• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.802-805
• /
• 2000

Anistropic [Ta/NdFeB/Ta] thin film was sputtered on heated Si substrate by Nd$\_$17/Fe$\_$74/B$\_$9/ target. The grain size of the films increased according to the increase of substrate temperature, and the film deposited at 650$^{\circ}C$ showed optimum coercivity. 4$\pi$M$\_$r/, $\_$i/H$\_$c/ and (BH)$\_$max/ measured perpendicular to the film plane of thin film deposited at 650$^{\circ}C$ are 12.3 kG, 9.9 kOe and 37 MGOe, respectivly.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.100-103
• /
• 2001

In order to investigate the magnetic properties of CoCr-based bilayered thin films on kind of underlayer, we introduced amorphous Si layer to Co-Cr(-Ta) magnetic layer as underlayer. With the thickness of CoCr, CoCrTa single layer, crystalline orientation and perpendicular coercivity was improved. It was revealed that by introducing the Si underlayer, the c-axis orientation of CoCr, CoCrTa magnetic layer was improved largely. However, with increasing Si film thickness, perpendicular coercivity and saturation magnetization of Cocr/si, CoCrTa/Si bilayered thin films was decreased. Grain size of bilayered thin films became larger.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.492-495
• /
• 2000

In order to develop an ultra-thin CoCr perpendicular magnetic recording layer, we prepared CoCrTa/Ti double layer for perpendicular magnetic recording media by new facing targets sputtering system, Crystallgraphics and magnetic characteristics of CoCrTa on underlayer substrate temperature have been investigated. Crystallgraphic and magnetic characteristic of thin films were evaluated by X-ray diffractometry(XRD), vibrating sample magnetometer(VSM) and atomic force microscopy(AFM). The coercivity and anisotropy field was increased by increasing under layer substrate temperature, c-axis orientation of CoCrTa magnetic recording layer was improved 8$^{\circ}$ to 5.6$^{\circ}$when under layer substrate temperature was 250[$^{\circ}C$]. Also, through annealing effect for CoCrTa/Ti double layer, it was certain that crystallgraphics and magnetic characteristics was improved.

• Journal of the Korean institute of surface engineering
• /
• v.37 no.4
• /
• pp.196-199
• /
• 2004

Seedlayers with low surface energy which increases the density of nucleation sites in the initial growth region of the recording layer deposited on them was studied to reduce grain size in recording layer. The seedlayer with low surface energy was so effective to attain finer grain in magnetic upper-layers. The Ni-Fe-O intermediate layer with low surface energy was found to be effective in reduction of grain size as well as magnetic cluster size of Co-Cr-Ta-Pt recording layer. Furthermore, the reduction of grain size in Co-Cr-Ta-Pt recording layer on Ni-Fe-O intermediate layer with low surface energy led to decrease the noise level in the high recording density region.

• Journal of the Korean Magnetics Society
• /
• v.3 no.1
• /
• pp.41-47
• /
• 1993

Effects of Ta addition on Co-Cr pependicular magnetic recording media were studied to obtain high perpen-dicular coercivity at lower substrate temperature. For the purpose. magnetic properties and microstructures of Co-Cr-(Ta) films were studied by varying the Cr contents from 17 to 21 at.% and Ta contents for 0 to 3.2 at.%. Effectiveness of Ta addition in increasing perpendicular coercivity was significant for lower Cr content films. The increasement of perpendicular coercivity was more pronounced for the films deposited on $100^{\circ}C$ heated substrate in the case of ${(Co_{83}Cr_{17})}_{98.4}Ta_{1.6}$ composition. The cause of the increase of perpendicular coercivity was considered due to not the grain refinement effects and the improvement of c-axis alignments but increase of Ta and Cr segregation.

