• Applied Chemistry for Engineering
• /
• v.28 no.6
• /
• pp.705-713
• /
• 2017

A novel material, $Bi_2WO_6-GO-TiO_2$ composite, was successfully synthesized using a facile hydrothermal method. During the hydrothermal reaction, the loading of $Bi_2WO_6$ and $TiO_2$ nanoparticles onto graphene sheets was achieved. The obtained $Bi_2WO_{6-GO-TiO2}$ composite photo-catalysts were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray (EDX) analysis, transmission electron microscopy (TEM), Raman spectroscopy, ultraviolet-visible diffuse reflectance spectroscopy (UV-vis-DRS), and X-ray photoelectron spectroscopy (XPS). The $Bi_2WO_6$ nanoparticle showed an irregular dark-square block nanoplate shape, while $TiO_2$ nanoparticles covered the surface of the graphene sheets with a quantum dot size. The degradation of rhodamine B (RhB), methylene blue trihydrate (MB), and reactive black B (RBB) dyes in an aqueous solution with different initial amount of catalysts was observed by UV spectrophotometry after measuring the decrease in the concentration. As a result, the $Bi_2WO_6-GO-TiO_2$ composite showed good decolorization activity with MB solution under visible light. The $Bi_2WO_6-GO-TiO_2$ composite is expected to become a new potential material for decolorization activity. Photocatalytic reactions with different photocatalysts were explained by the Langmuir-Hinshelwood model and a band theory.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.112-112
• /
• 1999

고분자 표면에 MeV급 이온을 주입하게 되면 화학적, 광학적, 물리적, 전기적 특성 등 기존의 재래식 공정으로는 불가능한 다양한 특성변화가 일어나게 된다. 본 실험에서는 이온 조사에 따른 micro-hardness의 변화에 중점을 두어 관찰하였다. 수 MeV로 가속시킨 Cl과 C 이온을 Kapton, Teflon, PMMA에 조사량을 바꾸어가며 조사하였다. 이때 조사 전후 고분자 시료의 표면 경도는 depth-sensing nanoindentation technique (Nano Indenter II, USA)을 이용하여 측정하였다. 측정깊이는 극표면 효과와 기측효과의 영향을 무시할 수 없는 100nm로 결정하였다. 또한 이와 같은 경도변화를 규명하기 위하여 각각의 시료에 대해 FTIR, Raman, UV-VIS, RBS, XPS 스펙트럼을 측정하였으며, 조사중에 발생되는 가스상 분자들을 RGA를 이용하여 측정하였다. 1 MeV Cl 이온을 Kato에 4x1015ions/cm2 조사하면 경도가 0.35 GPa에서 7.1GPa로 약 20배 정도 증가하게 되며, 이 경도는 stainless steel 경도 2~3 GPa, martensite steel 8~12와 비교하여 보면 상당히 높은 수준임을 알 수 있다. Teflon과 PMMA 시료의 경우 1MeV Cl 이온 4X1015ions/cm2를 조사시키면 각각 경도가 0.31GPa에서 4.1a, 0.30 GPa에서 3.9GPa로 변화하였으며 Kapton에 비하여 상대적으로 경도의 변화가 적음을 알 수 있었다. 이온 주입된 Kapton의 경우 FT-IR측정에 의하여 이온 조사량이 증가함에 따라 C=O 진동, 이미드그룹의 CONH, tertiary amine의 C-N 흡수 피크가 감소되며, 1X1014ions/cm2 이상의 양이 조사되어야 개질변화가 일어남을 알 수 있었다. XPS 측정 결과 Kapton에 조사되는 이온양이 증가할수록 C=O, C-O 및 C-N의 탄소는 감소하고 페닐고리 탄소가 증가함을 알 수 있었다. 또한 이온 조사 중 측정한 RGA에서도 CO 가스가 대량 방출되는 현상을 관찰하였으며 FTIR 및 XPS에서의 C=O 결합의 감소와도 일치하였다. RBS에 의한 CNO 원소의 변화에서도 다른 원소보다 O의 감소가 현저하게 나타남을 확인하였다. UV-VIS 측정을 통해 조사 이온량에 따라 에너지 준위가 변동하여 흡수스펙트럼이 장파장으로 확대됨을 알 수 있었으며, 이는 공액 2중 결합의 형성에 의한 $\pi$-전자 및 기타 결함에 기인한다. PMMA 및 Teflon의 경우 FTIR 측정에 의하여 이온 조사됨에 따라 function group 들의 peak가 세기가 감소되면서 완만해지는 경향을 보이며 원래의 구조를 상실하게 된다. PMMA와 Teflon은 이온 조사가 되면 가교형서보다는 사슬절단이 주로 일어나므로 가교형성이 잘 일어나는 Kapton보다는 상대적으로 경도의 증가가 적음을 알 수 있었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.58-58
• /
• 1999

