• Elastomers and Composites
• /
• v.48 no.1
• /
• pp.18-23
• /
• 2013

Nylon 12 elastomer was slightly crosslinked in molten state by the addition of small amount of dicumyl peroxide (DCP) as a crosslink agent and triallycyanuate (TAC) as a co-agent during melt compounding at $160^{\circ}C$ in an internal mixer. The effect of the peroxide crosslinking on mechanical, dynamic mechanical and rheological properties of the nylon 12 elastomer was investigated by means of tensile testing, dynamic mechanical analysis (DMA) and small amplitude oscillating rheometer, respectively. With modification, there is an improvement in tensile modulus and Young's modulus with decease in elongation at break. DMA results for peroxide modified nylon 12 elastomers demonstrated that the glass transiaiton temperature of PTMG segment shifted to higher temperature and the storage modulus remained constant above the melting temperature of nylon 12 segments. Melt rheological studies revealed that the peroxide modified nylon 12 elastomer exhibited a more solid like behavior and stronger shear thinning behavior compared to neat nylon 12 elastomer, which was more prominent at higher TAC content in the polymer matrix. The peroxide modified nylon 12 elastomer exhibited good elastic recoverability and improved mechanical properties without sacrificing melt processibilty, and especially the service temperature range increased as compared to neat nylon 12 elastomer.

• Elastomers and Composites
• /
• v.44 no.3
• /
• pp.274-281
• /
• 2009

Nylon 6 and nylon elastomer were prepared by anionic polymerization route. Nylon elastomers, composed of hard segment of polyamide(PA) and soft segment of polyether(PE), were synthesized by use of TDI terminated polyol with caprolactam. The morphology of the electrospun webs of nylon and nylon elastomers, observed by FE-SEM, showed that the porous electrospun web was composed of nanofibers, whose diameter were in the range of 100 to 180 nm. Their behavior of melting and crystallization and the chemical structure of nylon elastomers were investigated by DSC and ATR FT-IR. Result of tensile testing indicated that nylon has higher tensile strength and lower elongation than nylon elastomers. Atmospheric plasma(APP) with $O_2$ and $N_2$ as reactive gas modified the surface of electrospun nylon and electrospun nylon elastomers allowing them higher hydrophilicity, while APP with $CH_4$ as reactive gas modified the surface of polymers allowing higher hydrophobicity.

• Polymer(Korea)
• /
• v.29 no.2
• /
• pp.127-134
• /
• 2005

The relationships among mechanical properties, rheological properties, and morphology by reactive extrusion based on commingled pckaging film wastes contains polypropylene (PP) pckaging film system [PP/polyethylene (PE)/aluminum (Al)/poly(ethylene terephthalate) (PET)] and Nylon packaging film system[Nylon/PE/linear-low density polyethylene (LLDPE)] were investigated to improve the compatibility and toughness of these wastes using various compatibilizers such as ethylene vinylacetate (EVA), styrene-ethylene/butylene-styrene triblock copolymer (SEBS), styrene-ethylene/butylene-styrene-graft-maleic anhydride copolymer (SEBS-g-MA), polyethylene-graft-maleic anhydride (PE-g-MA), polypropylene-graft-maleic anhydride (PP-g-MA) , polyethylene-graft-acrylic acid (PE-g-AA) and polypropylene-graft-acrylic acid (PP-g-AA). Compared with simple melt blend system, the blends showed improvement of about $50\%$ increase in physical properties when SEBS and EVA were added. However, SEBS-g-MA thermoplastic elastomer which is highly reactive with amine terminal group of nylon, resulted in about $200\%$ increase in impact strength. This compatibilization effect resulted from the increase of interfacial adhesion and the reduction of domain size of dispersed phase in PP/Nylon blend system.