• 한국분말재료학회지
• /
• 제20권6호
• /
• pp.439-444
• /
• 2013

Fe foam with above 90% porosity and 2 millimeter pore size was successfully fabricated by a slurry coating process. In this study, the binder contents were controlled to produce the Fe foam with different pore size, strut thickness and porosity. Firstly, the slurry was prepared by uniform mixing with Fe powders, distilled water and polyvinyl alcohol(PVA) as initial materials. After slurry coating on the polyurethane(PU) foam the sample was dried at $80^{\circ}C$. The PVA and PU foams were then removed by heating at $700^{\circ}C$ for 3 hours. The debinded samples were subsequently sintered at $1250^{\circ}C$ with holding time of 3 hours under hydrogen atmosphere. The three dimensional geometries of the obtained Fe foams with open cell structure were investigated using X-ray micro CT(computed tomography) as well as the pore morphology, size and phase.

• 한국산학기술학회논문지
• /
• 제10권3호
• /
• pp.476-481
• /
• 2009

판유리 폐기물과 hydroxyapatite를 사용하여 미세기공 함유 다공성유리를 제조하여 미세기공의 형태와 기계적 강도를 평가하였다. 발포제의 함량은 7%이상 함유시 기공이 조대하여지고 불균질하게 형성되었으며, $3{\sim}5%$ 함유시 발포 열처리온도 $830{\sim}840^{\circ}C$에서 $10{\mu}m$전후의 균일한 기공크기를 생성하였다. 기공성유리의 압축강도 및 곡강도는 각각 $18kg/cm^2$, $8kg/cm^2$를 나타내었다.

• Computers and Concrete
• /
• 제26권2호
• /
• pp.175-183
• /
• 2020

Fly ash has become an important component of concrete as supplementary cementitious material with the development of concrete technology. To make use of fly ash efficiently, four types of fly ash with particle size distributions that are in conformity with four functions, namely, S.Tsivilis, Andersen, Normal and F distribution, respectively, were prepared. The four particle size distributions as functions of the strength and pore structure of concrete were thereafter constructed and investigated. The results showed that the compressive and flexural strength of concrete with the fly ash that conforming to S.Tsivilis, Normal, F distribution increased by 5-10 MPa and 1-2 MPa, respectively, compared to the reference sample at 28 d. The pore structure of the concrete was improved, in which the total porosity of concrete decreased by 2-5% at 28 d. With regarding to the fly ash with Andersen distribution, it was however not conducive to the strength development of concrete. Regression model based on the grey multiple linear regression theory was proved to be efficient to predict the strength of concrete, according to the characteristic parameters of particle size and pore structure of the fly ash.

• KSBB Journal
• /
• 제6권2호
• /
• pp.135-141
• /
• 1991

This study thus looks into two treatment processess : i) Anaerobic digester coupled with hollow fibre membrane unit. Treatment of starch waste with anaerobic digester-membrane system was studied. $0.17\m^2$ area of hollow fibre membrane unit of known pore size was immersed into laboratory-scale anaerobic digestion system. The pore size of membrane was varied from 0.03 to $\0.15mu$m. The hydraulic retention time of anaerobic digester was varied from 1.5 to 10 days. The effect of hydraulic retention time on treatment efficiency was significant while effect of membrane size was not significant. The gas production was about 0.74㎥/kg COD treated. The COD removal efficient was about 80-95% depending on the hydraulic retention time. ii ) Crossflow ultrafiltration as post treatment to anaerobic filter. The effluent from anaerobic filter, which had a total COD in the range of 4,500-5,200 mg/L was treated by crossflow ultrafiltration units. The study conducted with different membrane pore size indicated that membrace with 1,000,000 molecular weight cut-off size gave a higher COD removal efficiency in the range of 83-87% while giving a study flux of $120-130 L/\m^2$.h. A study was conducted to see the long term clogging effect of membrane also.

• 한국분말재료학회지
• /
• 제25권5호
• /
• pp.415-419
• /
• 2018

Porous metals demonstrate not only excessively low densities, but also novel physical, thermal, mechanical, electrical, and acoustic properties. Thus, porous metals exhibit exceptional performance, which are useful for diesel particulate filters, heat exchangers, and noise absorbers. In this study, SUS316L foam with 90% porosity and $3,000{\mu}m$ pore size is successfully manufactured using the electrostatic powder coating (ESPC) process. The mean size of SUS316L powders is approximately $12.33{\mu}m$. The pore properties are evaluated using SEM and Archimedes. As the quantity of powder coating increases, pore size decreases from 2,881 to $1,356{\mu}m$. Moreover, the strut thickness and apparent density increase from 423.7 to $898.3{\mu}m$ and from 0.278 to $0.840g/cm^3$, respectively. It demonstrates that pore properties of SUS316L powder porous metal are controllable by template type and quantity of powder coating.

