Properties and Manufacture of High Density Woodceramics by Re-carbonization - Effect of Carbonization Temperature -

재 탄화에 의한 고밀도 우드세라믹 제조 및 성질 - 탄화온도의 영향 -

  • Oh, Seung Won (College of Agriculture and Life Science, Institute of Agriculture Science & Technology Chonbuk National University) ;
  • Hwang, Jung Woo (College of Agriculture and Life Science, Institute of Agriculture Science & Technology Chonbuk National University)
  • 오승원 (전북대학교 농업생명과학대학, 농업과학기술연구소) ;
  • 황정우 (전북대학교 농업생명과학대학, 농업과학기술연구소)
  • Received : 2009.06.29
  • Accepted : 2009.07.29
  • Published : 2009.11.25

Abstract

Repeated impregnation and carbonization processes were performed to prepare high-density woodceramics using a sawdust board. The physical properties were investigated to confirm morphological and structural changes of one-time and two-time phenolic resin-treated and carbonized woodceramics. As comparing between one-time and two-time carbonized woodceramics, the weight and the density of the two-time carbonized woodceramics decreased with an increase of the carbonization temperature. When the carbonization temperature was $600^{\circ}C$, the weight increased by 21.7% and density increased by 20.6% from $0.68g/cm^3$ to $0.82g/cm^3$, respectively, as a maximum value.

고밀도 우드세라믹 제조를 위한 기초연구로서 수지함침율 60%인 톱밥보드를 이용하여 탄화온도별로 제조된 1차 탄화 우드세라믹을 수지 재 함침한 후 2차 탄화하여 우드세라믹을 제조하고 그 물성을 조사하였다. 1, 2차 탄화 우드세라믹 성질 비교에서 탄화온도가 높아질수록 2차 탄화 후 중량 및 밀도증가율은 감소하였고 탄화온도 $600^{\circ}C$일 때 1차 탄화 시보다 중량은 21.7%, 그리고 밀도는 1차 탄화 시 $0.68g/cm^3$에서 2차 탄화 시 $0.82g/cm^3$로 20.6% 증가하여 최고치를 나타냈다.

Keywords

References

  1. Hirose, T., T. X. Fan, T. Okabe, and M. Yoshimura. 2001. Effect of carbonizing temperature on the basic properties of woodceramics impregnated with liquefied wood. Journal of Materials Science 36: 4145~4149 https://doi.org/10.1023/A:1017952502431
  2. Hirose, T., T. X. Fan, T. Okabe, and M. Yoshimura. 2002. Effect of carbonizing speed on the property change of woodceramics impregnated with liquefacient wood. Materials Letters 52: 229~233 https://doi.org/10.1016/S0167-577X(01)00399-8
  3. Hokkirigawa, K., T. Okabe, and K. Saito. 1995. Development of porous carbon materials "woodceramics"-Fundamental wear properties under unlubricated condition on air, under base-oil impregnated condition in water-. Journal of the Society of Materials Science Japan. 44(501): 800~804 https://doi.org/10.2472/jsms.44.800
  4. Hokkirigawa, K., T. Okabe, and K. Saito. 1996. Wear properties of new porous carbon materials: woodceramics. Journal of Porous Materials 2: 229~235 https://doi.org/10.1007/BF00488113
  5. Hokkirigawa, K., T. Okabe, and K. Saito. 1996a. Friction properties of new porous carbon materials: woodceramics. Journal of Porous Materials 2: 237~243 https://doi.org/10.1007/BF00488114
  6. Kasai, K., K. Shibata, K. Saito, and T. Okabe. 1996. Humidity Sensor characteristics of woodceramics. Transactions of the Materials Research Society of Japan 20: 92~95
  7. Oh, S. W. and H. S. Byeon. 2003. Change of surface temperature in woodceramics made from MDF(Ⅱ) -Effect of impregnation rate and burning temperature-. Journal of the Korea Wood Science and Technology 31(1): 41~45
  8. Oh, S. W., T. Hirose, and T. Okabe. 2000. Manufacturing characteristics of woodceramics from thinned small logs(I) - Resin impregnation rate and bending strength -. Journal of the Korean Wood Science and Technology 28(4): 51~55
  9. Oh, S. W. and T. Okabe. 2001. Properties of woodceramics chip tile made from waste wood (Ⅱ) -Effect of additions and woodceramics chip-. Journal of the Korean Wood Science and Technology 29(3): 68~72
  10. Oh, S. W. and T. Okabe. 2003. Manufacture of woodceramics chip tile from waste wood. Forest Products Journal 53(7/8): 50~53
  11. Okabe, T. and K. Saito. 1995. Development of woodceramics. Transactions of the Material Research Society of Japan 18: 681~684
  12. Okabe, T., K. Saito, and K. Hokkirigawa. 1996. The effect of burning temperature on the structural changes of woodceramics. Journal of Porous Materials 2: 215~221 https://doi.org/10.1007/BF00488111
  13. Okabe, T., K. Saito, and K. Hokkirigawa. 1996a. New porous carbon materials woodceramics : Development and fundamental properties. Journal of Porous Materials 2: 207~213 https://doi.org/10.1007/BF00488110
  14. Xian, Q. X., X. Tong, Di Z. Fan, T. Sakata, and Mori, H. 2002. Mechanical Properties and damping behavior of woodcermics/ Zk 60A Mg alloy composite. Materials Research Bulletin 37: 1133~1140 https://doi.org/10.1016/S0025-5408(02)00728-6
  15. Xian, Q. X., D. Zang, T. K. Fan, Sakata, T., H. Mori, T. Okabe, and T. Hirose. 2002. The fabrication of composites with interpenetrating networks based on woodceramics. Materials Letters 56: 102~107 https://doi.org/10.1016/S0167-577X(02)00426-3
  16. Xie, X. Q., T. X. Fan, B. H. Sun, D. T. Zang, T. Sakata, H. Mori, and T. Okabe. 2002. Dry sliding friction and wear behavior of woodceramics/ Al-Si composites. Material Science and Engineering. 1~7 https://doi.org/10.1016/S0921-5093(02)00320-9
  17. 岡部敏弘. 1996. 木質系多孔質炭素材料 ウツドセラミツクス. 內田老鶴圃. p. 269