• The korean journal of orthodontics
• /
• v.32 no.1 s.90
• /
• pp.51-57
• /
• 2002

The purpose of this study was to compare in vitro shear bonding strength with three different enamel surface preparations (1) 30% sulfated polyacrylic acid with 0.3M lithium sulfate (2) 40% sulfated polyacrylic acid with 0.3M lithium sulfate (3) 37% phosphoric acid. 105 extracted human premolar teeth were divided into each three groups of 35. Metal brackets were bonded to teeth in the three groups. The same self curing resin was used for all groups. A shearing force was applied to the teeth. After debonding, bases of bracket and enamel surfaces were examined under steroscopic microscope to determine the failure modes. Statistical analysis of the data was carried out with one way ANOVA and Student t- test. The results were as follows. 1. Shear bond strength values for the 30% polyacrylic acid and 40% polyacrylic acid group were approximately two thirds of the phosphoric acid group. It maintains clinically acceptable but not enough bond strength. 2. There was no statistically significant difference in shear bond strengths between 30% and 40% polyacrylic acid group. 3. The failure modes of brackets had some differences. In polyacrylic acid groups, the percentage of adhesive/enamel failure was higher than that of adhesive/ bracket interface failure. On the contrary in phosphoric acid groups, the results were reversed. Further study of bond strength could be required. If polyacrylic acid enamel conditioning is used clinically.

• Restorative Dentistry and Endodontics
• /
• v.25 no.1
• /
• pp.46-55
• /
• 2000

During bonding procedure of composite resin, the prepared cavity can be contaminated by saliva. In this study, marginal microleakage and shear bond strength of a composite resin to primed enamel and dentin treated with artificial saliva(Taliva$^{(R)}$) were evaluated. For the marginal microleakage test, Class V cavities were prepared in the buccal surfaces of fifty molars. The samples were randomly assigned into 5 groups with 10 samples in each group. Control group was applied with a bonding system (Scotchbond$^{TM}$ Multi-Purpose plus) according to manufacture's directions without saliva contamination. Experimental groups were divided into 4 groups and contaminated with artificial saliva for 30 seconds after priming: Experimental 1 group ; artificial saliva was dried with compressed air only, Experimental 2 group ; artificial saliva was rinsed and dried. Experimental 3 group ; cavities were etched with 35% phosphoric acid for 15 seconds after rinsing and drying artificial saliva. Experimental 4 group ; cavities were etched with 35% phosphoric acid for 15 seconds and primer was reapplied after rinsing and drying artificial saliva. All the cavities were applied a bonding agent and filled with a composite resin (Z-100$^{TM}$). Specimens were immersed in 0.5% basic fuschin dye for 24 hours and embedded in transparent acrylic resin and sectioned buccolingually with diamond wheel saw. Four sections were obtained from one specimen. Degree of marginal leakage was scored under stereomicroscope and their scores were averaged from four sections. The data were analyzed by Kruscal-Wallis test and Fisher's LSD. For the shear bond strength test, the buccal or occlusal surfaces of one hundred molar teeth were ground to expose enamel(n=50) or dentin(n=50) using diamond wheel saw and its surface was smoothed with Lapping and Polishing Machine(South Bay Technology Co., U.S.A.). Samples were divided into 5 groups. Treatment of saliva-contaminated enamel and dentin surfaces was same as the marginal microleakage test and composite resin was bonded via a gelatin capsule. All specimens were stored in distilled water for 48 hours. The shear bond strengths were measured by universal testing machine (AGS-1000 4D, Shimaduzu Co., Japan) with a crosshead speed of 5 mm/minute. Failure mode of fracture sites was examined under stereomicroscope. The data were analyzed by ANOVA and Tukey's studentized range test. The results of this study were as follows : 1. Enamel marginal microleakage showed no significant difference among groups. 2. Dentinal marginal microleakages of control, experimental 2 and 4 groups were lower than those of experimental 1 and 3 groups (p<0.05). 3. The shear bond strength to enamel was the highest value in control group (20.03${\pm}$4.47MPa) and the lowest value in experimental 1 group (13.28${\pm}$6.52MPa). There were significant differences between experimental 1 group and other groups (p<0.05). 4. The shear bond strength to dentin was higher in control group (17.87${\pm}$4.02MPa) and experimental 4 group (16.38${\pm}$3.23MPa) than in other groups, its value was low in experimental 1 group (3.95${\pm}$2.51 MPa) and experimental 2 group (6.72${\pm}$2.26MPa)(p<0.05). 5. Failure mode of fractured site on the enamel showed mostly adhesive failures in experimental 1 and 3 groups. 6. Failure mode of fractured site on the dentin did not show adhesive failures in control group, but showed mostly adhesive failure in experimental groups. As a summary of above results, if the primed tooth surface was contaminated with artificial saliva, primer should be reapplied after re-etching it.

