• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.2
• /
• pp.182-190
• /
• 2009

Statement of problem: Microleakage at the occlusal and gingival margin of Class V cavities restored with composite resin has traditionally been considered an obstacle to successful restoration. Purpose: The aim of this study was to assess the effectiveness of three different surface sealants(Fortify, Permaseal and Biscover LV) on the marginal sealing of Class V light-activated composite resin restorations(Z250). Material and methods: Forty noncarious human premolars and molars extracted within a three-month period were selected. Class V cavities with the occlusal margin in enamel and gingival margin in cementum were prepared in both buccal and lingual surfaces. The teeth, randomly assigned in four groups with twenty cavities in each group, were restored with composite resin after applying an adhesive system(Clearfil SE bond). After the finishing and polishing procedures, the restorations were covered with a specific surface sealants, except for the control samples, which were not sealed. After placing restorations, the specimens were thermocycled, and immersed in a 2% methylene blue solution for twenty four hours and sectioned longitudinally. The marginal microleakage was evaluated at the occlusal and gingival interfaces using a microscope and compared among the four groups using ANOVA test and Wilcoxon Rank-Sum test($\alpha$=0.05). Results: Statistical analysis showed that there was significantly less leakage when the surface sealants were used than there was in control group(P<.05). There were no significant differences of microleakage at occlusal and gingival margins among groups. There were no significant differences between microleakage of occlusal and gingival margins in each group. Fortify was not statistically different from control group at the gingival margin(P>.05). Conclusion: Application of surface sealants was an effective method of surface coating in reducing microleakage at occlusal and gingival margins of Class V composite resin restorations. However, it is certain that some microleakage still occurred despite the application of surface sealants, especially gingival margins.

• Restorative Dentistry and Endodontics
• /
• v.32 no.2
• /
• pp.111-120
• /
• 2007

The purpose of this study is to evaluate the effects of surface treatment and composition of reinforcement material on fracture strength of fiber reinforced composite inlay bridges. The materials used for this study were I-beam, U-beam TESCERA ATL system and ONE STEP(Bisco, IL, USA). Two kinds of surface treatments were used; the silane and the sandblast. The specimens were divided into 11 groups through the composition of reinforcing materials and the surface treatments. On the dentiform, supposing the missing of Maxillary second pre-molar and indirect composite inlay bridge cavities on adjacent first pre-molar disto-occlusal cavity, first molar mesio-occlusal cavity was prepared with conventional high-speed inlay bur. The reinforcing materials were placed on the proximal box space and build up the composite inlay bridge consequently. After the curing, specimen was set on the testing die with ZPC. Flexural force was applied with universal testing machine (EZ-tester; Shimadzu, Japan). at a cross-head speed of 1 mm/min until initial crack occurred. The data was analyzed using one-way ANOVA/Scheffes post-hoc test at 95% significance level. Groups using I-beam showed the highest fracture strengths (p<0.05) and there were no significant differences between each surface treatment (p>0.05) Most of the specimens in groups that used reinforcing material showed delamination. 1. The use of I-beam represented highest fracture strengths (p<0.05) 2. In groups only using silane as a surface treatment showed highest fracture strength, but there were no significant differences between other surface treatments (p>0.05). 3. The reinforcing materials affect the fracture strength and pattern of composites inlay bridge. 4 The holes at the U-beam did not increase the fracture strength of composites inlay bridge.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.31 no.4
• /
• pp.329-339
• /
• 2015

Purpose: To investigate the information acquisition, selection criteria and selection methods of Mongolian dentists regarding adhesive agents for bonded restorations, and to provide future direction for continuing education. Materials and Methods: One hundred Mongolian dentists were interviewed and asked to complete a questionnaire containing 7 questions on general information about the responder, 8 questions on information acquisition and selection of bonded restoration agents, and 10 questions on continuing education. Results: Objective and credible information regarding bonded restoration materials were not being acquired, and logical material selection was not being made. The extent of continuing education was inadequate and not enough information regarding education was being acquired. The participants responded positively to online supplementary education. Conclusion: A systemized approach needs to be established in Mongolian dentistry to enable organized delivery of evidence-based guidelines and information, and logical selection of the numerous and various bonded restoration agents. Furthermore, the education of dentists, through various means, is required to enable proper use of the selected materials.

