• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.132-135
• /
• 2002

MI(Magneto-Impedance) sensor which is made by thin films has significantly high detecting sensitivity in weak magnetic field. It also has a merit to be able to build in the low power system. Its structure is simple, which makes it easier to prepare a miniature. In this study, its magnetic permeability and anisotropy field($H_{k}$) as a function of a thickness of sputtered amorphous CoZrNb films with zero-magnetostriction and soft magnetic property are investigated. In order to make a uniaxial anisotropy, film was subjected to the post annealing in a static magnetic field with 1KOe intensity at 250, 300, and $320^{\circ}C$ respectively for 2 hours. Magnetic properties of film are measured by using a MH loop tracer. Its magnetic permeability of a film is measured over the frequency range 1 MHz to 750MHz. And, it was examined on the permeability and impedance to design the MI sensor which acts at 50MHz by thickening a CoZrNb film relatively, and fabricated the MI sensor which acts at the 50MHz.

• Journal of the Korean Magnetics Society
• /
• v.10 no.4
• /
• pp.165-170
• /
• 2000

The purpose of this study is to investigate the effect of annealing conditions on physical and magnetic properties of Fe-Hf-N thin films. When the thin films were annealed in $N_2$ gas, a surface oxide layer, comprised of Fe$_2$O$_3$ and Fe$_3$O$_4$, was formed at the surface of the thin films and a Fe-Hf-O-N layer was also formed under this surface oxide layer. It was found that the thicknesses of the surface oxide layer and the Fe-Hf-O-N layer increased, as the annealing temperature increased. It was also found that if the thickness of the surface oxide layer was excluded in the property calculation, the soft magnetic properties of the annealed thin films were not much different from those of the as-deposited thin films. Therefore, it was suggested that the Fe-Hf-O-N layer formed under the surface oxide layer did not lose significantly the soft magnetic properties of the Fe-Hf-N films and the Fe-Hf-N films annealed in $N_2$gas showed the soft magnetic properties of the Fe-Hf-N and Fe-Hf-O-N multi-layers.

• Journal of the Korean Magnetics Society
• /
• v.5 no.1
• /
• pp.34-37
• /
• 1995

$Nd_{x}Fe_{77}B_{23-x}(x=4,\;6,\;8,\;11,\;13)$ alloys were prepared by rapid quenching technique. They were crystallized at higher than $650^{\circ}C$ and subsequently the magnetic properties were investigated The melt-spun alloy of x=8 consisted of nearly single metastable compound $Nd_{2}Fe_{23}B_{3}$ and showed the soft magnetic property. In $8{\leq}x{\leq}13$ alloys, the coercivities were increased according to the increase of Nd content but the remanences decreased. In $4{\leq}x{\leq}6$ alloys, the coercivities and the remanences were increased by lowering Nd content. In x=4 alloy, the ratio of soft to hard magnetic phase was 70:30 and the energy product was $96kJ/m^{3}(12MG.Oe)$.

• Journal of the Korean Magnetics Society
• /
• v.25 no.1
• /
• pp.4-9
• /
• 2015

This study was carried out to investigate a influence of humidity variation (%) on the magnetic properties and the surface flaws in the fabrication of Fe-based $Fe_{78}Si_9B_{13}$ amorphous alloy ribbon by Planar Flow Casting process. As a result, the size of the air pocket and the droplet which is observed in the contact surface and the free face of the amorphous alloy ribbon becomes large when the humidity increases and the size highly increases with the surface roughness at the same time. Especially, the surface roughness value which is made in the 65 % of the humidity is the lowest in the contact surface ($Ra=0.60{\mu}m$, $Rz=3.11{\mu}m$) and the free face ($Ra=0.47{\mu}m$, $Rz=3.00{\mu}m$). Also, in case of the soft magnetic property of the magnetic core which is made with the toroidal core of $23(OD)^*20(ID)^*20(H)$ size, in the sample of the amorphous alloy ribbon which is made in 65% of the humidity, the most excellent value is gained as $B_s(B_{700})=1.055T$, $H_c=0.083Oe$, permeability = 1,197 and core loss = 0.276W/kg.

• Journal of the Korean Magnetics Society
• /
• v.21 no.4
• /
• pp.132-135
• /
• 2011

The exchange bias field ($H_{EX}$) and the coercivity ($H_C$) variation and change depending on the thickness of intermediately super-soft magnetic NiFeCuMo layer with different thickness of the bottom NiFe layer were investigated. The $H_{EX}$ of triple pinned NiFe(4 nm)/NiFeCuMo($t_{NiFeCuMo}$= 1 nm)/NiFe(4 nm)/FeMn multilayer has the maximum value more less than one of single pinned NiFe(8 nm)/FeMn layer. If NiFeCuMo layer is inserted each into between the pinned and free NiFe layers, we can be used as GMR-SV device for a bio-sensor that has improved magnetic sensitivity.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.2
• /
• pp.94-98
• /
• 2005

Coptp films with the additive elements (X=Fe, Mn) of varying concentrations were prepared by in-situ electrodeposition, to tailor their magnetic properties. Alloys of CoPtP-X (X=Fe, Mn) were synthesized by changing the solution concentrations of Fe and Mn for electrodeposition. In the electrodeposited CoFePtP alloys, preferred orientation of the electrodeposited films changed from hexagonal (001) to (100) direction with increasing iron contents as revealed by X-ray diffraction, and these films exhibited various magnetic properties ranging from a typical hard magnetic to a soft magnetic property in accordance with microstructural variations. In the case of Mn addition, excellent hard magnetic property was observed at a specific Mn concentration of 0.0126 M in the electrolyte, with the coercivity of 4630 Oe and squareness of 0.856 and this was attributed to the fact that magnetization easy-axis (hexagonal c-axis) coincides with the preferred growth orientation of the film confirmed by transmission electron microscopy.

