• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.29 no.12 s.243
• /
• pp.1329-1334
• /
• 2005

Synthesis of silver nanoparticles by the supersonic nozzle expansion method with corona discharge ions was investigated. Corona discharge ions functioned as seeds for heterogeneous nucleation in the silver nanoparticles formation process and provided silver nanoparticles with electronic repulsive force that prevents aggregation of the particles. For ion ejecting, we used sonic-jet corona discharger. Upon application of the corona discharge ions, the mean diameter of the produced particles was decreased from 12.54 to 6.22nm and the standard deviation was decreased from 5.02 to 3.34nm. In addition, the agglomeration of silver nanoparticles was reduced.

• Journal of Powder Materials
• /
• v.13 no.6 s.59
• /
• pp.432-438
• /
• 2006

Aluminum nitride (AlN) nanopowders with low degree of agglomeration and uniform particle size were synthesized by carbothermal reduction of alumina and subsequent direct nitridization. Boehmite powder was homogeneously admixed with carbon black nanopowders by ball milling. The powder mixture was treated under ammonia atmosphere to synthesize AlN powder at lour temperature. The effect of process variables such as boehmite/carbon black powder ratio, reaction temperature and reaction time on the synthesis of AlN nanopowder was investigated.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1999.11a
• /
• pp.42-48
• /
• 1999

An experimental study was performed to discover the effect of environment on the tribological behavior of Si-incorporated diamond-like carbon(Si-DLC) film slid on a steel ball. The films were deposited on Si(100) wafers from radio-frequency glow discharge of mixtures of benzene and dilute silane gases. Experiments using a ball-on-disk test-rig was performed under vacuum, dry air and ambient air conditions. It was observed that coefficient of friction was decreased as the environmental condition changes from vacuum, to dry air. It was also observed that the coefficient of friction decreased with increasing silicon concentration in the film. Chemical analyses of debris suggested that the low and stable friction coefficient is closely related to the silicon rich oxide debris and the rolling action.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.7
• /
• pp.49-54
• /
• 2010

The cryogenic ball milling was performed on carbon nanotubes (CNTs) at an extremely low temperature to increase the dispersion of CNTs. The effects of milling speed and time on the deagglomeration and structural changes of CNTs were studied. FESEM was used to analyze the dispersion and the change of particle size before and after milling process. Transmission electron microscopic (TEM) analysis was also investigated the effect of cryogenic ball milling on the morphological characteristics of CNTs. The structural changes by the cryogenic ball milling process were further confirmed by x-ray diffraction (XRD) and Raman spectroscopic analysis. The results showed that the agglomeration of CNTs was significantly reduced and amorphous structure was observed at high milling speed. However, the milling time has no great effect on the dispersion property and structural change of CNTs compared with milling speed.

• Journal of the Korean Ceramic Society
• /
• v.35 no.6
• /
• pp.529-534
• /
• 1998

Agglomeration-free indium oxide particles were produced by ultrasonic pyrolysis of indium nitrate(3 hy-drate) solution. Th mean size of particles was increased from 3 $\mu\textrm{m}$ to 11$\mu\textrm{m}$ with increasing intial con-centrations of indium nitrate from 0.05mol% to 4.83 mol% When the input rate of indium nitrate solution was increased from 0.1 cm3/min to 0.8cm3/min the size of particles remained same and only the pro-duction rate of particles was increased. At 300$^{\circ}C$ the particles were white color with low crystallinity. But the color turned into yellow with increasing reaction temperature. The change of particle size was not ob-served with increasing temperatuer up to 700$^{\circ}C$ IR spectrum and TGA analysis confirmed that the purity of indium oxide was increased with temperature of reaction.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.442-446
• /
• 1999

