• Journal of the Korea Concrete Institute
• /
• v.13 no.4
• /
• pp.397-405
• /
• 2001

In clod weather regions, a strong seasonal wind brings sea salts to the land. In addition to it, recently, the spreading amount of deicing salts has increased numerously for purpose of removing snow and ice. Thus the salts environment around concrete structures becomes so severe that various damages of concrete due to applied salts will be brought up. Much of countries such as America, Europe etc. is carried out study for effects of deicing salts on concrete. However, there are not test methods for deterioration of concrete subjected to both freezing-thawing and chloride in Korea. In this study, we carried out test for the compound deterioration subjected to both freezing-thawing and chloride attack, to investigate the effects of sodium chloride on the deterioration of concrete. The test was performed to investigate the effects of cement type, strength and air content on the scaling deterioration of concrete. As a result, the scaling deterioration was accelerated in the presence of salts. And the resistance to scaling was strongly influenced by the type of cement, the strength and air content of concrete.

• Journal of the Korean Society of Industry Convergence
• /
• v.25 no.2_2
• /
• pp.289-297
• /
• 2022

Deterioration in durability of structures due to the steel corrosion is difficult to determine whether or not corrosion is initiated and how much propagated, and moreover, repair and maintenance are not easy to deal with. Therefore, preventive treatments can be the best option to avoid the deterioration. Various methods for preventing corrosion of steel, such as electrochemical treatments, anti-corrosion agents and steel surface coatings, are being developed, but economic and environmental aspects make it difficult to apply them to in-situ field. Thus, the purpose of this study was to improve corrosion resistance by using CA-based clinker that are relatively simple and expected to be economically profitable Existing CA-based clinkers had problems such as flash setting and low strength development during the initial hydration process, but in order to solve this problem, CA clinker with low initial reactivity were used as binder in this study. The cement paste used in the experiments was replaced with CA₂ clinker for 0%, 10%, 20%, and 30% in OPC. And the mixture used in the chloride binding test for the extraction of water-soluble chloride was intermixed with Cl- 0.5%, 1%, 2%, and 3% by weight of binder content. To evaluate characteristic of hydration heat evolution, calorimetry analysis was performed and simultaneously chloride binding capacity and acid neutralization capacity were carried out. The identification of hydration products with curing ages was verified by X-ray diffraction analysis. The free chloride extraction test showed that the chlorine ion holding ability improved in order OC 10 > OC 30 > OC 20 > OC 0 and the pH drop resistance test showed that the resistance capability in pH 12 was OC 0 > OA 10 > OA 20 > OA 30. The XRD analyses showed that AFm phase, which can affect the ability to hold chlorine ions, tended to increase when CA₂ was mixed, and that in pH12 the content of calcium hydroxide (Ca(OH)₂), which indicates pH-low resistance, decreased as CA₂ was mixed

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.116-117
• /
• 2017

The most important factor when designing coastal and offshore concrete structures is durability. However, concrete in marine environment is exposed to physical and chemical deterioration of seawater, which might easily lead to low quality. The purpose of the present study is to understand advantages of adding ground solidificaton materials by comparatively analyze the seawater resistance of general concrete and environmental-friendly ground solidification materials.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.10a
• /
• pp.183-188
• /
• 1996

The durability of concrete structures decrease due to deterioration of concrete when they are constructed in marine or pollutional environments. In this study, the mortar specimens made from the five different types of cement were immersed in artificial seawater and four kinds chemical solution, and were measured the change of compressive strength and weight. The results show that the longer the immersed days are, the more the compressive strength reduction is. It has been remarked that the resistance of slag cement and ground granulated blast-furnace slag is excellent in chemical attack.

• Journal of the Korean Wood Science and Technology
• /
• v.49 no.5
• /
• pp.471-481
• /
• 2021

This study investigated the hygroscopicity and UV deterioration characteristics of 3 domestic and 4 imported woods using natural oil, stain, and varnish paints. In terms of hygroscopicity, it was found that the hygroscopicity of the painted wood was lower than that of the unpainted wood, and that as the number of coatings increased, the hygroscopicity decreased. In terms of anti-absorption, oil-based chemical paints showed higher resistance than water-based paints, and natural oils showed results comparable to oil-based paints. As for the UV deterioration, the amount of color change of the painted wood was lower than that of the unpainted wood, and there was no significant difference according to the number of times of painting. The amount of color change was found to be low in oil-based paints and hardwoods. Through this study, we confirmed effective moisture blocking and small color changes during painting using paints, and it is believed that wood can be protected from internal and external defects through selective and efficient painting based on data for excellent painting performance.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.04a
• /
• pp.704-709
• /
• 2000

