• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.05a
• /
• pp.46-47
• /
• 2013

This study investigates the effect of a grading of aggregate on the properties of concrete. It is a common sense in Korea that the production of coarse aggregate in ready mixed concrete industry excludes particular aggregate size ranged from 5 mm to 13 mm for saving the production cost. This causes a gap grading of the aggregate for concrete, which can lead to the increase of unit water, the development of drying shrinkage-induced crack and the reduction of compressive strength. In this study, conventional aggregate obtained from a ready mixed concrete factory and the aggregate with a modified grading produced in lab. condition were prepared. Results showed that a good grading of aggregate (i.e., the ratio of 5~13 mm and 13~25 mm is 6 to 4) produced in the lab. condition significantly improved the slump and the compressive strength of the concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.2
• /
• pp.81-88
• /
• 2011

This study ascertained the possibility of use of sulfur abstracted from waste sulfur as a construction material through modification process and manufacturing high efficiency modification sulfur with superior quality on dispersibility and hydrophilic in normal temperature. Mechanic, behavior and chemical durability of mortar with added modification sulfur. The results of the study are as follows. The fluidity of mortar mixed with modification sulfur and compressive strength decreased as ratio of mixing of them increases. Flexural, tensile and bond strength of the mortar are also improved and shrinkage of it increases. Especially chemical durability of the mortar showed excellent resistance with the increase of ratio of mixing. Therefore this research has confirmed the modification sulfur can be used as a addmixture for cement.

• Journal of Powder Materials
• /
• v.21 no.4
• /
• pp.266-270
• /
• 2014

Metal foams have a cellular structure consisting of a solid metal containing a large volume fraction of pores. In particular, open, penetrating pores are necessary for industrial applications such as in high temperature filters and as a support for catalysts. In this study, Fe foam with above 90% porosity and 2 millimeter pore size was successfully fabricated by a slurry coating process and the pore properties were characterized. The Fe and $Fe_2O_3$ powder mixing ratios were controlled to produce Fe foams with different pore size and porosity. First, the slurry was prepared by uniform mixing with powders, distilled water and polyvinyl alcohol(PVA). After slurry coating on the polyurethane(PU) foam, the sample was dried at $80^{\circ}C$. The PVA and PU foams were then removed by heating at $700^{\circ}C$ for 3 hours. The debinded samples were subsequently sintered at $1250^{\circ}C$ with a holding time of 3 hours under hydrogen atmosphere. The three dimensional geometries of the obtained Fe foams with an open cell structure were investigated using X-ray micro CT(computed tomography) as well as the pore morphology, size and phase. The coated amount of slurry on the PU foam were increased with $Fe_2O_3$ mixing powder ratio but the shrinkage and porosity of Fe foams were decreased with $Fe_2O_3$ mixing powder ratio.

• Computers and Concrete
• /
• v.26 no.4
• /
• pp.367-375
• /
• 2020

Today, the use of special technologies in the admixture of concrete has made tremendous progress, but the problem that has always existed in the construction of concrete members is the brittleness and lack of loading bearing after cracking, which leads to reduced strength and energy absorption. One of the best ways to fix this is to reinforce the concrete with steel fibers. Steel fibers also control cracks due to dry shrinkage, reduce structural crack width, and improve impact resistance. In this study, recycled steel fibers from worn tires have been used in the manufacture of concrete samples, the secondary benefits of which are the reduction of environmental pollution. One of the disadvantages of steel fiber reinforced concrete is the corrosion of steel fibers and their deterioration in harsh environments such as coastal areas. Corrosion caused by chlorine ions in metal fibers causes deterioration and early decommissioning of structures in corrosive environments. In this study, the effect of the dosage of steel fibers (dosages of 15, 30, and 45 kg of fibers per cubic meter of concrete) and aspect ratio of fibers (aspect ratio of 25 and 50) on compressive and flexural strength of concrete samples are investigated. In the following, the effect of fiber corrosion on the results of the mechanical properties of concrete samples is examined. The results show that the increase in fiber causes a relative increase in compressive strength, and a significant increase in flexural strength, and corrosion of steel fibers without reducing workability reduces compressive strength and flexural strength by up to 6 to 11%, respectively.

• Geomechanics and Engineering
• /
• v.22 no.3
• /
• pp.227-236
• /
• 2020

Expansive soils are renowned for their swelling-shrinkage property and these volumetric changes resultantly cause huge damage to civil infrastructures. Likewise, subgrades consisting of expansive soils instigate serviceability failures in pavements across various regions of Pakistan and worldwide. This study presents the use of polypropylene fibers to improve the engineering properties of a local swelling soil. The moisture-density relationship, unconfined compressive strength (UCS) and elastic modulus (E₅₀), California bearing ratio (CBR) and one-dimensional consolidation behavior of the soil treated with 0, 0.2, 0.4, 0.6 and 0.8% fibers have been investigated in this study. It is found that the maximum dry density of reinforced soil slightly decreased by 2.8% due to replacement of heavier soil particles by light-weight fibers and the optimum moisture content remained almost unaffected due to non-absorbent nature of the fibers. A significant improvement has been observed in UCS (an increase of 279%), E₅₀ (an increase of 113.6%) and CBR value (an increase of 94.4% under unsoaked and an increase of 55.6% under soaked conditions) of the soil reinforced with 0.4% fibers, thereby providing a better quality subgrade for the construction of pavements on such soils. Free swell and swell pressure of the soil also significantly reduced (94.4% and 87.9%, respectively) with the addition of 0.8% fibers and eventually converting the medium swelling soil to a low swelling class. Similarly, the compression and rebound indices also reduced by 69.9% and 88%, respectively with fiber inclusion of 0.8%. From the experimental evaluations, it emerges that polypropylene fiber has great potential as a low cost and sustainable stabilizing material for widespread swelling soils.