• Journal of the Korean Wood Science and Technology
• /
• v.18 no.2
• /
• pp.67-78
• /
• 1990

This study was performed to determine the characteristics of physical and mechanical properties of domestic wood based materials; plywood, particleboard, medium density fiberboard. Main items of tested properties were panel size, moisture content, water absorption, linear expansion and thickness swelling, glue bond shear strength, bending properties(stress at proportional limit, modulus of rupture. modulus of elasticity), tensile strength, screw holding strength, and internal bond as neccessary. the results were discussed mainly with Korean Standards. The obtained conclusions are as follows; 1. Length and width of 3mm thin plywood(3-ply) and 12mm thick plywood(7-ply) were satished with KS-standard, but thicknesses of these panels were not- passed tolerance limit except one of eight makers. 2. Length and width of particleboard and medium density fiberboard were greater than the tolerance limit value of KS standard, but the thicknesses of these panels were passed this value. 3. Moisture contents of 12mm thick and 3mm thin plywood were satisfied with KS-standard except one mill made 3mm thin plywood. 4. Moisture absortion of plywood was not passed tolerance limit of KS-standard but particleboard was satisfied with this standard value. 5. Dry and wet shear strengths in glue bond of 3mm thin plywood were not reached to KS-standard, but those of 12mm thick plywood were sufficiently satisfied with KS standrad. 6. Modulus of ruptures, parallel to grain and perpendicular to grain of plywood, and particleboard and medium density fiberboard were satisfied with KS-standard. 7. Tensile strengths, parallel to grain and perpendicular to grain of plywood were satisfied with allowance stress of US product standard PS 1-74. 8. Screw holding strength of particleboard was not reached to KS standard, but internal bond was satisfied with KS standard.

• Korean Journal of Materials Research
• /
• v.4 no.4
• /
• pp.439-444
• /
• 1994

The influence of the direction of applied compressive stress on degradation mechanism ofpoled PZT sample was studied. When compressive stress perpendicular to poling direction was appliedon poled PZT sample, the degradation phenomena was explained by the diffusion of space chargepolarization. On the contrary, compressive stress parallel to poling direction was applied, it wasexplained by the rearrangement of 90" domains. As the grain size increased, the degradation phenomenawas promoted. It is attributed to different internal stress due to difference of grain size. of grain size.

• Korean Journal of Materials Research
• /
• v.4 no.5
• /
• pp.581-589
• /
• 1994

Magnetic properties and microstructures of the $Co_{83}Cr_{17}$ films growing under the applied magnetic field were studied. In comparison, those of the films growing without magnetic field were also studied. Magnetic field does not affect saturation magnetization and in-plane coercivity of the films. On the contrary perpendicular coercivity and effective perpendicular anisotropy field decreased. Grain size and the thickness of the so-called transition layer were not affected and the C-axis alignment of the films was slightly deteriorated due to magnetic field. Also, microstructures of the sputtered films showed larger grain sizes of strong (002) preferred orientation for thicker film specimens independent of applied magnetic field.

• Journal of the Korean Magnetics Society
• /
• v.9 no.5
• /
• pp.256-262
• /
• 1999

Sputter deposited CoCr(Mo)/Si film were studied with emphasis on the correlation between magnetic properties and crystallographic orientation. The perpendicular coercivities of CoCr films decreased with Si underlayer thickness, whereas those of CoCrMo films increased with Si underlayer thickness. It has been explained that additions of the larger atomic radius Mo atoms in CoCr films impedes crystal growth resulting in a decrease in grain size, thus this small grain size may induce high perpendicular coercivity. The c-axis alignment of CoCrMo film was improved due to addition of 2at.%Mo. It means CoCrMo layer grow self-epitaxial directly from orientation and structure of Si underlayer when the main layer grow on underlayer.

• Korean Journal of Materials Research
• /
• v.20 no.1
• /
• pp.37-41
• /
• 2010

Creep tests were conducted under a condition of constant stress on two aluminum-based alloys containing particles: Al-5% Mg-0.25% Fe and Al-5% Zn-0.22% Fe. The role of grain boundary sliding was examined in the plane of the surface using a square grid printed on the surface by carbon deposition and perpendicular to the surface using two-beam interferometry. Estimates of the contribution of grain boundary sliding to the total strain, $\varepsilon_{gbs}/\varepsilon_t$ reveal two trends; (i) the sliding contribution is consistently higher in the Al-Mg-Fe alloy, and (ii) the sliding contribution is essentially independent of strain in the Al-Mg-Fe alloy, but it shows a significant decrease with increasing strain in the Al-Zn-Fe alloy. Sliding is inhibited by the presence of particles and its contributions to the total strain are low. This inhibition is attributed to the interaction between the grain boundary dislocations responsible for sliding and particles in the boundaries.