• 대한치과보철학회지
• /
• 제31권4호
• /
• pp.482-505
• /
• 1993

The purpose of this study was to evaluate the fracture characteristics and the effect of resin bonding of laminate porcelain. In order to characterize the indentation-induced crack, Young's moduli and characteristic indentation dimensions were measured. The fatigue life under three point flexure test was measured using the electro-dynamic type fatigue machine, and the crack propagation with thermocycling was investigated on the condition of 15 second dwell time each in $5^{\circ}C\;and\;55^{\circ}C$ bath. The Vickers indentation pattern and the fracture surface were examined by an optical microscope and a scanning electron microscope (SEM). The results obtained were summarized as follows ; 1. Young's moduli(E) of the laminate porcelain and the resin cement used in this experiment were $62.56{\pm}3.79GPa$ and $15.01{\pm}0.12GPa$, respectively. 2. The initial crack size of the laminate porcelain was $69.19{\pm}5.94{\mu}m$ when an indentation load of 9.8N was applied, and the fracture toughness was $1.065{\pm}0.156MPa\;m^{1/2}$. 3. The fatigue life of laminate porcelain showed the constant fracture range at the stress level 27.46-35.30MPa. 4. When a cyclic flexure load was applied, the fatigue life of resin-bonded laminate porcelain was more decreased than that of laminate porcelain. 5. When a thermocycling was conducted, the crack growth rate of resin-bonded laminate porcelain was more increased than that of laminate porcelain. 6. Fracture surface showed the radial crack, the lateral crack, and the macroscopic crack branching region beneath the plastic deformation region when an indentation load of 9.8N was applied.

• 한국표면공학회지
• /
• 제49권6호
• /
• pp.560-566
• /
• 2016

In this study, porcelain bonding strength and mechanical properties of sintered Ni-Cr-Ti alloy for dental prosthodontics have been researched experimentally. Mechanical and morphological characteristics of the alloys were examined by Vickers hardness test, tensile and bonding strength test, surface roughness test, field-emission scanning electron microscopy, energy dispersive X-ray spectroscopy, and X-ray diffraction. In the sintered Ni-13Cr-xTi alloys, morphology of sintered alloy showed porous matrix diffused with alloying elements of Cr and Ti, and showed dendritic structure after melting process. From the XRD results, the second phases of NiCr, $Ni_3Cr$, and $Ni_3Ti$ were formed in the case of sintered and melted Ni-13Cr-xTi alloys. The tensile strength and hardness of Ni-13Cr-xTi alloys increased, as Ti content increased. Surface roughness increased, as Ti content increased. The bonding strength between metal and porcelain of Ni-13Cr-5Ti alloy was higher than those of Ni-13Cr and Ni-13Cr-10Ti alloys

• 보존과학회지
• /
• 제35권1호
• /
• pp.33-40
• /
• 2019

During the conservation and maintenance of the birthplace center yard of President Asan Yoon Bosun, four porcelain enamel dishware were excavated from the central yard well. The glaze layer of excavated enamel was severely damaged; hence, the conservation process was done rapidly. In addition, scientific investigation and analysis were conducted to confirm the material properties of the glaze layer. It was confirmed that the outer surface was inverted and dried, while the inner surface was upright and fired during the glazing and drying process by measuring the film thickness. By examining the breakup phenomenon, the breaking up of the white enamel on the colored enamel was confirmed. This indicates that the colored glaze rose to the surface depending on the density of the colored glaze and white glaze. The investigation of the cross-section of the film confirmed that the lower layer formed according to the bonding properties with metal during the glazing process. Analysis of the constituents of the identified lower layer confirmed that there are differences between the specific components of the metal oxide of the lower layer and the surface color development of the upper layer.

• 대한치과기공학회지
• /
• 제19권1호
• /
• pp.13-19
• /
• 1997

The purpose of this study was carried out by oberserving to composition of an oxide on the surface of Dental porcelain alloy according to the conditions of its heat treatment and analysing the change composition on its surface. Morphological change of the heat treated dental porcelain alloy have been investigated with SEM and EDX. The result of this study is summarized ad follows. The surface indium concentration of specimens increased as the heat treatment temperature and the oxygen partial pressure increased.

