• Journal of the Korean Chemical Society
• /
• v.29 no.6
• /
• pp.608-614
• /
• 1985

Electrical conductivities of $ZrO_2-Sm_2O_3$ systems containing 10, 20, 30, 40, and 50 mol% of $ZrO_2$ have been measured as a function of temperature and of oxygen partial pressure at temperature from 500 to 1000${\circ}C$ and oxygen partial pressures from 1 ${\times}10^{-5}to 1{\times}10^{-1}$ atm. Plots of log conductivity vs. 1/T are found to be linear with an inflection point at around 650$^{\circ}C$ and the temperature dependence of conductivity shows two different defect structures. The conductivities are increased with increasing pressure, slowing a p-type character. The electrical conductivity dependences on $Po_2$ are found to be ${\sigma}{\propto}Po_2^{1/5.3}$ at 650∼1000$^{\circ}C$ and ${\sigma}{\propto}Po_2^{1/6}$ at 500∼650$^{\circ}C$, respectively, The defect structures are Oi" at 650-1000$^{\circ}C$ and $Vs_m$"' at 500-650$^{\circ}C$. The electron hole is main carrier type, however ionic contribution is found at low temperature portion. Ionic contributions increased with the increasing amount of $ZrO_2$ dopant. In 60mol% $ZrO_2-Sm_2O_3$ system, the conductivity is increased with decreasing oxygen pressure.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.1
• /
• pp.32-43
• /
• 1996

A $CdIn_{2}Te_{4}$ single crystal was grown by modified veritical bridgman method. The $CdIn_{2}Te_{4}$ single crystal was evaluated to be tetragonal by the powder method. The $CdIn_{2}Te_{4}$ single crystal was confirmed to be grown with its c axis along the lengthe of the boule by the Laue reflection method. Hall effect of $CdIn_{2}Te_{4}$ single crystal was estimated by van der pauw method from 293 K to 30 K. Hall data of the sample perpendicular to c axis was $n=8.75{\times}10^{23}electrons/m^{3},\;R_{H}=7.14{\times}10^{-5}m^{3}/C,\;{\sigma}=176.40{\omega}^{-1}m^{-1},\;{$\mu}=3.41{\times}10^{-2}m^{2}/V.s$ and the sample parallel to c axis was $n=8.61{\times}10^{23}electrons/m^{3},\;R_{H}=7.26{\times}10^{-5}m^{3}/C,\;{\sigma}=333.38{\omega}^{-1}m^{-1}\;and\;{$\mu}=2.42{\times}10^{-2}m^{2}/V.s$ for room temperature. The value of Hall coefficient on sample perpendicular or parallel to c axis were positive. There $CdIn_{2}Te_{4}$ single crystal was p-type semiconductor.

• Korean Journal of Crystallography
• /
• v.7 no.1
• /
• pp.44-56
• /
• 1996

CuInTe2 synthesised in a horizontal electric furnace was found to be polycrystalline. Single crystals of CuInTe2 were grown with the vertical Bridgman technique. The structure, Hall effect of the crystals were measured in the temperature range 30 to 293K. Both the polycrystals and single crystals of CuInTe2 were tetragonal in structure. The lattice constants of the polycrytals were measured as a=6.168Å and c=12.499Å, with c/a=2.026, these of the single crystals were measured as a=6.186Å and c=12.453Å, with c/a=2.013. The growth plane of the oriented single crystals was confirmed to be a (112) plane from the back-reflection Laue patterns. The Hall effect of the CuInTe2 single crystals was measured with the method of van der Pauw The Hall data of the samples measured at room temperature showed a carrier concentration of 2.14×1023holes/m3, a conductivity of 739.58Ω-1m-1, and a mobility of 2.16×10 -2m 2/V·s for the sample perpendicular to the c-axis. Values of 1.51×1023holes/m3, 717.55Ω-1m-1, and 2.97×10-2 m2/V·s were obtained for the sample parallel to the c-axis. The Hall coefficients for the samples both perpendicular and parallel to the c-axis in the temperature range 30K to 293K were always positive values. Thus the CuInTe2 single crystal was determined to be a p-type semiconductor.

