• Journal of the Korean Ceramic Society
• /
• v.35 no.1
• /
• pp.55-65
• /
• 1998

The oxidation behavior of Ag-36.8a%Cu-7.4at%Ti alloy brazed on Si3N4 substrate was investigated at 400, 500 and 600$^{\circ}C$ in air. Under this experimental condition Si3N4 and Ag were not oxidized whereas Cu and Ti among the brazing alloy components were oxidizied obeying the parabolic oxidation rate law. The activation energy of oxidation was found to be 80kj/ mol which was smaller than that of pure Cu owing to the presence of oxygen active element of Ti. The outer oxide scale formed from the initial oxidation state was always composed of Cu oxides which were known to be growing by the outward diffusion of Cu ions. As the oxidation progressed the concentration gradient occurred due to the continuous consumption of Cu as Cu oxides and consequently build-up of an Ag-enriched layer below the Cu oxides resulted in the formation of multiple oxide scales composed of Cu oxide (CuO) /Ag-enriched layer/Cu oxide (Cu2O) /Ag-enriched layer. Also the inward diffusing of oxygen through Cu oxide and Ag-enriched layers led to the formation of internal oxides of TiO2.

• Journal of Electrochemical Science and Technology
• /
• v.6 no.3
• /
• pp.88-94
• /
• 2015

In this study we investigated the electrocatalytic oxidation of saccharose on conductive polymer- Nickel oxide modified graphite electrodes based on the ability of anionic surfactants to form micelles in aqueous media. This NiO modified electrode showed higher electrocatalytic activity than Ni rode electrode in electrocatalytic oxidation of saccharose. The anodic peak currents show linear dependency with the square root of scan rate. This behavior is the characteristic of a diffusion controlled process. Under the CA regime the reaction followed a Cottrellian behavior and the diffusion coefficient of saccharose was found in agreement with the values obtained from CV measurements.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.2
• /
• pp.112-118
• /
• 2005

Study was focused on the effect of the cooling rate on the embrittlement behavior of Zircaloy-4 cladding simulated Loss Of Coolant Accident (LOCA) environment. Claddings were oxidized at given temperature and given time followed by various water quenching in the range of $0.6^{\circ}C$ and $100^{\circ}C$ per second. Cladding failed after water quenching above the threshold oxidation. Threshold oxidation was decreased as the cooling rate increased, which is due to the matensite structure formed during fast cooling rate.

• Proceedings of the KIEE Conference
• /
• 1988.07a
• /
• pp.328-331
• /
• 1988

Sealed Interface Local Oxidation (SILO) technology has been investigated using a nitride/oxide/nitride three-layered sandwich structure. P-type silicon substrate was either nitrided by rapid thermal processing, or silicon nitride was deposited by LPCVD method. A three-layered sandwich structure was patterned either by reactive ion etch (RIE) mode or by plasma mode. Sacrificial oxidation conditions were also varied. Physical characterization such as cross-section analysis of field oxide, and electrical characterization such as gate oxide integrity, junction leakage and transistor behavior were carried out. It was found that bird's beak was nearly zero or below 0.1um, and the junction leakages in plasma mode were low compared to devices of the same geometry patterned in RIE mode, and gate oxide integrity and transistor behavior were comparable. Conclusively, SILO process is compatible with conventional local oxidation process.

• Nuclear Engineering and Technology
• /
• v.30 no.2
• /
• pp.173-179
• /
• 1998

The corrosion behavior of KOFA cladding which is a standard Zircaloy-4 manufactured by Westinghouse Specialty Metal Plant according to the Siemens/KWU's HCW (Highly Cold Worked) standard Zircaloy-4 specification was analyzed using the oxide measurement data of KOFA fuel irradiated in Kori-2 nuclear power plant. Analysis of the measured KOFA cladding oxidation showed that oxidation of KOFA cladding was lower than the design prediction based upon Siemens/KWU's HCW standard Zircaloy-4 cladding. Although the measured fuel rods have relatively low burnup and oxidation and the amount of the measured data are small, analysis of manufacturing and in-reactor operation conditions of KOFA cladding indicates that the differences in the manufacturing processes and chemical composition of the Siemens/KWU's HCW (Highly Cold Worked) standard Zircaloy-4 and KOFA cladding may have somewhat contributed to lower corrosion of KOFA cladding than the expected.

