• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04b
• /
• pp.743-746
• /
• 1998

Pine bark waste was delignified with various sulfite liquors in order to use its spent liquor as concrete additives. The bark was easily deliginfied in alkaline sulfite-anthraquinone(ASAQ) cooking, resulting in more than 90% delignification. The dispersing ability of the ASAQ spent liquor was almost equivalent to or better than that of the commercial wood lignosufonate(CSL), Sanflo R.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.36 no.5 s.108
• /
• pp.78-84
• /
• 2004

Lignin precipitated from black liquor of soda pulping of bagasse was used to prepare cation-exchange resin. The effect of sulfuric acid treatment, concentration of phenol and formaldehyde on the properties of the prepared cation-exchange resin was investigated. It was found that sulfonated resinified phenolated lignin gave a resin with an ion-exchange capacity higher than that of resin, which resulted from sulfonation of resinified lignin at zero phenol concentration. Infrared spectroscopy of the prepared ion-exchange resin shows anew bands at 1060, 1160, 1280 and $1330\;cm^{-1}$ which indicated to the presence of $SO_{3}$.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1996.10a
• /
• pp.71-72
• /
• 1996

Polyetherimide(PEI)계의 고분자는 막 성능이 우수하고 내열성과 내유기용매성 등이 우수한 열가소성수지로서 film, sheet, tubular형으로 만들 수 있어 한외여과막이나 역삼투막, 기체분리막 등에 이용되고 있다. 한편 투과속도를 높이고, fouling을 줄이기 위한 친수성 향상은 막 소재의 화학적 개질에 있어서 주된 목표이다. sulfonation은 막 재질의 소수성을 감소시켜 water permeability를 향상시키는데 있어서 매우 유용한 방법으로 이온교환수지, 이온교환막, anion형 하전막의 제조에 이용되어 왔다. 본 실험에서는 polyetherimide계 고분자를 chlorosulfonic acid(CSA)를 이용하여 술폰화시킨 sulfonated polyetherimide(SPEI)를 제조하여 막 성능을 측정하였다.

• Korean Membrane Journal
• /
• v.5 no.1
• /
• pp.10-17
• /
• 2003

1,3,5-Sustitituted polyphenylene type dendrimers were synthesized. The dendrimer was heated in cone. H$_2$SO$_4$ at 120$^{\circ}C$. The reaction mixture was precipitated to ether after simple filtration to get para-sulfonated dendrimer as the chief product. To give mechanical properties to the sulfonated dendrimer, it was partially cross-linked with phenyl ether in the medium of P$_2$O$\sub$5/ and CH$_3$SO$_3$H.

• Bulletin of the Korean Chemical Society
• /
• v.11 no.5
• /
• pp.403-406
• /
• 1990

Two types of new silica catalysts modified with benzenesulfonic acid derivatives were prepared by esterification or phenylation followed by sulfonation. Both catalysts thus prepared were tested as acid catalysts for 2-propanol dehydration and cumene dealkylation reactions. B catalyst () were more active than A catalyst (). Highter catalytic activity for B catalyst may be accounted for by higher resistance to water, higher acid strength, more acidity, and better thermal stability as compared with A catalyst.

• Magazine of the Korea Concrete Institute
• /
• v.7 no.2
• /
• pp.175-182
• /
• 1995

Styrene-Maleic anhydride copolymer (SMA) was prepared by the radical copolmerization of styrene and maleic anhydride using ${\alpha}-{\alpha}'$ azobis(isobutyronitrile) as an initiatrr. SMA was further reacted with m-amino phenol to obtain aminophenol-substituted SMR (mSMA). Sulfonated SMA and mSMA were also prepared by the reaction of copolymers with sulfuric acid The copolyniers were characterized by infrared spectroscopy. It was found from the results of elemental analysis that the substitution degree of aminophenol in the mSMR is 44% and the degree is lowered to 35% after sulfonation. The percentage of copolymers adsorbed on the surface of cement particles was increased with a decrease of added copolymers. While, the arnourit of sulfonated SMA absorbed on the surface of cement particles was larger than that of the sulfonated mSMA The copolymers synthesized in this study are probably expected as a high range water reducer for coiicxte.

