• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.11
• /
• pp.968-972
• /
• 2008

Ni/Ti/Al multilayer system ('/'denotes the deposition sequence) was tested for low-resistance ohmic contact formation to Al-implanted p-type 4H-SiC. Ni 30 nm / Ti 50 nm / Al 300 nm layers were sequentially deposited by e-beam evaporation on the 4H-SiC samples which were implanted with Al (norminal doping concentration = $4\times10^{19}cm^{-3}$) and then annealed at $1700^{\circ}C$ for dopant activation. Rapid thermal anneal (RTA) temperature for ohmic contact formation was varied in the range of $840\sim930^{\circ}C$. Specific contact resistances were extracted from the measured current vs. voltage (I-V) data of linear- and circular transfer length method (TLM) patterns. In constrast to Ni contact, Ni/Ti/Al contact shows perfectly linear I-V characteristics, and possesses much lower contact resistance of about $2\sim3\times10^{-4}\Omega{\cdot}cm^2$ even after low-temperature RTA at $840^{\circ}C$, which is about 2 orders of magnitude smaller than that of Ni contact. Therefore, it was shown that RTA temperature for ohmic contact formation can be lowered to at least $840^{\circ}C$ without significant compromise of contact resistance. X-ray diffraction (XRD) analysis indicated the existence of intermetallic compounds of Ni and Al as well as $NiSi_{1-x}$, but characteristic peaks of $Ti_{3}SiC_2$, a probable narrow-gap interfacial alloy responsible for low-resistance Ti/Al ohmic contact formation, were not detected. Therefore, Al in-diffusion into SiC surface region is considered to be the dominant mechanism of improvement in conduction behavior of Ni/Ti/Al contact.

• Korean Journal of Materials Research
• /
• v.19 no.8
• /
• pp.417-420
• /
• 2009

This study develops a highly transparent ohmic contact using phosphorus doped ZnO with current spreading for p-GaN to increase the optical output power of nitride-based light-emitting diodes (LEDs). The phosphorus doped ZnO transparent ohmic contact layer was prepared by radio frequency magnetron sputtering with post-deposition annealing. The transmittance of the phosphorus doped ZnO exceeds 90% in the region of 440 nm to 500 nm. The specific contact resistance of the phosphorus doped ZnO on p-GaN was determined to be $7.82{\times}10^{-3}{\Omega}{\cdot}cm^2$ after annealing at $700^{\circ}C$. GaN LED chips with dimensions of $300\times300{\mu}m$ fabricated with the phosphorus doped ZnO transparent ohmic contact were developed and produced a 2.7 V increase in forward voltage under a nominal forward current of 20 mA compared to GaN LED with Ni/Au Ohmic contact. However, the output power increased by 25% at the injection current of 20 mA compared to GaN LED with the Ni/Au contact scheme.

• Transactions on Electrical and Electronic Materials
• /
• v.14 no.1
• /
• pp.32-35
• /
• 2013

In this paper, a manufacturing process was developed for fabricating high-quality AlGaN/GaN high electron mobility transistors (HEMTs) on silicon carbide (SiC) substrates. Various conditions and processing methods regarding the ohmic contact and pre-metal-deposition $BCl_3$ etching processes were evaluated in terms of the device performance. In order to obtain a good ohmic contact performance, we tested a Ti/Al/Ta/Au ohmic contact metallization scheme under different rapid thermal annealing (RTA) temperature and time. A $BCl_3$-based reactive-ion etching (RIE) method was performed before the ohmic metallization, since this approach was shown to produce a better ohmic contact compared to the as-fabricated HEMTs. A HEMT with a 0.5 ${\mu}m$ gate length was fabricated using this novel manufacturing process, which exhibits a maximum drain current density of 720 mA/mm and a peak transconductance of 235 mS/mm. The X-band output power density was 6.4 W/mm with a 53% power added efficiency (PAE).

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.26 no.10
• /
• pp.1545-1553
• /
• 1989

The ohmic contact behavior in HEMT structure was compared with that in MESFET one throughout the specific contact resistance and microstructural change in both structures. A Au-Ge-Ni based metallization scheme was used and the alloying temperature of the ohmic materials was changed from 330\ulcorner to 550\ulcorner. The alloying temperature to obtain the minimum specific contact resistance in HEMT structure was 60k higher than that in MESFET. The volume fraction of NiAs (Ge) in MESFET structure increases with alloying temperature and/or the alloying time, which makes the decrease of specific contact resistance at the initial stage of ohmic metallization. In contrast, the volume fraction of NiAs(Ge) in HEMT structure was not dependent upon the specific contact resistance, which implies that the ohmic contacts are dominantly formed by the Ge diffusion to 2-DEG(two dimensional electron gas) layer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.406-407
• /
• 2006

This paper describes the ohmic contact formation between a TiW film as a contact material deposied by RF magnetron sputter and polycrystalline 3C-SiC films deposied on thermally grown Si wafers. The specific contact resistance (${\rho}_c$) of the TiW contact was measured by using the C-TLM. The contact phase and interfacial reaction between TiW and 3C-SiC at high-temperature were also analyzed by XRD and SEM. All of the samples didn't show cracks of the TiW film and any interfacial reaction after annealing. Especially, when the sample was annealed at $800^{\circ}$ for 30min., the lowest contact resistivity of $2.90{\times}10^{-5}{\Omega}cm^2$ was obtained due to the improved interfacial adhesion.