• Korean Journal of Heritage: History & Science
• /
• v.56 no.3
• /
• pp.158-171
• /
• 2023

Pottery filled with organic materials was excavated from the G-2 building site of Yongjangseong Fortress, Jingo, a relic of the Goryeo Dynasty. In this study, the characteristics of organic material were confirmed by a scientific analysis of organic material in pottery found at the palace in Yongjangseong, Jindo. In addition, it was intended to review the analysis method to identify the natural resin and to secure characteristic components(biomarkers) for each natural resin and use them as basic data in the future. The organic materials in the pottery were analyzed using attenuated total reflectance Fourier-transformed infrared spectroscopy(ATR-FTIR) and gas chromatography mass spectrometry(GC-MS). The infrared spectral characteristics were estimated to be natural resin, and biomarkers of organic materials were identified as sesquiterpene-based compounds(C₁₅H₂₄, MW 204) and derivatives. The lacquer(T.vemicifluum) is composed mainly of alkenes, alkanes, and catechol. Pine resin(P.densiflora), on the other hand, is primarily composed of diterpenoid(abietic acid, pimaric acid) and Whangchil(yellow lacquer) is identified to have sesquiterpenes(such as selinene, muurolene, calamenene) as its main components. So, the organic material in the pottery can be identified as Whangchil by comparing their compounds with modern resin materials from Dendropanax. morbifera that correspond with the results. Whangchil, which is exuded from the Dendropanax. morbifera, has been used as a natural coating materials since ancient times, and it has been confirmed that the characteristic components are well preserved even 700 years later. It can be assumed that the interior Whangchil was stored not for use as a coating, but rather for ritual purposes when the building was constructed, because the pottery was found near the cornerstone. Furthermore, based on simplified sample preparation using pyrolysis-gas chromatography mass spectrometry(Py-GC-MS), the thermal decomposition products were found to be similar to the characteristic components, suggesting that this method can be applied to the identification of natural resins used in historic artifacts.

• Applied Chemistry for Engineering
• /
• v.4 no.3
• /
• pp.627-636
• /
• 1993

Anionic acrylic resin utilizing macromer(TBMA-g-MMA) copolymer was synthesized by preparing (TBMA) macromer using anionic living polymerization, followed by graft copolymerization with MMA macromer. To control the anionic site content in graft copolymer, the relative composition((TBMA) macromer/MMA ratio) of the graft copolymer was controlled at 7/3, 10/90, 15/85, 20/80, 30/70, 40/60, 50/50 in weight content. In the course of anionic living polymerization of(TBMA) macromer, broad molecular weight distribution (1.4~1.5) was obtained by using n-butyllithium-diphenyethylene initiatior system at $-78^{\circ}C$. To introduce the double bond at the end of chain in termination step, methacryloyl chloride was reacted after insertion of benzaldehyde as capping material. Moreover, TBMA parts in graft copolymer were hydrolyzed in the presence of p-toluenesulfonic acid catalyst, and neutralization of graft copolymer with triethylamine was granted acrylic resin to anionic site. Molecular weight and molecular weight distribution of(TBMA) macromer were determined by GPC, and the hydrolysis of TBMA with neutralization of acrylic resin were determined by IR and NMR. From water dispersion and stability point of view, stable dispersion state appeared at low molecular weight(TBMA) macromer with a small TBMA content as a result of scrutiny about the relation to TBMA content and branch length for(TBMA) macromer molecular weight in graft copolymer.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.41 no.2
• /
• pp.125-133
• /
• 2014

The purpose of this study was to investigate the effect of various surface treatment methods on the shear bond strength of orthodontic brackets in vitro. Ninety six specimens, 6 mm in diameter and 5 mm in height, were made with composite resin ($Filtek^{TM}$ Z350 XT, 3M ESPE, USA) and treated with an aging procedure. After aging, the specimens were randomly separated in six groups: (1) control with no surface treatment, (2) 37% phosphoric acid gel, (3) 4% hydrofluoric acid gel, (4) sodium bicarbonate particle abrasion, (5) diamond bur, and (6) 1 W carbon dioxide laser for 5s. The metal brackets were bonded to composite surfaces by means of an orthodontic adhesive (Transbond XT, 3M Unitek, USA). Shear bond strength values were evaluated with a universal testing machine (R&B Inc., Korea). Analysis of variance showed a significant difference between the groups. Group 5 had the highest mean shear bond strength (11.9 MPa), followed by group 6 (11.1 MPa). Among the experimental groups, group 2 resulted in the weakest mean shear bond strength (5.22 MPa). The results of this study suggest that the repair shear bond strength of the aged composite resin was acceptable by surface treatment with a carbon dioxide laser.

