• Journal of Powder Materials
• /
• v.18 no.6
• /
• pp.517-525
• /
• 2011

In this study, the used DOCs, which could remove the air pollutants such as CO and HC in the exhaust gas from diesel vehicle, were remanufactured by various conditions. Their catalytic performances and characterization were also investigated. The remanufacturing process of the deactivated DOCs includes high temperature cleaning of incineration, ultrasonic cleaning for washing with acid/base solutions to remove deactivating materials deposited to the surface of the catalysts, and active component reimpregnation for reactivating catalytic activity of them. The catalytic performance tests of the remanufactured DOCs were carried out by the diesel engine dynamo systems and chassi dynamo systems in CVS-75 mode. All prepared catalysts were characterized by the optical microscopes, SEM, EDX, porosimeter and BET to investigate correlations between catalytic reactivity and surface characteristics of them. The remanufactured DOCs at various conditions showed the improved catalytic performances reaching to 90% of fresh DOC, which is attributed to remove the deactivating materials from the surface of the used DOC through the analysis of catalytic performance test and their characterization.

• Corrosion Science and Technology
• /
• v.6 no.3
• /
• pp.133-139
• /
• 2007

Nickel powder was coated with aluminum nitrate solution to increase the thermal stability of a porous nickel support and control the nickel content in the Pd-Cu-Ni ternary alloyed membrane. Raw nickel powder and alumina coated nickel powder were uniaxialy pressed by home made press with metal cylindrical mold. Though the used nickel powder prepared by pulsed wire evaporation (PWE) method has a good thermal stability, the porous nickel support was too much sintered and the pores of porous nickel support was plugged at high temperature (over $800^{\circ}C$) making it not suitable for the porous support of a palladium based composite membrane. In order to overcome this problem, the nickel powder was coated by alumina and alumina modified porous nickel support resists up to $1000^{\circ}C$ without pore destruction. Furthermore, the compositions of Pd-Cu-Ni ternary alloy membrane prepared by magnetron sputtering and Cu-reflow could be controlled by not only Cu-reflow temperature but also alumina coating amount. SEM analysis and mercury porosimeter analysis evidenced that the alumina coated on the surface of nickel powder interrupted nickel sintering.

• Journal of the Korean Ceramic Society
• /
• v.54 no.4
• /
• pp.331-339
• /
• 2017

Porous alumina-based ceramics are of special interest due to their outstanding mechanical properties and their thermal and chemical stability. Nevertheless, the high electrical resistance of alumina-based ceramics, due to the generation of static electricity, leads to difficulty in applying a vacuum chuck in the semi-conductor process. Therefore, development of alumina-based ceramics for applications with vacuum chucks aims to have primary properties of low electrical resistance and high air permeability. In this study, we tailored the electrical resistance of porous alumina-based ceramics by adjusting the amount of $MnO_2$ (with $TiO_2$ fixed at an amount of 2 wt%) and by using coarse alumina powder for high air permeability. The characteristics of the specimens were studied using scanning electron microscopy, mercury porosimeter, capillary flow porosimetry, universal testing machine, X-ray diffraction and high-resistance meter.

• Journal of Technologic Dentistry
• /
• v.36 no.3
• /
• pp.179-184
• /
• 2014

Purpose: This study was performed to investigate the release behavior of bioactive materials as a BMP-2 embedding on the porous titanium implant. Methods: Porous Ti implant samples were fabricated by sintering of spherical Ti powders in a high vacuum furnace. Specimens diameter and height were 4mm and 10mm. Embedding materials were used to stamp ink. Sectional images, porosity and release behavior of porous Ti implants were evaluated by scanning electron microscope(SEM), mercury porosimeter and UV-Vis-NIR spectrophotometer. Results: Internal pore structure was formed fully open pore. Average pore size and porosity were $8.993{\mu}m$ and 8.918%. Embedding materials were released continually and slowly. Conclusion: Porous Ti implant was fabricated successfully by sintering method. Particles are necking strongly each other and others portions were vacancy. Therefore bioactive materials will be able to embedding to porous Ti implants. If the development of the fusion implant of the bioactive material will be able to have the chance to several patients.