• Journal of the Korean Ceramic Society
• /
• v.52 no.4
• /
• pp.253-263
• /
• 2015

Ordinary Portland cement is a widely favored construction material because of its good strength and durability and its reasonable price; however, spalling behaviour during fire exposure can be a serious risk that can lead to strength degradation or collapse of a building. Geopolymers, which can be synthesized by mixing aluminosilicate source materials such as metakaolin and fly ash, and alkali activators, are resistant to fire. Because the chemical composition of geopolymers controls the properties of the geopolyers, geopolymers with various Si:Al ratios were synthesized and evaluated as fire resistant construction materials. Rejected fly ash generated from a power plant was quantitatively analyzed and mixed with alkali activators to produce geopolymers having Si:Al ratios of 1.5, 2.0, and 3.5. Compressive strength of the geopolymers was measured at 28 days before and after heating at $900^{\circ}C$. Geopolymers having an Si:Al ratio of 1.5 presented the best fire resistance, with a 44% increase of strength from 29 MPa to 41 MPa after heating. This material also showed the least expansion-shrinkage characteristics. Geopolymer mortar developed no spalling and presented more than a 2 h fire resistance rating at $1,050^{\circ}C$ during the fire testing, with a cold side temperature of $74^{\circ}C$. Geopolymers have high potential as a fire resistant construction material in terms of their increased strength after exposure to fire.

• Journal of the Korea Concrete Institute
• /
• v.13 no.1
• /
• pp.23-29
• /
• 2001

This study presented the experimental results on the durability properties of recycled aggregate concrete incorporating fly ash. The main experimental variables were the substitution ratio of recycled aggregate and fly ash, where the substitution ratios of recycled aggregate were 0, 30, and 50%, and those of fly ash were 0, 10, 20, and 30%. The tests for evaluating compressive strength, freezing-thawing resistance, and drying shrinkage were conducted for each specimen. As a result, the compressive strength and the durability of the recycled aggregate concrete were compared from those of ordinary concrete. The followings were conclusion; The compressive strengths of recycled aggregate concrete were less than those of ordinary concrete by 5-10%. However, the durability factor of recycled aggregate concrete remained above 90% at the substitution ratio of 30%. The quality of recycled aggregate concrete were improved by substitution at the range of less that 20% of fly ash and 30% of recycled aggregate.

• Journal of the Korean Wood Science and Technology
• /
• v.45 no.5
• /
• pp.519-524
• /
• 2017

Physical, mechanical and deteriorating properties of Phellodendron amure were investigated. Air dried density located indoor was 0.41 but $0.43g/cm^3$ outdoor. In oven dry shrinkage, T/R ratio for located indoor was 1.40 but 1.32 outdoor. Hygroscopic property at $40^{\circ}C$ with 90% relative humidity was 16.30% for indoor and 15.80% for outdoor. Compressive strength for outdoor conditioned sample was 43.81 MPa but 40.33 MPa for indoor conditioned. Also bending strenght for outdoor conditioned was 84.63 MPa but 68.80 MPa for indoor conditioned. Impact strength was 3.43 and $4.00J/cm^2$ indoor and outdoor, respectively. Hardness at cross-section was 47.92 and 49.20 MPa indoor and outdoor, respectively. With one-year conditioning at indoor or outdoor, there was no significantly different in strength properties, which came from strong resistance for deterioration. Also Phellodendron amure wood showed dimensionally stable raw material based on low T/R ratio.

• Proceedings of the KIEE Conference
• /
• 1998.11c
• /
• pp.795-797
• /
• 1998

A $BaTiO_3$, ferroelectric material, was mixed $SrTiO_3$, $(x)BaTiO_3-(1-x)SrTiO_3$($0.7{\leq}x{\leq}1$) ceramic capacitor with stable electrical properties in high voltage was fabricated. And microstructure, electrical property were investigated with $SrTiO_3$ mol ratio. The shrinkage, open porosity, sintering density were predominated at $9BaTiO_3-0.1SrTiO_3$. Increasing $SrTiO_3$ mol ratio, curie temperature was shifted at low temperature and maximum permittivity was increased. Also, $0.9BaTiO_3-0.1SrTiO_3$ was showed stable dielectric properties at $25{\sim}80[^{\circ}C]$. V-I properties of specimen were observed in the temperature range of $21{\sim}143[^{\circ}C]$, were divided into three regions. The region I below 10[kV/cm] was shown Ohmic conduction, the region II from 10 to 30[kV/cm] was explained by the Poole-Frenkel emission theory and the region III above 30[kV/cm] was analysed by the tunneling effect.

• Elastomers and Composites
• /
• v.36 no.4
• /
• pp.268-277
• /
• 2001

The MDI(4,4'-diphenyl methane diisocyanate) was mixed with PPG, PEG and trimethylolpropane(TMP) respectively to prepare polyurethane resin. The various physical properties were measured for the mixtures. The gel-time was shortened by adding of PEG and TMP The molecular weight made a greater influence on the gel-time than the number of functional groups. The NCO-OH reaction was more active and faster than the NCO-NCO reaction. The hardness was influenced by crosslinking-density and molecular structure. The NCO-OH reactions yielded the flexible films and the NCO-NCO reactions yielded the brittle films. The increase of crystallinity and shrinkage induced the low adhesion ratio but the adding of TMP induced the high adhesion ratio. The flame-retardancy was influenced by quantity and kinds of flame-retardant. IXOL B-251 was the most excellent among the flame-retardants employed in this study. TCCP was partially separated because of the lack of solubility.