• 한국분말재료학회지
• /
• 제27권4호
• /
• pp.325-332
• /
• 2020

In this study, the effects of kaolin addition on the properties of reticulated porous diatomite-kaolin composites are investigated. A reticulated porous diatomite-kaolin composite is prepared using the replica template method. The microstructure and pore characteristics of the reticulated porous diatomite-kaolin composites are analyzed by controlling the PPI value (45, 60, and 80 PPI) of the polyurethane foam (which are used as the polymer template), the ball-milling time (8 and 24 h), and the amount of kaolin (0-50 wt. %). The average pore size decreases as the amount of kaolin increases in the reticulated porous diatomite-kaolin composite. As the amount of kaolin increases, it can be determined that the amount of inter-connected pore channels is reduced because the plate-shaped kaolin particles connect the gaps between irregular diatomite particles. Consequently, a higher kaolin percentage affects the overall mechanical properties by improving the pore channel connectivity. The effect of kaolin addition on the basic properties of the reticulated porous diatomite-kaolin composite is further discussed with characterization data such as pore size distribution, scanning electron microscopy images, and compressive strength.

• 한국연초학회지
• /
• 제16권2호
• /
• pp.191-197
• /
• 1994

Relationships between surface structure and adsorption properties of smoke components were investigated in surface-modified and un-modified activated carbon filter cigarettes. Commercially available activated carbon was treated with nitric acid and hydrogen peroxide as oxidant, and their pore volume, surface structure, BET surface area, pore type and size were studied. BET surface area and pore volume were decreased by nitric acid treatment, but median pore diameter was 8.1 $\AA$, which showed better development of pore compared with that of un-modified activated carbon, 6.9 $\AA$. In case of hydrogen peroxide treatment, BET surface area and pore volume were increased. Their pore was found to be a slit type based on V-t plot analysis. Neutralization capacities for bases of different strength (NaHCO3, Na2CO3, NaOEt and NaOH) showed that the majority of the acidic surface groups are of weak acidity. Modification of the activated carbon surface led to a slight change in adsorption properties when analyzing the smoke of triple-filter cigarette with surface-modified activated carbon.

• 한국세라믹학회지
• /
• 제33권5호
• /
• pp.547-555
• /
• 1996

Porous alumina ceramics were fabricated by pseudo-boehmite phydosol-gel process within/without commercial $\alpha$-alumina particles average 1 and 40 micron respectively. The pore characteristics of fired specimens were studied by the measurement of bulk density total porosity thyermal analysis pore volume pore distribution BET area XRD and SEM. with increasing of firing temperature pore volume and BET surface area were decreased and the average pore size was increased to approximately 146$\AA$ upto 80$0^{\circ}C$ by de-watering of [OH] and formation of $\alpha$-alumina. The fired relative density of the alumina-dispersed specimen with average 1 micron particle was increased with the amounts of dispersed particle by bimodal packing theory which is compared to the ones of specimen including of average 40 micron particle. It was confirmed that the percola-tion threshold in porous ceramics with coarser particle (40 micron) has formed between the transformed-alumina from hydrogel and dispersed-alumina of above 50 vol% particle and the total porosity was increased at the threshold point above.

• 한국세라믹학회지
• /
• 제31권9호
• /
• pp.1044-1052
• /
• 1994

Tape casting technique was successfully applied to produce porous ceramics and multi-layered ceramics containing porous layers, where spherical hollow polymer particles were introduced as pore precursors. In the presence of extreme differences in density and size between Al2O3 and pore precursor particles, hindered settling was effective in preventing segregation of component particles and packing behavior of mixed powders was improved through bimodal packing. There were two transitions in packing behavior of mixed powders. The first transition took place at 40~50 vol% pore precursor addition, where majority of pores changed from close to open pore state. The other transition occured at 60~70 vol% pore precursor addition, where pore precursor particles formed a continuous network structure.

• 한국지진공학회:학술대회논문집
• /
• 한국지진공학회 2003년도 추계 학술발표회논문집
• /
• pp.90-97
• /
• 2003

The purpose of this study is to understand the dissipation pattern of excess pore pressure after liquefaction which governs the post-liquefaction behavior of liquefied sand deposits. 1-g shaking table tests were carried out on 5 different kinds of sands, all of which had high liquefaction potentials. During the tests excess pore pressure at various depths, and surface settlements were measured. The measured curve of the excess pore pressure dissipation was simulated using the solidification theory, and from the analysis of the velocity of dissipation, the dissipation pattern of excess pore pressure after liquefaction was examined. The dissipation velocity of excess pore pressure after liquefaction had a linear correlation with the effective grain size ( $D_{10}$) divided by the coefficient of uniformity ( $C_{u}$), and the increase in the initial relative density of the ground played a role in shifting this correlation curve toward an increased dissipation velocity. From the correlation, an approximate method was recommended for prediction of the dissipation curve of excess pore pressure after liquefaction in saturated sand deposits.s.s.