• Journal of Sensor Science and Technology
• /
• v.15 no.6
• /
• pp.386-390
• /
• 2006

This paper describes the ohmic contact formation of polycrystalline 3C-SiC films deposited on thermally grown Si wafers. In this work, a TiW (titanium tungsten) film as a contact material was deposited by RF magnetron sputter and annealed with the vacuum process. The specific contact resistance (${\rho}_{c}$) of the TiW contact was measured by using the C-TLM (circular transmission line method). The contact phase and interfacial reaction between TiW and 3C-SiC at high-temperature as also analyzed by XRD (X-ray diffraction) and SEM (scanning electron microscope). All of the samples didn't show cracks of the TiW film and any interfacial reaction after annealing. Especially, when the sample was annealed at $800^{\circ}$ for 30 min., the lowest contact resistivity of $2.90{\times}10{\Omega}cm^{2}$ was obtained due to the improved interfacial adhesion. Therefore, the good ohmic contact of polycrystalline 3C-SiC films using the TiW film is very suitable for high-temperature MEMS applications.

• Journal of the Korean Vacuum Society
• /
• v.11 no.1
• /
• pp.43-49
• /
• 2002

Pd/Ge/Pd/Ti/Au ohmic contact to n-type InGaAs was investigated with rapid thermal annealing conditions. Minimum specific contact resistivity of $1.1\times10^{-6}\Omega\textrm{cm}^2$ was achieved after annealing at $400^{\circ}C$/10sec, and a ohmic performance was degraded at higher annealing temperature due to the chemical reaction between the ohmic contact materials and the InGaAs substrate. However, non-spiking planar interface and relatively good ohmic contact($high-10^{-6};{\Omega}\textrm{cm}^2$) were maintained. This ohmic contact system is expected to be a promising candidate for compound semiconductor devices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.290-293
• /
• 2003

Ohmic contact characteristics of Al ion implanted n-type SiC wafer were investigated. Al ions implanted with high dose to obtain the final concentration of $5{\times}10^{19}/cm^3$, then annealed at high temperature. Firstly, B ion ion implanted p-well region were formed which is needed for fabrication of SiC devices such as DIMOSFET and un diode. Secondly, Al implanted high dose region for ohmic contact were formed. After ion implantation, the samples were annealed at high temperature up to $1600^{\circ}C\;and\;1700^{\circ}C$ for 30 min in order to activate the implanted ions electrically. Both the inear TLM and circular TLM method were used for characterization. Ni/Ti metal layer was used for contact metal which is widely used in fabrication of ohmic contacts for n-type SiC. The metal layer was deposited by using RF sputtering and rapid thermal annealed at $950^{\circ}C$ for 90sec. Good ohmic contact characteristics could be obtained regardless of measuring methods. The measured specific contact resistivity for the samples annealed at $1600^{\circ}C\;and\;1700^{\circ}C$ were $1.8{\times}10^{-3}{\Omega}cm^2$, $5.6{\times}10^{-5}{\Omega}cm^2$, respectively. Using the same metal and same process of the ohmic contacts in n-type SiC, it is found possible to make a good ohmic contacts to p-type SiC. It is very helpful for fabricating a integrated SiC devices. In addition, we obtained that the ratio of the electrically activated ions to the implanted Al ions were 10% and 60% for the samples annealed at $1600^{\circ}C\;and\;1700^{\circ}C$, respectively.

• Journal of the Korean Vacuum Society
• /
• v.12 no.4
• /
• pp.218-227
• /
• 2003

Pd/Si/Ti/Pt and Pd/Si/Pd/Ti/Au ohmic contacts to n-type InCaAs were investigated for applications to AlGaAs/GaAs HBT emitter ohmic contacts. In the Pd/Si/Ti/Pt ohmic contact, as-deposited contact showed non-ohmic behavior, and high specific contact resistivity of $5\times10^{-3}\Omega\textrm{cm}^2$ was achieved by rapid thermal annealing at $375^{\circ}C$/10 sec. However, the specific contact resistivity decreased remarkably to $2\times10^{-6}\Omega\textrm{cm}^2$ by annealing at $425^{\circ}C$/10sec. In the Pd/Si/Pd/Ti/Au ohmic contact, minimum specific contact resistivity of $3.9\times10^{-7}\Omega\textrm{cm}^2$ was achieved by annealing at $400^{\circ}C$/20sec. In both ohmic contacts, low contact resistivity and non-spiking planar interface between ohmic materials and InGaAs were maintained. Therefore, these thermally stable ohmic contact systems are promising candidates for compound semiconductor devices. RF performance of the AlGaAs/GaAs HBT was also examined by employing the Pd/Si/Ti/Pt and Pd/Si/Pd/Ti/Au systems as emitter ohmic contacts. Cutoff frequencies were 63.9 ㎓ and 74.4 ㎓, respectively, and maximum oscillation frequencies were 50.1 ㎓ and 52.5 ㎓, respectively. It shows very successful high frequency operations.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.25 no.12
• /
• pp.1663-1668
• /
• 1988

Ohmic contact process for the fabrication of GaAs integrated circuits is very important. Specific contact resistivities, assuming Rsm=Rs, were measured after the rapid and the conventional alloying process, respectively. The results show that the characteristics of ohmic contact through the rapid alloying process is much better (Apc=1.3~3.3x10**-7 \ulcorner-(m\ulcorner. This is probably due to intensive and compound energy densities during the rapid alloying process. New analysis method of TLM patterns viz. measurements of normlaized specific contact resistivities are proposed to reduce measurement errors that could occur when measuring the small contact end resistances. The adoption of rapid alloying process for the mass production of GaAs integrated circuits could greatly reduce the total processig time.