• Advances in materials Research
• /
• v.8 no.1
• /
• pp.1-10
• /
• 2019

Roll bonding (RB) process of bi-metal laminates as a new noble method of bonding has been widely used in the production of bimetal laminates. In the present study, asymmetric roll bonding process as a new noble method has been presented to produce Al/Cu bimetallic laminates with the thickness reduction ratios 10%, 20% and 30% together with mismatch rolling diameter ($\frac{R_2}{R_1}$) ratio 1:1, 1:1.1 and 1:1.2. ABAQUS as a finite element simulation software was used to model the deformation of samples. The main attention in this study focuses on the bonding properties of Al/Cu samples. The effect of the $\frac{R_2}{R_1}$ ratios was investigated to improve the bond strength. During the simulation, for samples produced with $\frac{R_2}{R_1}=1:1.2$, the vertical plastic strain of samples was reach the maximum value with a high quality bond. Moreover, the peeling surface of samples after the peeling test was investigated by the scanning electron microscopy (SEM).

• Structural Engineering and Mechanics
• /
• v.9 no.5
• /
• pp.491-504
• /
• 2000

A convenient method for enhancing the strength and stiffness of existing reinforced concrete beams is to bond adhesively steel plates to their tension faces. However, there is a limit to the applicability of tension face plating as the tension face plates are prone to premature debonding and, furthermore, the addition of the plate reduces the ductility of the beam. An alternative approach to tension face plating is to bond adhesively steel plates to the sides of reinforced concrete beams, as side plates are less prone to debonding and can allow the beam to remain ductile. Debonding at the ends of the side plates due to flexural forces, that is flexural peeling, is studied in this paper. A fundamental mathematical model for flexural peeling is developed, which is calibrated experimentally to produce design rules for preventing premature debonding of the plate-ends due to flexural forces. In the companion paper, the effect of shear forces on flexural peeling is quantified to produce design rules that are applied to the strengthening and stiffening of continuous reinforced concrete beams.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.2 no.3
• /
• pp.205-211
• /
• 1998

The purpose of this study is to evaluate shear strengthening effects of R/C beams with carbon fiber sheets. The major variables are shear reinforcement ratios, CFS strengthening ratios and strengthening methods of CFS. Following conclusions can be extracted. The shear capacity of beam strengthened with CFS is about 32~87% higher than that of beams without shear reinforcement. The strengthening effects of patch type is larger than those of strip type. The strain distribution in CFS intersected with shear crack is similar to that in stirrup and larger strain is observed in the middle of the shear span. It can be estimated that shear strength reduction factor ${\alpha}$=0.3 is appropriate for peeling effect of CFS.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.2 no.2
• /
• pp.195-201
• /
• 1998

The purpose of this study is to evaluate the flexural strengthening effects of RC beams reinforced with carbon fiber sheets (CFS) in variable of strengthening amount and anchorage length of CFS. This study can be summarized as follows ; The CFS shares the tensile stress such as rebar during loading test. Also, as the strengthening amount of CFS is increased, the maximum flexural strength of RC beams reinforced with CFS is increased. Therefore, it is confirmed that the CFS's strengthening method is very effective to improve the flexural strength of RC beams. The maximum flexural strength of RC beams with CFS is determined by bond failure between CFS and concrete surface. So, the evaluation of CFS's strengthening effect can be calculated using the tensile stress of CFS which is peeling. When the anchorage length of CFS is increased, the ductility of RC beams is increased because of delaying the peeling of CFS. But, in case of same anchorage length of CFS, when the strengthening amount of CFS is increased, the ductility is decreased. Therefore, it is considered that the anchorage of CFS in the end zone is necessary.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2008.10a
• /
• pp.103-104
• /
• 2008

Radio-frequency(RF) weldable polyurethane-coated fabric was prepared by knife coating of presetted and cire-finished nylon fabric using optimized coating formulation including RF-sensitive commercial polyurethane resins. The physical properties, adhesion strength, peeling strength, abrasion strength, flexibility, and hydrostatic water resistance of the prepared coated fabric were good enough to show no significant difference with regular coating. Additionally the prepared coated fabric had silky and soft touch without tackiness.

