^{\circ}C$ were as high as 37-38 K regardless of the heat treatment temperature. However, because $MgB_4$ is more stable than $MgB_2$ at above $850^{\circ}C$, no superconducting signals were detected in the susceptibility-temperature curves of the samples prepared above $850^{\circ}C$. As for the critical current density ($J_c$), the sample heat-treated at a low temperature ($600^{\circ}C$) for a prolonged period (40 h) showed a Jc higher than those prepared at $650^{\circ}C-850^{\circ}C$ for a short period (1 h). The FWHM (full width at half maximum) result showed that the grain size of $MgB_2$ of the $600^{\circ}C$ sample was smaller than that of the other samples. The high $J_c$ of the $600^{\circ}C$sample is attributed to the presence of large numbers of grain boundaries, which can act as flux pinning centers of $MgB_2$.

• Progress in Superconductivity and Cryogenics
• /
• v.19 no.1
• /
• pp.47-50
• /
• 2017

Carbon is proven to be very effective in pinning the magnetic vortices and improving the superconducting performance of $MgB_2$ at high fields. In this work, we have used polymethyl methacrylate (PMMA) polymer as a safe and cost effective carbon source. The effects of molecular weight of PMMA on crystal structure, microstructure as well as on superconducting properties of $MgB_2$ were studied. X-ray diffraction analysis revealed that there is a noticeable shift in (100) and (110) Bragg reflections towards higher angles, while no shift was observed in (002) reflections for $MgB_2$ doped with different molecular weights of PMMA. This indicates that carbon could be substituted in the boron honeycomb layers without affecting the interlayer interactions. As compared to undoped $MgB_2$, substantial enhancement in $J_c(H)$ properties was obtained for PMMA-doped $MgB_2$ samples both at 5 K and 20 K. The enhancement could be attributed to the effective carbon substitution for boron and the refinement of crystallite size by PMMA doping.

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.74-79
• /
• 2007

We characterized the highly refined boron precursor powders which were attrition milled for different milling times. $MgB_2$ powder precursor was formed from elemental crystalline Mg and amorphous B powder. The microstructure was investigated by SEM. SEM results indicate that the size of the milled powders was reduced with increasing milling time, which were varied from 0 to 8 hours. We also studied thermal behavior of the starting precursor by DSC as a function of milling time. The thermal behavior of the powder precursors was influenced by milling time. In order to determine the thermal events at DSC peaks, we annealed the milled powder mixture at $600^{\circ}C$ and $650^{\circ}C$ under protective gas and then analyzed the formation of $MgB_2$ by the XRD. We observed that superconducting $MgB_2$ phase was formed at lower temperature by the longer high energy milling. These results show that the high energy milling of the boron precursor powder can improve the reactivity for the formation of $MgB_2$.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1245-1246
• /
• 2006

We fabricated Bi-2212/$SrSO_4$ composite superconductors and evaluated the effects of the powder mixing method and melting temperature on their microstructure and superconducting properties. The Bi-2212 powders were mixed with $SrSO_4$ by hand-mixing (HM) and planetary ball milling (PBM) and then the powder mixtures were melted at $1100^{\circ}C{\sim}1200^{\circ}C$, solidified, and annealed. We found that the powder mixture prepared by PBM was finer and more homogeneously mixed than that prepared by HM, resulting in more homogeneous microstructure and smaller $SrSO_4$ and second phases after annealing.