Abstract
This study investigated the microstructure and wear resistance property of HPHT(high pressure high temperature) sintered PDC(polycrystalline diamond compact) in accordance with initial molding pressure. After quantifying an identical amount of diamond powder, the powder was inserted in top of WC-Co sintered material, and molded under four different pressure conditions (50, 100, 150, $200kgf/cm^2$). The obtained diamond compact underwent sintering in high pressure, high temperature conditions. In the case of the $50kgf/cm^2$ initial molding pressure condition, cracks were formed on the surface of PDC. On the other hand, PDCs obtained from $100{\sim}200kgf/cm^2$ initial molding pressure conditions showed a meticulous structure. As molding pressure increased, low Co composition within PDC was detected. A wear resistance test was performed on the PDC, and the $200kgf/cm^2$ condition PDC showed the highest wear resistance property.