• Journal of Technologic Dentistry
• /
• v.37 no.2
• /
• pp.57-62
• /
• 2015

Purpose: This study was performed to investigate mechanical properties of the porous Ti implants according to porosity. Porous Ti implant will be had properties similar to human bone such as microstructure and mechanical properties. Methods: Porous Ti implant samples were fabricated by sintering of spherical Ti powders(below $25{\mu}m$, $25{\sim}32{\mu}m$, $32{\sim}38{\mu}m$, and $38{\sim}45{\mu}m$) in a high vacuum furnace. Specimen's diameter and height were 4mm and 40 mm. Surface and sectional images of porous Ti implants were evaluated by scanning electron microscope(SEM). Porosity and average pore size were evaluated by mercury porosimeter. Young's modulus and tensile strength were evaluated by universal testing machine(UTM). Results: Porosity of Implant was increased according to larger particle size of the powder. Boundary portions of particles are sintered fully and others portions were formed pore. Young's modulus was decreased by formed porous structure. Tensile strength was decreased according to larger the particle size of the powder, but higher than human bone. Conclusion: If prepared by adjust the porosity of the porous Ti implant will be able to resolve the stress shielding phenomenon.

• Textile Coloration and Finishing
• /
• v.12 no.6
• /
• pp.380-388
• /
• 2000

The porosity of polyester fibers treated with sodium hydroxide aqueous solution was investigated using a nitrogen porosimeter, and the dyeability of the treated fibers was discussed in terms of the porosity. In pore distribution, the polyester fibers treated with sodium hydroxide aqueous solution were characterized by higher amount of pores below $10\AA$ than those of the untreated fibers, and by shift of the pore size having maximum accumulated volume from $10\AA$ for the untreated fibers to $5~6\AA$. As the weight loss of the polyester fibers treated with sodium hydroxide aqueous solution increased, BET surface area and total pore volume increased linearly, but average pore size, showing some different aspect, increased steeply at earlier stage and then approached the maximum value. The dye uptakes of the polyester fibers treated with sodium hydroxide aqueous solution increased with the BET surface area, the total pore volume and the average pore size. The alkali treatment increased the surface area of polyester fibers, so that the chance of contact between the fiber and dye molecules increased. In addition, the pores created on the surface of polyester fibers by alkali treatment might act as pathways for dye molecules into the polyester fibers.

• Korean Journal of Materials Research
• /
• v.18 no.12
• /
• pp.645-649
• /
• 2008

Graphite for the nuclear reactor is used to the moderator, reflector and supporter in which fuel rod inside of nuclear reactor. Recently, there are many researches has been performed on the various characteristics of nuclear graphite, however most of them are restricted to the structural and the mechanical properties. Therefore we focused on the thermal property of nuclear graphite. This study investigated the thermal emissivity following the oxidation degree of nuclear graphite with IG-11 used as a sample. IG-11 was oxidized to 6% and 11% in air at 5 l/min at $600^{\circ}C$. The porosity and thermal emissivity of the sample were measured using a mercury porosimeter and by an IR method, respectively. The thermal emissivity of an oxidized sample was measured at $100^{\circ}C$, $200^{\circ}C$, $300^{\circ}C$, $400^{\circ}C$ and $500^{\circ}C$. The porosity of the oxidized samples was found to increase as the oxidation degree increased. The thermal emissivity increased as the oxidation degree increased, and the thermal emissivity decreased as the measured temperature increased. It was confirmed that the thermal emissivity of oxidized IG-11 is correlated with the porosity of the sample.

• Journal of the Korean Ceramic Society
• /
• v.31 no.10
• /
• pp.1218-1230
• /
• 1994

In manufacturing process of porous glass-ceramics by the filler method, the sintering behaviour of crystallizable glass powder mixed with various salts was studied and also the effects of precipitated crystal phases on the properties of porous glass-ceramics were investigated. Fine-grained crystallizable glass powder was homogeneously mixed with various slat having grain size 100~200 ${\mu}{\textrm}{m}$ and sintered for densification. After washing out the inorganic salt with distilled water, the porous sintered body was heat treated additionly for crystallization. The MgO-Al2O3-SiO2 base glass was used as crystallizable glass powder and the water soluble salts such as K2SO4 and MgSO4 were used as filler. When K2SO4 was used, leucite crystal phase was formed as a result of the ion exchange and porous glass-ceramics which exhibit high temperature resistance and high thermal expansion coefficient of 17$\times$10-6/$^{\circ}C$ could be obtained. On the contrary, when MgSO4 was used, only slight ion exchange is observed and $\mu$-cordierite and $\alpha$-cordierite crystal phases were formed and porous glass-ceramics which exhibit low thermal expansion coefficient schedule were determined with the results of DTA curves, thermal shrinkage curves and XRD patterns analysis. From DTA curves and thermal shrinkage curves, it was found that the sintering densification have been completed at the temperature range of exothermic peak for crystallization. The pore size distributions and pore diameters were measured by mercury porosimeter. The pore diameter of porous glass-ceramics was 10~15 ${\mu}{\textrm}{m}$ when 100~200${\mu}{\textrm}{m}$ grain size of K2SO4 was used and it was 25~30 ${\mu}{\textrm}{m}$ when the same grain size of MgSO4 was used. The porous glass-ceramics K2SO4 used shows bimodal pore size distribution and its porous skeleton structure was ascertained by SEM observation.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2001.04a
• /
• pp.79-79
• /
• 2001

