• Molecular & Cellular Toxicology
• /
• 제4권4호
• /
• pp.311-317
• /
• 2008

Zebrafish were exposed to commercial silver nanoparticles (${\sim}$10-20 nm) at 0.4 and 4 ppm during cadual fin regeneration. The silver was in the $Ag^+$ ionic form. Fin regeneration was slow in the group exposed to the lower concentration. The cadual fin, gill, and muscle were assayed after 48 hours and subjected to histological analysis. In all tissues sampled, fish exposed to nanoparticles exhibited infiltration, large mitochondria with empty matrices, and accumulation of nano-sized silver in blood vessels. The results suggested mitochondrial damage and induction of inflammation. Microarray analysis of RNA from young zebrafish (52 hours post-fertilization) that were exposed to nanometer-sized silver particles, showed alteration in expression of the p53 gene pathway related to apoptosis. Gene expression changes in the nanoparticle-treated zebrafish led to phenotypic changes, reflecting increased apoptosis.

• 동굴
• /
• 제76호
• /
• pp.1-13
• /
• 2006

Electrophoretic deposition (EPD) of alcohol YBCO suspensions on the Ag wire electrode is studied. Poly(ethylene glycol) was coordinated to a structure formed by the EPD process with YBCO particles. The suspension is characterized in terms of zeta potential and conductivity. The d.c electric fields of 200-300 V/cm are applied for 1-10 min. The optimal condition for the EPD allows modifying the properties and microstructure of the deposited films. Superconducting coatings with nanometer-sized pores and a preferred orientation along the c-axis were prepared from the result with chemically modified precursor solution. In contrast, YBCO coatings of submicrometer-sized pores and randomly orientated grains were prepared from the solution without PEG.

• Journal of information and communication convergence engineering
• /
• 제1권1호
• /
• pp.27-30
• /
• 2003

Electrophoretic deposition (EPD) of alcohol YBCO suspensions on the Ag wire electrode is studied. Poly(ethylene glycol) was coordinated to a structure formed by the EPD process with YBCO particles. The suspension is characterized in terms of zeta potential and conductivity. The d.c electric fields of 200-300 V/cm are applied for 1-10 min. The optimal condition for the EPD allows modifying the properties and microstructure of the deposited films. Superconducting coatings with nanometer-sized pores and a preferred orientation along the c-axis were prepared from the result with chemically modified precursor solution. In contrast, YBCO coatings of submicrometer-sized pores and randomly orientated grains were prepared from the solution without PEG.

• Transactions on Electrical and Electronic Materials
• /
• 제4권5호
• /
• pp.6-9
• /
• 2003

Electrophoretic deposition (EPD) of alcohol YBCO suspensions on the Ag wire electrode is studied. Polyethyleneglycol was coordinated to a structure formed by the EPD process with YBCO particles. The d.c electric fields of 200-300 V/cm are applied for 1-10 min. The optimal condition for the EPD allows modifying the properties and microstructure of the deposited films. Superconducting coatings with nanometer-sized pores and a preferred orientation along the caxis were prepared from the result with chemically modified precursor solution. In contrast, YBCO coatings of submicrometer-sized pores and randomly orientated grains were prepared from the solution without PEG.

• 한국정보통신학회:학술대회논문집
• /
• 한국해양정보통신학회 2004년도 SMICS 2004 International Symposium on Maritime and Communication Sciences
• /
• pp.117-122
• /
• 2004

Electrophoretic deposition (EPD) of alcohol YBCO suspensions on the Ag wire electrode was studied. Poly(ethylene glycol) was coordinated to a structure formed by the EPD process with YBCO particles. The suspension is characterized in terms of zeta potential and conductivity. The d.c electric fields of 200-300V/cm are applied for 1-10 min. The optimal condition for the EPD allows modifying the properties and microstructure of the deposited films. Superconducting coatings with nanometer-sized pores and a preferred orientation along the c-axis were prepared from the result with chemically modified precursor solution. In contrast, YBCO coatings of sub-micrometer sized pores and randomly orientated grains were prepared from the solution without PEG

• 한국표면공학회지
• /
• 제40권4호
• /
• pp.190-196
• /
• 2007

Dye sensitized solar cells(DSSC) are the most promising future energy resource due to their high energy efficiency, low production cost, and simple manufacturing process. But one problem in DSSC is short life time compared to silicon solar cells. This problem occurred from photocatalytic degradation of dye material by nanometer sized $TiO_2$ particles. To prevent dye degradation as well as to increase its life time, the transparent coating film is needed for UV blocking. In this study, we synthesized nanometer sized $TiO_2$ particles in sols by increasing its internal pressure up to 200 bar in autoclave at $120^{\circ}C$ for 10 hrs. The synthesized $TiO_2$ sols were all formed with brookite phase and their particle size was several nm to 30 nm. Synthesized $TiO_2$ sols were coated on the backside of fluorine doped tin oxide(FTO) glass by ink jet printing method. With increasing coating thickness by repeated ink jet coating, the absorbance of UV region (under 400 nm) also increases reasonably. Decomposition test of titania powders dispersed in 0.1 mM amaranth solution covered with $TiO_2$ coating glass shows more stable dye properties under UV irradiation, compared to that with as-received FTO glass.