• Restorative Dentistry and Endodontics
• /
• v.27 no.6
• /
• pp.569-576
• /
• 2002

This study was peformed to evaluate the interfacial shear bond strength of base (direct and indirect) and repair composites with aging and surface treatment methods. Direct composite resin specimens ($Charisma^{\circledR}$, Heraeus Kulzer, Germany) were aged for 5 min, 1 hour, 24 hours, and 1 week in $37^{\circ}C$ distilled water before surface treatment, and then divided into five groups Group 1, grinding; Group 2, grinding and application of bonding agent, Group 3, grinding, etching with 37% phosphoric acid for 30sec, and application of bonding agent, Group 4, grinding, etching with 37% phosphoric acid for 30sec, silane treatment, and application of bonding agent ; Group 5, grinding, etching with 4% hydrofluoric acid for 30sec. silane treatment, and application of bonding agent. Indirect composite resin specimens ($Artglass^{\circledR}$, Heraeus Kulzer, Germany) were aged for 1 week in $37^{\circ}C$ distilled water and divided into seven groups Group 1 - Group 5, equal to Charisma specimens; Group 6, grinding, etching with 37% phosphoric acid for 60sec, silane treatment, and application of bonding agent; Group7, grinding, etching with 4% hydrofluoric acid for 60 sec, silane treatment, and application of bond-ing agent. The repair material($Charisma^{\circledR}$) was then added on the center of the surface (5 mm in diameter. 5 mm in height). The shear bond strength was tested and the data was analyzed using one-way ANOVA and the Student- Newman-Keuls test. The following conclusions were drawn. 1 The shear bond strength of $Charisma^{\circledR}$ specimens aged for 1 hour was significantly higher in Group 2 and Group 5 than in Group 1 (p<0.05), and that of $Charisma^{\circledR}$ specimens aged for 1 week was signifi-cantly higher in Group 3 and Group 5 than in Group 1 (p<0.05). No significant difference was found in the bond strength of specimens aged for 5 min and 24 hours. 2. In Group 2 of the $Charisma^{\circledR}$ specimens, there was significant difference between the bond strength of 24 hours and that of 1 week (p<0.05). 3. In Group 4 of the $Charisma^{\circledR}$ specimens, the shear bond strength of specimens aged for 24 hours was significantly higher than the others(p<0.05) 4. There was no significant difference between the shear bond strength of the $Artglass^{\circledR}$ specimens, 5. Most of the $Charisma^{\circledR}$ specimens showed cohesive fractures. Artglass^{\circledR}$ specimens that were etched with acid (phosphoric or hydrofluoric) for 30 sec showed more cohesive fractures.

• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.3
• /
• pp.33-41
• /
• 1991

Cermic has been widely used because of its excellent esthetics and strength. The recently introduced castable ceramic system is regarded as the more esthetic and biocompatible restorative material. The purpose of this study was to compare the shear bond strength of Dicer & G-Cera porcelain laminate veneer according to the type of cement and surface treatment and to observe the surface of bonding failure with SEM. Total forty disks(3.5mm $diam.\times2.0mm$ thickness) were prepared. Forty extracted human maxillary central incisor teeth were stored in saline solution. Ten teeth were bonded to Dicer specimen with Dicer ZPC cement and ten teeth were bonded with Dicer resin cement. Ten silicoated G-Cera specimen and ten non-silicoated G-Cera specimen were bonded to teeth with G-Cera resin cement. Bonded units were mounted in a plastic tube with hard stone and stored in a humidor at $37^{\circ}C$ for 24 hours. Shear bond strength was measured by Instron Universal Testing Machine (Model 1125) and all the specimen were observed with SEM(JEOL, JSM-T2000)and modes of failure were recorded. The obtained results were as follows: 1. The mean shear bond strength of Dicer bonded with Dicer resin cement was 11.62 MPa and that bonded with Dicor ZPC cement was 0.88 MPa : Shear bond strength of Dicer bonded with Dicer resin cement was significantly increased(P<0.05). 2. The mean shear bond strength of silicoated G-Cera was 13.10 MPa and that of non silicoated G-Cera was 10.93 MPa : Shear bond strength of silicoated G-Cera was not significantly increased (P>0.05). 3. Shear bond strength of Dicer and G-Cera porcelain laminate veneer was not significantly different (P>0.05). 4. In observation of bond failure with SEM, Dicer bonded with Dicer ZPC cement exhibited adhesive failure. Dicer bonded with Dicer resin cement and silicoated and non silicoated G-Cera exhibited cohesive failure.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.34 no.3
• /
• pp.398-407
• /
• 2007

