• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.1
• /
• pp.25-31
• /
• 2010

In this study, we investigated the morphology and thermal stability of interfacial phases in joint between lead free solder(Sn-3.0Ag-0.5Cu) and electroless Ni-W-P under bump metallizations(UBM) with different tungsten contents as a function of thermal aging. Content of phosphorus of each deposits was fixed at 8 wt.%, and content of tungsten was variated each 0, 3, 6 and 9 wt.%. Specimens were prepared by reflowing at $255^{\circ}C$, aging range was $200^{\circ}C$ and up to 2 weeks. After reflow process, in the electroless Ni(W)-P/solder joint, the interfacial intermetallic compound(IMC) was showed both $(Cu,Ni)_6Sn_5$ and $(Ni,Cu)_3Sn_4$. UBM and generated IMC at the interface of lead free solder was proportionally increased with aging time. The thickness of IMC was increased because the generation rate of $Ni(W)_3P$ decreased with increasing contents of W.

• 한국초전도학회:학술대회논문집
• /
• v.15
• /
• pp.58-58
• /
• 2005

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.3
• /
• pp.566-576
• /
• 1997

This study was performed to evaluate the tensile strength of solder joint in titanium and the wettability of 14K gold solder on titanium. Two pieces of titanium rod 30 mm in length and 3mm in diameter were butt-soldered with a 14K gold solder using the electric resistance heating under flux-argon atmosphere, the infrared heating under argon atmosphere, and the infrared heating under vacuum-argon atmosphere. A tensile test was performed at a crosshead speed of 0.5 mm/min, and fracture surfaces were examined by SEM. To evaluate the wettability of 14K gold solder on titanium, titanum plates of a $17{\times}17{\times}1mm$ were polished with #80-#2000 emery papers, and the spreading areas of solder 10 mg were measured by heating at 840 * for 60 seconds. The solder-matrix interface regions were etched by the solution of 10% KCN-10% (NH4)2S2O8, and analyzed by EPMA. The results obtained were summarized as follows ; 1. The maximum tensile strength was obtained when the titanium surface was polished with #2000 emery paper and soldered using the electric resistance heating under flux-argon atmosphere. Soldering strengths showed the significant difference between the electric resistance heating and the infrared heating(p<0.05). 3. The fracture surfaces showed the aspect of brittle fracture, and the failure developed along the interfaces of solder-matrix reaction zone. 4. The EPMA data for the solder-matrix interface region revealed that the diffusion of Au and Cu occurred to the titanium matrix, and the reaction zone showed the higher contents of Au, Cu and Ti than others.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.204-207
• /
• 2003

The flip chip bonding utilizing self-aligning characteristic of solder becomes mandatory to meet to tolerances for the optical device. In this paper, a parametric study of aging condition and pad size of sample was conducted. A TiW/Cu UBM structure was adopted and sample was aging treated to analyze the effect of intermetallic compound with time variation. After aging treatment, the tendency to decrease in shear strength was measured and the structure of the fine joint area was observed by using SEM, TEM and EDS. In result, the shear strength was decreased of about 20% in the $100{\mu}m$ sample at $170^{\circ}C$ aging compared with the maximum shear strength of same pad size sample. In the case of the $120^{\circ}C$ aging treatment, 17% of decrease in shear strength was measured at the $100{\mu}m$ pad size sample. Also, intremetallic compound of $Cu_6Sn_5$ and $Cu_3Sn$ were observed through the TEM measurement by using an FIB technique that is very useful to prepare TEM thin foil specimens from the solder joint interface.

