• Korean Journal of Materials Research
• /
• v.15 no.10
• /
• pp.621-625
• /
• 2005

Effects of rf power, pressure, sputtering gas composition, and substrate temperature on the deposition rate of the $WC_x$ coatings were investigated. The effects of rf power and sputtering gas composition on the hardness and corrosion resistance of the $WC_x$ coatings deposited by reactive sputtering were also investigated. X-ray diffraction (XRD) and Auger electron spectroscopy (AES) analyses were performed to determine the structures and compositions of the films, respectively. The hardnesses of the films were investigated using a nanoindenter, scanning electron microscopy, ana a salt-spray test, respectively. The deposition rate of the films was proportional to rf power and inversely proportional to the $CH_4$ content of $Ar/CH_4$ sputtering gas. The deposition rate linearly increased with increasing chamber pressure. The hardness of the $WC_x$ coatings Increased as rf power increased. The highest hardness was obtained at a $Ar/CH_4$ concentration of $10 vol.\%$ in the sputtering gas. The hardness of the $WC_x$ film deposited under optimal conditions was found to be much higher than that of the electroplated chromium film, although the corrosion resistance of the former was slightly lower than that of the latter.

• Progress in Superconductivity
• /
• v.4 no.2
• /
• pp.153-156
• /
• 2003

We have studied fabrication of $MgB_2$ thin film on $SrTiO_3$ (001) and r-cut $A1_2$$O_3$ substrates by rf magnetron sputtering method using and $ MgB_2$ single target and two targets of Mg and B, respectively. Based on P -T phase diagram of $MgB_2$ and vapor pressure curves of Mg and B, a three-step process was employed. B layer was deposited at the bottom to enhance the film adhesion to the substrate. Secondly, co-sputtering of Mg and B was done. Finally, Mg was sputtered on top to compensate fur the loss of Mg during annealing. Subsequently, $MgB_2$ films were in-situ annealed in various conditions. The sample fabricated using the three-step process showed $T_{c}$ of 24 K and formation of superconducting $MgB_2$ phase was confirmed by XRD spectra. In case of co-sputtering deposition, $T_{c}$ depended on annealing time and argon pressure. However, those made by single-target sputtering showed non-superconducting behavior or low transition temperature, at best.est.

• Journal of the Korean Magnetics Society
• /
• v.10 no.5
• /
• pp.232-236
• /
• 2000

CoSm thin films with a Cr underlayer have received continuous attention as a potential material for a high density longitudinal magnetic recording media. In this study the Ax gas sputtering pressure effects on the magnetic properties of CoSm thin films, which were fabricated by using a dc magnetron sputtering machine, were investigated. The magnetic switching volume is especially important parameter to understand the thermal stability of the written information, magnetization reversal process and media noise. Therefore, in this paper the effects of sputtering pressure on the magnetic switching volume of CoSm thin films grown on Cr underlayer with the same sputtering conditions was studied. As the Ar sputtering pressure during sputtering of the CoSm magnetic layer increases from 5 to 30 mTorr, the measured switching volumes decreased from 9.0 to 5.2$\times$10$^{-18}$ cm$^3$. The calculated diameter of switching unit from V＊ was less than 22 nm, which satisfies the Sharrock's requirement on the thermal stability of the high density longitudinal magnetic recording media.

• Journal of the Korean Vacuum Society
• /
• v.9 no.4
• /
• pp.367-372
• /
• 2000

ZnO thin films were deposited on amorphous slide glass and $SiO_2$/Si substrates by Facing Targets Sputtering method with sputtering current 0.1~0.8 A, working pressure 0.5~3 mTorr and substrate temperature R.T~$400^{\circ}C$. When the sputtering current was 0.4 A, working pressure was 0.5 mTorr and substrate temperature was 30$0^{\circ}C$, ${\Delta}{\Theta}_{50}$ value of ZnO/glass and ZnO/$SiO_2$/si thin film was $3.8^{\circ}$ and $2.98^{\circ}$, respectively. In these conditions, we knew that ZnO thin film were deposited with good c-axis orientation on amorphous slide glass by FTS system.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.135-136
• /
• 2002

