• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.3
• /
• pp.603-609
• /
• 1990

Detection and non-propagating cracks of small fatigue crack for smooth and pre-cracked specimens were examined in a carbon steel. The fretting oxide induced crack closure triggered by the roughness induced crack closure has an important role in determing the length. The fatigue limit for the with no cracks or with a short pre-crack is lower at R=-1 than that at R=0. A non-propagating crack are quite different between points near the specimen's surface and those of deepest penetration.

• Corrosion Science and Technology
• /
• v.3 no.1
• /
• pp.14-19
• /
• 2004

Crack growth rate and threshold stress intensity factor for stress corrosion cracking(SCC), $K_{ISCC}$ were measured for type 403 stainless steel in 3,5% NaCl solution at room temperature and SCC was monitored by electrochemical noise technique during $K_{ISCC}$ testing. In rising load test, pits were formed at the tip of pre-crack for the pre-cracked compact tension specimen unlike in smooth round specimen in which only unstable pits were observed and hence immune to SCC. Micro-cracks were found to initiate from the pits in the former specimen, and initiation of micro-crack as well as macro-crack was detected by electrochemical noise technique in rising load $K_{ISCC}$ tests. Crack growth rate increased with increasing either displacement rate or stress intensity factor at crack initiation and was higher in rising load $K_{ISCC}$ test compared to constant load $K_{ISCC}$ test at given stress intensities.

• Structural Engineering and Mechanics
• /
• v.55 no.4
• /
• pp.885-900
• /
• 2015

This paper introduces Romberg-Richardson's method as one of the numerical integration tools for computation of stress intensity factor in a pre-cracked specimen subjected to a complex stress field across the crack faces. Also, the computation of stress intensity factor for various stress fields using existing three methods: average stress over interval method, piecewise linear stress method, piecewise quadratic method are modified by using Richardson extrapolation method. The direct integration method is used as reference for constant and linear stress distribution across the crack faces while Gauss-Chebyshev method is used as reference for nonlinear distribution of stress across the crack faces in order to obtain the stress intensity factor. It is found that modified methods (average stress over intervals-Richardson method, piecewise linear stress-Richardson method, piecewise quadratic-Richardson method) yield more accurate results after a few numbers of iterations than those obtained using these methods in their original form. Romberg-Richardson's method is proven to be more efficient and accurate than Gauss-Chebyshev method for complex stress field.

• Proceedings of the KWS Conference
• /
• 1998.05a
• /
• pp.49-51
• /
• 1998

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.2
• /
• pp.402-407
• /
• 1995

The effects of room temperature and strain aging treatment are discussed on the critical condition for the onset of growth of non-propagating cracks on 0.15% C low carbon steel, with special emphasis on the length of the critical non-propagating crack and on the crack opening displacement(COD) at the crack tip. It is found from the experimental analysis that room temperature and strain aging of a fatigue pre-cracked specimen introduced the closure of a crack tip of the pre-crack and the reduction of crack opening displacement at the wake of crack, together with an improvement in crack growth resistance of the microstructure. This may cause an increase in the endurance limit of the specimen, through the enhancement of effective stress for the onset of growth of the critical non-propagating crack.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.4 no.2
• /
• pp.42-51
• /
• 2001

The effects of pre-indentation technique are presented for A12024-T3 Alclad alloy using as skin material for aircraft fuselage and wing. Indentations were applied to specimens to be placed on the presumed path of fatigue crack growth before fatigue tests. Tension-tension fatigue tests were conducted on the edge cracked specimens in the L-T orientation. Test results were analyzed to investigate the effectiveness of pre-indentation with the variation of specimen's thickness, position of indentation and applied maximum stress. Fatigue crack retardation by pre-indentation is well recognized in the various conditions.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.32 no.4
• /
• pp.355-361
• /
• 2012

This paper presents an experimental study on the detection and location of nonlinear scattering source due to the presence of fatigue crack in a laboratory specimen. The proposed technique is based on a combination of nonlinear elastic wave spectroscopy(NEWS) and time reversal(TR) focusing approach. In order to focus on the nonlinear scattering position due to the fatigue crack, we employed only one transmitting transducer and one receiving transducer, taking advantage of long duration of reception signal that includes multiple linear scattering such as mode conversion and boundary reflections. NEWS technique was then used as a pre-treatment of TR for spatial focusing of reemitted second harmonic signal. The robustness of this approach was demonstrated on a cracked specimen and the nonlinear TR focusing behavior is observed on the crack interface from which the second harmonic signal was originated.

• Journal of Mechanical Science and Technology
• /
• v.20 no.2
• /
• pp.197-204
• /
• 2006

The purpose of this study is to evaluate the AE characteristics for the basemetal, PWHT (post-weld heat treatment) and weldment specimens of SA-516 steel during fracture testing. Four-point bending and AE tests were conducted simultaneously. AE signals were emitted in the process of plastic deformation. AE signal strength and amplitude of the weldment was the strongest, followed by PWHT specimen and basemetal. More AE signals were emitted from the weldment samples because of the oxides, and discontinuous mechanical properties. AE signal strength and amplitude for the basemetal or PWHT specimen decreased remarkably compared to the weldment because of lower strength. Pre-cracked specimens emitted even lower event counts than the corresponding blunt notched specimens. Dimple fracture from void coalescence mechanism is associated with low-level AE signal strength for the basemetal or PWHT. Tearing mode and dimple formation were shown on the fracture surfaces of the weldment, but only a small fraction produced detectable AE.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.13 no.3
• /
• pp.7-13
• /
• 1993

Fracture behavior of pre-cracked compact tension specimens made of AISI 4130 steel was investigated using acoustic emission (AE) and ultrasonic C-scan measurements. While each specimen was loaded up to a certain level, various acoustic emission parameters were recorded together with the crack opening displacement (COD). An elastic-plastic finite element analysis was performed to calculate COD and the damage (plastic) zone size ahead of crack tip. Ultrasonic C-scans, in a pulse-echo, immersion mode, were done for mapping the damage zone size. The agreement between the finite element results and the measured COD was satisfactory. Based on AE results, the test specimens were found to show ductile behavior. The slope of the total ringdown counts vs. COD curve was useful to determine the crack initiation. The preliminary C-scan images showed evidence of changes in the amplitude of ultrasonic signal in the damaged region, and the shape and size of the damage zone matched qualitatively with the finite element results. A further work on the damage zone sizing was also pointed out.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.12 no.1
• /
• pp.62-69
• /
• 2016

Current guidance considers that uniaxially loaded specimen with a deep crack is used for the determination of the ductile-to-brittle transition temperature. However, reactor pressure vessel is under biaxial loading in real and the existence of deep crack is not probable through periodic in-service-inspection. The elastic stress intensity factor and the elastic-plastic J-integral which were used for crack-tip stress field and fracture mechanics assessment parameters. The difference of the loading condition and crack geometry can significantly influence on these parameters. Thus, a constraint effect caused by differences between standard specimens and a real structure can over/underestimate the fracture toughness, and it affects the results of the structural integrity assessment, consequentially. The present paper investigates the constraint effects by evaluating the master curve $T_0$ reference temperature of PCVN (Pre-cracked Charpy V-Notch) and small scale cruciform specimens which was designed to simulate biaxial loading condition with shallow crack through the fracture toughness tests and 3-dimensional elastic-plastic finite element analyses. Based on the finite element analysis results, the fracture toughness values of a small scale cruciform specimen were estimated, and the geometry-dependent factors of the cruciform specimen considered in the present study were determined. Finally, the transferability of the test results of these specimens was discussed.