• Journal of Hydrogen and New Energy
• /
• v.25 no.6
• /
• pp.561-569
• /
• 2014

Ceria ($CeO_2$) was used to increase the durability of the membrane in the polymer electrolyte membrane water electrolysis (PEMWE) circumstance. The sulfonated polyether ether ketone (SPEEK) as polymer matrix was prepared in the sulfonation reaction of polyether ether ketone (PEEK) to improve electrochemical characteristics. After sulfonation reaction, the organic-inorganic blended composite membranes were prepared by means of sol-gel casting method with loading the highly dispersed $CeO_2$ and Cs-substituted molybdophosphoric acid (Cs-MoPA) with cross-linking agent (tetrapropyl orthosilicate). Consequently, the composite membrane CL-SPEEK/Silane 4wt%/Cs-MoPA/Ceria(1%) showed the improved characteristics such as 82% of water content, 0.11136 S/cm of proton conductivity at $80^{\circ}C$, 55.50 MPa of tensile strength and 4.37% of breeding out of MoPA.

• Polymer(Korea)
• /
• v.25 no.5
• /
• pp.642-648
• /
• 2001

An attempt was made to synthesize an ammonia adsorbent by the photo-induced grafting of styrene (St) onto polypropylene (PP) nonwoven using benzoin ethyl ether (BEE) as a photosensitizer with urea and trimethylol propane triacrylate in methanol medium. As styrene concentration was increased, the graft yield was increased. It was also found that the graft yield increased with reaction time. The polypropylene grafted with styrene (PP-g-St) was sulfonated by chlorosulfonic acid in dichloroethane and complexed with several metal ion, such as $cO^{+2}$, $nI^{+2}$, $cU^{+2}$, $Zn^{+2}$. The amount of ammonia gas adsorbed by these sample was dependent on the degree of sulfonation, adsorption time, and ammonia gas pressure. The adsorption capacity of ammonia gas by the sulfonated PP-g-St(SPP-g-St) nonwoven with 4. 25 mmol $H^+$/g was 6.61 mmol/g. Metal ion complexed SPP-g-St nonwovens had higher adsorption capacity than SPP-g-St nonwoven and the $Co^{+2}$ complexed SPP-g-St showed 9.90 mmol $NH_3$/g, which was much higher than that of active carbon or silica gel.

• Polymer(Korea)
• /
• v.31 no.1
• /
• pp.74-79
• /
• 2007

Polypyrrole (PPy) was made by an emulsion polymerization using iron (III) chloride ($FeCl_3$) as an initiator and dodecyl benzene sulfuric acid (DBSA) as an emulsifier and dopant. Poly (2,6-dimethyl-1,4-phenylene oxide) (PPO) was sulfonated by chlorosulfonic acid (CSA). The cathode was composed of $PPy^+DBS^-$ complex, conductor powder, and PPO or sulfonated poly (2,6-dimethyl-1,4-phenylene oxide) (SPPO) as a binder or dopant. The charge-discharge performance of $PPy^+DBS^-/SPPO$ cathode was increased as the extent of about 50%, than $PPy^+DBS^-/PPO$. This is because SPPO played a role as a binder as well as a dopant. In addition, sulfonation brings out the increase of miscibility between PPy and SPPO, and the increase of contact area between cathode and electrolyte.

• Polymer(Korea)
• /
• v.31 no.1
• /
• pp.1-7
• /
• 2007

In this study, the sulfonated ion exchange fiber was synthesized by $Co^{60}\;{\gamma}-ray$ radiation-induced graft copolymerization. Degree of grafting (DG) increased with increasing the total dose and showed the highest value at 50 v/v% styrene monomer. And also, the degree of sulfonation (DS) increased with increasing the DG and reaction temperature. DS showed the maximum value at 20 min. Ion exchange capacity and swelling ratio of ion exchange fibers increased with increasing the DS and their maximum values were 4.76 meq/g and 23.5%, respectively. Ammonia adsorption increased as increasing the ammonia concentration and ion exchange capacity and remained constant over 10 cycles.