• 대한치과교정학회지
• /
• 제28권5호
• /
• pp.803-812
• /
• 1998

도재의 표면처리가 세라믹 브라켓의 전단 접착강도에 미치는 영향과 브라켓 탈락 양상을 알아보기 위해 60개의 ceradent 도재 시편을 glazing 후 군당 10개씩 여섯 군으로 다음과 같이 분류하였다: 1군(silane), 2군(etching+silane), 3군(stone+silane), 4군(sandblasting+silane), 5군(stone+etching+silane), 6군(sandblasting+etching+silane) 통상적인 방법으로 세라믹 브라켓을 접착한 후 전단 접착강도를 측정하고 탈락양상을 육안 및 주사전자현미경으로 관찰하여 다음과 같주 결론을 얻었다. 1. 표면처리 후 silane을 도포한 2군부터 6군은 silane만을 도포한 1군에 비해 유의성 있는 전단 접착강도의 증가를 보였다(P<0.05). 2. 한 가지 방법 이상으로 표면처리한 3군부터 6군은 서로 유의한 차이를 보이지 않았다(P>0.05). 3. etching 표면 처리한 2군은 sandblasting 표면 처리한 4군과 복합 표면 처리한 5,6 군에 비해 전단 접착 강도가 낮았다. (p<0.05) 4. sandblasting 표면 처리한 4군은 주사 전자 현미경 소견상 복합 처리한 5,6군보다 감소된 요철 정도를 보였으나 전단접착 강도 측정 결과 유의한 차이를 보이지 않았다. (p>0.05) 이상의 결론을 종합해볼 때 도재에 세라믹 브라켓을 접착하기 위해서는 한가지 이상의 방법에 의한 도재의 표면처리 후 silane을 도포해야 임상적으로 적절한 접착강도를 얻을 수 있으며, 술식의 간편성을 고려할 때 sandblasting 후 silane 처리를 하는 것이 효율적일 것으로 사료된다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.332-332
• /
• 2012

All-ceramic prostheses are widely used to fulfill the high esthetic demand. However, bonding failure between zirconia and porcelain is one of the all-ceramic prostheses failures. In order to improve clinical sucess of all-ceramic prostheses, laboratory or in-office surface conditioning techniques on zirconia have been studied.

• 대한치과보철학회지
• /
• 제45권5호
• /
• pp.589-600
• /
• 2007

Statement of Problem: Titanium has many advantages of high biocompatibility, physical porperties, low-weight, low price and radiolucency, but it is incompatible with conventional dental porcelain due to titanium's oxidative nature. Many previous studies have shown that they used the method of sandblast surface treatment prior to porcelain application, the researchs are processing about the method of acid etching or surface coating. Purpose: The purpose of this research is to study the effect on bond strength between titanium and porcelain when using macro-surface treatment and micro-surface treatment and macro and micro surface treatment. Material and method: In this study, we evaluated the bond strength by using 3-point bending test based on ISO 9693 after classified 7 groups-group P : polished with #1200 grit SiC paper, group SS : sandblasted with $50{\mu}m$ aluminum oxides, group LS : sandblasted with $250{\mu}m$ alumium oxides, group HC : treated with 10% hydrochloric acid, group NF : treated with 17% solution of fluoric acid and nitric acid, group SHC : treated with 10% hydrochloric aicd after sandblsting with $50{\mu}m$ alumium oxides, group SNF treated with 17% solution of fluoric acid and nitric acid. Results : Within the confines of our research, the following results can be deduced. 1. Group SS which was sandblasted with $50{\mu}m$ aluminum oxides showed the highest bond strength of 61.74 MPa and significant differences(P<0.05). The bond strengths with porcelain in groups treated acid etching after sandblasting decreased more preferable than the group treated with sandblasting only. It gives significant differences(P<0.05). 2. After surface treatments, the group treated with sandblasting showed irregular aspect formed many undercuts, in the SEM photographs. The group treated with hydrochloric acid had the sharp serrated surfaces, the group treated with the solution of fluoric acid and nitric acid had the smooth surfaces, the group with sandblasting and hydrochloric acid had irrigular and porous structure, the group with sandblasting and the solution of fluoric acid and nitric acid had crater-like surfaces. But all of the groups treated with acid etching was not found and undercut. Conclusion: In above results, average surface roughness increase, bond strength also increase, but surface topographs influences more greatly on bond strengths.

• 대한치과보철학회지
• /
• 제30권1호
• /
• pp.85-91
• /
• 1992

The purpose of this study was to evaluate the bonding strength between porcelain laminate and Ni-Cr alloy in the various surface treatments of the bonding faces. For this study the metal surface of specimens were treated : 1) etching only, 2) sandblasting only, and 3) sandblasting and etching. The porcelain laminate were made and bonded to the metal specimens with light curing composite resin cement. Instron testing machine was used to measure their bonding strength : and the result was obtained as follows : 1. The bonding strength of the double treatment of the sandblasting and etching group was higher than that of the single treatment of sandblasting or the etching group. 2. The bonding strength of the sand blasting group was higher than that of the etching group. 3. The debonding were mainly occurred between the Ni-Cr alloy and the composite resin cement.

