• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.89-90
• /
• 2006

Austenitic stainless steel has been used as a corrosion resistance material. However, austenitic stainless steel has poor wear resistance property due to its low hardness. In this investigation, we apply powder composite process to obtain hard layer of Stainless steel. The composite material was fabricated from planetary ball milled SUS316L stainless steel powder and WC powder and then sintered by Pulsed Current Sintering (PCS) method. We also added TiC powder as a hard particle in WC layer. Evaluations of wear properties were performed by pin-on-disk wear testing machine, and a remarkable improvement in wear resistance property was obtained.

• The Journal of Advanced Prosthodontics
• /
• v.14 no.3
• /
• pp.173-181
• /
• 2022

PURPOSE. This analysis aimed to evaluate the intaglio surface trueness, antagonist's wear volume loss, and fracture resistance of full-contour crowns of (Y, Nb)-stabilized fully-sintered zirconia (FSZ), 4 mol% or 5 mol% yttria-stabilized partially sintered zirconia (4YZ or 5YZ) with high-speed sintering. MATERIALS AND METHODS. A total of 42 zirconia crowns were separated into three groups: FSZ, 4YZ, and 5YZ (n = 14). The intaglio surface trueness of the crowns was evaluated at the inner surface, occlusal, margin, and axial areas and reported as root-mean-square, positive and negative average deviation. Half of the specimens were aged for 120,000 cycles in the chewing simulator, and the wear volume loss of antagonist was measured. Before and after chewing, the fracture load was measured for each group. The trueness values were analyzed with Welch's ANOVA, and the wear volume loss with the Kruskal-Wallis tests. Effect of the zirconia type and aging on fracture resistance of crowns was tested using two-way ANOVA. RESULTS. The intaglio surface trueness measured at four different areas of the crown was less than 50 ㎛, regardless of the type of zirconia. No significant P in wear volume loss of antagonists were detected among the groups (P > .05). Both the type of zirconia and aging showed statistically significant effects on fracture resistance (P < .05). CONCLUSION. The full-contour crowns of FSZ as well as 4YZ or 5YZ with high-speed sintering were clinically acceptable, in terms of intaglio surface trueness, antagonist's wear volume loss, and fracture resistance after simulated mastication.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.11
• /
• pp.1003-1009
• /
• 2008

In this study, liquid phase sintered SiC (LPS-SiC) materials were made by hot pressing method. The particle size of nano-SiC powder was 30nm. Alumina ($Al_2O_3$), yttria ($Y_2O_3$) and silica ($SiO_2$) were used for sintering additives. To investigate effects of $SiO_2$, ratios of $SiO_2$ contents were changed by five kinds. Materials have been sintered for 1 hour at $1760^{\circ}C$, $1780^{\circ}C$ and $1800^{\circ}C$ under the pressure of 20MPa. The system of sintering additives which affects a property of sintering as well as the influence depending on compositions of sintering additives were investigated by measurement of density, mechanical properties such as flexural strength, vickers hardness and sliding wear resistance were investigated to make sure of the optimum condition which is about matrix of $SiC_f$/SiC composites. The abrasion test condition apply to load of 20N at 100RPM for 20min. Sintered density, flexural strength of fabricated LPS-SiC increased with increasing the sintering temperature. And in case of LPS-SiC with low $SiO_2$, sliding wear resistance has very excellent. Monolithic SiC $1800^{\circ}C$ sintering temperatures and 3wt% have excellent wear resistance.

• Journal of Powder Materials
• /
• v.22 no.3
• /
• pp.203-207
• /
• 2015

This study investigated the microstructure and wear resistance property of HPHT(high pressure high temperature) sintered PDC(polycrystalline diamond compact) in accordance with initial molding pressure. After quantifying an identical amount of diamond powder, the powder was inserted in top of WC-Co sintered material, and molded under four different pressure conditions (50, 100, 150, $200kgf/cm^2$). The obtained diamond compact underwent sintering in high pressure, high temperature conditions. In the case of the $50kgf/cm^2$ initial molding pressure condition, cracks were formed on the surface of PDC. On the other hand, PDCs obtained from $100{\sim}200kgf/cm^2$ initial molding pressure conditions showed a meticulous structure. As molding pressure increased, low Co composition within PDC was detected. A wear resistance test was performed on the PDC, and the $200kgf/cm^2$ condition PDC showed the highest wear resistance property.

• Journal of the Korean Ceramic Society
• /
• v.46 no.5
• /
• pp.505-509
• /
• 2009

In this study, bulk nano-crystalline $Si_3N_4$ ceramics were fabricated by spark plasma sintering (SPS) and their mechanical properties, in particular wear, were investigated. A wide range of grain sizes, from 80 nm and 250 nm were obtained by varying sintering conditions ($1550^{\circ}C$-5 min to $1650^{\circ}C$-20 min). The elastic modulus of obtained ceramics was ${\sim}250$ GPa and hardness was in the range of $13{\sim}14$ GPa. The indentation fracture toughness increased from $2.58MPa{\cdot}m^{1/2}$ to $3.24MPa{\cdot}m^{1/2}$ with increasing sintering temperature possibly due to the elongated grains. Sliding wear tests revealed at least an order magnitude improvement in wear resistance with grain refinement. Microstructure analysis indicated that nano-$Si_3N_4$ specimens worn mainly through delamination and microcracking, while that of coarser specimens revealed severe wear with grain debonding and fracture.