• Carbon letters
• /
• v.7 no.3
• /
• pp.196-200
• /
• 2006

Graphite has hexagonal closed packing structure with two bonding characteristics of van der Waals bonding between the carbon layers at c axis, and covalent bonding in the carbon layer at a and b axis. Graphite has high tolerant to the extreme conditions of high temperature and neutron irradiations rather than any other materials of metals and ceramics. However, carbon elements easily react with oxygen at as low as 400C. Considering the increasing production of today of hydrogen and electricity with a nuclear reactor, study of oxidation characteristics of graphite is very important, and essential for the life evaluation and design of the nuclear reactor. Since the oxidation behaviors of graphite are dependent on the shapes of testing specimen, critical care is required for evaluation of nuclear reactor graphite materials. In this work, oxidation rate and amounts of the isotropic graphite (IG-110, Toyo Carbon), currently being used for the Koran nuclear reactor, are investigated at various temperature. Oxidation process or principle of graphite was figured out by measuring the oxidation rate, and relation between oxidation rate and sample shape are understood. In the oxidation process, shape effect of volume, surface area, and surface to volume ratio are investigated at $600^{\circ}C$, based on the sample of ASTM C 1179-91.

• Nuclear Engineering and Technology
• /
• v.32 no.4
• /
• pp.309-315
• /
• 2000

The changes of Np oxidation state in nitric acid and the effect of nitrous acid on the oxidation state were analyzed by spectrophotometry, solvent extraction, and electrochemical methods. An enhancement of Np extraction to 30 vol.% TBP was carried out through adjustment of Np oxidation state by using a glassy carbon fiber column electrode system. The information of electrolytic behavior of nitric acid was important because the nitrous acid affecting the Np redox reaction was generated during the electrolytic adjustment of the Np oxidation state. The Np solution used in this work consisted of Np（V) and Np（Ⅵ）without （IV）. The composition of Np（V) in the range of 0.5M -5.5 M nitric acid was 32% ~ 19%. The electrolytic oxidation of Np（V) to Np（Ⅵ）in the solution enhanced Np extraction efficiency about five times higher than the case without the electrolytic oxidation. It was confirmed that the nitrous acid of less than about 10-5 M acted as a catalyst to accelerate the chemical oxidation reaction of Np（V) to Np（Ⅵ）.

• Journal of the Korean institute of surface engineering
• /
• v.28 no.6
• /
• pp.333-342
• /
• 1995

Stainless steels are widely selected as commercial engineering materials mainly because of their excellent corrosion resistance, oxidation resistance and strength. Because the manufacturing temperature of stainless steels is relatively high, the chemical and physical properties of the oxide film which was formed on the stainless steels are of importance in determining the rate of oxidation and the life of equipment exposed to high temperature oxidizing environments. In this study, the oxidation behavior of S. S. 304 and S. S. 430 added by a small amount of oxygen active elements(each +0.5wt% Hf and Y) was studied to improve oxidation resistance. The results of cyclic and isothermal oxidation on S. S. 304 added by OAE showed relatively poor oxidation resistance due to spallations and cracks of $Cr_2O_3$ layer. But all S. S. 430+0.5wt% OAE maintained constant oxidation rates and stable oxide layers at high temperature environment. Especially S. S. 430+0.5wt% Y formed a $Cr_2O_3$ oxide layer and improved cyclic oxidation resistance preventing loss of protective layers about 1000 hours at $1000^{\circ}C$

• Journal of the Korean Ceramic Society
• /
• v.55 no.5
• /
• pp.498-503
• /
• 2018

Using the thermal ablation method, the oxidation behavior of $SiC_f/SiC$ composites was investigated in air and in the temperature range of $1,300^{\circ}C$ to $2,000^{\circ}C$. At the relatively low temperature of $1,300^{\circ}C$, passive oxidation, which formed amorphous phase, predominantly occurred in the thermal ablation test. When the oxidation temperature increased, SiO (g) and CO (g) were formed by active oxidation and the dense oxide layer changed to a porous one by vaporization of gas phases. In the higher temperature oxidation test, both active oxidation due to $SiO_2$ decomposition on the surface of the oxide layer and active/passive oxidation transition due to interfacial reaction between oxide and base materials such as SiC fiber and matrix phase simultaneously occurred. This was another cause of high temperature degradation of $SiC_f/SiC$ composites.

• Corrosion Science and Technology
• /
• v.19 no.3
• /
• pp.138-145
• /
• 2020

Immersion tests of Alloy 600 were conducted in simulated primary water environments of a pressurized water reactor at 325 ℃ for 10, 100, and 1000 h to obtain insight into effects of surface deformation on internal and intergranular (IG) oxidation behavior through precise characterization using various microscopic equipment. Oxidized samples after immersion tests were covered with polyhedral and filamentous oxides. It was found that oxides were abundant in mechanically ground (MG) samples the most. The number density of surface oxides increased with time irrespective of the method of surface finish. IG oxidation occurred in mechanically polished (MP) and chemically polished (CP) samples with thin internal oxidation layers. However, IG oxidation was suppressed with relatively thick internal oxidation layers in MG samples compared to MP and CP samples, suggesting that MG treatment could increase resistance to primary water stress corrosion cracking (PWSCC) from the standpoint of IG oxidation. As a result, appropriate surface treatment for Alloy 600 could prevent oxygen diffusion into grain boundaries, inhibit IG oxidation, and finally induce its high PWSCC resistance.