• 한국분말재료학회지
• /
• 제19권1호
• /
• pp.60-66
• /
• 2012

In this study, Platinum(Pt) nanoparticles were synthesized by using polyol process which is one of the liquid phase reduction methods. Dihydrogen hexachloroplatinate (IV) hexahydrate $(H_2PtCl_6{\cdot}6H_2O)$, as a precursor, was dissolved in ethylene glycol and silver nitrate ($AgNO_3$) was added as metal salt for shape control of Pt particle. Also, polyvinylpyrrolidone (PVP), as capping agent, was added to reduce the size of particle and to separate the particles. The size of Pt nanoparticles was evaluated particle size analyzer (PSA). The size and morphology of Pt nanoparticles were observed by transmission electron microscopy (TEM) and high resolution TEM (HRTEM). Synthesized Pt nanoparticles were studied with varying time and temperature of polyol process. Pt nanoparticles have been successfully synthesized with controlled sizes in the range 5-10 and 20-40 nm with cube and multiple-cube shapes.

• Macromolecular Research
• /
• 제17권6호
• /
• pp.378-387
• /
• 2009

This research compared three methods for producing and processing nanocomposite polypropylene filament yarns with permanent antimicrobial efficiency. The three methods used to mix antimicrobial agents based on silver nano particles with PP were as follows: 1) mixing of PP powder and inorganic nanocomposite filler with the appropriate concentration using a twin-screw extruder and preparing granules, 2) method 1 with a singlerather than twin-screw extruder, and 3) producing the masterbatch by a twin-screw extruder and blending it with PP in the melt spinning process. All pure polypropylene samples and other combined samples had an acceptable spinnability at the spinning temperature of $240^{\circ}C$ and take-up speed of 2,000 m/min. After producing as-spun filament yarns by a pilot plant, melt spinning machine, the samples were drawn, textured and finally weft knitted. The physical and structural properties (e.g., linear density, tenacity, breaking elongation, initial modulus, rupture work, shrinkage and crystallinity) of the as-spun and drawn yarns with constant and variable draw ratios (the variable draw ratio was used to gain a constant breaking elongation of 50%) were investigated and compared, while DSC, SEM and FTIR techniques were used to characterize the samples. Finally, the antibacterial efficiency of the knitted samples was evaluated. The experimental results revealed that the crystallinity reduction of the as-spun yarn obtained from method 1 (5%) was more than that of method 2 (3%), while the crystallinity of the modified as-spun yarns obtained with method 3 remained unchanged compared to pure yarn. However, the drawing procedure compensated for this difference. By applying methods 2 and 3, the drawing generally improved the tenacity and modulus of the modified fibers, whereas method 1 degraded the constant draw ratio. Although the biostatic efficiency of the nanocomposite yarns was excellent with all three methods, the modified fabrics obtained from methods 1 and 2 showed a higher bioactivity.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.21-21
• /
• 2009

후막 광식각 기술을 이용하여 형성된 Ag 전극과 LTCC 기판 사이의 접착력을 향상시키기 위하여 무기 바인더로서 anorthite, diopside 및 MLS-62 glass frit을 첨가하여 감광성 Ag paste를 제조하였다. 소성 후의 glass pool effect를 감소시키기 위해 attrition mill을 통하여 미세 glass 분말을 준비하였다. Glass frit은 Ag powder의 5vol%~25vol%의 함량으로 첨가하여 감광성 Ag paste를 제조하였고 패턴 형성 후 $850^{\circ}C$에서 1시간 소결하였다. 전극과 기판 사이의 접착력은 micro-ball shear test 법으로 측정하였으며, Ag 전극 부착력은 glass frit의 함량 증가에 따라 증가하다가 감소하는 경향을 보이는데, 이는 과량의 glass frit 첨가로 인한 전극 내부에 액상 풀의 형성에 기인한 것으로 보여진다. Ag 전극의 면저항은 glass frit의 함량이 증가함에 따라 $0.13m{\Omega}{/\square}$에서 $2.06m{\Omega}{/\square}$까지 증가하는 경향을 나타내었다. 소성 전후의 전극 패턴의-수축율은 $100{\mu}m$의 선폭을 기준으로 glass frit의 첨가랑이 증가할수록 43.3%에서 35.0%로 감소하였으며, 그 결과 최소 선폭 $25{\mu}m$의 미세 전극 패턴의 형성이 가능하였다.