백판지는 포장용기로 사용되기 때문에 인쇄적성 이외에 다양한 후가공적성이 요구 된다. V Varnish Coating도 이러한 후가공적성 중의 하나로서 국내 인쇄소에서는 기계 코팅으로 불리 우며, 목적은 표면에 고분자수지 피막을 입힘으로써 인쇄물의 광택을 높여서 상품가치를 높이고 수운침투와 같은 외부환경의 변화로부터 상품을 안전하게 보관하기 위함이다. arnish C Coating은 인쇄기의 마지막 Unit에서 인쇄와 동일한 방식으로 진행되는데, 코팅액의 배합은 인쇄소와 인쇄물에 따라 상이하다. 본 연구는 Varnish Coating(OI하 기계코팅) 광택향상을 통 한 품질개선 목적으로 수행되었다. 기계 코팅의 특 성 을 파 악 하 기 위 해 서 Gas Chromatography / Mass Spectrometer와 FT -IR Sp e ectrometer를 사용하여 성문운석을 실시해본 결과 코팅액으로 사용되는 광택바니스는 아크 랄과 페놀수지를 툴루엔 계열의 용매에 녹인 용액이고, 흐$\mid$석제로 쓰이는 인쇄바니스는 스티 렌수지를 동일한 용매에 녹인 용액으로 조사되었다. 기계코팅광택 저하현상의 원인파악을 위해서 도공층의 공극구조를 Mercury Porosimeter를 이용하여 파악한 결과 기공의 부피가 상 대적으로 크게 나타났다. 위의 결과를 토대로 기계코팅광택 저하는 코팅액이 과도한 기공부피를 갖는 도공층 내부 로 대부분 홉수되고 표면에 적은 양만이 잔류하기 때문으로 판단하고 해결방안은 도공층의 기공부피를 줄이는 쪽으로 정하였다. Mayor Coater와 QC를 이용하여 Coating Color Formula t tion 번경실힘을 진행하여 도공지 물성을 분석하였다. 그 결과 Double Coating의 Top Color에 서 강력한 상호작용을 하는 Protein과 콜레이를 감량 하고 경질탄산칼숨을 배제하여 기공의 부피를 줄인 경우 기계코팅광택 향상효과가 두드러지게 나타났다. 이러한 Lab 실험을 바탕으로 결정된 Color Formulation에 대한 현장실험을 진행하였고 Lab 평가 및 실인쇄 평가 결과 원하는 수준의 기계코팅광택 향상을 얻을 수 있었다. 몇 차례의 현장실험과 Long-Run Test한 제품들에 대한 물성을 문석한 결과 기계코팅굉택은 인쇄 광택과 같은 경향을 나타냈으며 실협실적으로 간단하게 측정되는 물성 중에서 Air Permeability와 강한 음의 상관관계롤 보였다.

• Journal of the Society of Disaster Information
• /
• v.20 no.2
• /
• pp.390-397
• /
• 2024

Purpose: In this study, PCM was used to give thermal performance to concrete and analyze its effect on durability to prevent disasters that may occur in concrete when exposed to hot and cold environments. Method: After preparing concrete specimens containing 10, 30, and 50% of the two types of PCMs compared to the cement volume, the pore volume, freeze melting resistance, and scaling resistance were evaluated. Result: Regardless of the type, when PCM powder was mixed with concrete, the amount of pores decreased, and when 10% and 30% were mixed, the freeze-melting resistance was also improved. It was also confirmed that the higher the mixing amount, the better the scaling resistance. Conclusion: When mixing powdered PCM into concrete, it is believed that durability can be improved to a certain level by the filling effect, and additional various studies should be supported for actual field application.