• Journal of the Korean Vacuum Society
• /
• v.20 no.2
• /
• pp.135-140
• /
• 2011

By investigating photoluminescence (PL) spectra (20 K) of undoped and Be-doped p-type GaSb/GaAs epilayers, the origin has been analyzed by the change due to doping density. We have observed that the PL peak shifts to higher energy and the full-width half-maximum (FWHM) decreases with increasing the doping density below ${\sim}10^{17}cm^{-3}$, contrasted to shift to low energy and increasing FWHM above the density of ${\sim}10^{17}cm^{-3}$. From the variation of the integrated PL intensities of three peaks dissolved by Gaussian fit, it has been analyzed that, as the density increases, the $Be[Be_{Ga}]$ acceptor level (0.794 eV) reduces, whereas the intrinsic defect of $A[Ga_{Sb}]$ (0.778 eV) enhances together with a new $Be^*$ level (0.787 eV) locating between A and Be. We have discussed that it is due to coexistence of the Be acceptor level (${\Delta}E=16meV$) and the complex level (${\Delta}E=23meV$), $Be^*[Ga_{Sb}-Be_{Ga}]$combined by Be and A, in Be-doped p-GaSb, and that the level density of $Be[Be_{Ga}]$ may be reduced above ${\sim}10^{17}cm^{-3}$.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.2
• /
• pp.43-48
• /
• 2017

Conductive $Sn_xO_y$ thin films were fabricated via RF reactive sputtering using SnO:Sn (80:20 mol%) composite target. The composite target was used to produce a chemically stable composition of $Sn_xO_y$ thin film while controlling structural defects by chemical reaction between tin and oxygen. During sputtering pressure, RF power, and substrate temperature were fixed, and oxygen partial pressure was varied from 0% to 12%. Annealing process was carried out at $300^{\circ}C$ for 1 hour in vacuum. Except $P_{O2}=0%$ sample, all samples showed the transmittance of 80~90% and amorphous phase before and after annealing. Electrically stable p-type $Sn_xO_y$ thin film with high transmittance was only obtained from the oxygen partial pressure at 12%. The carrier concentration and mobility for the $P_{O2}=12%$ were $6.36{\times}10^{18}cm^{-3}$ and $1.02cm^2V^{-1}s^{-1}$ respectively after annealing.

• Journal of Sensor Science and Technology
• /
• v.8 no.3
• /
• pp.283-290
• /
• 1999

The $n^+/p/p^+$ junction PERL solar cell of $0.1{\sim}2{\Omega}{\cdot}cm$ (100) p type silicon wafer was fabricated through the following steps; that is, wafer cutting, inverted pyramidally textured surfaces etching by KOH, phosphorus and boron diffusion, anti-reflection coating, grid formation and contact annealing. At this time, the optical characteristics of device surface and the efficiency of doping concentration for resistivity were investigated. And diffusion depth and doping concentration for n+ doping were simulated by silvaco program. Then their results were compared with measured results. Under the illumination of AM (air mass)1.5, $100\;mW/cm^2$ $I_{sc}$, $V_{oc}$, fill factor and the conversion efficiency were 43mA, 0.6 V, 0.62. and 16% respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.73-73
• /
• 2000