• Journal of Welding and Joining
• /
• v.29 no.3
• /
• pp.35-38
• /
• 2011

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2004.11a
• /
• pp.54-54
• /
• 2004

• Journal of Welding and Joining
• /
• v.21 no.7
• /
• pp.59-64
• /
• 2003

Microstructure and shear strength of Sn-Zn lead-free solders and Au/Ni/Cu UBM joint under thermal aging conditions was investigated. The samples were aged isothermally at 10$0^{\circ}C$ and 15$0^{\circ}C$ for 300, 600, and 900 hours. The IMCs(Intermetallic Compound) at the interface between solder and UBM were examined by FESEM and TEM. The results showed that the shear strength was decreased with aging time and temperature. The solder ball with high activated RA flux had about 8.2% higher shear strength than that of RMA flux. Poor wetting and many voids were observed in the fractured solder joint with of RMA flux. The decreased shear strengths were caused by IMC growth and Zn grain coarsening. Zn reacted with Au and then was transformed to the $\beta$ -AuZn compound. Although AuZn grew first, $r-Ni_5Zn_{21}$ compounds were formed with aging time. The layers indicated by $Ni_5Zn_{21}(1)$, (2), and (3) were formed with the thickness of ∼0.7 ${\mu}{\textrm}{m}$, ∼4 ${\mu}{\textrm}{m}$, and ∼2 ${\mu}{\textrm}{m}$, respectively.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.151-155
• /
• 2003

The requirements for harsh environment electronic controllers in automotive applications have been steadily becoming more and more stringent. Electronic substrate technologists have been responding to this challenge effectively in an effort to meet the performance, reliability and cost requirements. An effect of the plasma cleaning at the alumina substrate and the IMC layer between $Sn-37wt\%Pb$ solder and Ag-Pd thick film conductor after reflow soldering has been studied. Organic residual carbon layer was removed by the substrate plasma cleaning. So the interfacial adhesive strength was enhanced. As a result of AFM measurement, Ag-Pd conductor pad roughness were increased from 304nm to 330nm. $Cu_6Sn_5$ formed during initial ref]ow process at the interface between TiWN/Cu UBM and solder grew by the succeeding reflow process so the grains had a large diameter and dense interval. A cellular-shaped $Ag_3Sn$ was observed at the interface between Ag-Pd conductor pad and solder. The diameters of the $Ag_3Sn$ grains ranged from about $0.1\~0.6{\mu}m$. And a needle-shaped $Ag_3Sn$ was also observed at the inside of the solder.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.2
• /
• pp.49-55
• /
• 2011

The failure of electronic instruments is mostly caused by heat and shock. This shock causes the crack initiation at the solder joint interface of PCB component which is closely related with the formation of intermetallic compound(IMC). The Ag content in Pb-free Sn-xAg-0.5Cu solder alloy used in this study was 1.0, 1.2 and 3.0 wt.%, respectively. After soldering with PCB component, isothermal aging was performed to 1000 hrs. The growth of IMC layer was observed during isothermal aging. The drop impact property of solder joint was evaluated by impact bending test method. The solder joint made with the solder containing lower Ag content showed better impact bending property compared with that with higher Ag content. On the contrary to this result, the solder joint made with solder containing higher Ag content showed better impact bending property after aging. It should be caused by the formation of fine $Ag_3Sn$, which relieved the impact. It showed consequently the different effect of fine $Ag_3Sn$ and coarse $Cu_6Sn_5$ particles formed in the IMC layer on the impact bending property.

• Journal of Welding and Joining
• /
• v.29 no.6
• /
• pp.65-70
• /
• 2011

The effect of flip chip bonding parameters on formation of intermetallic compounds (IMCs) between Au stud bumps and Sn-3.5Ag solder was investigated. In this study, flip chip bonding temperature was performed at $260^{\circ}C$ and $300^{\circ}C$ with various bonding times of 5, 10, and 20 sec. AuSn, $AuSn_2$ and $AuSn_4$ IMCs were formed at the interface of joints and (Au, Cu)$_6Sn_5$ IMC was observed near Cu pad side in the joint. At bonding temperature of $260^{\circ}C$, $AuSn_4$ IMC was dominant in the joint compared to other Au-Sn IMCs as bonding time increased. At bonding temperature of $300^{\circ}C$, $AuSn_2$ IMC clusters, which were surrounded by $AuSn_4$ IMC, were observed in the solder joint due to fast diffusivity of Au to molten solder with increased bonding temperature. Bond strength of Au stud bump joined with Sn-3.5Ag solder was about 23 gf/bump and fracture mode of the joint was intergranular fracture between $AuSn_2$ and $AuSn_4$ IMCs regardless bonding conditions.