• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.3 s.55
• /
• pp.127-134
• /
• 2009

This study investigated their properties of spalling resistance and residual compressive strength after fire test corresponding to various ISO, RABT heating curves, and contents of hybrid organic fiber of high strength concrete. The results were summarized as following. As fundamental characters of concrete with hybrid organic fiber, the flowability was directly declined as the increase of fiber contents, and air contents were decreased or increased a little bit, but there was not big difference. The compressive strength was gradually declined sluggishly at 28 days. As properties of fire resistance, in case of RABT heating curves, compare with ISO heating curves a spalling aspect showed till range that has much contents of hybrid organic fiber, but they are mostly peeling spalling, which means spalling aspect didn't happen to inside. In conclusion, in case of W/B 25% high strength concrete, the spalling was prevented over 0.04% of contents of fiber at ISO heating curve and over 0.10% of contents of fiber at the RABT heating curve. In case of spalling was prevented, mass reduction rate according to the change of heating temperature curves showed around 7% at ISO heating curves and around 9% at RABT heating curves. The residual compressive strength rate corresponding to the change of heating temperature curves showed 50%~60% at ISO heating temperature curves and 30%~35% at RABT heating temperature curves in case of spalling was prevented.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.3
• /
• pp.284-291
• /
• 2016

To evaluate the properties of inorganic composites using a great quantity of high-calcium fly ash generated in combined heat and power plants, high-calcium fly ash and F-class fly ash commonly used as concrete admixtures were substituted with binding materials to examine changes of fluidity and compressive strength depending on the substitution ratio for each curing temperature. According to the experimental result, CFA-mixed mortar showed a tendency to reduce its flow unlike FFA-mixed mortar as the substitution ratio was increased, but its flow loss showed smaller than FFA as time passed. As a result of examining compressive strength depending on mixing FA, FFA-mixed mortar had an optimum range within 50% when curing at ambient temperature, but it was found that the compressive strength is reduced when mixing CFA. When curing at high temperature, FFA did not relatively have a great effect on the substitution ratio, but CFA could expect a strength enhancement effect compared with 100% of OPC when using within 25% of binding materials.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.6
• /
• pp.91-97
• /
• 2016

Evaluation on the test of actual concrete member to confirm the fire resistance of the concrete member using ultra-high strength concrete is required. However, test equipment which has large loading capacity is needed to the actual member experiment. So, many researchers evaluated the fire performance through analytical studies using the material models. This study experimentally evaluated strain properties on ultra-high-strength concrete of 80, 130 and 180 MPa with heating and examined to apply the existing strain model about ultra-high-strength concrete. As a results, constants are drawn by method of least squares applying experimental values and calculated values by the existing strain model, it proposed strain model that can be applied to ultra-high-strength concrete.

• Computers and Concrete
• /
• v.6 no.4
• /
• pp.269-280
• /
• 2009

In this paper an experimental study of the influence of hot springs curing upon concrete properties was carried out. The primary variables of the investigation include water-to-binder ratio (W/B), pozzolanic material content and curing condition. Three types of hot springs, in the range $40-90^{\circ}C$, derived from different regions in Taiwan were adopted for laboratory testing of concrete curing. In addition, to compare with the laboratory results, compressive strength and durability of practical concrete were conducted in a tunnel construction site. The experimental results indicate that when concrete comprising pozzolanic materials was cured by a hot spring with high temperature, its compressive strength increased rapidly in the early ages due to high temperature and chloride ions. In the later ages, the trend of strength development decreased obviously and the strength was even lower than that of the standard cured one. The results of durability test show that concrete containing 30-40% Portland cement replacement by pozzolanic materials and with W/B lower than 0.5 was cured in a hot spring environment, then it had sufficient durability to prevent steel corrosion. Similar to the laboratory results, the cast-inplace concrete in a hot spring had a compressive strength growing rapidly at the earlier age and slowly at the later age. The results of electric resistance and permeability tests also show that concrete in a hot spring had higher durability than those cured in air. In addition, there was no neutralization reaction being observed after the 360-day neutralization test. This study demonstrates that the concrete with enough compressive strength and durability is suitable for the cast-in-place structure being used in hot spring areas.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.4
• /
• pp.119-125
• /
• 2010

The performance deformation of concrete can be caused by many factors such as load, thermal strain and creep at high temperature. Japan, Europe and America have been doing various experimental studies to solve these problems about thermal properties of concrete at high temperature, each study has generated different results due to a heating methods, heating hours, size of specimens and performance of a the loading, heating method, size of specimen and heating machine. There has been no unified experimental method so far. Therefore, this study reviewed experimental studies on the strength performance of concrete subject to heating and loading method. As a result, compressive strength of specimen prestressed increase in the temperature range of between $100^{\circ}C$ and about $400^{\circ}C$. Also, results can be analyzed as compare equation of compressive strength at elevated temperature with CEN and CEB code.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.4
• /
• pp.369-376
• /
• 2012

