• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1041-1042
• /
• 2006

High heat-resistant Al-Fe-V-Si and Al-Fe-V-Si-X rapidly solidified powder metallurgy (RS P/M) alloys have been developed under well-controlled high purity argon gas atmosphere. The $Al_{90.49}Fe_{6.45}V_{0.68}Si_{2.38}$ (at. %) RS P/M alloy exhibited high elevated-temperature strength exceeding 300 MPa and good ductility with elongation of 6 % at 573 K. Reduction of $H_2O$ partical pressure in P/M processing atmosphere led to improvement in mechanical properties of the powder-consolidated alloys under elevated-temperature service conditions. Ti addition to the Al-Fe-V-Si conduced to enhancement of the strength at room temperature. The tensile yeild strength and ultimate strenght were 545 MPa and 722 MPa, respectively.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.133-134
• /
• 2021

In this study, the effects of aggregates on the properties of concrete as a study to determine the mechanical properties of high-temperature damaged concrete were examined. The samples to be reviewed are cement paste, mortar, and concrete, and the strength characteristics were reviewed after heating the compression strength and tensile strength properties. The increase in magnetic shrinkage at around 100℃ showed a significant drop in strength in mortar, which does not contain aggregates or has a small diameter, and after 300℃, concrete showed a sharp drop in strength due to the hydration and aggregation of cement.