• Journal of Forest and Environmental Science
• /
• v.37 no.1
• /
• pp.79-89
• /
• 2021

Cement bonded boards of 10 mm in thickness were produced from the mixture of Gmelina arborea sawdust and corn cob particles. The strength and dimensional stability of cement bonded composites produced from these two mixtures were examined. A total of thirty experimental boards were produced at density level of 1,000 kg/㎥ with cement to fibre ratio of 2.5:1 and 3:1 and five (5) blending proportions of G. arborea sawdust to corn cob particles of 100:0; 75:25; 50:50; 25:75 and 100:0. The effect of the cement to fibre ratio and blending proportion on the Water Absorption (WA), Thickness Swelling (TS), Modulus of Rupture (MOR), and Modulus of Elasticity (MOE) were determined. The result indicates that as the mixing ratio of cement to fibre and blending proportion of maize cob (75%) to G. arborea (25%) increased, the thickness swelling, water absorption decreased, whereas the MOR and MOE increased. It also shows that most dimensionally stable and flexural strength boards were produced at the highest level of mixing ratios (3:1) and blending proportion of G. arborea to corn cob 25:75. However, the analysis of variance shows that TS and WA were significantly different, whereas, MOE and MOR were not significantly affected by mixing ratios and blending proportions. Finding of this study has shown that maize cob particles are suitable for cement bonded board production.

• Journal of agriculture & life science
• /
• v.46 no.1
• /
• pp.29-34
• /
• 2012

To examine possibilities to make use of woodceramics for the lower material of hot-floored ondol boards, woodceramics made from sawdust board with Pinus densiflora, put them in a wood frame and concrete block and heated them sending an electric current, and measured changes in surface temperature of a laminated floor board and a plywood floor board. As the sending an electric current to time passed, their surface temperature increased rapidly up to 20 minutes, and then gradually ascended. In terms of the surface temperature in the wood frame, the beginning temperature of a plywood floor board was higher than that of laminated floor one; however, as time passed, a laminated floor board's temperature rose, and after 60 minutes, it showed similar to the temperature of a floor board of lamination. On the other hand, the surface temperature in a concrete block showed that the laminated floor board was higher than the plywood floor board in both early and 60-minute later temperatures. With the lapse of time after switching off, the surface temperature of floor boards slowly dwindled up to 9 minutes, and from that time on, began to drop sharply. In terms of the descent speed of surface temperature, when woodceramics' surface temperature was adjusted at $70^{\circ}C$, the laminated floor board was the highest; when it was at $80^{\circ}C$, the plywood floor board was the highest, resulting in rapid descent speed of heat.

• Journal of Forest and Environmental Science
• /
• v.36 no.3
• /
• pp.219-224
• /
• 2020

Urea formaldehyde resins are widely used in the manufacturing of wood composite and their usage is always combined with release of formaldehyde characterized to be hazardous to health during and after the manufacturing of the products. This study investigates the effectiveness of wood-based adhesive from oil of pyrolysed Triplochiton scleroxylon sawdust for the production of composite board. The wood-derived Pyrolytic Oil (PyO) was blended with Urea Formaldehyde (UF) resin to formed Pyrolytic Oil-Urea Formaldehyde (PyOUF). The obtained PyOUF called Wood-Based Adhesives at four blends and control (UF) viz; 1:1, 1:2, 1:3, 2:1, 1:3 were further employed to prepare the composite board and test for their bonding strength by physical (water absorption-WA and thickness swelling-Th.S) and mechanical properties (modulus of elasticity-MOE, modulus of rupture-MOR, and impact bending-IB). Data obtained was analysed using analysis of variance at α 0.05. The result of analysis of variance conducted on physical properties show significant difference (p≤0.05) between the WA values obtained when testing the different blending proportion of PyOUF and likewise between 2 and 24 h of immersion. PyOUF had significant effect (p≤0.05) on Th. S for 24 h but no significant different (p>0.05) for the 2 h period of soaking. The analysis of variance on mechanical properties of the composite board (MOE, MOR, and IB) show significance differences (p≤0.05) between the strength values obtained when testing the different ratios of PyO with UF. PyO content influenced the properties of the boards and it is evident that PyO can be used in the manufacture of composite board.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.3
• /
• pp.22-28
• /
• 2007

Using woodceramics made from sawdust board of pine thinning logs, changes in surface temperature were investigated, by the heating rate and keeping time at maximum temperature. The heating rate of $2^{\circ}C/min$ and keeping time at maximum temperature 1 hour, were the highest in surface temperature. Also, it was found that woodcermics maintained heat for a long time because the descending velocity of their surface temperature was slower than that of the heater.