This study was performed to evaluate possibility to reduce treatment time for child patient who have limited control activity during flowable composite resin restoration according to comparing microleakage and shear bond strength. Group I, II with Single $Bond^{TM}$, group III, IV with AQ Bond $Plus^{TM}$, group V, VI with Prompt L-$Pop^{TM}$, and group VII as control group without adhesive system. 12 premolars and 10 molars were assigned into each group. Restorative material was used the Filtek $Z350^{TM}$ flowable. The results were as follows; 1. The result of microleakage evaluation, in the group I, II with Single $Bond^{TM}$ showed low dye penetration score. Dye penetration between group I and group II were similar. 2. Results for shear bond strength at group I and group II showed values higher than other groups. (p<0.05) There were no statistical differences between group I and group II. (p>0.05) 3. There was no statistical differences among I and II, III and IV, V and VI groups. 4. Group VII showed significantly low shear bond strength than group I, II, V, VI(p<0.05). Group VII showed low value than group with III and IV, but no statistical significances. In conclusion, adhesive bonding resin was not affect significantly to microleakage and shear bond strength of flowable resin restoration. Therefore, to reduce the operation time, adhesive bonding resin and flowable composite resin can be cured at once. But contamination of saliva, location of cavities can affect to bond strength in clinical field.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.37 no.4
• /
• pp.422-428
• /
• 2010

Giomer is fluoride-releasing, resin-based dental materials that comprise PRG(pre-reacted glass ionomer) filler. The purpose of this study was to evaluate the shear bond strength of Giomer using self-etching primer systems to bovine dentin. Bovine incisors were mounted in self-curing orthodontic resin and the facial surfaces were wet ground on SIC paper to expose the dentin. Total 100 samples were made and divided randomly into 4 groups, Giomer group(I), Composite resin group(II) and Compomer group(III), Giomer and single bottle adhesive group(IV). The shear bond strengths of 25 samples per each group were measured using universal testing machine. And data were analyzed statistically with One-way ANOVA and Scheffe test. Giomer group(I) showed the significantly higher bond strength than Compomer group(III)(p<0.05). There was no significant difference between Giomer group(I) and Composite resin group(II)(p>0.05). And there is no significant difference between gourp(I) and group(IV). Based on the results of present study, the use of Giomer as an esthetic restorative material for primary teeth might be justified. It is considered that more study about the fluoride releasing ability is needed to evaluate the anticariogenic effect of giomer.

• Restorative Dentistry and Endodontics
• /
• v.21 no.1
• /
• pp.136-149
• /
• 1996