• Restorative Dentistry and Endodontics
• /
• v.24 no.1
• /
• pp.240-250
• /
• 1999

The purpose of this study was to evaluate the effect of different etching time on the shear bond strength and adaptibility of composite to enamel and dentin when used one-bottle adhesive Prime & Bond$^{TM}$ 2.0. The proximal and occlusal surfaces of 88 extracted human molars were ground to expose enamel(n=44) and dentin (=44) using diamond wheel saw. Teeth were randomly assigned to four test groups(n=11) and received the following treatments : Control group were conditioned with 36% phosphoric acid for 20 sec. according to the manufacturer's directions. Experimental 10 sec. group, 30 sec. group and 60 sec. group were conditioned with 36% phosphoric acid for 10 sec., 30 sec. and 60 sec., respectively. Teeth were rinsed and dried for 2 sec. Prime & Bond$^{TM}$ 2.0 were applied according to the manufacturer's directions and Spectrum$^{TM}$ TPH composite resins were bonded to enamel and dentin surfaces. All specimens were stored in distilled water for 24 hours. Eighty specimens were sheared in a Universal Testing Machine with a crosshead speed of 5mm/minute. One way ANOVA and LSD test were used for statistical analysis of the data. Failure modes of all specimens after shear bond strength test were examined and listed. Also, representive postfracture modes and eight specimens were examined under scanning electron microscope. The results of this study were as follows: 1. The shear bond strength to enamel was the highest value in 30 sec. group (20.68${\pm}$8.54MPa) and the lowest value in 10 sec. group (14.92${\pm}$6.07MPa), so there was significant difference of shear bond strength between two groups (p<0.05). But there was no significant difference among other groups (p>0.05). With longer etching time to enamel from 10 sec. to 30 sec., higher the shear bond strength was obtained, but the shear bond strength was decreased at 60 sec. etching time. 2. The shear bond strength to dentin was the highest value in control group (13.08${\pm}$6.25MPa) and the lowest value in 60 sec. group (9.47${\pm}$3.35MPa), but there was no significant difference among the all groups (p>0.05). The eching time over 20 sec. decreased the shear bond strength to dentin. 3. In SEM observation, the enamel and resin interfaces were showed close adaptation with no relation to etching time of enamel. And the dentin and resin interfaces were showed close adaptation at 20 sec. and 30 sec. etching time, but showed some gaps at 10 sec. and 60 sec. etching time. Accordingly, these results indicated that a appropriate etching time in Prime & Bond$^{TM}$ 2.0 was required to be 30 sec. in enamel and 20 sec. in dentin for the high shear bond strength and good adaptation between the composite resin and tooth substance.

• Journal of the Korean Wood Science and Technology
• /
• v.33 no.4 s.132
• /
• pp.53-59
• /
• 2005

This study was performed to understand the changes in wood extractives, mainly acetone extracts, in pine woods (Pinus densiflora and Pinus rigida) treated by three blue stain fungi (BSF) such as native BSF in Korea, Leptographium sp., screened Albino strain (BSFcs-1) and commercial Cartapip. BSF treatment has significantly reduced acetone extracts, 25.1~30.4% decreasing in red pine and 22.9~28.1% in pitch pine. The decreasing rates of fatty acids and sterols in woods were 10.6~11.2% by 3 week aging and 36~41.1% by BSF treatments, respectively. Triglycerides were also decreased to 5.68~9.4% by 3 week aging and 38.5~40.0% by BSF treatments, respectively. Resin acids were 6.1~11.3% by 3 week aging and 36~41.5% by BSF treatments, respectively. There were not so significant differences in extracts among native BSF and Albino-type strains (Albino strain, BSFcs-1, and commercial Cartapip). It was known that the Albino strain (BSFcs-1) screened for the biocontrol of wood discoloration has effectively decreased acetone extractives in pine woods.

