• 한국정밀공학회지
• /
• 제21권7호
• /
• pp.22-29
• /
• 2004

As a result of high integration of semiconductor device, the global planarization of multi-layer structures is necessary. So the chemical mechanical polishing(CMP) is widely applied to manufacturing the dielectric layer and metal line in the semiconductor device. CMP process is under influence of polisher, pad, slurry, and process itself, etc. In comparison with the general CMP which uses the slurry including abrasives, fixed abrasive pad takes advantage of planarity, resulting from decreasing pattern selectivity and defects such as dishing & erosion due to the reduction of abrasive concentration especially. This paper introduces the manufacturing technique of fixed abrasive pad using hydrophilic polymers with swelling characteristic in water and explains the self-conditioning phenomenon. And the tungsten CMP using fixed abrasive pad achieved the good conclusion in terms of the removal rate, non-uniformity, surface roughness, material selectivity, micro-scratch free contemporary with the pad life-time.

• 한국표면공학회지
• /
• 제32권3호
• /
• pp.410-415
• /
• 1999

The adhesion strength of sputtered copper films to Inconel substrates has been studied using the scratch test. The effects of substrate treatments before deposition such as chemical or ion bombardment etching were investigated by means of a mean critical load derived from a Weibull-like statistical analysis. It was found that the mean critical load was very weak unless the amorphous layer produced by mechanical polishing on the substrate surface was eliminated. Chemical etching in a nitric-hydrochloric acid bath was shown to have practically no effect on the enhancement of the adhesion. In contrast, the addition in this bath of nickel and copper sulphates allowed removal of the amorphous layer and an increase in the values of the mean critical load. However, it was observed that excessive chemical etching could cancel out the mean critical load enhancement. The results obtained in the case of ion bombardment etching pretreatments could be far higher than those obtained with chemical etching. Moreover, for a sufficiently long period of ion bombardment etching, the adhesion strength was so high that it was impossible to observe evidence of an adhesion failure.

• 한국정밀공학회지
• /
• 제14권10호
• /
• pp.58-67
• /
• 1997

Generally, die polishing process occupies about 30 .approx. 50% of the whole die manufacturing time. However, die polshing has not been automated yet, since it needs a great deal of experience and skill. This study aims at development of an expert system for die polishing which gives such optimal parameters as tool and polishing conditions. Through experiments, polishing characteristics such as surface roughness, stock removal and scratch were analyzed quantitatively for each polishing tool, and a knowledge base for the expert system was established. Evaluation tests show that the developed system works well to suggest the optimal polishing conditions and it is very promising.

• 한국재료학회지
• /
• 제25권1호
• /
• pp.21-26
• /
• 2015

CMP(Chemical Mechanical Polishing) Processes have been used to improve the planarization of the wafers in the semiconductor manufacturing industry. Polishing performance of CMP Process is determined by the chemical reaction of the liquid sol containing abrasive, pressure of the head portion and rotational speed of the polishing pad. However, frictional heat generated during the CMP process causes agglomeration of the particles and the liquidity degradation, resulting in a non-uniform of surface roughness and surface scratch. To overcome this chronic problem, herein, we introduced NaCl salt as an additive into silica sol for elimination the generation of frictional heat. The added NaCl reduced the zata potential of silica sol and increased the contact surface of silica particles onto the sapphire wafer, resulting in increase of the removal rate up to 17 %. Additionally, it seems that the silica particles adsorbed on the polishing pad decreased the contact area between the sapphire water and polishing pad, which suppressed the generation of frictional heat.

• 한국표면공학회지
• /
• 제50권6호
• /
• pp.473-479
• /
• 2017

CrN coatings have been used as protective coatings for cutting tools, forming tools, and various tribological machining applications because these coatings have high hardness. Cr-Al-N coatings have been investigated to improve the properties of CrN coatings. Cr-Al-N coatings were fabricated by a hybrid physical vapor deposition method consisting of unbalanced magnetron sputtering and arc ion plating with different working pressure and substrate bias voltage. The phase analysis of the composition was performed using XRD (x-ray diffraction). Cr-Al-N coatings were grown with textured CrN phase and (111), (200), and (220) planes. The adhesion strength of the coatings tested by scratch test increased. The friction coefficient and removal rate of the coatings were measured by a ball-on-disk test. The friction coefficient and removal rate of the coatings decreased from 0.46. to 0.22, and from $2.00{\times}10^{-12}m^2/N$ to $1.31{\times}10^{-13}m^2/N$, respectively, with increasing bias voltage. The tribological properties of the coatings increased with increasing substrate bias voltage.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.140-143
• /
• 2004

Chemical mechanical polishing(CMP) is essential technology to secure the depth of focus through the global planarization of wafer. But a variety of defects such as contamination, scratch, dishing, erosion and corrosion are occurred during CMP. Especially, dishing and erosion defects increase the resistance because they decrease the interconnect section area, and ultimately reduce the life time of the semiconductor. Due to this dishing and erosion must be prohibited. The pattern density and size in chip have a significant influence on dishing and erosion occurred over-polishing. Decreasing of abrasive concentration results in advanced pattern selectivity which can lead the uniform removal in chip and decrease of over-polishing. The fixed abrasive pad was applied and tested to reduce dishing and erosion in this paper. Consequently, reduced dishing and erosion was observed in CMP of tungsten pattern wafer with proposed fixed abrasive pad and chemicals.