The diamond films which can be applied to SOD (silicon-on-diamond) structure were deposited on Si(100) substrate using CO/H2 CH4/H2 source gases by microwave plasma chemical vapor deposition(MPCVD), and SOD structure have been fabricated by poly-silicon film deposited on the diamond/Si(100) structure y low pressure chemical vapor deposition(LPCVD). The phase of the diamond film, surface morpholog, and diamond/Si(100) interface were confirmed by X-ray diffraction(XRD), scanning electron microscopy(SEM), atomic force microscopy(AFM), and Raman spectroscopy. The dielectric constant, leakage current and resistivity as a function of temperature in films are investigated by C-V and I-V characteristics and four-point probe method. The high quality diamond films without amorphous carbon and non-diamond elements were formed on a Si(100), which could be obtained by CO/H2 and CH4/H2 concentration ratio of 15.3% and 1.5%, respectively. The (111) plane of diamond films was preferentially grown on the Si(100) substrate. The grain size of the films deposited by CO/H2 are gradually increased from 26nm to 36 nm as deposition times increased. The well developed cubo-octahedron 100 structure nd triangle shape 111 are mixed together and make smooth and even film surface. The surface roughness of the diamond films deposited by under the condition of CO/H2 and CH4/H2 concentration ratio of 15.3% and 1.5% were 1.86nm and 3.7 nm, respectively, and the diamond/Si(100) interface was uniform resistivity of the films deposited by CO/H2 concentration ratio of 15.3% are obtained 5.3, 1$\times$10-9 A/cm, 1 MV/cm2, and 7.2$\times$106 $\Omega$cm, respectively. In the case of the films deposited by CH4/H2 resistivity are 5.8, 1$\times$10-9 A/cm, 1 MV/cm, and 8.5$\times$106 $\Omega$cm, respectively. In this study, it is known that the diamond films deposited by using CO/H2 gas mixture as a carbon source are better thane these of CH4/H2 one.

• Journal of the Korean Vacuum Society
• /
• v.7 no.4
• /
• pp.348-354
• /
• 1998

To investigate an influence of the thermal preheating for the substrates exerted on the heteroepilayers, the ZnTe epilayers are grown on the GaAs (100) at the substrate temperature of 450~$630^{\circ}C$ by hot wall epitaxy (HWE). For this purpose, double crystal rocking curve (DCRC) and photoluminescence (PL) are measured. The full width at half maximum of DCRC are the smallest in the ZnTe epilayers grown on the GaAs thermally etched at around both $510^{\circ}C$ and $590^{\circ}C$. However, at around $550^{\circ}C$ they increase due to the reconstruction of the atoms in the surface. And they increase due to the oxide layer at below $490^{\circ}C$ and due to the surface defects at above $610^{\circ}C$. From PL analysis, the full width at half maximum of the light hole exciton $X_{1s,th}$ and of the second-order Raman line increase at around $550^{\circ}C$. With the increasing preheating temperature, the intensities of Y-bands and of the oxygen bound exciton (OBE) peak related to an oxide layer on the GaAs surface generally decrease. From these experimental results, it's confirmed that the GaAs substrate thermally etched influences the ZnTe pilayers.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.54-54
• /
• 1999