• Proceedings of the KIEE Conference
• /
• 2003.04a
• /
• pp.47-49
• /
• 2003

수직 기록 방식은 그 기록 방식의 차이로 인하여 수평 기록 방식에서 쓰여 오던 Write Head의 Design을 적용하였을 경우 기록 밀도를 높이는데 많은 문제점과 낮은 기록 밀도 상승률을 동반하게 된다. 따라서 수직 기록 방식의 자기 기록에서는 수직 기록 방식에 적합한 Write Head의 Design을 적용하여야만 한다. 본 논문에서는 3차원 유한요소법을 이용하여 수직 기록용 Write Head의 한 종류인 SPT Head(Single Pole Tip Head)를 최적 설계하여 그 Write Field의 특성을 분석 제시하였다. 또한 기록 Media의 차이에 따른 기록 특성을 분석하기 위하여 기존 Single Layer 방식과 SUL (Soft Magnetic Under layer)를 사용한 Double Layer 방식을 이용하였을 경우 SUL이 자기 기록에 미치는 영향에 대한 내용을 연구 분석하여 제시하였다.

• Journal of the Korean Electrochemical Society
• /
• v.5 no.1
• /
• pp.17-20
• /
• 2002

Various compositions of CoFeNi alloys have been electrodeposited in chloride bath and in sulfate bath, and evaluated for electrodeposition characteristics and magnetic properties. For electrodeposited CoFeNi thin film alloys, the increase of Fe content in the deposits from sulfate bath was considerably faster than those from chloride bath. The current efficiencies in sulfate bath showed observable decrease from $75\%\;to\;50\%$ while those in chloride bath showed no significant decrease. From the low coercivity of 3 Oe in the minimum and the higher squarenesses of the alloys from sulfate bath than those from chloride bath, the alloy at Co, Fe, and Ni contents of $80wt.\%,\;10wt.\%,\;and\;10wt.\%$ can be considered to be the best CoFeNi alloy in this research for the soft magnetic material.

• Tribology and Lubricants
• /
• v.31 no.1
• /
• pp.6-12
• /
• 2015

This paper investigates the stick-slip characteristic of magnetorheological elastomer (MRE) between an aluminum plate and the surface of the MRE. MRE is a smart material and it can change its mechanical behavior with the interior iron particles under the influence of an applied magnetic field. Stick-slip is a movement of two surfaces relative to each other that proceeds as a series of jerks caused by alternate sticking from friction and sliding when the friction is overcome by an applied force. This special tribology phenomenon can lead to unnecessary wear, vibration, noise, and reduced service life of work piece. The stick-slip phenomenon is avoided as far as possible in the field of mechanical engineering. As this phenomenon is a function of material property, applied load, and velocity, it can be controlled using the characteristics of MRE. MRE as a soft smart material, whose mechanical properties such as modulus and stiffness can be changed via the strength of an external magnetic field, has been widely studied as a prospective replacement for general rubber in the mechanical domain. In this study, friction force is measured under different loads, speed, and magnetic field strength. From the test results, it is confirmed that the stick-slip phenomenon can be minimized under optimum conditions and can be applied in various mechanical components.

• Korean Journal of Metals and Materials
• /
• v.49 no.2
• /
• pp.167-173
• /
• 2011

Nickel cobalt ferrite($Ni_{0.5}Co_{0.5}Fe_2O_4$) powder was prepared through the ceramic route by the calcination of a stoichiometric mixture of NiO, CoO and $Fe_2O_3$ at $1100^{\circ}C$. The pressed pellets of $Ni_{0.5}Co_{0.5}Fe_2O_4$ were isothermally reduced in pure hydrogen at $800{\sim}1100^{\circ}C$. Based on the thermogravimetric analysis, the reduction behavior and the kinetic reaction mechanisms of the synthesized ferrite were studied. The initial ferrite powder and the various reduction products were characterized by X-ray diffraction, scanning electron microscopy, reflected light microscope and vibrating sample magnetometer to reveal the effect of hydrogen reduction on the composition, microstructure and magnetic properties of the produced Fe-Ni-Co alloy. The arrhenius equation with the approved mathematical formulations for the gas solid reaction was applied to calculate the activation energy($E_a$) and detect the controlling reaction mechanisms. In the initial stage of hydrogen reduction, the reduction rate was controlled by the gas diffusion and the interfacial chemical reaction. However, in later stages, the rate was controlled by the interfacial chemical reaction. The nature of the hydrogen reduction and the magnetic property changes for nickel cobalt ferrite were compared with the previous result for nickel ferrite. The microstructural development of the synthesized Fe-Ni-Co alloy with an increase in the reduction temperature improved its soft magnetic properties by increasing the saturation magnetization($M_s$) and by decreasing the coercivity($H_c$). The Fe-Ni-Co alloy showed higher saturation magnetization compared to Fe-Ni alloy.