• 한국재료학회지
• /
• 제16권9호
• /
• pp.538-542
• /
• 2006

Nano-sized cobalt oxide powders were prepared by low pressure spray pyrolysis process. The precursor powders obtained by low pressure spray pyrolysis process from the spray solution with ethylene glycol had several microns size and hollow structure. The precursor powders obtained from the spray solution with optimum concentration of ethylene glycol formed the nano-sized cobalt oxide powders with regular morphology after post-treatment without milling process. On the other hand, the cobalt oxide powders obtained from the spray solution without ethylene glycol had submicron size and spherical shape before and after posttreatment. The mean size of the cobalt oxide powders formed from the spray solution with concentration of ethylene glycol of 0.7M was 180 nm after post-treatment at temperature of $800^{\circ}C$. The mean size of the powders could be controlled from several tens nanometer to micron sizes by changing the post-treatment temperatures in the preparation of cobalt oxide powders by low pressure spray pyrolysis process.

• 한국재료학회지
• /
• 제29권1호
• /
• pp.59-64
• /
• 2019

This study investigates the optical characteristics of InGaN multiple quantum wells(MQWs) light emitting diodes(LEDs) on planar sapphire substrates(PSSs), nano-sized PSS(NPSS) and micro-sized PSS(MPSS). We obtain the results as the patterning size of the sapphire substrates approach the nanometer scale: The light from the back side of the device increases and the total light extraction becomes larger than the MPSS- and planar-LEDs. The experiment is conducted by Monte Carlo ray-tracing, which is regarded as one of the most suitable ways to simulate light propagation in LEDs. The results show fine consistency between simulation and measurement of the samples with different sized patterned substrates. Notably, light from the back side becomes larger in the NPSS LEDs. We strongly propose that the increase in the light intensity of NPSS LEDs is due to an abnormal optical distribution, which indicates an increase of extraction probability through NPSS.

• Metals and materials international
• /
• 제24권6호
• /
• pp.1285-1292
• /
• 2018

Microstructural properties of as-grown and annealed CoCrFeMnNi high entropy alloy (HEA) oxynitride thin films were investigated. The CoCrFeMnNi HEA oxynitride thin film was grown by magnetron sputtering method using an air gas, and annealed under the argon plus air flow for 5 h at $800^{\circ}C$. The as-grown film was homogeneous and uniform composed of nanometer-sized crystalline regions mixed with amorphous-like phase. The crystalline phase in the as-grown film was face centered cubic structure with the lattice constant of 0.4242 nm. Significant microstructural changes were observed after the annealing process. First, it was fully recrystallized and grain growth happened. Second, Ni-rich region was observed in nanometer-scale range. Third, phase change happened and it was determined to be $Fe_3O_4$ spinel structure with the lattice constant of 0.8326 nm. Hardness and Young's modulus of the as-grown film were 4.1 and 150.5 GPa, while those were 9.4 and 156.4 GPa for the annealed film, respectively.

• 한국진공학회지
• /
• 제20권1호
• /
• pp.63-69
• /
• 2011

본 연구에서는 기존 실리콘 반도체 기술 기반의 포토 및 이빔 리소그래피 공정을 통하여 유기 반도체 소자를 패터닝하였다. P3HT나 PEDOT 등의 유기 반도체는 용매에 녹기 때문에 MIMIC (micro-molding in capillaries)이나 inkjet printing 기술을 이용하여 마이크로미터 크기의 소자 제작이 가능하였으나, 펜타신은 용매에 녹지 않기 때문에 매우 복잡한 방법으로 마이크로미터 크기의 소자를 제작하여왔다. 그러나, 본 연구에서는 원자층 증착 방법으로 증착한 산화 알루미늄막을 펜타신의 보호층으로 이용하여 기존의 포토 및 이빔 리소그래피 방법으로 마이크로미터크기의 펜타신 소자를 제작하였으며 그 전기 특성을 확인하였다.