• Elastomers and Composites
• /
• v.39 no.2
• /
• pp.95-104
• /
• 2004

New compounds were made using various NR/BR blend ratio and oil content to improve mechanical properties of rubber isolator at low temperature. Mechanical properties were investigated as a function of NR/BR blend ratio and oil content. Hardness and tensile modulus generally increased, but tensile strength and elongation at break decreased with increasing BR content. Hardness, tensile modulus and tensile strength decreased, but elongation at break were nearly the same with increasing oil content. The glass transition temperature of NR and BR were found to be $-50^{\circ}C$ and $-90^{\circ}C$ respectively based on the abrupt drops in storage elastic modulus and peak of loss factor. Two distinct transition temperature were observed in NR/BR blend compounds and each transition point was not affected by blend level indicating incompatible nature of NR/BR blend.

• Elastomers and Composites
• /
• v.44 no.1
• /
• pp.41-46
• /
• 2009

The effects of temperature and curing systems on the compression set of natural rubber (NR) at constant load were investigated. NR was compounded with various amounts of sulfur and DCP in order to obtain various crosslink densities and curing systems. Compression sets at constant load were compared with those at constant strain. Compression set at constant load was more affected by changes in crosslink density than compression set at constant strain, due to the differences of exerted strain energy density. Compression set of sulfur cured NR under constant load was increased with increasing load and temperature, but the compression set of DCP cured NR was not changed by increasing load and temperature.

• Journal of the Society of Naval Architects of Korea
• /
• v.57 no.3
• /
• pp.168-174
• /
• 2020

Recently, the size of Liquified Natural Gas (LNG) carriers has been increasing, in turn increasing the load generated during operation. To handle this load, the thickness of LNG Cargo Containment Systems (CCSs) should be increased. Despite increasing the thickness of LNG CCSs, a secondary barrier is still used in conventional thickness. Therefore, the mechanical performance of the existing secondary barrier should be verified. In this study, tensile test of the secondary barrier was performed to evaluate mechanical properties under several low- and cryogenic-temperature conditions considering LNG environment, and in each fiber direction considering that the secondary barrier is composed of anisotropic composite materials depending on the glass fibers. Additionally, the coefficient of thermal expansion was measured by considering the degradation of the mechanical properties of the secondary barrier caused by the generated thermal stress during periodical unloading. As a result, the mechanical performance of secondary barrier in the Machine Direction (MD) was generally found to be superior than that in the Transverse Direction (TD) owing to the warp interlock structure of the glass fibers.

• Fire Science and Engineering
• /
• v.20 no.4 s.64
• /
• pp.72-76
• /
• 2006

Polymer/clay nanocomposites have generated considerable interests in the past decade because adding just tiny amount of clay to the polymer matrix could produce a dramatic enhancement in physical, thermal and mechanical properties. Smectite clays, such as montmorillonite (MMT), are of great industrial value because of their high aspect ratio, plate morphology, intercalative capacity, natural abundance and low cost. In this study, PE/MMT nanocomposites were directly prepared by melt intercalating PE and the modified clay. The nanostructure was verified by X-ray diffraction (XRD) and transmission electron microscopy (TEM), and their flame retardant properties were measured and discussed by limiting oxygen index (LOI), char yield and smoke mass concentration. And their thermal stabilities were measured by differential thermogravimetric (DTG) and thermogravimetric analysis (TGA). The PE/MMT nanocomposites proved more effective the conventional composites in reinforcement. Two functions in the thermal stability of the PE/MMT nanocomposite, one is the barrier effect to improve the thermal stability, and another is catalysis, leading to a decrease of the thermal stability. The flammability was greatly decreased due to the formation of the clay-enriched protective char during the combustion.

• Elastomers and Composites
• /
• v.40 no.1
• /
• pp.29-36
• /
• 2005

Mixing condition and procedure affect properties or a filled rubber compound such as filler dispersion, viscosity, and bound rubber formation. Influence of separate load of styrene-butadiene rubber (SBR) and acrylonitrile-butadiene rubber (NBR) on properties or silica-filled SBR compounds containing NBR was studied. Cure time and cure rate became faster as NBR content increased. The crosslink density increased with increase in the NBR content. The bound rubber content also increased as the NBR content increased. NBR content of the bound rubber was higher than that of the compounded rubber. The bound rubber content was higher when SBR and NBR were loaded separately than when loading simultaneously. The cure time and cure rate were slower for the separate load than for the simultaneous one. The crosslink density was also lower for the former case than for the latter one.

