• Journal of Magnetics
• /
• 제2권3호
• /
• pp.96-100
• /
• 1997

A spin valve structure of NiO(40 nm)/Co(2 nm)/Cu(2.6 nm)/Co(x nm)/Ta(5 nm) has been investigated for the application of magnetic random access memory (MRAM). The spin valve structure exhibited very large difference in the coercivities between pinned and free layers, a relatively high GMR ratio, and a low free layer coercivity. The spin valves were prepared by sputtering and were characterized by dc 4-point probe, and VSM. The spin valves with combined free layer exhibited a maximun GMR ratio of 10.4% with a free layer coercivity of about 82 Oe. The spin valves with a single 10 nm thick a-CoNbZr free layer exhibited a GMR ratio of about 4.3% with a free layer coercivity of about 12 Oe. The GMR ratio of the spin valves increased by addition of Co between Cu and a-CoNbZr. It has been confirmed that the coercivity of free layer can be decreased by increasing the thickness of a-CoNbZr. It has been confirmed that the coercivity of free layer can be decreased by increasing the thickness of a-CoNbZr layer without losing the GMR ratio substantially, which was mainly due to high resistivity of the amorphous "layers".

• Bulletin of the Korean Chemical Society
• /
• 제33권6호
• /
• pp.1989-1992
• /
• 2012

We present a low temperature (${\approx}70^{\circ}C$) method to prepare anatase, vertically aligned feather-like $TiO_2$ (VAFT) nanowire arrays $via$ reactive pulsed DC magnetron sputtering. The synthesis method is general, offering a promising strategy for preparing crystalline nanowire metal oxide films for applications including gas sensing, photocatalysis, and 3rd generation photovoltaics. As an example application, anatase nanowire films are grown on fluorine doped tin oxide coated glass substrates and used as the photoanode in dye sensitized solar cells (DSSCs). AM1.5G power conversion efficiencies for the solar cells made of 1 ${\mu}m$ thick VAFT have reached 0.42%, which compares favorably to solar cells made of the same thickness P25 $TiO_2$ (0.35%).

• 한국정밀공학회지
• /
• 제31권3호
• /
• pp.207-213
• /
• 2014

A study was carried out to fabricate the cutting tool geometry with micro/nanoscale on the single crystal diamond tool by using the FIB. The FIB technique is an ideal tool for TEM sample preparation that allows for the fabrication of electron-transparent foils. The FIB is appropriate techniques to sample and subsequently define the chemical composition and the structural state of mineral inclusion on the micro/nanoscale. The combination of FIB with a SEM allows for 3D information to be obtained from samples including 3D imaging. Cutting strategies were demonstrated to improve the performance of cutting tool geometry and to generate high aspect ratio micro cutting tool. A finely focused beam of 30keV Ga+ ions was used to mill cutting tool shapes for various micro patterns. Therefore FIB sputtering is used to shape a variety of cutting tools with dimensions in the $1-5{\mu}m$ range and cutting edge radii of curvature of under 50nm.

• The Korean Journal of Ceramics
• /
• 제2권2호
• /
• pp.95-101
• /
• 1996

Variations of the leakage current behaviors and interface potential barrier $({\Phi}_B)$ of rf-sputter deposited (Ba, Sr)$TiO_3$ (BST) thin films with thicknesses ranging from 20 nm to 150nm are investigated as a function of the thickness and bias voltages. The top and bottom electrodes are dc-sputter-deposited Pt films. ${\Phi}_B$ critically depends on the BST film deposition temperature, postannealing atmosphere and time after the annealing. The postannealing under $N_2$ atmosphere results in a high interface potential barrier height and low leakage current. Maintaining the BST capacitor in air for a long time reduces the ${\Phi}_B$ from about 2.4 eV to 1.6 eV due to the oxidation. ${\Phi}_B$ is not so dependent on the film thickness in this experimental range. The leakage conduction mechanism is very dependent on the BST film thickness; the 20 nm thick film shows tunneling current, 30 and 40 nm thick films show Shottky emission current.

• 한국세라믹학회지
• /
• 제56권3호
• /
• pp.317-324
• /
• 2019

Cr-diamond-like carbon (Cr-DLC) films were deposited using a hybrid method involving both physical vapor deposition and plasma-enhanced chemical vapor deposition. DLC sputtering was carried out using argon and acetylene gases. With an increase in the DC power, the Cr content increased from 14.7 to 29.7 at%. The Cr-C bond appeared when the Cr content was 17.6 at% or more. At a Cr content of 17.6 at%, the films showed an electrical conductivity of > 363 S/cm. The current density was 9.12 × 10^-2 ㎂/㎠, and the corrosion potential was 0.240 V. Therefore, a Cr content of 17.6 at% was found to be optimum for the deposition of the Cr-DLC thin films. The Cr-DLC thin films developed in this study showed high conductivity and corrosion resistance, and hence, are suitable for applications in separators.