다이아몬드 합성시 질소 첨가는 Cn 화합물의 합성가능성을 비롯하여 다이아몬드의 질소 도핑, 성장 속도 및 결정성 변화 등 다양한 관점에서 중요한 의미를 가지고 있다. 본 연구에서는 다이아몬드의 일반적인 합성조건에서 질소를 첨가하여 합성된 막의 형상 및 상 변화에 대해 고찰하였다. 막은 다이아몬드 전처리시킨 Si 기판위에 microwave plasma CVD 장치를 이용하여 합성하였다. 유입되는 혼합가스(CH4+H2+N2)에서 N2 첨가량을 0-95%까지 변화시켰다. 이때 CH4 농도는 5%로 고정하였고, 합성온도는 90$0^{\circ}C$-115$0^{\circ}C$까지 변화시켰다. 이와 같이 합성된 막의 표면조직 및 성장 두께를 측정하기 위해 주사전자현미경을 이용하였다. 상의 분석은 Raman, XRD 및 TEM 분석을 이용하였으며, 조성분석을 위해 XPS 및 AES를 사용하였다. 질소 첨가량에 따라 합성된 막은 첨가하지 않은 경우에 다이아몬드 결정에서 시작하여 질소첨가에 따라 결정면이 깨지는 것으로 나타났다. 그러나 30%, 45%의 경우는 다시 결정면이 나타났다. 다량의 질소가 첨가되었을 때, 다시 결정면을 보이는 다이아몬드가 합성된 것은 매우 흥미로운 결과이다. 한편 질소와 메탄만의 기체하에서는 다시 결정면이 관찰되지 않았다. 이들 상의 구조는 XRD 및 TED 분석을 통해 모두 다이아몬드로 확인되었다. 기체내의 질소의 첨가에 관계없이 고상내에 질소는 확인되지 않았다. 따라서 이방법에 의한 CN 화합물의 합성은 힘든 것으로 보여진다. 이들 실험 결과를 근거로 온도 및 조성에 따른 기체의 열역학적 계산을 통하여 합성거동과의 연관성을 검토하였다. anode는 매우 높은 충전용량을 갖는데 첫 번째 방전시에 Li2O를 생성하여 비가역적 반응을 나타내고 계속되는 충방전 동안 Li-Sn 합금이 생성되어 2차전지의 가역적 반응을 가능하게 한다. SnO2 는 대기중에서 Li 금속보다 안정하기 때문에 전지의 제작 공정 및 사용 면에서 매우 우수한 물질이지만 아직까지 SnO2 구조적 특성과 전지의 충, 방전 특성에 대한 관계의 규명을 위한 정확한 정설은 제시되고 있지 못하다. 본 연구에서는 TFSB anode 물질로써 SnOx박막을 상온에서 여러 전도성 콜렉터 위에 증착하여 그 충, 방전 특성을 보고하였다. 증착된 SnOx박막의 표면은 SEM, AFM으로 분석하였으며 구조의 분석은 XR와 Auger electron spectroscope로 하였다. 충, 방전 특성을 분석하기 위하여 리늄 foil을 대극과 참조 전극으로 하여 EC:DMC=1:1, 1M LiPF6 액체 전해질을 사용한 Half-Cell를 구성하여 100회 이상의 정전류 충, 방전 시험을 행하였다. Half-Cell test 결과 박막의 구조, 콜렉터의 종류 및 Sn/O비에 따라 서로 다른 충, 방전 거동을 나타내었다.다. 거의 없었다. 5mTorr 일 때가 가장 좋았다.수 있음을 알 수 있었다. 그러므로, RNA바이러스의 하나인 BVDV의 viral replicon을 이용하여 다양한 종류의 포유동물 세포에 유전자 발현벡터로써 사용할 수 있음으로 post-genomics시대에 다양한 종류의 단백질 기능연구에 맡은 도움이 되리라 기대한다.다양한 기능을 가진 신소재 제조에 있다. 또한 경제적인 측면에서도 고부가 가치의 제품 개발에 따른 새로운 수요 창출과 수익률 향상, 기존의 기능성 안료를 나노(na