• 대한치과보철학회지
• /
• 제45권2호
• /
• pp.169-181
• /
• 2007

Statement of problem: Titanium is well known as a proper metal for the dental restorations, because it has an excellent biocompatibility, resistance to corrosion, and mechanical property. However, adhesion between titanium and dental porcelains is related to the diffusion of oxygen to the reaction layers formed on cast-titanium surfaces during porcelain firing and those oxidized layers make the adhesion difficult to be formed. Many studies using mechanical, chemical and physical methods to enhance the titanium-ceramic adhesion have been actively performed. Purpose: This study meant to comparatively analyse the adhesion characteristics depending on different titanium surface coatings after coating the casts and wrought titanium surfaces with Au and TiN. Material and method: In this study, the titanium specimens (CP-Ti, Grade 2, Kobe still Co. Japan) were categorized into cast and wrought titanium. The wrought titanium was cast by using the MgO-based investment(Selevest CB, Selec). The cast and wrought titanium were treated with Au coating($ParaOne^{(R)}$., Gold Ion Sputter, Model PS-1200) and TiN coating(ATEC system, Korea) and the ultra low fusing dental porcelain was fused and fired onto the samples. Biaxial flection test was done on the fired samples and the porcelain was separated. The adhesion characteristics of porcelain and titanium after firing and the specimen surfaces before and after the porcelain fracture test were observed with SEM. The atomic percent of Si on all sample surfaces was comparatively analysed by EDS. In addition, the constituents of specimen surface layers after the porcelain fracture and the formed compound were evaluated by X-ray diffraction diagnosis. Result: The results of this study were obtained as follows : 1. The surface characteristics of cast and wrought titanium after surface treatment(Au, TiN, $Al_2O_3$ sandblasting) were similar and each cast and wrought titanium showed similar bonding characteristics. 2. Before and after the biaxial flection test, the highest atomic weight change of Si component was found in $Al_2O_3$ sandblasted wrought titanium(28.6at.% $\rightarrow$ 8.3at.%). On the other hand, the least change was seen in Au-Pd-In alloy(24.5at.% $\rightarrow$ 9.1at.%). 3. Much amount of Si components was uniformly distributed in Au and TiN coated titanium, but less amount of Si's was unevenly dispersed on Al2O3 sandblasting surfaces. 4. In X-ray diffraction diagnosis after porcelain debonding, we could see $Au_2Ti$ compound and TiN coating layers on Au and TiN coated surfaces and $TiO_2$, typical oxide of titanium, on all titanium surfaces. 5. Debonding of porcelain on cast and wrought titanium surface after the biaxial flection is considered as a result of adhesion deterioration between coating layers and titanium surfaces. We found that there are both adhesive failure and cohesive failure at the same time. Conclusion: These results showed that the titanium-ceramic adhesion could be improved by coating cast and wrought titanium surfaces with Au and TiN when making porcelain fused to metal crowns. In order to use porcelain fused to titanium clinically, it is considered that coating technique to enhance the bonding strength between coating kKlayers and titanium surfaces should be developed first.

• The Journal of Advanced Prosthodontics
• /
• 제4권4호
• /
• pp.179-186
• /
• 2012

PURPOSE. The aim of this study was to evaluate the efficiency of manual polishing over autoglazed and overglazed porcelain and their effect on plaque accumulation. MATERIALS AND METHODS. Thirty-six porcelain discs were fabricated out of which 18 each was subjected for autoglazing and overglazing. Half surface of the discs was left intact; the remaining half was roughened with medium grit diamond bur. Roughened surfaces were repolished by porcelain polishing kits (Shofu, DFS, Eve). All the surfaces were evaluated by the perthometer and SEM. Six discs from each sample were placed in human volunteer's mouth for 72 hours to evaluate the plaque accumulation. Acquired data was subjected to ANOVA comparative evaluation. RESULTS. Roughened surfaces had average roughness value of $2.88{\pm}0.1935{\mu}m$. The repolished surfaces by porcelain correction kits Shofu, DFS and Eve, average roughness value reduced to $0.6250{\pm}0.1036$, $0.9192{\pm}0.0953$, $0.9017{\pm}0.1305$ respectively. Autoglazed and overglazed surfaces showed the mean roughness value (Ra) of $0.4217{\pm}0.0685$, $0.3450{\pm}0.0729$. SEM study showed the improved surfaces when subjected for polishing. Plaque accumulation percentage was the highest on roughened surface ($93.83{\pm}6.2552%$), followed by porcelain discs polished by commercial kits. Autoglazed surfaces found to be the best surfaces with the least plaque accumulation ($0.5237{\pm}0.4209%$). CONCLUSION. All the polishing kits used in the study reduced the average roughness by approximately 77%. Corrected porcelain surfaces should ideally be reglazed, alternatively, polish the surfaces before final cementation.