• Restorative Dentistry and Endodontics
• /
• v.21 no.1
• /
• pp.242-253
• /
• 1996

Penetration degree of several dyes into dentinal tubules in vivo was compared with in vitro, and experimental sensitivity of those dyes was investigated in 64 canines of 16 cats. Dentin 1mm below cusp tip was exposed by cross-sectioning with diamond disc. Pulp of 32 canines were extirpated through cervical cavities. In the presence of smear layer or after add-etching with 37% phosphoric acid to the exposed dentin surface, acrylic collar and resin cap was attached to keep dyes. 52 mmol/$\ell$ Evans' blue, 2% Methylene blue, 10 % Silver nitrate and 5% Fluorescene were then applicated on each 4 canines respectively for 30 minutes. After rinsing, the canines were ground-sectioned longitudinally and linear dye penetration was measured under microscope. The results obtained were as follows ; 1. Evans' blue and Methylene blue penetrated significantly(P<0.05) more in vitro than in vivo only in the cases that exposed dentin surfaces were not etched with acid. 2. Silver nitrate penetrated significantly(P<0.05) more in vitro than in vivo in both cases that exposed dentin surfaces remained intact and were etched with acid. 3. The penetration degree of Fluorescene did not show statistical significance between in vivo and in vitro or in acid-etched and in not acid-etched cases.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.4
• /
• pp.457-463
• /
• 2013

PURPOSE. The purpose of this study was to compare the effect of a diode laser and traditional irrigants on the bond strength of self-adhesive cement. MATERIALS AND METHODS. Fifty-five incisors extracted due to periodontal problems were used. All teeth were instrumented using a set of rotary root canal instruments. The post spaces were enlarged for a No.14 (diameter, 1.4 mm) Snowlight (Abrasive technology, OH, USA) glass fiber reinforced composite post with matching drill. The teeth were randomly divided into 5 experimental groups of 11 teeth each. The post spaces were treated with the followings: Group 1: 5 mL 0.9% physiological saline; Group 2: 5 mL 5.25% sodium hypochlorite; Group 3: 5 mL 17% ethylene diamine tetra acetic acid (EDTA), Group 4: 37% orthophosphoric acid and Group 5: Photodynamic diode laser irradiation for 1 minute after application of light-active dye solution. Snowlight posts were luted with self-adhesive resin cement. Each root was sectioned perpendicular to its long axis to create 1 mm thick specimens. The push-out bond strength test method was used to measure bond strength. One tooth from each group was processed for scanning electron microscopic analysis. RESULTS. Bond strength values were as follow: Group 1 = 4.15 MPa; Group 2 = 3.00 MPa; Group 3 = 4.45 MPa; Group 4 = 6.96 MPa; and Group 5 = 8.93 MPa. These values were analysed using one-way ANOVA and Tukey honestly significant difference test (P<.05). Significantly higher bond strength values were obtained with the diode laser and orthophosphoric acid (P<.05). There were no differences found between the other groups (P> .05). CONCLUSION. Orthophosphoric acid and EDTA were more effective methods for removing the smear layer than the diode laser. However, the diode laser and orthophosphoric acid were more effective at the cement dentin interface than the EDTA, Therefore, modifying the smear layer may be more effective when a self-adhesive system is used.

• Journal of Korean society of Dental Hygiene
• /
• v.10 no.5
• /
• pp.947-953
• /
• 2010

Objectives : The purpose of this investigation was to evaluate the remineralization and acid resistance in fluoride varnish by Micro-computed tomography (micro CT). Methods : Specimens of bovine teeth enamel were embedded in resin, polished and randomly divided into 3 groups (a control group, a NaF solution group, a fluoride varnish group). Each group has 3 specimens that was standardized according to Vickers hardness number (VHN). Specimens were immersed in demineralization solution for 72 hours. The control group had no treatment, the NaF solution group was treated by a 5% NaF solution for 4 minutes, and the fluoride varnish group was treated by a fluoride varnish for one hour. All specimens were subjected to a chemical pH cycling method for 14 days. After a chemical pH cycling method, the density were measured using micro CT. Then, specimens were immersed in each demineralization solution for 72 hours. After demineralization processed, the density were measured using micro CT. Results : 1. The density was significantly higher in the fluoride varnish and 5% NaF solution group than that of the control group after 14 days cycling (p<0.05). And the density value of the fluoride varnish group was higher than that of the 5% NaF solution, with no significant difference. 2. The differences of density after acid resistance treatment were statistically significant among 3 groups(p<0.05). Conclusions : It is suggested that fluoride varnish showed the remineralizing effect and acid resistance effect on the enamel, and micro CT could be used to evaluate the change of enamel lesion.