This study is to test effects of sulfate attack on deterioration of cement mortar. Four tests have been carried out with four types of mortars mixed by ordinary portland cement and sulfate-resistant portland cement containing blast-furnace slag and fly-ash. It was immersed in sulfate solution for 7, 28, 91, and 180 days. from the test results, sulfate attack resistance of cement mortar was improved by admixtures (blast-furnace slag and fly-ash), sulfate-resistance portland cement mortar showed high resistance than ordinarily portland cement at compressive strength, and similar the resistance of sulfate attack with ordinarily portland cement mortar with admixtures.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.9 no.4
• /
• pp.177-186
• /
• 2005

The latest concrete structure has showed that the deterioration of durability has been increased by the damage from salt, carbonization, freezing & thawing and the others. Therefore, the measures for the concrete which has deteriorated durability have been taken. Among them, it has been often used that surface treatment which cuts off the deterioration factors of durability by protecting the surface of concrete. However, troubles such as fracture and rupture in the repair layer have been reported as time goes by due to the difference between the organic repair material like epoxy and concrete properties. Researchers have been developing the repair material which can cut off the deterioration factors of durability such as $CO_2$ gas, chloride ion and water by making the formation of concrete elaborate through the reaction with calcium ion when the surface improving agent is coated on the concrete. The main ingredient of that is inorganic substance which is the same as the concrete property. This study was evaluated the surface improving agent for permeability, watertightness, air-permeability, chemical resistance and elution resistance. As a result, it has been reported that the surface improving agent improves watertightness and air-permeability by penetration more than 10mm within concrete. Therefore, it is concluded that the surface improving agent developed in this research prevents deterioration of concrete durability when it is coated on the concrete structure.

• International Journal of Highway Engineering
• /
• v.16 no.1
• /
• pp.31-39
• /
• 2014

PURPOSES : Surface treatment material for pavement preventive maintenance should be inspected field applicability. This study(Part II) aimed to checkup coating characteristics and performance analysis using lab and field tests. The hydrophobic - low viscosity filling material for pavement preventive maintenance is presented in Part I, which is a series of companion study. METHODS : Relative comparison between general asphalt mixtures and surface treatment asphalt mixtures are analyzed and measured for the field application such as indirect tensile strength ratio(TSR), abrasion resistance, crack propagation resistance, temperature resistance, coating thickness, permeability resistance and skid resistance in terms of british pendulum number(BPN). RESULTS : It is found that TSR, crack propagation resistance and permeability resistance is increased as against uncoated asphalt specimen. Abrasion resistance and temperature resistance is secured from the initial coating thickness point of view, which is about 0.2~0.3mm. Skid resistance on the surface treatment pavement is satisfied with the BPN criteria of national highway because of exposed aggregate and crack sill induced pavement deterioration and damage cracks. CONCLUSIONS : The hydrophobic - low viscosity surface treatment material for pavement preventive maintenance is validated on field applicability evaluation based on quantitative analysis of coating thickness and performance analysis using lab and field tests.

• The Journal of the Institute of Internet, Broadcasting and Communication
• /
• v.14 no.4
• /
• pp.205-211
• /
• 2014

With a development of modern industry, demand for electric power is rapidly increasing and the capacity of power transfer is required to become bigger and bigger. At power station, the high-voltage power cable is used as the only method in order to transfer electric power. In this paper, we have analyzed the deterioration characteristics of 6.6kV power cable systems in operation. For the time duration of 2000 days, we have measured the cable in operation in order to extract the data for the deterioration characteristics. By analyzing the data by means of several steps of filtering processes, we could obtain the linear relations of insulation resistances as a function of time. Furthermore, we can verify that the progress characteristics in deterioration process of 6.6kV power cable systems follows the process of heat deterioration.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.2
• /
• pp.623-631
• /
• 2018

In this study, the degree of deterioration of concrete was investigated in the laboratory under conditions of carbonation and freeze-thaw cycling, which are the major causes of the deterioration of its performance. In this test, the carbonated concrete was subjected to combined freeze-thaw deterioration tests for up to 300 cycles, and its dynamic elastic modulus and compressive strength were measured. The evaluation of the effect of the water-binder ratio on normal concrete subjected to combined carbonization and freezing-thawing showed that its resistibility against such combined deterioration decreased more rapidly in the concrete with a water-binder ratio of 55 % compared with that having a water-binder ratio of 35 %. In the case where the concrete was blended with a mineral admixture consisting of fly ash and blast furnace slag at the same water-binder ratio, it showed an increase of its resistibility against combined deterioration.