• Journal of the Korean Wood Science and Technology
• /
• v.16 no.2
• /
• pp.1-41
• /
• 1988

For the purpose of utilizing the sawdust having poor combining properties as board raw material and resulting in dimensional instability of board, polypropylene chip (abbreviated below as PP chip) or oriented PP thread was combined with sawdust particle from white meranti(Shorea sp.). The PP chip was prepared from PP thread in length of 0.25, 0.5, 1.0 and 1.5 cm for conventional blending application. Thereafter, the PP chip cut as above was combined with the sawdust particle by 3, 6, 9, 12 and 15% on the weight basis of board. Oriented PP threads were aligned with spacing of 0.5, 1.0 and 1.5cm along transverse direction of board. The physical and mechanical properties on one, two and three layer boards manufactured with the above combining conditions were investigated. The conclusions obtained at this study were summarized as follows: 1. In thickness swelling, all one layer boards combined with PP chips showed lower values than control sawdustboard, and gradually clear decreasing tendendy with the increase of PP chip composition. Two layer board showed higher swelling value than one layer board, but the majority of boards lower values than control sawdustboard. All three layer boards showed lower swelling values than control sawdustboard. 2. In the PP chip and oriented thread combining board, the swelling values of boards combining 0.5cm spacing oriented thread with 1.0 or 1.5cm long PP chip in 12 and 15% by board weight were much lower than the lowest of one or three layer. 3. In specific gravity of 0.51, modulus of rupture of one layer board combined with 3% PP chip showed higher value than control sawdustboard. However, moduli of rupture of the boards with every PP chip composition did not exceed 80kgf/cm2, the low limit value of type 100 board, Korean Industrial Standard KS F 3104 Particleboards. Moduli of rupture of 6%, 1.5cm-long and 3% PP chip combined boards in specific gravity of 0.63 as well as PP chip combined board in specific gravity of 0.72 exceeded 80kgf/$cm^2$ on KS F 3104. Two layer boards combined with every PI' chip composition showed lower values than control sawdustboard and one layer board. Three layer boards combined with.1.5cm long PP chip in 3, 6 and 9% combination level showed higher values than control sawdustboard, and exceeded 80kgf/$cm^2$ on KS F 3104. 4. In modulus of rupture of PP thread oriented sawdustboard, 0.5cm spacing oriented board showed the highest value, and 1.0 and 1.5cm spacing oriented boards lower values than the 0.5cm. However, all PP thread oriented sawdustboards showed higher values than control saw-dustboard. 5. Moduli of rupture in the majority of PP chip and oriented thread combining boards were higher than 80kgf/$cm^2$ on KS F 3104. Moduli of rupture in the boards combining longer PP chip with narrower 0.5cm spacing oriented thread showed high values. In accordance with the spacing increase of oriented thread, moduli of rupture in the PP chip and oriented thread combining boards showed increasing tendency compared with oriented sawdustboard. 6. Moduli of elasticity in one, two and three layer boards were lower than those of control sawdustboard, however, moduli of elasticity of oriented sawdustboards with 0.5, 1.0 and 1.5cm spacing increased 20, 18 and 10% compared with control sawdustboard, respectively. 7. Moduli of elasticity in the majority of PP chip and oriented thread combining boards in 0.5, 1.0 and 1.5cm oriented spacing showed much higher values than control sawdustboard. On the whole, moduli of elasticity in the oriented boards combined with 9% or less combination level and 0.5cm or more length of PP chip showed higher values than oriented sawdustboard. The increasing effect on modulus of elasticity was shown by the PP chip composition in oriented board with narrow spacing. 8. Internal bond strengths of all one layer PP chip combined boards showed lower values than control sawdust board, however, the PP chip combined boards in specific gravity of 0.63 and 0.72 exceeded 1.5kgf/$cm^2$, the low limit value of type 100 board and 3kgf/$cm^2$, type 200 board on KS F 3104, respectively. And also most of all two, three layer-and oriented boards exceeded 3kgf/$cm^2$ on KS F. 9. In general, screw holding strength of one layer board combined with PP chip showed lower value than control sawdustboard, however, that of two or three layer board combined with PP chip did no decreased tendency, and even screw holding strength with the increase of PP chip composition. In the PP chip and oriented PP thread combining boards, most of the boards showed higher values than control sawdustboard in 9% or less PP chip composition.

