• Korean Journal of Materials Research
• /
• v.19 no.4
• /
• pp.207-211
• /
• 2009

In this study, we attempted to develop a convenient aluminizing process, using Al-Ti mixed slurry as an aluminum source, to control the Al content of the aluminized layer as a result of a one-step process and can be widely adopted for coating complex-shaped components. The aluminizing process was carried out by the heat treatment on disc and rod shaped S45C steel substrates with Al-Ti mixed slurries that were composed of various mixed ratios (wt%) of Al and Ti powders. The surface of the resultant aluminized layer was relatively smooth with no obvious cracks. The aluminized layers mainly contain an Fe-Al compound as the bulk phase. However, the Al concentration and the thickness of the aluminized layer gradually decrease as the Ti proportion among Al-Ti mixed slurries increases. It has also been shown that the Al-Ti compound layer, which formed on the substrate during heat treatment, easily separates from the substrate. In addition, the incorporation of Ti into the substrate surface during heat treatment was not observed.

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.691-695
• /
• 2002

A low temperature anode-supported tubular solid oxide fuel cell was developed. The anode-supported tube was fabricated using extrusion process. Then the electrolyte layer and the cathode layer were coated onto the anode tube by slurry dipping process, subsequently. The anode tube and electrolyte were co-fired at $140^{\circ}C$, and the cathode was sintered at $1200^{\circ}C$. The thickness and gas permeability of the electrolyte depended on the number of coating and the slurry concentration. Anode-supported tube was satisfied with SOFC requirements, related to electrical conductivity, pore structure, and gas diffusion limitations. At operating temperature of $800^{\circ}C$, open circuit voltage of the cell with gastight and dense electrolyte layer was 1.1 V and the cell showed a good performance of 450 mW/$\textrm{cm}^2$.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.4
• /
• pp.331-339
• /
• 2017

The purpose of this study is to evaluate the effect of curing age and thickness of coating material on the bond strength of polymer cement slurry(PCS)-coated rebar that can replace epoxy-coated rebar. The test specimens were prepared with two types of cement, two types of polymer dispersion as St/BA and EVA, two polymer-cement ratios, two coating thicknesses and three curing ages, and tested for bond strength test to cement concrete. The flexural behavior of RC beam that is made by optimum conditions such as polymer-cement ratio of 80%, coating thickness of $100{\mu}m$ and curing age of 7 days of PCS recommended from the bond strength test is also conducted. From the test results, The maximum bond strength of PCS-coated rebar at curing age of 7-day and coating thickness of $100{\mu}m$ was about 1.52 and 1.58 times respectively, the strength of plain and epoxy-coated rebar. The ultimate loads of RC beam using PCS-coated rebar were range of 81.1% to 102.3% of that of plain rebar, and 98.4% to 124.1% of that of epoxy-coated rebar. It is apparent that PCS-coated rebar with EVA, curing age at 7-day and $100{\mu}m$ can replace epoxy-coated rebar in construction field.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.9
• /
• pp.1491-1497
• /
• 1997

The purpose of this research is to improve the surface roughness of cast-iron pipe porduced by the centrifugal casting. A twin-fluid atomizer of mold-wash slurry is designed for this project. New atomizer is equipped with the existing manufacturing facility to produce pipes. Cast-iron pipes (.cent.125*L3000mm) are produced and the surface roughnesses of those are analysed by UBM. The average surface roughness of new products is 6.7.mu.m while the old products of sand-resin coating method have 17.0.mu.m of average surface roughness. The surface roughness of cast-iron pipe is improved very much than before.

• The Korean Journal of Ceramics
• /
• v.7 no.2
• /
• pp.74-79
• /
• 2001

Alumina composite reinforced by chopped alumina fiber was fabricated by filter-pressing the fiber slurry followed by the infiltration of alumina slurry. The chopped fiber was coated with nickel by electroless plating method. The green samples were densified by hot-pressing. Microstructures were studied by SEM and the mechanical properties such as bending strength and fracture toughness were measured. The resulting mechanical properties were analyzed in relation with processing parameters such as preform density and resulting microstructures. The load-displacement curve of the specimen with Ni interlayer but without Ni inclusion showed brittle fracture mode due to the direct contact between matrix and fiber. The load-displacement curve of the specimen with Ni interlayer and Ni inclusion in the matrix which is introduced by high applied pressure during specimen preparation showed non-brittle fracture mode due to the fiber pull-out and dutile phases in the matrix.