• Journal of the Korean Ceramic Society
• /
• v.40 no.12
• /
• pp.1202-1207
• /
• 2003

Using a recently developed Hybric Plasma-Particle Accelerating Impact Deposition (HP-PAID) process, synthesis of nanostructured silicon coatings has been investigated by injecting vapor-phase TEOS (tetraethosysilane, (C$_2$H$\_$5/O)$_4$Si) into an Ar hybrid plasma. The plasma jet with reactants was expanded through nozzle into a deposition chamber, with the pressure dropping from 700 to 10 torr. Ultrafine particles accelerated in the free jet downstream of the nozzle, deposited by an inertial impaction onto a temperature controlled substrate. By using this process, nanostructured amorphous silicon coatings with grain size smaller than 10 nm could be synthesized. These samples were annealed in an Ar and crystallized at 900$^{\circ}C$ for 30 min. TEM analysis showed that the annealed coatings were also composed of nanoparticles smaller than 10 nm, which showed a good consistency that the average grain size of 7 nm was also estimated from a peak shift of 2.39 cm$\^$-1/ and Full Width at Half Maximum (FWHM) 5.92 cm$\^$-1/ of Raman analysis. The noteworthy is that a strong PL peak at 398 nm was also obtained for this sample, which indicates that the deposited coatings also contained 3∼4 nm nanostructured grains.

• Progress in Medical Physics
• /
• v.12 no.1
• /
• pp.1-8
• /
• 2001

Diamond thin films were synthesized by a chemical vapor deposition (CVD). Raman spectrum showed the diamond line at 1332 $cm^{-1}$ / and x-ray diffraction pattern exhibited a strong (111) peak of diamond. The scanning electron microscopy analysis showed that the CVD diamond thin film was grown to be unepitaxial crystallites with pyramidal hillocks. A wavelength-resolved thermoluminescence (TL) of the CVD diamond thin film irradiated with X-rays showed one peak at 430 nm around 560 K. The glow curve of the CVD diamond thin film produced one dominant 560-K peak that was caused by first-order kinetics. Its activation energy and the escape frequency were calculated to be 0.92 ～ 1.05 eV and 1.34 $\times$ 10$^{7}$ sec$^{-1}$ , respectively. The emission spectrum at 560 K was split into 1.63-eV, 2.60-eV, and 3.07-eV emission bands which is known to be attribute to silicon-vacancy center, A center, and H3 center, respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.413-413
• /
• 2014

In this paper, we present a fabrication method of functionalized gold nanostructures on flexible substrate that can be implemented for plasmonic sensing application. For biomolecular sensing, many researchers exploit unconventional lithography method like nanoimprint lithography (NIP), contact transfer lithography, soft lithography, colloidal transfer printing due to its usability and easy to functionalization. In particular, nanoimprint and contact transfer lithography need to have anti-adhesion layer for distinctive metallic properties on the flexible substrates. However, when metallic thin film was deposited on the anti-adhesion layer coated substrates, we discover much aggravation of the mold by repetitive use. Thus it would be impossible to get a high quality of metal nanostructure on the transferred substrate for developing flexible electronics based transfer printing. Here we demonstrate a method for nano-pillar mold and transfer the controllable nanoparticle array on the flexible substrates without an anti-adhesion layer. Also functionalization of gold was investigated by the different length of thiol applied for effectively localized surface plasmonic resonance sensing. First, a focused ion beam (FIB) and ICP-RIE are used to fabricate the nanoscale pillar array. Then gold metal layer is deposited onto the patterned nanostructure. The metallic 130 nm and 250 nm nanodisk pattern are transferred onto flexible polymer substrate by bi-layer functionalized contact imprinting which can be tunable surface energy interfaces. Different thiol reagents such as Thioglycolic acid (98%), 3-Mercaptopropionic acid (99%), 11-Mercaptoundecanoic acid (95%) and 16-Mercaptohexadecanoic acid (90%) are used. Overcoming the repeatedly usage of the anti-adhesion layer mold which has less uniformity and not washable interface, contact printing method using bi-layer gold array are not only expedient access to fabrication but also have distinctive properties including anti-adhesion layer free, functionalized bottom of the gold nano disk, repeatedly replicate the pattern on the flexible substrate. As a result we demonstrate the feasibility of flexible plasmonic sensing interface and anticipate that the method can be extended to variable application including the portable bio sensor via mass production of stable nanostructure array and other nanophotonic application.

