• 한국표면공학회지
• /
• 제34권5호
• /
• pp.421-428
• /
• 2001

New WC-CrN superlattice film was deposited on Si substrate (500$\mu\textrm{m}$) using cathodic arc ion plating system. The microstructure and mechanical properties of the film depend on the superlattice period (λ). In the X-ray diffraction analysis (XRD), preferred orientation of microstructure was changed according to various superlattice periods(λ). During the Transmission Electron Microscope analysis (TEM), microstructure and superlattice period (λ) of the WC - CrN superlattice film was confirmed. Hardness and adhesion of the deposited film was evaluated by nanoindentation test and scratch test, respectively. As a result of nanoindentation test, the hardness of WC - CrN superlattice film was gained about 40GPa at superlattice period (λ) with 7nm. Also residual stress with various superlattice period (λ) was measured on Si wafer (100$\mu\textrm{m}$) by conventional beam-bending technique. The residual stress of the film was reduced to a value of 0.2 GPa by introducing Ti - WC buffer layers periodically with a thickness ratio ($t_{buffer}$/$t_{buffer+superlattice}$ ). To the end, for the evaluation of oxidation resistance at the elevated temperature, CrN single layer and WC - CrN superlattice films with various superlattice periods on SKD61 substrate was measured and compared with the oxidation resistance.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2000년도 추계학술대회 논문집
• /
• pp.147-153
• /
• 2000

The fatigue crack propagation behavior of the SA516/70 steel which is used for pressure vessels was examined experimentally at room temperature, $150^{\circ}C$, $250^{\circ}C$ and $370^{\circ}C$ with stress ratio of R=0.1 and 0.3. The fatigue crack propagation rate da/dN related with the stress intensity factor range $\Omega\textrm{K}$ was influenced by the stress ratio within the stable growth of fatigue crack(Region II) with an increase in $\Omega\textrm{K}$. The resistance to the fatigue crack growth at high temperature is higher in comparison with that at room temperature, and the resistance attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and high temperatures are mainly explained by the crack closure and oxide-induced by high temperature.

• 한국해양공학회지
• /
• 제15권2호
• /
• pp.105-110
• /
• 2001

The fatigue crack propagation behavior of the SA516/70 steel which is used for pressure vessels was examined experimentally at room temperature, 150$^{\circ}C $, 250$^{\circ}C $ and 370$^{\circ}C $ with stress ratio of R=0.1 and 0.3. The fatigue crack propagation rate da/dN related with the stress intensity factor range $\Delta K$ was influenced by the stress ratio within the stable growth of fatigue crack(Region II) with an increase in $\Delta K$. The resistance to the fatigue crack growth at high temperature is higher in comparison with that at room temperature, and the resistance attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and high temperature are mainly explained by the crack closure and oxide-induced by high temperature.

• Structural Engineering and Mechanics
• /
• 제87권2호
• /
• pp.151-164
• /
• 2023

The latest earthquake's costly repairs and economic disruption were brought on by excessive residual drift. Self-centering systems are one of the most efficient ways in the current generation of seismic resistance system to get rid of and reduce residual drift. The mechanics and behavior of the self-centering system in response to seismic forces were impacted by a number of important factors. The amount of post-tensioning (PT) force, which is often employed for the standing posture after an earthquake, is the first important component. The energy dissipater element is another one that has a significant impact on how the self-centering system behaves. Using the damper as a replaceable and affordable tool and fuse in self-centering frames has been recommended to boost energy absorption and dampening of structural systems during earthquakes. In this research, the self-centering steel moment frame connections are equipped with cushion flexural dampers (CFDs) as an energy dissipator system to increase energy absorption, post-yielding stiffness, and ease replacement after an earthquake. Also, it has been carefully considered how to reduce permanent deformations in the self-centering steel moment frames exposed to seismic loads while maintaining adequate stiffness, strength, and ductility. After confirming the FE model's findings with an earlier experimental PT connection, the behavior of the self-centering connection using CFD has been surveyed in this study. The FE modeling takes into account strands preloading as well as geometric and material nonlinearities. In addition to contact and sliding phenomena, gap opening and closing actions are included in the models. According to the findings, self-centering moment-resisting frames (SF-MRF) combined with CFD enhance post-yielding stiffness and energy absorption with the least amount of permeant deformation in a certain CFD thickness. The obtained findings demonstrate that the effective energy dissipation ratio (β), is increased to 0.25% while also lowering the residual drift to less than 0.5%. Also, this enhancement in the self-centering connection with CFD's seismic performance was attained with a respectable moment capacity to beam plastic moment capacity ratio.

• 한국해양공학회지
• /
• 제18권5호
• /
• pp.43-49
• /
• 2004

The lightness of components required in the automobile and machine industry necessitates the use of high strength components. In particular, the fatigue failure phenomena, which occurs when using metal, increases the danger to human life and property. Therefore, antifatigue failure technology is an integral part of current industries. Currently, the shot peening is used for removing the defect from the surface of steel, while improving the fatigue strength on surface. Therefore, in this paper, the effect of compressive residual stress of spring steel(JISG SUP-9) by shot-peening on fatigue crack growth characteristics in a stress ratio(R=0.1, R=0.3, R=0.6) was investigated, giving consideration to fracture mechanics. By using the methods mentioned above, following conclusions are drawn: (1) The fatigue crack growth rate(da/dN) of the shot-peening material was lower than that of the un-peening material and in stage I, ΔKth, the threshold stress intensity factor of the shot-peen processed material is high in critical parts, unlike the un-peening material. Also m, fatigue crack growth exponent and number of cycle of the shot-peening material, was higher than that of the un-peening material, as concluded from effect of da/dN. (2) Fatigue life shows more improvement in the shot-peening material than in the un-peening material, and the compressive residual stress of surface on the shot-peen processed operate resistance of fatigue crack propagation.