• 한국정밀공학회지
• /
• 제22권2호
• /
• pp.38-45
• /
• 2005

Chemical mechanical polishing(CMP) has been widely accepted for the planarization of multi-layer structures in semiconductor fabrication. But a variety of defects such as abrasive contamination, scratch, dishing, erosion and corrosion are occurred during CMP. Especially, dishing and erosion defects increase the metal resistance because they decrease the interconnect section area, and ultimately reduce the lift time of the semiconductor. Due to this reason dishing and erosion must be prohibited. The pattern density and size in chip have a significant influence on dishing and erosion occurred by over-polishing. The fixed abrasive pad(FAP) was applied and tested to reduce dishing and erosion in this paper. The abrasive concentration decrease of FAP results in advanced pattern selectivity which can lead the uniform removal in chip and declining over-polishing. Consequently, reduced dishing and erosion was observed in CMP of tungsten pattern wafer with proposed FAP and chemicals.

• 한국표면공학회지
• /
• 제39권6호
• /
• pp.268-275
• /
• 2006

In this study, effect of sputtering on the plasma-nitriding substrate and before PVD coating on the microstucture, microhardness, surface roughness and the adhesion strength of CrZrN thin films were investigated. Experimental results showed that this sputtering process not only removed surface compound layer which formed during a plasma nitriding process but also induced an alteration of the surface of plasma nitrided substrate in terms of microhardness distribution, surface roughness. This in turn affected the adhesion strength of PVD coatings. After sputtering, microhardness distribution showed general decrease and the surface roughness became increased slightly. The critical shear stress measured from the scratch test on the CrZrN coatings showed an approximately 1.4 times increase in the adhesion strength through the sputtering prior to the coating and this could be attributed to a complete removal of compound layer from the plasma nitrided surface and to an increase in the surface roughness after sputtering.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 하계학술대회 논문집 Vol.9
• /
• pp.112-112
• /
• 2008

최근 Ruthenium (Ru) 은 높은 화학적 안정성, 누설전류에 대한 높은 저항성, 저유전체와의 높은 안정성 등과 같은 특성으로 인해 금속층-유전막-금속층 캐패시터의 하부전극으로 각광받고 있다. 또한 Cu와의 우수한 Adhesion 특성으로 인해 Cu 배선에서의 Cu 확산 방지막으로도 주목받고 있다. 그러나 이렇게 형성된 Ru 하부전극의 각 캐패시터간의 분리와 평탄화를 위해서는 CMP 공정이 도입이 필요하다. 이러한 CMP 공정에 공급되는 Slurry 에는 부식액, pH 적정제, 연마입자 등이 첨가되는데 이때 연마입자가 응집하여 Slurry의 분산 안전성 저하에 영향을 줄수 있다. 이로 인해 응집된 Slurry는 Scratch와 Delamination 과 같은 표면 결함을 유발할 수 있으며, Slurry의 저장 안정성을 저하시켜 Slurry의 물리적 화학적 특성을 변화시킬 수 있다. 그리하여 본 연구에서는 Ru CMP Slurry에서의 Surfactant와 같은 분산 안정제에 따른 Surface tension, Zeta potential, Particle size, Sedimentation의 분석을 통해 Slurry 안정성에 대한 영향을 살펴보았다. 그 결과 pH9 조건의 31ppm Dispersant 농도에서 50%이상의 Sedimentation 상승효과를 얻을 수 있었다. 또한 선택된 Surfactant가 첨가된 Ru CMP Slurry를 제조하여 Ru wafer의 Static etch rate, Passivation film thickness 와 Wettability를 비교해 보았다. 그리고 CMP 공정을 실시하여 Ru의 Removal rate와 TEOS에대한 Selectivity를 측정해 보았다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.185-188
• /
• 2001

Chemical mechanical polishing(CMP) process is widely used for global planarization of inter-metal dielectric (IMD) layer and inter-layer dielectric (ILD) for deep sub-micron technology. However, as the IMD and ILD layer gets thinner, defects such as micro-scratch lead to severe circuit failure, which affect yield. In this paper, for the improvement of CMP Process, deionized water (DIW) pressure, purified $N_2$ (P$N_2$) gas, slurry filter and high spray bar were installed. Our experimental results show that DIW pressure and P$N_2$ gas factors were not related with removal rate, but edge hot-spot of patterned wafer had a serious relation. Also, the filter installation in CMP polisher could reduce defects after CMP process, it is shown that slurry filter plays an important role in determining consumable pad lifetime. The filter lifetime is dominated by the defects. However, the slurry filter is impossible to prevent defect-causing particles perfectly. Thus, we suggest that it is necessary to install the high spray bar of de-ionized water (DIW) with high pressure, to overcome the weak-point of slurry filter. Finally, we could expect the improvements of throughput, yield and stability in the ULSI fabrication process.