• Journal of Fashion Business
• /
• v.23 no.2
• /
• pp.77-88
• /
• 2019

One way of appling 3D printing to garments is through the combination of 3D polymer filaments in textile fabrics. it is essential to understand the interface between the polymer and the 3D composite fabric in order to enhance the adhesion strength between the polymers and the peeling strength between the fabric and the polymer. In this study, the adhesion of composite printed specimens using a combination of fabric and polymers for 3D printing was investigated, and also the change in adhesion was investigated after the composite fabric printed with polymers was subjected to constant pressure. Through this process, the aims to help develop and utilize 3D printing textures by providing basic data to enhance durability of 3D printing composite fabrics. The measure of the peeling strength of the composite fabric prepared by printing on a fabric using PLA, TPU, Nylon polymer was obtained as follows; TPU polymer for 3D printing showed significantly higher peel strength than polymers of composite fabric using PLA and Nylon polymer. In the case of TPU polymer, the adhesive was crosslinked because of the reaction between polyurethane and water on the surface of the fabric, thus increasing the adhesion. It could be observed that the adhesion between the polymer and the fiber is determined more by the mechanical effect rather than by its chemical composition. To achieve efficient bonding of the fibers, it is possible to modify the fiber surface mechanically and chemically, and consider the deposition process in terms of temperature, pressure and build density.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.3
• /
• pp.23-26
• /
• 2006

For mechanical and electrical stability and environment protection. Cu and stainless steel stabilizers are laminated to a Ag layer to produce a composite neutral-axis(N-A) architecture in which the YBCO layer is centered between the oxide buffered metallic substrate and stabilizer strip lamination. This architecture allows the wire to meet operational requirements including stresses at cryogenic temperature. winding tensions as well as mechanical bending requirements including thermal and electrical stability under fault current conditions. We have experimentally studied mechanical properties of the laminated stainless steel and Cu stabilizers on YBCO coated conductors. We have laminated YBCO coated conductors by continuous dipping soldering process. We have investigated lamination interface between solder and stabilizer of the YBCO coated conductor. We evaluated bonding properties. tensile / shear bonding strength. and peeling strength laminated YBCO coated conductors.

• Journal of the Korean Wood Science and Technology
• /
• v.31 no.3
• /
• pp.61-69
• /
• 2003

This study investigated the effect of moisture content and loading direction on dowel bearing strength of two types of SCL. Dowel bearing tests of LVL and PSL were conducted with two different MC level, 7.5% and 19%, and two different oriention, L-direction(loading parallel to grain) and X-direction(loading perpendicular to grain). Most of specimens showed typical load-deformation curves and intersected 5% offset line. Failure modes were classified into two categories; spliting(for L-direction specimens) and peeling(for X-direction specimens). Dowel bearing strength generally decreased with increasing MC. The decreasing rate was more significant in X-directon. ESG also decreased with increasing MC, and the ratio of ESG of 7.5% versus 19% was about 1.47. Dowel bearing strength of LVL and PSL in L-direction was higher than that of X-direction. This results indicated that MC and loading orientation had a significant effect on dowel bearing strength of SCL. The average dowel bearing strength of LVL were higher than that of PSL in each loading direction. Two types of probability distribution model were chosen to quantify strength distribution, normal and 2-parameter weibull distribution. The two models showed good agreement with the data, especially in lower tail of the cumulative distribution. Normal and 2-parameter weibull distribution seemed to proper model of the dowel bearing strength for each MC levels.

• The Korean Journal of Ceramics
• /
• v.3 no.2
• /
• pp.105-109
• /
• 1997

The effects of surface conditions of the C-2 cemented carbide substrate on the adhesion of diamond film were investigated. The substrates were pretreated for different times with Murakami's reagent and then the acid solution of an H2SO4-H2O2. The adhesion strength was estimated by a peeling area around the Rockwell-A indentation. The cutting performance of the diamond-coated tools was evaluated by measuring flank wears in dry turning of Al-17% Si alloy. The morphology of deposited diamond crystallites was dominated by (111) and (220) surfaces with a cubooctahedral shape. The diamond film quality was hardly affected by the surface conditions of the substrate. The variation of tool life with longer substrate etching times resulted from a compromies between the increase of film adhesion at the interface and the decrease of toughness at the substrate surface. The coated tools were mainly deteriorated by chipping and flaking of the diamond film form a lock of adhesion strength, differently from the wear phenomena of PCD tools.

• Textile Coloration and Finishing
• /
• v.7 no.1
• /
• pp.23-31
• /
• 1995

Changes of the properties of waterproof and moisture-permeable nylon fabric were investigated when softener, anti-static agents, anti-biosis agents were added to the polyurethane resin solution, and when they were applied after resin coating. The adding method of finishing agents into polyurethane layer resulted in an increase in water permeability but a severe decrease in peeling strength. It was found that the desired functionality such as softness, anti-staticity, anti-biosis were successfully introduced into waterproof and moisture-permeable nylon fabric by after-treatment of finishing agents.