• 센서학회지
• /
• 제18권3호
• /
• pp.202-206
• /
• 2009

Flat type catalytic combustible hydrogen sensors were fabricated using platinum micro-heaters and sensing material pastes. The platinum micro-heater was formed on an alumina substrate by sputtering method. The paste for the sensing materials was prepared using ${\gamma}-Al_2O_3$ 30 wt%, $SnO_2$ 35 wt%, and Pd/Pt 30 wt% and coated on the platinum micro-heater. The sensing performances were tested for the prepared sensors with different substrate sizes. The micro catalytic combustible hydrogen sensors showed quick response time, high reliability, and good selectivity against various gases(CO, $C_3H_8,\;CH_4$) at low operating temperature of $156^{\circ}\C$.

• 센서학회지
• /
• 제22권5호
• /
• pp.327-332
• /
• 2013

Nickel oxide films using RF sputter was formed on the $SiO_2/Si$ substrate at the room temperature controlled with water circulation system. The feasibility of nickel oxide film as a bolometric material was demonstrated. GIXRD spectrum on NiO(111), NiO(200), and NiO(220) orientation expected as the main peaks were appeared in the grown nickel oxide films. The typical resistivity acquired at the RF power of 100W was about $34.25{\Omega}{\cdot}cm$. And it was reduced to $18.65{\Omega}{\cdot}cm$ according to the increase of the RF power to 400W. The TCR of fabricated micro-bolometer with the resistivity of $34.25{\Omega}{\cdot}cm$ was $-2.01%/^{\circ}C$. The characteristics of fabricated nickel oxide film and micro-bolometer were analyzed with XRD pattern, resistivity, TCR, and SEM images.

• 센서학회지
• /
• 제19권3호
• /
• pp.209-213
• /
• 2010

This paper describes the fabrication and characteristics of AlN piezoelectric MPG(micro power generator). The micro energy harvester was fabricated to convert ambient vibration energy to electrical power as a AlN piezoelectric cantilever with Si proof-mass. To be compatible with CMOS process, AlN thin film was grown at low temperature by RF magnetron sputtering and micro power generators were fabricated by MEMS technologies. X-ray diffraction pattern proved that the grown AlN film had highly(002) orientation with low value of FWHM(full width at the half maximum, $\theta=0.276^{\circ}$) in the rocking curve around(002) reflections. The implemented harvester showed the $198.5\;{\mu}m$ highest membrane displacement and generated 6.4 nW of electrical power to $80\;k{\Omega}$ resistive load with $22.6\;mV_{rms}$ voltage from 1.0 G acceleration at its resonant frequency of 389 Hz. From these results, the AlN piezoelectric MPG will be possible to suitable with the batch process and confirm the possibility for power supply in portable, mobile and wearable microsystems.

• 한국표면공학회지
• /
• 제49권1호
• /
• pp.98-103
• /
• 2016

The dry etching characteristics of SnO thin films were investigated using inductively coupled plasma (ICP) in Ar, $CF_4$, $Cl_2$ chemistries. the SnO thin films were deposited by reactive rf magnetron sputtering with Sn metal target. In order to study the etching rates of SnO, the processing factors of processing pressure, source power, bias power, and etching gas were controlled. The etching behavior of SnO films under various conditions was obtained and discussed by comparing to that of $SiO_2$ films. In our results, the etch rate of SnO film was obtained as 94nm/min. The etch rates were mainly affected by physical etching and the contribution of chemical etching to SnO films appeared relatively week.

• 조명전기설비학회논문지
• /
• 제27권3호
• /
• pp.107-112
• /
• 2013

Cu(In,Ga)$Se_2$ (CIGS) thin films were annealed on molybdenium/sodalime glass substrates of $300{\times}300mm^2$ by rapid thermal processing (RTP) with 2-step rising-temperature times in $N_2$ ambient. Morphological property, structural characteristics and chemical composition of the precursor of CIGS thin films were influenced directly with a change of $1^{st}$-step rising-temperature time in RTP whereas there is no significant difference with the different $2^{nd}$-step rising-temperature time (final crystallization temperature). The shorter $1^{st}$-step rising-temperature time in RTP obtained the higher photovoltaic cell efficiency from 7.469% to 8.479% even though the ideal composition in CIGS thin films could not be accoplished in this study.