The effects of various All-Etching Agents (10% phosphoric acid, 10% maleic acid and 10 % citric acid) and 32 % phosphoric acid and varied etching time were evaluated by observing the morphology of the etched enamel surfaces using Scanning electron microscopy and by measuring the shear bond strength of a composite resin to human enamel. A total of 156 extracted premolar and molar teeth free of irregularities were employed in this study. Specimens for the observation of enamel morphology were divided into 12 groups of 3 teeth each, based on the type of etchant used and application time. After exposure to the etching agent specimens were washed air-dried and then glued to aluminum stubs and coated with a layer of gold for examination in the scanning electron microscope. Specimens for the evaluation of bond strength were divided into 12 groups of 10 teeth each also based on the type of etchant used and application time. After exposure to the etching agent the specimens were washed, air-dried and a thin layer of bonding agent was applied using a brush. Z 100 composite resin was light cured to the surface and stored at $37^{\circ}C$, 100% humidity for 7 days. An Instron Universal Testing Machine was used to apply a shearing force at $90^{\circ}$ angle from the enamel surface. It is concluded from this study that commercial All-etching agents can be used with a 15-second etching without adversely affecting retention of dental resin materials. At the same time, the acid concentration is probably a suitable compromise regarding the acid's function as a dentin demineralizing all-etch conditioning agent. The following results were obtained. 1. Specimens etched with 10 % citric acid showed a random superficial etching pattern which could not be related to prism morphology. 2. Specimens etched with 10 % and 32 % phosphoric acid and 10 % maleic acid showed a type I pattern in which core material was preferentially removed leaving the prism peripheries relatively intact or a type II pattern in which prism peripheries were preferentially removed. This delineation became more distinguished as etching time was increased. 3. All-Etching Agents and 32 % phosphoric acid showed a statistically significant higher shear bond strength at 15 seconds etching time.(p<0.05) 4. 10 % maleic acid and 32 % phosphoric acid exhibited a statistically significant higher shear bond strength than 10 % phosphoric and citric acid at 15 seconds etching time.(p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.36 no.3
• /
• pp.219-230
• /
• 2011

Objectives: The aim of this study was to evaluate the optical characteristics such as color and translucency changes before and after light curing, to quantify the CQ and to measure refractive indices of body and opaque shade of resin composites materials. Materials and Methods: Resin composites used in this study were A2 body and A2 opaque shade of Esthet-X, Filtek supreme, Gradia Direct, Clearfil Majesty and Beautifil II. Color and translucency changes before and after light curing were evaluated by colorimeter, the CQ was quantified by GC-MS and refractive index changes were measured by spectroscopic ellipsometer. Results: Translucency parameter (TP) was significantly increased after curing. The CQ content of body shades are higher than that of opaque shades in all resin composites. Refractive index increased after polymerization in all materials and significant difference in ${\Delta}$refractive index was found between body and opaque shade (significance level 0.05). Conclusions: For an accurate shade match, direct shade matching of resin composite should be performed by using the cured material.

• Restorative Dentistry and Endodontics
• /
• v.33 no.2
• /
• pp.115-124
• /
• 2008

The purpose of this study was to measure the polymerization shrinkage and hygroscopic expansion of resin-based temporary filling materials and to evaluate microleakage at the interface between the materials and cavity wall. Five resin-based temporary filing materials were investigated: Fermit (Vivadent), Quicks (Dentkist), Provifil (Promedica), Spacer (Vericom), Clip (Voco). Caviton (GC) was also included for comparison. Polymerization shrinkage of five resin-based temporary filling materials was measured using the bonded disc method. For the measurement of hygroscopic expansion, the discs of six cured temporary filling materials were immersed in saline and a LVDT displacement sensor was used to measure the expansion for 7 days. For estimating of microleakage, Class I cavities were prepared on 120 extracted human molars and randomly assigned to 6 groups of 20 each. The cavities in each group were filled with six temporary filling materials. All specimens were submitted to 1000 thermocycles, with temperature varying from $5^{\circ}C/55^{\circ}C$. Microleakage was determined using a dye penetration test. The results were as follows: 1. Fermit had significantly less polymerization shrinkage than the other resin-based temporary fill ing materials. Fermit (0.22%) < Spacer (0.38%) < Quicks (0.64%), Provifil (0.67%), Clip (0.67%) 2. Resin-based temporary filling materials showed 0.43-1.1% expansion in 7 days. 3. Fermit showed the greatest leakage, while Quicks exhibited the least leakage. 4. There are no correlation between polymerization shrinkage or hygroscopic expansion and microleakage of resin-based temporary filling materials.