• Journal of Applied Biological Chemistry
• /
• v.55 no.1
• /
• pp.55-59
• /
• 2012

We designed a new rapid detection method for volatilized formaldehyde from wood. The process was installed with volatilizing and collecting parts in an incubator. For rapid sampling of formaldehyde from wood, we pulverized the wood to sawdust, and used 0.15-2.0 mm particles for the tests. The highest sampling rate (94.8%) was obtained at 40 mL/min flow rate and $100^{\circ}C$. Under the optimized condition, we could collect the volatilized formaldehyde with good recovery rate. The developed method was applied to the monitoring of the formaldehyde from wood, and the measured concentrations were 0.7-4.6 ${\mu}g/g$ from natural wood, 5.9-12.3 ${\mu}g/g$ from preserved wood, and 5.9-211.5 ${\mu}g/g$ from chemical adhesive processed wood. From the results, we identified natural wood sawdust and chemically processed wood (medium density fiberboard, high density fiberboard, particle board) by the formaldehyde contents except preserved wood.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.6
• /
• pp.517-523
• /
• 2009

Repeated impregnation and carbonization processes were performed to prepare high-density woodceramics using a sawdust board. The physical properties were investigated to confirm morphological and structural changes of one-time and two-time phenolic resin-treated and carbonized woodceramics. As comparing between one-time and two-time carbonized woodceramics, the weight and the density of the two-time carbonized woodceramics decreased with an increase of the carbonization temperature. When the carbonization temperature was $600^{\circ}C$, the weight increased by 21.7% and density increased by 20.6% from $0.68g/cm^3$ to $0.82g/cm^3$, respectively, as a maximum value.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.3
• /
• pp.39-46
• /
• 2008

Repeated impregnation and carbonization processes were performed to prepare high-density woodceramics using a sawdust board. The physical properties were investigated to confirm morphological and structural changes of one-time and two-time phenolic resin-treated and carbonized woodceramics. As comparing between one-time and two-time carbonized woodceramics, the weight and the density of the two-time carbonized woodceramics decreased with an increase of the amount of impregnated phenolic resin. In addition, when the amount of impregnated phenolic resin was about 40% in these woodceramics, the two-time carbonized woodceramics showed higher weight (23.8%) and density (30.0%) than the one-time treatment.

• Journal of the Korean Wood Science and Technology
• /
• v.13 no.4
• /
• pp.67-72
• /
• 1985

To improve the bending strength of sawdustboard, verious resin contents of 10, 13, 16, and 19% were applied to the thin shell (face layer) composed with wire net or not. The shell effect of sawdust and wire net composition formed with core sawdustboard were evaluated. Forcusing on the effects of wire net composition and noncomposition including a comparison with chipboard and veneer complyboard, bending properties (Modulus of rupture (MOR), Modulus of elasticity (MOE), Stress at proportional limit ($S_{pl}$). Work to maximum load ($W_{ml}$))were analyzed and discussed. 1. In modulus of rutpute, veneer comply was the highest (621.5 kg/$cm^2$), and next decreasing order was wire net composition (159.1 kg/$cm^2$), chipboard (81.75 kg/$cm^2$), and wire net noncomposition (76.21 kg/$cm^2$) as in modulus of elasticity, work to maximum load, except for stress at proportional limit. 2. The highly significant effects were shown in both wire net composition and noncomposition, at the same time wire net composition exceeded two times of noncomposition throughout resin contents in bending properties. Chipboard was similar to the mean or 16% resin content in noncomposirion. 3. Every board in wire net composition above 10% resin content was beyond 100 kg/$cm^2$ in MOR, minimum allowable strength for structural use according to KS F 3104. In conclusion, the feasibility for improving the bending strength of weak sawdustboard by wire net composed shell was offered.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.1
• /
• pp.73-79
• /
• 2004

Research investigated the variation of density, weight loss and dimensional decreasing rate, heat conduction rate by the resin impregnation rate and burning temperature of woodceramics, which were formed by impregnation rate of 40~80% and burning temperature of 600~1500℃ with sawdust board impregnated with phenolic resin made from thinned logs of pinus densiflora, Larix kaemferi and pinus koraiensis. As the resin impregnation rate and the burning temperature increased, the density increased, however, as the burning temperature increased to at 1200℃ or more, the density decreased. The more the resin impregnation rate increased, the more the decreasing rate of weight and size decreased; the more the burning temperature increased, the more the decreasing rate of weight and size increased. When the resin impregnation rate was high, the heat conduction (mm/sec) was superior.