Molybdenum Nitrided (MoNx) films were deposited by DC planar magnetron sputtering. Silicon wafers and real nitrided stainless steel piston rings are employed as substrates. 12 different combinations of nitrogen and argon partial pressure, from 1:7 to 7:1, were applied to deposit MoNx films. X-ray diffraction (XRD) was used to determine the phase structures of films. When nitrogen vs. argon partial pressure is 1:7, the film is mainly $Mo_2N$ phase. With increase of nitrogen partial pressure, MoN phase emerges, but $Mo_2N$ phase still exists. Composition analysis with atomic emission spectrometry (AES) also agreed with this. The films have very high nanohardness (max 2400Hv) and good adhesion to the substrates.

• Journal of Information Display
• /
• v.9 no.4
• /
• pp.15-20
• /
• 2008

A DC-magnetron inline sputter was established, and the influence of the base pressure on the structural characteristics of the ITO thin films was studied. When the inline sputter system was established and operated for ITO sputtering, its initial vacuum level did not go below $5\times10^{-6}$ torr. The vacuum leak test was conducted by measuring t he elapsed time until the vacuum level reached $1\times10^{-6}$ torr. The base pressure was successfully maintained at $1\times10^{-6}$ torr for 900 min, and the uniformity of the ITO film that had been deposited at this pressure significantly improved.

• Journal of the Korean Vacuum Society
• /
• v.12 no.S1
• /
• pp.83-87
• /
• 2003

Zirconium oxide films have been synthesized by radio-frequency magnetron sputtering deposition on n-Si(001) substrate with metal zirconium target at variant $O_2$ partial pressures. The influences of $O_2$ partial pressures of the morphology, deposition rate, microstructure, and the dielectric constant of $ZrO_2$ have been discussed. The results show that deposition rate of $ZrO_2$ films decreases, the roughness, and the thickness of the native $SiO_2$ interlayer increases with the increase of $O_2$ partial pressure. $ZrO_2$ films synthesized at low $O_2$ partial pressure are amorphous and monoclinic polycrystalline in nanometer scale at low $O_2$ partial pressure. The relative dielectrics of $ZrO_2$ films are in the range of 12 to 25.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.05a
• /
• pp.84-89
• /
• 1996

The nucleation and growth of microporosities was observed during the course of annealing treatment of sputter-deposited AgInSbTe thin films. There was a close correlation between the density of microporosity and the sputtering gas pressure in annealed thin films. The void density for a given composition decreased with sputtering gas pressure. It was shown from the present study that the number of porosities decreased while the average porosity size increased as the annealing temperature and holding time increased. The mechanism of porosity formation in the sputter-deposited AgInSbTe thin flus containing Ar-impurity trapped from the Ar-plasma is discussed in the present article.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.6
• /
• pp.671-676
• /
• 1999

ITO (indium tin oxide) thin films on PET (polyethylene terephthalate) substrate have been deposited by a dc reactive magnetron sputtering without heat treatments such as substrate heater and post heat treatment. Each sputtering parameter during the sputtering deposition is an important factor for the high quality of ITO thin films deposited on polymeric substrate. Particularly, the material, electrical and optical properties of as-deposited ITO oxide films are dominated by the ratio of oxygen partial pressure. As the experimental results, the excellent ITO films are prepared on PET substrate at the operating conditions as follows : operating pressure of 5 mTorr, target-substrate distance of 45mm, do power of 20~30W, and oxygen gas ratio of 10%. The optical transmittance is above 80% at 550 nm, and the sheet resistance and resistivity of films are 24 Ω/square and $1.5\times$10$^{-3}$ Ωcm, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.106-107
• /
• 2006

Cadmium telluride (CdTe) films have been prepared on Corning 7059 glass, molybdenum (Mo), and polyimide (PI) substrates by r.f. magnetron sputtering technique. The influence of the sputter pressure on the structural and optical properties of these films was evaluated. In addition, a comparison of the properties of the films deposited on fferent substrates was performed.