안티퓨즈 소자는 프로그램 가능한 절연층의 상하 각각에 금속층이나 다결정 실리콘 등의 전도 가능한 전극으로 구성된다. 프로그램은 상하 전극간에 임계전압을 가했을 때 일어나게 되며 이때 절연층이 파괴되므로 비가역적이어서 재사용은 불가능하게 된다. 안티퓨즈 소자는 이러한 프로그램 특성으로 인하여 메모리 소자를 이용한 스위치 보다 속도나 집적도 면에서 우수하다. FPGAsdp 사용되는 안티퓨즈 소자는 집적도의 향상과 적정 절열파괴전압 구현을 위해 절연막의 두께를 감소시키는 것이 바람직하다. 그러나 두께나 감소될 경우 바닥전극의 hillock에 큰 영향을 받게 되며, 그로 인해 절연막의 두께를 감소시키는 것는 한계가 있는 것으로 보고되어 있다. 본 논문에서는 낮은 구동 전압에서 동작하고 안정된 on/pff 상태를 갖는 Al/TiO2-SiO2/Mo 형태의 안티퓨즈 소자를 제안하였다. 만들어진 antifuse cell은 0.6cm2 크기로 약 300개의 샘플을 제작하여 측정하였다. 비저항이 6-9 $\Omega$-cm인 P형의 실리콘 웨이퍼에 RF 마그네트론 스퍼터링(RF magnetron sputtering) 방법으로 하부전극인 Mo를 3000 증착하였다. SiO2는 안티퓨즈에서 완충막의 역할을 하며 구조적으로 antifuse cell을 완전히 감싸고 있는 형태로 제작되었다. 완충막 구조를 만들기 dln해 일반적인 포토리소그라피(Photo-lithography)작업을 거처 형성하였다. 형성된 hole의 크기는 5$mu extrm{m}$$\times$5$\mu\textrm{m}$ 이었다. 완충막이 형성된 기판위에 안티퓨즈 절연체인 SiO2를 PECVD 방식으로 100 증착하였다. 그 후 이중 절연막을 형성시키기 위해 LPCVD를 이용하여 TiO2를 150 증착시켰다. 상부 전극은 thermal evaporation 방식으로 Al을 250nm 증착하여Tejk. 하부전극으로 사용된 Mo 금속은 표면상태가 부드럽고 녹는점이 높은 매우 안정된 금속으로, 표면위에 제조된 SiO2의 특성을 매우 안정되게 유지시켰다. 제안된 안티푸즈는 이중절연막을 증착함으로서 전체적인 절연막의 두께를 증가시켜 바닥전극의 hillock의 영향을 적게 받아 안정성을 유지할 수 있도록 하였다. 또한, 두 절연막 사이의 계면 반응에 의해 SiO2 막을 약화시켜 절연막의 두께가 두꺼워졌음에도 기존의 SiO2 절연막의 절연 파괴 전압 및 누설 전류오 비교되는 특성을 가졌다. 이중막을 구성하고 있는 안티퓨즈의 ON-저항이 단일막과 비교해 비슷한 것을 볼 수 잇는데, 그 이유는 TiO2에 포함된 Ti가 필라멘트에 포함되어 있어 필라멘트의 저항을 감소시켰기 때문으로 사료된다. 결국 이중막을 구성시 ON-저항 증가에 의한 속도 저하 요인은 없다고 할 수 있다. 5V의 절연파괴 시간을 측정한느 TDDB 테스트 결과 1.1$\times$103 year로 기대수치인 수십 년보다 높아 제안된 안티퓨즈의 신뢰성을 확보 할 수 있었다. 제안된 안티퓨즈의 이중 절연막의 두께는 250 이고 프로그래밍 전압은 9.0V이고, 약 65$\Omega$의 on 저항을 얻을수 있었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.160-160
• /
• 2010

