• Korean Journal of Metals and Materials
• /
• v.49 no.1
• /
• pp.40-45
• /
• 2011

Using the spark plasma sintering process (SPS process), the WC-6wt.%Co hard materials were densified using an ultra fine WC-Co powder. The WC-Co was almost completely dense with a relative density of up to 100% after the simultaneous application of a pressure of 60 MPa and the DC pulse current for 3 min without any significant change in the grain size. The average grain size of WC that was produced through this experiment was about $0.2{\sim}0.8{\mu}m$. The hardness and fracture toughness were about $1816kg/mm^2$ and $15.1MPa{\cdot}m^{1/2}$, respectively, for 60 MPa at $1200^{\circ}C$.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2000.11a
• /
• pp.362-365
• /
• 2000

Rapid Prototyping(RP) techniques have revolutionized traditional manufacturing methods. These techniques allow the user to fabricate a part directly from a conceptual model before investing in production tooling and help develop new models with significant short time. This paper suggests to new process to manufacture large size hollow shape parts for prototype-car using Rapid Prototyping technology and Vacuum Molding with the reduction of delivery time. In addition, This paper introduces the dividing and combining method to make large size RP master model in spite of the limit of the build chamber dimensions of commercialized RP system and post-processing method to achieve sufficient surface quality.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2000.11a
• /
• pp.330-333
• /
• 2000

Dimensional accuracy and surface quality are very important in rapid prototyping especially when the models are used for the production of tools. This paper presents the development of benchmarking part to investigate dimensional accuracy and surface finish. A new test part is designed to perform benchmarking of major rapid prototyping processes such as selective laser sintering, laminated object manufacturing, stereolithography apparatus, and fused deposition modeling. The test part design includes basic manufacturing features such as holes, walls, squares, cylinder and etc. In addition, the small features are included in order to evaluate the fine details that can be manufactured by a specific RP process. The CMM program that automatically measures different features in the test part is also developed. The evaluation of accuracy as well as surface roughness are discussed for major rapid prototyping processes.

• Journal of the KSME
• /
• v.50 no.1
• /
• pp.55-57
• /
• 2010

3차원 쾌속조형(RP: Rapid Prototyping) 기술의 일종인 Selective Laser Sintering(SLS)을 기능성 경사구조(FGM: Functionally graded Materials)의 제작에 응용하기 위하여 마이크로/나노 복합체의 제작 공정을 최적화하고 실험으로 1차원의 FGM 제작을 수행하였다.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2007.06a
• /
• pp.721-722
• /
• 2007

• Journal of Powder Materials
• /
• v.24 no.2
• /
• pp.115-121
• /
• 2017

In this work, p-type Bi-Sb-Te alloys powders are prepared using gas atomization, a mass production powder preparation method involving rapid solidification. To study the effect of the sintering temperature on the microstructure and thermoelectric properties, gas-atomized powders are consolidated at different temperatures (623, 703, and 743 K) using spark plasma sintering. The crystal structures of the gas-atomized powders and sintered bulks are identified using an X-ray diffraction technique. Texture analysis by electron backscatter diffraction reveals that the grains are randomly oriented in the entire matrix, and no preferred orientation in any unique direction is observed. The hardness values decrease with increasing sintering temperature owing to a decrease in grain size. The conductivity increases gradually with increasing sintering temperature, whereas the Seebeck coefficient decreases owing to increases in the carrier mobility with grain size. The lowest thermal conductivity is obtained for the bulk sintered at a low temperature (603 K), mainly because of its fine-grained microstructure. A peak ZT of 1.06 is achieved for the sample sintered at 703 K owing to its moderate electrical conductivity and sustainable thermal conductivity.

• Korean Journal of Metals and Materials
• /
• v.49 no.11
• /
• pp.845-852
• /
• 2011

The Spark Plasma Sintering(SPS) method offers a means of fabricating a sintered-body having high density without grain growth through short sintering time and a one-step process. A titanium compact having high density and purity was fabricated by the SPS process. It can be used to fabricate a Ti sputtering target with controlled parameters such as sintering temperature, heating rate, and pressure to establish the optimized processing conditions. The compact/target(?) has a diameter of ${\Phi}150{\times}6.35mm$. The density, purity, phase transformation, and microstructure of the Ti compact were analyzed by Archimedes, ICP, XRD and FE-SEM. A Ti thin-film fabricated on a $Si/SiO_2$ substrate by a sputtering device (SRN-100) was analyzed by XRD, TEM, and SIMS. Density and grain size were up to 99% and below $40{\mu}m$, respectively. The specific resistivity of the optimized Ti target was $8.63{\times}10^{-6}{\Omega}{\cdot}cm$.

• Journal of Powder Materials
• /
• v.11 no.6 s.47
• /
• pp.528-534
• /
• 2004

Using the nano Fe powders having 50 nm in diameter, Fe compact bodies were fabricated by injec-tion molding process. The relationship between microstructure and material properties depending on the volume ratio of powder/binder and sintering temperature were characterized by SEM, TEM techniques. In the compact body with the volume percentage ratio of 45(Fe powder) : 55(binder), which was sintered at $700^{\circ}C,$ the relative density was about $97{\%},$ and the values of volume shrinkage and hardness were about $66.3{\%}$ and 242.0 Hv, respec-tively. Using the composition of 50(Fe powder) : 50(binder) and sintered at $700^{\circ}C,$ the values of relative density, volume shrinkage and hardness of Fe sintered bodies were $73.3{\%},\;47.6{\%}$ and 152.8 Hv, respectively. They showed brittle fracture mode due to the porous and fine microstructure.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.04a
• /
• pp.552-556
• /
• 1997

The Direct Metal Prototyping(DMP), one of the rapid prototyping technologies, allows the manufacturing of three-dimensional metallic parts using metal powders directly from the CAD data. Laser power and scanning speed are the most important variables of the process. The objective of this study is to obtain the design data for laser power and scanning speed to bond metal powders effectively using the finite element method. To obtain the design values, a numerical analysis considering two-dimensional heat transfer during the sintering of metal powder layers of the process was performed. The laser beam has been modeled to have directionality in its heat flux distribution, i. e., in the scanning direction a Gaussian beam mode distribution has been assumed and in the thickness direction a square beam mode distribution. The three-dimensional irregular distribution of metal powders of the powder layer is idealized as two-dimensional distribution in which metal powders are located regularly and periodically on the plate. In this study the design values of laser power vs scanning speed have been obtained. Temperature distribution and temperature variation of the powder layers with respect to time have been predicted. The commputed dsign data will be useful in determining the initial conditions of the process.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.50-53
• /
• 2003

Most companies use technologies such as stereolithography, selective laser sintering, and fused deposition modeling to make parts for such small consumer products as telephones, heads, and shoes. The largest part that the existing RP systems can make is only 600 mm in length. Because most RP systems build parts by depositing, solidifying, or sintering material point-by-point, making larger objects takes a long time. and in many cases, large objects won't fit the build size. A new effective thick-layered RP process. Transfer type Variable Lamination Manufacturing using expandable polystyrene foam (VLM-ST) has been developed with thick layers and sloped surfaces. In this paper, a scaledown model of F16 Fighter with the length of 800 mm is rapidly fabricated using the VLM-ST process. In order to build a CAD model of F16 larger than 600 mm in length, the approach in VLM-ST is to build larger parts in multiple sub-parts and then glue them together. The fabricated result shows that the VLM-ST process employing thick layers and sloped surfaces is adequate for creating the real-sized large objects in the diverse fields such as automobiles, electric home appliances, electronics. and etc.