• 한국전산구조공학회논문집
• /
• 제25권3호
• /
• pp.219-226
• /
• 2012

기둥은 건물에서 하중을 지지하는 중요한 구성요소이므로 기둥의 손상 또는 파괴는 건물의 연쇄붕괴의 원인이 된다. 특히 폭발하중에 의한 기둥의 거동평가는 연쇄붕괴 방지에 있어 중요한 요소이다. 본 논문에서는 축하중을 받고 있는 기둥이 폭발하중을 받을 때의 거동과 폭발 저항성능을 평가하였다. 이를 위해 동일단면적과 비슷한 철근비를 가지는 기둥에서 주 철근의 개수를 달리하여 각 변수에 따른 폭발하중에 대한 폭발 저항성능을 평가하였다. 또한, 동일한 성능을 지니는 기둥에서 단면비를 달리하여 기둥의 폭발 저항성능을 비교하였다. 해석결과, 폭발 직후 충격량에 대한 수직 변형률은 철근의 개수 및 단면비에 영향을 받지 않는 것으로 나타났다. 그러나 수평변형의 경우 폭발압력을 받는 면의 철근 개수가 증가함에 따라 기둥의 저항성능이 증가하는 것으로 나타났다. 또한, 기둥 단면의 단면 2차모멘트가 클수록 폭발하중에 대한 저항 성능 및 복원력이 더 큰 것을 확인하였다.

• International Journal of Concrete Structures and Materials
• /
• 제18권2E호
• /
• pp.103-109
• /
• 2006

Spalling is defined as damages to concrete exposed to high temperature during fire, causing cracks and localized bursting of small pieces of concrete. As the concrete strength increases, the degree of damage caused by spalling becomes more serious due to impaired permeability. It is reported that polypropylene(PP) fiber has an important role in protecting concrete from spalling, and the optimum dosage of PP fiber is 0.2%. However, this study was conducted on non-reinforced concrete specimens. The high-temperature behavior of high-strength reinforced concrete columns with various concrete strength and various quantity of PP fibers is investigated in this study. The results revealed that the ratio of unstressed residual strength of columns increased as the concrete strength increased and as the quantity of PP fiber increased from 0% to 0.2%. However, the effect of PP fiber quantity on residual strength of column was barely above 0.2%.

• 한국표면공학회지
• /
• 제39권5호
• /
• pp.199-205
• /
• 2006

Titanium nitride (TiN) coatings were produced on AISI 420 stainless steel by DC magnetron sputtering of a Ti target changing the processing variables, such as the flow rate of $N_2/Ar$, substrate temperature and the existence of Ti interlayer between TiN coatings and substrates. The hardness and residual stress in the films were investigated using nanoindentation and a laser scanning device, respectively. The stoichiometry and surface morphology were investigated using X-Ray Diffraction and SEM. The corrosion property of the films was also studied using a polarization method in NaCl (0.9%) solution. Mechanical properties including hardness and residual stress were related to the ratio of $N_2/Ar$ flow rate. The corrosion resistance also was related to the processing variables.

• Journal of Welding and Joining
• /
• 제5권3호
• /
• pp.53-61
• /
• 1987

Post weld heat treatment(PWHT) is usually carried out to remove the residual stress and to improve the microstructure and mechanical properties of welded joints. By the way, welding structure transformed owing to PWHT and reheating for repair loads the random cycles fatigue as offshore welding structure of constant low cycle fatigue as pressure vessel, and then, pre-existing flaws or cracks exist in a structural component and those cracks grow under cyclic loading. Therefore, the effects of PWHT and stress ratio on fatigue crack growth behaviors were studied on the three regions such as HAZ, sub-critical HAZ and deposit metal of welded joints in SM53 steel. Fatigue crack growth behavior of as-weld depended on microstructure and fatigue crack growth rate of HAZ was the lowest at eac region, but after PWHT it was somewhat higher than that of as-wel. In case of applying the stress($10kg/mm^2$) during PWHT, fatigue crack growth resistance tended to increase in the overall range of .DELTA.K.

• 한국구조물진단유지관리공학회 논문집
• /
• 제10권2호
• /
• pp.83-90
• /
• 2006

고강도 콘크리트는 구조적인 장점에도 불구하고 화재 시 폭렬과 함께 취성적인 파괴를 나타내는 단점으로 인하여 내화설계 시 주의하여 사용하여야 한다. 고강도 콘크리트의 폭렬제어를 위하여 폴리프로필렌 섬유(PP섬유)의 혼입이 가장 효율적인 것으로 여러 연구결과를 통하여 보고 되었으나, 이들은 대부분 콘크리트 공시체를 대상으로 한 내화실험의 결과로서 최적의 PP섬유 혼입량에 대한 부재수준의 연구는 매우 부족한 실정이다. 본 연구에서는 고강도 콘크리트 기둥의 내화설계를 위한 최적의 PP섬유 혼입량을 제시하기 위하여 콘크리트 강도와 PP섬유의 혼입량을 변수로 하는 기둥부재의 내화실험 및 잔존강도 실험을 수행하였으며, 실험결과 콘크리트 강도가 증가 할수록 기둥 실험체의 잔존 축강도비는 증가하였으며, PP섬유 혼입량을 0%에서 0.2%까지 증가 시킬수록 기둥의 잔존 축강도비가 증가하는 것으로 나타났다. 따라서 최적의 PP섬유 혼입량으로서 0.2%가 적절할 것으로 판단된다.