테라헤르츠 소스로 저온 InGaAs를 대체하기 위해 저온에서 성장한 $In_{0.64}Al_{0.36}Sb$의 성장 온도에 따른 광학적 photoluminescence (PL)과 time-resolved PL (TRPL) 측정을 이용하여 분석하였다. 또한 Be 도핑 농도에 따른 p형 $In_{0.64}Al_{0.36}Sb$의 PL과 TRPL 특성을 undoped $In_{0.64}Al_{0.36}Sb$와 Si-doped $In_{0.64}Al_{0.36}Sb$ 결과와 비교 분석하였다. 본 연구에 사용한 시료는 분자선 엑피탁시 (molecular beam epitaxy)법으로 GaAs 기판 위에 $In_{0.64}Al_{0.36}Sb$을 다양한 성장온도에서 ${\sim}3.7\;{\mu}m$두께 성장하였다. $In_{0.64}Al_{0.36}Sb$의 성장온도는 $400^{\circ}C$ 에서 $460^{\circ}C$까지 변화시키며 성장하였으며, Si과 Be 도핑한 $In_{0.64}Al_{0.36}Sb$ 시료는 약 $420^{\circ}C$에서 성장하였다. 모든 시료의 PL 피크는 ~1450 nm 근처에서 나타나며 단파장 영역에 shoulder 피크가 나타났다. 그러나 가장 낮은 온도 $400^{\circ}C$에서 성장한 시료는 1400 nm에서 1600 nm에 걸쳐 매우 넓은 피크가 측정되었다. PL 세기는 $450^{\circ}C$ 에서 성장한 시료가 가장 강하게 나타났으며, $435^{\circ}C$에서 성장한 시료의 PL 세기가 가장 약하게 나타났다. 방출파장에 따른 PL 소멸곡선을 측정하였으며 double exponential function을 이용하여 운반자 수명시간을 계산하였다. 운반자 수명시간은 빠른 소멸성분 $\tau_1$과 느린 소멸성분 $\tau_2$가 존재하고 빠른 성분 $\tau_1$의 PL 진폭이 약 80%로 느린 성분 $\tau_2$보다 우세하게 나타났다. 각 PL 피크에서의 운반자 수명시간 $\tau_1$은 ~1 ns로 성장온도에 따른 변화는 관찰되지 않았다. 또한 방출파장이 1400 nm에서 1480 nm까지 PL 피크 근처에서 운반자 수명시간은 거의 일정하게 나타났다. Be-doped 시료의 PL 피크는 1236 nm에서 나타나며, Si-doped 시료는 1288 nm, undoped 시료는 1430 nm에서 PL 피크가 측정되었다. PL 피크에서 PL 소멸곡선은 Be-doped 시료가 가장 빨리 감소하였으며, Si-doped 시료가 가장 길게 나타났다. 이러한 결과로부터 $In_{0.64}Al_{0.36}Sb$의 광학적 특성은 성장 온도, dopant type, 도핑 농도에 따라 변화하는 것을 확인하였다.

• Korean Journal of Materials Research
• /
• v.6 no.8
• /
• pp.833-840
• /
• 1996

Diamond thin films were deposited on p-type (100) Si wafers using MPECVD. Prior to deposition, ultrasonic striking was done to improve density of nucleation sites with dimond powder of 40~$60\mu$m size. Then diamond thin films were deposited at $^900{\circ}C$, 40Torr and 1000W microwave power using ${CH}_{4}$ and ${H}_{2}$ gases. The purity, the morphology and the microstructur'e and microdefects of diamond thin films were characterized by Raman spectroscopy, SEM and TEM, repectively. In Raman spectroscopy the peaks of non-diamond phase increased as ${CH}_{4}$, concentration increased. In SEM, the morphology of diamond thin films varied from crystalline to cauliflower as ${CH}_{4}$, concentration increased. As ${CH}_{4}$ con centration increased, the density of defects increased, with most defects being {III} twin. ${MTP}_{5}$, were formed with five (II]) planes. As these (Ill) Planes were twinned, ${MTP}_{5}$, represented five-fold symmetry. ]n the interfaces, defects in diamond thin films fanned out from small regions implying nucleation sites.

• Korean Journal of Soil Science and Fertilizer
• /
• v.19 no.3
• /
• pp.239-244
• /
• 1986

This study was conducted to investigate the characteristics of humic substances and the fractional distribution of organic nitrogen in Korean paddy soils. The results are obtained as follows: 1. The content of humus in soils used was 665-2680 mg/100g and the average contents of humic acid in normal paddy soils and in sandy paddy soils were 1436 mg/100g, 970 mg/100g respectively. 2. The humic acid diagrams classed by Kumada method belong to B type, P type and Rp type. 3. The content of Mineral - N to Total - N was 1.04-2.86% and the average contents of that in sandy paddy soils and in normal paddy soils were 1.72% and 1.75% respectively. 4. The fractionations of acid hydrolysable organic - N in sandy paddy soils were Amino acid - N (31.52%), Humin - N (20.63%), Amino sugar - N (18.70%), and Unknown - N (25.73%).