Melting behavior and bridge phenomenon of solder paste, which is essential for surface mount technology in packaging, were investigated. solder paste of Sn-37%Pb was printed on Sn-coated Cu-pattern of PCB, and heated over melting point. Melting behavior of the paste was observed using CCD-camera. In order to modelize the melting and agglomeration phenomena of the paste, two solder balls of 0.76mm diameter were used. As experimental results, the paste start to melt from the margin of the printed shape. The hight of the melted paste decreased from 270 $\mu$m to 200 $\mu$m firstly, and finally recovered to 250 $\mu$m. During the melting procedure, pores were evolved from the molten paste. Bridge Phenomenon of the molten Paste depends upon the pitch of the pattern.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.264-265
• /
• 2006

The directions of further developments in the modeling of sintering are pointed out, including multi-scale modeling of sintering, on-line sintering damage criteria, particle agglomeration, sintering with phase transformations. A true multi-scale approach is applied for the development of a new meso-macro methodology for modeling of sintering. The developed macroscopic level computational framework envelopes the mesoscopic simulators. No closed forms of constitutive relationships are assumed for the parameters of the material. The model framework is able to predict the final dimensions of the sintered specimen on a global scale and identify the granular structure in any localized area for prediction of the material properties.

• Tribology and Lubricants
• /
• v.16 no.3
• /
• pp.188-193
• /
• 2000

An experimental study was performed to discover the effect of environment on the tribological behavior of Si-incorporated diamond-like carbon(Si-DLC) film slid on a steel ball. The films were deposited on Si(100) wafers by a radio-frequency glow discharge of mixtures of benzene and dilute silane gases. Experiments using a ball-on-disk test-rig was performed in vacuum, dry air and ambient air conditions. It was observed that coefficient of friction decreased as the environment changed from vacuum, to dry air. Chemical analyses of debris suggested that low and stable friction is closely related to the formation of silicon-rich oxide debris and the rolling action.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.11
• /
• pp.537-543
• /
• 2019

Alumina(Al₂O₃) is a ceramic material used in industry with a range of particle sizes and characteristics. In this study, a boehmite sol was prepared by a hydrolysis and peptizing process using the Sol-Gel method from aluminum isopropoxide (AIP). γ-Al₂O₃ was prepared by drying and calcining. To prevent particle agglomeration during the manufacturing process, four kinds of polyvinyl alcohol (PVA) with molecular weights of 9,000~10,000, 31,000~50,000, 89,000~98,000, and 130,000 were added and three concentrations of HNO₃ (0.1, 0.3, 0.5 molar ratio) were added to determine their effects on the particles. The crystal structure, composition, particle size and shape of the prepared γ-Al₂O₃ were confirmed through x-ray diffraction (XRD), x-ray fluorescence analyzer (XRF), particle size analyzer (PSA), and field emission scanning electron microscopy (FE-SEM). As a result, γ-Al₂O₃ with a purity of approximately 98.2% was synthesized, and the particle size decreased and the uniformity increased with increasing ratio of HNO₃ addition and PVA molecular weight. From these results, the particle size can be controlled during the manufacturing process of γ-Al₂O₃ by controlling the addition ratio of PVA and HNO₃.

• Applied Chemistry for Engineering
• /
• v.16 no.4
• /
• pp.549-555
• /
• 2005

To evaluate the posterior and anterior restoration of polymeric dental restorative composite (PDRC), PDRC was prepared using a silica filler treated by heat at various temperatures. Compressive strength (CS) and diametral tensile strength (DTS) values were investigated to study the effect of a heat-treated silica on the mechanical properties of PDRC using the recommended dental specifications. Both the particle size and specific volume of silica were decreased upon increasing the heat treatment temperature. CS and DTS values of PDRC containing a heat-treated silica showed 1.2 and 1.3 times, respectively, higher than that of the PDRC containing a neat silica. Also, it was found that the lower heat treatment temperature, the better mechanical properties of PDRC were observed because there was less agglomeration between silica particles. Specially, PDRC using a silica treated at $600^{\circ}C$ showed superior mechanical strength.