• Elastomers and Composites
• /
• v.33 no.4
• /
• pp.281-289
• /
• 1998

Tensile properties including Young's modulus and tear strength were measured for four different rubber compounds; natural rubber(NR), styrene-butadiene copolymer(SBR), ethylene-propylene diene monomer (EPDM), and brominated isobutylene-p-methyl-styrene copolymer(BIMS) as a function of temperature and degree of cure. To see the effect of over cure, a measurement was made of the tensile strength and swelling behavior of the over-cured rubber compounds. Young's modulus, E, was found to have linear dependency on the degree of cure for all rubber compounds. EPDM and BIMS showed the highest and lowest slopes, respectively. The slope of NR and SBR lay between EPDM and BIMS. Tear strength, Gc, decreased in the order of NR>BIMS>SBR>EPDM. As the cure time was extended the degree of cure of NR and SBR decreased, while that of BIMS increased. EPDM showed little change in the degree of cure.

• Elastomers and Composites
• /
• v.39 no.4
• /
• pp.301-308
• /
• 2004

Three types of parylene (PA-N, PA-C, PA-D) were used for coating the surface on natural latex rubbers in order to improve surface characteristics including mechanical properties and biocompatibility. The parylene coating was the CVD (chemical vapor deposition) method, and the surface properties of the modified latex were measured. Annealing effects on the mechanical properties of the coated latex were also investigated. The adhesion between latex and parylene was good for all the types of parylene used. As annealing temperature was increased, latex modified with PA-N became more hydrophobic, while the latex treated with PA-C and PA-D became more hydrophilic. As the annealing temperature was raised, the tensile strength was increased, and the elongation was decreased. The biocompatibility was noticeably improved on the latex surface modified with the parylenes through CVD method.

• Elastomers and Composites
• /
• v.38 no.3
• /
• pp.273-280
• /
• 2003

Elastic responses on both pure natural rubber melts with different molecular weights and the rubber compounds mixed with various types of carbon blacks were investigated in this study. Furthermore, the degree of bound rubber was measured for various carbon blacks with different sizes and structures in order to study the interaction between the rubber and carbon blacks, and to study the correlation between the interaction and the elastic responses. As a loading amount of carbon black increased, the degree of bound rubber became higher, particularly far carbon-black particles with smaller sizes and higher structures. The elastic responses of the rubber melt filled with carbon black remarkably improved, as compared with those of unfilled rubber melt, specially in carbon black showing higher contents of bound rubber. Stress relaxation was more delayed and recovery behavior became more elastic, as the molecular weight of the rubber melt increased and the size of carbon-black particles was decreased. Permanent set became higher, as the molecular weight of the rubber melts decreased and the size of carbon-black particles increased.

• KOREAN JOURNAL OF PACKAGING SCIENCE & TECHNOLOGY
• /
• v.27 no.1
• /
• pp.41-48
• /
• 2021

In this study, ethylene vinyl acetate (EVA) and low density polyethylene (LDPE) composite films (EVA/LDPE-OSP) containing calcined oyster shell powder (OSP) were prepared using twin-screw extruder as an antimicrobial packaging material. The OSP composite was initially prepared and then incorporated into an EVA/LDPE blend at different ratios (0, 1, 3 and 5%) to develop the EVA/LDPE-OSP composite films. The as-prepared EVA/LDPE-OSP composites films were evaluated using FT-IR, DSC, TGA, OTR, WVTR, SEM and UTM as well as antimicrobial activity was examined using JIS Z 2801:2000 standard. OPS endowed the antimicrobial potency to the composite films against Gram-positive (Staphylococcus aureus) and Gram-negative (Escherichia coli) bacteria. In addition, the incorporation of OSP remarkably enhanced the thermal stability. OSP as a natural biocidal agent can be used as a multifunctional additive in packaging industry such as improving the thermomechanical properties and preventing the microbial contamination of packaged products.

• Elastomers and Composites
• /
• v.56 no.4
• /
• pp.234-242
• /
• 2021

The demand for truck bus radial (TBR) tires with enhanced fuel efficiency and wear resistance have grown in recent years. In addition, as the issue of particulate matter and air pollution increases, efforts are being made to reduce the generation of particulate matter. In this study, the properties of epoxidized natural rubber (ENR) containing a silica-friendly functional group were evaluated by considering it as a base rubber and varying the silica ratio in this binary filler system. The results showed that the wear resistance of the NR/BR blend compound decreased as the silica ratio increased. In contrast, the ENR/BR blend compound exhibited an increase in wear resistance as the silica ratio was increased. In particular, the ENR-50/BR blend compound showed the best wear resistance due to the presence of several epoxide groups. Furthermore, we observed that for tan 𝛿 at 60℃, higher epoxide content resulted in the higher T_g of the rubber, indicating a higher tan 𝛿 at 60℃. On the other hand, it was confirmed that increasing the silica ratio decreased the value of tan 𝛿 at 60℃ in all compounds. In addition, we measured the amount of wear particulate matters generated from the compound wear. These measurements confirmed that in the binary filler system, regardless of the filler type, the quantity of the generated wear particulate matters as the filler-rubber interaction increased. In conclusion, the silica filled ENR/BR blend compound exhibited the lowest generation of wear particulate matters.