In this study, to reduce the hydration heat velocity (HHV) of high-strength mass concrete at early ages, phase change materials (PCM) that could absorb hydration heat were applied, and the changes in autogenous shrinkage were investigated, as well as the relationship between the hydration temperature and autogenous shrinkage. The acceleration of the cement hydration process by the PCM leads to an early setting and a higher development of the compressive strength and elastic modulus of concrete at very early ages. The function of PCM could be worked below the original melting point due to the eutectic effect, while the hydration temperature and HHV of high-strength mass concrete can be decreased through the use of the PCM. A close relationship was found between the hydration temperature and autogenous shrinkage: the higher the HHV, the greater the ultimate autogenous shrinkage.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.769-772
• /
• 2006

The effects of high temperature on strength, elastic modulus and strain at peak stress of concrete were experimentally investigated. The type of test was the stressed test that a preload was applied to the specimen prior to heating and the load was sustained during the heating period. In this study, the level of preload was 25% of compressive strength at room temperature. All tests were conducted at various temperatures(20,100, 200, 300, 400, 500, 600 and $700^{\circ}C$) for concretes made with W/B ratios 46% and 32%. Test results showed that on the whole, the relative values of strength and elastic modulus, and the real strain value at peak stress were not influenced by the W/B ratio.

• Journal of the Korea Concrete Institute
• /
• v.29 no.2
• /
• pp.217-223
• /
• 2017

This research was planned to evaluate the structural performance of post tensioned(PT) concrete member subjected to fire. Prime objective was to suggest some techniques to evaluate the performance of post tensioned concrete beam and slab exposed to high temperature through experiment. To accomplish this objective, the following two scopes have been proceeded to verify the strength reducing ratio of strands and find out the difference of resisting force at the PT concrete members exposed to high temperature through the fire test. The properties of prestressing steel(tendon) in PT concrete beam and slab under variable temperatures were reviewed. The test of this study was shown that stress relaxation occurred at high temperature, and some restoration of tensional force appeared as it got cooling down. The residual tension of the post tensioned beams at 4 hours after reaching the target temperature were 70% at $400^{\circ}C$, 10% at $600^{\circ}C$ and 2% at $800^{\circ}C$. The post tensioned slabs were 94% at $400^{\circ}C$, 84.5% at $600^{\circ}C$ and 62% at $800^{\circ}C$. The reason why the residual tension loss of the post tensioned slab was relatively small was considered to be that the slab was exposed just one side to high temperature and the strength of the strand was restored larger than that of beam. Also, it was confirmed that the post tensioned member inevitably experienced the loss of strength by fire damage, and restoration design of the member should be required to compensate for the value as much as lost strength.

• Fire Science and Engineering
• /
• v.18 no.1
• /
• pp.31-36
• /
• 2004

The purpose of this study is to present data for the reusing, rehabilitation and estimation of safety of RC structure damaged by fire, and for the prevention of explosive spatting by investigation the properties of explosive spalling, compressive strength and ultrasonic pulse velocity according to kinds of fine aggregate, admixture and water-cement ratios. In explosive spalling properties with kinds of aggregate, explosive spalling does not appear or little at surface in the case of used sea sand, but the case of using recycled sand or crushed sand is worse and worse. Property with the kind of admixture does not appear specially. And high strength concrete with W/C 30.5% was taken spalling, but 55% does not appear. It is found that residual compressive strength after exposed at high temperature showed 45％ in W/C 55%, and 64％ in W/C 30.5％ of its original strength averagely. Ultrasonic pulse velocity is different with kinds of aggregate. W/C. and heating time. When 3 month age after heating ultrasonic pulse velocity is recovered abut 1.3％～8.4％ of its 1 month age after heating.

• Journal of Korean Society of Steel Construction
• /
• v.25 no.1
• /
• pp.71-80
• /
• 2013

Fire-resistant (FR) test data for a square concrete-filled steel tube (CFT) columns consisting of high-strength steel (fy>650MPa) and high strength concrete (fck>100MPa) under axial loads are insufficient. The FR behavior of square high-strength CFT members was investigated experimentally for two specimens having ${\Box}-400{\times}400{\times}15{\times}3,000mm$ with two axial load cases (5,000kN and 2,500kN). The results show that the FR performance of the high-strength CFT was rapidly decreased at earlier time (much earlier at high axial load) than expected due to high strength concrete spalling and cracks. In addition, a fiber element analysis (FEA) model was proposed and used to simulate the fiber behaviour of the columns. For steel and concrete, the mechanical and thermal properties recommended in EN 1994-1-2 are adopted. Test results were compared to those of numerical analyses considering a combination of temperature and axial compression. The numerical model can reasonably predict the time-axial deformation relationship.