• Journal of the Korean Ceramic Society
• /
• v.41 no.3
• /
• pp.229-234
• /
• 2004

In this study, we proposed new forming process for a porous ceramic body with unique pore structure. h tubular-type porous NiO-YSZ body with radially aligned pore channels was prepared by freeze-drying of aqueous slurry. A NiO-YSZ slurry was poured into the mold, which was designed to control the crystallization direction of the ice, followed by freezing. Thereafter the ice was sublimated at a reduced pressure. SEM observations revealed that the NiO-YSZ porous body showed aligned large pore channels parallel to the ice growth direction, and fine pores are formed around the outer surface of the tube. It was considered that the difference in the ice growth rate during the freezing process resulted in such a characteristic microstructure. Bilayer consisting of dense thin electrolyte film of YSZ onto the tubular type porous body has been successfully fabricated using a slurry-coating process followed by co-firing. It was regarded that the obtained bilayer structure is suitable for constructing electrode-support type electrochemical devices such as solid oxide fuel cells.

• Clean Technology
• /
• v.25 no.3
• /
• pp.256-262
• /
• 2019

Hydroxylammonium nitrate (HAN)-based liquid propellants are attracting attention as environmentally friendly propellants because they are not carcinogens and the combustion gases have little toxicity. The catalyst used to decompose the HAN-based liquid propellant in a thruster must have both low temperature activity and high heat resistance. The objective of this study is to prepare an Ru/alumina/metal foam catalyst by supporting alumina slurry on the surface of NiCrAl metal foam using a washing coating method and then to support a ruthenium precursor thereon. The decomposition activity of a HAN aqueous solution of the Ru/alumina/metal foam catalyst was evaluated. The effect of the number of repetitive coatings of alumina slurry on the physical properties of the alumina/metal foam was analyzed. As the number of alumina wash coatings increased, mesopores with a diameter of about 7 nm were well-developed, thereby increasing the surface area and pore volume. It was optimal to repeat the wash coating alumina on the metal foam 12 times to maximize the surface area and pore volume of the alumina/metal foam. Mesopores were also well developed on the surface of the Ru/alumina/metal foam catalyst. It was found that the metal form itself without the active metal and alumina can promote the decomposition reaction of the HAN aqueous solution. In the case of the Ru/alumina/metal foam-550 catalyst, the decomposition onset temperature was significantly lowered compared with that of the thermal decomposition reaction, and ${\Delta}P$ could be greatly increased in the decomposition of the HAN aqueous solution. However, when the catalyst was calcined at $1,200^{\circ}C$, the catalytic activity was lowered inevitably because the surface area and pore volume of the catalyst were drastically reduced and Ru was sintered. Further research is needed to improve the heat resistance of Ru/alumina/metal foam catalysts.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.124.1-124.1
• /
• 2007

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.11a
• /
• pp.183-183
• /
• 1999

Slurry sol(30at% anatase TiO$_2$)을 이용하여 스핀코팅으로 유리기판에 TiO$_2$박막을 제조하였다. 박막의 두께는 코팅주기의 횟수로 조절하였다. 한 코팅주기는 스핀코팅, 건조, 열처리를 포함한다. 박막의 반응성은 막 위에서의 자외선강도가 0.4mW/$\textrm{cm}^2$인 조건에서 벤젠기체의 광분해 속도를 통해 조사하였다. 박막의 두께가 증가할수록 표면적인 증가로 인해 반응성은 증가하였으며, 4$\mu\textrm{m}$정도이상의 두께에서 반응성은 더 이상 증가되지 않았다. porous한 TiO$_2$박막은 비교적 넓은 유효 표면적을 가지고 있으며, 그것은 두께증가에 따라 반응속도를 결정하는 결과를 낳았다.

• Journal of the Korean Ceramic Society
• /
• v.45 no.10
• /
• pp.584-588
• /
• 2008

Porous hydroxyapatite(HA) and HA-coated porous $Al_2O_3$ possessing pore characteristics required for bone substitutes were prepared by a slurry foaming method combined with gelcasting. The HA coating was deposited by heating porous $Al_2O_3$ substrates in an aqueous solution containing $Ca^{2+}$ and ${PO_4}^{3-}$ ions at $65{\sim}95^{\circ}C$ under ambient pressure. The pore characteristic, microstructure, and compressive strength were investigated and compared for the two kinds of samples. The porosity of the samples was about 81% and 80% for HA and $Al_2O_3$, respectively with a highly interconnected network of spherical pores with size ranging from 50 to $250{\mu}m$. The porous $Al_2O_3$ sample showed much higher compressive strength(25 MPa) than the porous HA sample(10 MPa). Fairly dense and uniform HA coating(about $2{\mu}m$ thick) was deposited on the porous $Al_2O_3$ sample. Since the compressive strength of cancellous bone is $2{\sim}12$ MPa, both the porous HA and HA-coated porous $Al_2O_3$ samples could be successfully utilized as scaffolds for bone repair. Especially the latter is expected suitable for load bearing bone substitutes due to its excellent strength.