• Journal of Powder Materials
• /
• v.20 no.3
• /
• pp.203-209
• /
• 2013

In this study, STS 316L powders with 3 wt.% Cu and 1 wt.% Sn known as corrosion-resistance reinforcement elements, are prepared to make different kinds of specimens, in which, 3 wt.% Cu and 1 wt.% Sn are added in different forms by mixing, alloying and fully alloying. After sintering in the same condition, the corrosion resistance, wear resistance and their mechanical properties of specimens are tested respectively. According to the comparison, STS 316L specimen sintered at $1270^{\circ}C$ showed the most excellent mechanical property: HRB 78 (hardness), 1130.7 MPa (RCS), 26.6% (Fraction Wear), It was similar with the specimen made of STS316L and fully alloyed Cu and Sn powders, meanwhile, the latter one appears the best corrosion resistance, 75hrs-salt immersion test results. In addition, the specimens with Cu and Sn powders additive showed relatively worse wear resistance in compared with STS316L specimen.

• International Journal of Ocean System Engineering
• /
• v.2 no.4
• /
• pp.244-249
• /
• 2012

In this study, a monolithic MoSi2 matrix reinforced with 20 vol% SiC particles, a SiC/MoSi2 composite matrix reinforced with 20 vol% ZrO2 particles, and a ZrO2/MoSi2 composite were fabricated using hot press sintering at $1350^{\circ}C$ for 1 h under a pressure of 30 MPa. The Vickers hardness and sliding wear resistance of the monolithic MoSi2, ZrO2/MoSi2, and SiC/MoSi2 composite were investigated at room temperature. A wear behavior test was carried out using a disk-type wear tester with a silicon nitride ball. The ZrO2/MoSi2 composite showed an average Vickers hardness value and excellent wear resistance compared with the monolithic MoSi2 and SiC/MoSi2 composite at room temperature.

• Korean Journal of Materials Research
• /
• v.10 no.3
• /
• pp.227-232
• /
• 2000

Cu-W composites containing 20wt.% W were fabricated by hot pressing. Hot pressing was carried out at temperatures ranging from 800 to $1000^{\circ}C$ under pressures of 15MPa for 30MPa for 30min and 60min. This process gave composites of higher density, higher hardness and higher wear resistance than the conventional sintering processes. However, the microstructure of Cu-W composites under pressure of 15MPa revealed there was an inhomogeneous distribution of W, segregation of W on some area. These undesirable results are attributed to the immiscibility of W in Cu and the pressure effect on sintering.

• Journal of Powder Materials
• /
• v.21 no.6
• /
• pp.460-466
• /
• 2014

Al-Si-SiC composite powders with intra-granular SiC particles were prepared by a gas atomization process. The composite powders were mixed with Al-Zn-Mg alloy powders as a function of weight percent. Those mixture powders were compacted with the pressure of 700 MPa and then sintered at the temperature of $565-585^{\circ}C$. T6 heat treatment was conducted to increase their mechanical properties by solid-solution precipitates. Each relative density according to the optimized sintering temperature of those powders were determined as 96% at $580^{\circ}C$ for Al-Zn-Mg powders (composition A), 97.9% at $575^{\circ}C$ for Al-Zn-Mg powders with 5 wt.% of Al-Si-SiC powders (composition B), and 98.2% at $570^{\circ}C$ for Al-Zn-Mg powders with 10 wt.% of Al-Si-SiC powders (composition C), respectively. Each hardness, tensile strength, and wear resistance test of those sintered samples was conducted. As the content of Al-Si-SiC powders increased, both hardness and tensile strength were decreased. However, wear resistance was increased by the increase of Al-Si-SiC powders. From these results, it was confirmed that Al-Si-SiC/Al-Zn-Mg composite could be highly densified by the sintering process, and thus the composite could have high wear resistance and tensile strength when the content of Al-Si-SiC composite powders were optimized.

• Journal of the Korean Ceramic Society
• /
• v.31 no.1
• /
• pp.25-30
• /
• 1994

W-Ti-C-N based multiphase hard materials have been prepared from WC/TiN powder mixture. By sintering at and above 190$0^{\circ}C$, the two phases of powder mixture has transformed into intermixed W, W2C and Ti(C, N) phases. For the temperature range between 180$0^{\circ}C$ and 210$0^{\circ}C$, the sintered or hot pressed samples show maximum density and hardness. The seems that metallic W grains enhance the fracture toughness of materials. The wear resistance of the material is found to increase with increasing hardness.