• Korean Journal of Materials Research
• /
• v.26 no.11
• /
• pp.604-610
• /
• 2016

We report on the fabrication and characterization of a novel $Cu_2O/CuO$ heterojunction structure with CuO nanorods embedded in $Cu_2O$ thin film as an efficient photocathode for photoelectrochemical (PEC) solar water splitting. A CuO nanorod array was first prepared on an indium-tin-oxide-coated glass substrate via a seed-mediated hydrothermal synthesis method; then, a $Cu_2O$ thin film was electrodeposited onto the CuO nanorod array to form an oxide semiconductor heterostructure. The crystalline phases and morphologies of the heterojunction materials were examined using X-ray diffraction and scanning electron microscopy, as well as Raman scattering. The PEC properties of the fabricated $Cu_2O/CuO$ heterojunction photocathode were evaluated by photocurrent conversion efficiency measurements under white light illumination. From the observed PEC current density versus voltage (J-V) behavior, the $Cu_2O/CuO$ photocathode was found to exhibit negligible dark current and high photocurrent density, e.g. $-1.05mA/cm^2$ at -0.6 V vs. $Hg/HgCl_2$ in $1mM\;Na_2SO_4$ electrolyte, revealing the effective operation of the oxide heterostructure. The photocurrent conversion efficiency of the $Cu_2O/CuO$ photocathode was estimated to be 1.27% at -0.6 V vs. $Hg/HgCl_2$. Moreover, the PEC current density versus time (J-T) profile measured at -0.5 V vs. $Hg/HgCl_2$ on the $Cu_2O/CuO$ photocathode indicated a 3-fold increase in the photocurrent density compared to that of a simple $Cu_2O$ thin film photocathode. The improved PEC performance was attributed to a certain synergistic effect of the bilayer heterostructure on the light absorption and electron-hole recombination processes.

• Journal of the Korean Vacuum Society
• /
• v.19 no.5
• /
• pp.377-384
• /
• 2010

Many routes have been developed for the synthesis of signle-walled carbon nanotubes (SWCNTs). We spun fibers of SWCNTs directly from vertical furnace using a liquid source of carbon and an iron-contained molecule. The solution was prepared by ethanol as a carbon source, in which ferrocene as a catalyst, thiophene were dissolved. It was then injected from the top of the furnace into hot zone with hydrogen as a carrier gas. We successfully synthesized high-quality SWCNTs by adjusting the various experimental conditions, such as concentration of ferrocene, solution injection rate, concentration of thiophene, and hydrogen flow rate. Measurement of Raman spectroscopy, scanning electron microscopy, and transmission electron microscopy were carried out to find the optimized conditions. The synthesized SWCNTs (1.16~1.64 nm) appeared a bundle structure and well-aligned parallel to the direction of furnace. These results also provide an simple way for high-quality SWCNTs mass production and fabricating direct spining SWCNTs fiber. It will allow one-step production of SWCNTs fiber with potentially excellent properties and wide-range applications.