• 한국표면공학회지
• /
• 제43권2호
• /
• pp.47-50
• /
• 2010

This work discusses a two-step electroless plating method for preparing a Pt thin film on p-type InGaAs substrate, which is defined as Pt I and Pt II. A thin Pt catalytic layer formed in Pt I bath on the substrate at $65^{\circ}C$. In the following Pt II bath, thick Pt films then easily grew on the sensitized layer on InGaAs previously formed in the Pt I bath. The growth of Pt film is strongly influenced by the plating temperature and pH value. To study the plating time effect, the plating of Pt II bath is 5 to 40 min at $80^{\circ}C$ after using Pt I bath at 50~$65^{\circ}C$ for 5min of pH 8~13. Pt film for ohmic contact to p-type InGaAs was successfully prepared by using the two-step Pt electroless plating.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2007년도 7th International Meeting on Information Display 제7권1호
• /
• pp.659-662
• /
• 2007

The characteristics of a $SiN_x$ passivation layer grown by a specially designed catalyzer enhanced chemical vapor deposition (CECVD) system and electrical and optical properties of OLEDs passivated with the $SiN_x$ layer are described. Despite the low substrate temperature, the single $SiN_x$ passivation layer, grown on the PC substrate, exhibited a low water vapor transmission rate of $2{\sim}6{\times}10^{-2}\;g/m^2/day$ and a high transmittance of 87 %. In addition, current-voltage-luminescence results of an OLED passivated with a 150 nm-thick $SiN_x$ film compared to nonpassivated sample were identical indicating that the performance of an OLED is not critically affected by radiation from tungsten catalyzer during the $SiN_x$ deposition.

• 한국결정성장학회지
• /
• 제28권1호
• /
• pp.14-20
• /
• 2018

에어로졸 증착법에 의해서 상온에서 $6{\mu}m/min$의 속도로 $5{\sim}10{\mu}m$ 두께의 PZT-PZN(0 %, 20 %, 40 %) 복합체의 막을 실리콘/사파이어 기판위에서 제조하였다. 에어로졸 증착에 사용된 PZT, 2PZN-8PZT, 4PZN-6PZT 초기분말입자는 불규칙한 형상을 가지고 있으며 submicron 크기임을 확인하였다. 증착된 막은 어떠한 뜯김이나 기공도 없는 치밀한 막임을 확인하였고 나노크기의 입자를 가진 페로브스카이트 단상이었다. 실리콘기판 및 사파이어 기판위에서 증착된 막은 전기로에서 $700^{\circ}C$ 및 $900^{\circ}C$에서 각각 어닐링처리 하였으며 PZT에 40 %의 PZN이 첨가된 조성의 막의 경우 pyrochlore의 2차상이 형성되었다. 미세구조에 미치는 PZN 첨가의 영향을 관찰하기 위해 FE-SEM 및 HR-TEM이 사용되었다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2015년도 제49회 하계 정기학술대회 초록집
• /
• pp.186-186
• /
• 2015

We have introduced multifunctional ITO single thin films formed by normal sputtering system equipped with a plasma limiter which effectively blocks the bombardment of energetic negative oxygen ions. MFSS ITO also possesses high gas diffusion barrier properties simultaneously low resistivity even it deposited at room temperature without post annealing on plastic substrate. Nano-crystalline enhancement by Ar energy has energy window from 20 to 30 eV under blocking NOI condition. Effect of blocking NOI and optimal Ar energy window enhancement facilitate that resistivity is minimized to $3.61{\times}10^{-4}{\Omega}cm$ and the WVTR of 100 nm thick MFSS ITO is $3.9{\times}10^{-3}g/(m^2day)$ which is measured under environmental conditions of 90% relative humidity and 50oC that corresponds to a value of ${\sim}10^{-5}g/(m^2day)$ at room temperature. The multifunctional MFSS ITO with low resistivity, and low gas permeability will be highly valuable for plastic electronics applications.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권1호
• /
• pp.59-66
• /
• 1996

Polyimides containing cyclobutane ring in main chain is known to be thermally stable and able to be developed in organic solvents after photolysis with 254 nm UV light. This type of polyimides can be used as promising positive photoresist in VLSI fabrication process. In the current VLSI process, photoresist films are formed by spin coating. The film thickness is more than several hundred nano meters. It seems that there is room for improvement of film coating process by introducing Langmuir Blodgett technique. Thereby ultra thin film photoresist can be formed, and higher density of integration in VLSI be achieved. In the present work, depositing procedure of LB films of this polyimide was investigated. LB film thickness was measured by ellipsometry to evaluate deposited film status. Chemical imidization procedure was studied to avoid several problems in thermal imidization. The pattern of submicron dimension has successfully formed on LB film of 8nm thick, which found showing good contrast.

• 센서학회지
• /
• 제20권6호
• /
• pp.406-411
• /
• 2011

$Co_3O_4$ thick film gas sensor using the powder prepared by hydrothermal reaction method(HRM) was fabricated. For comparison study, we also prepared the sensor using commercial $Co_3O_4$ powder under the same fabrication conditions. Sensitivity, time response, and selectivity of them to variable gases such as iso-$C_4H_{10}$, CO, $NH_3$, and $CH_4$ were investigated. The sensor from the powder prepared by HRM showed higher sensitivity to every gas than those from commercial powder. For iso-$C_4H_{10}$ gas, the sensitivities of both sensor to 100 ppm are 160 % and 40 %, respectively. Time response and selectivity of the sensor using the powder prepared by HRM were better than those of the sensor using commercial powder.

• 열처리공학회지
• /
• 제29권6호
• /
• pp.272-276
• /
• 2016

Al doped ZnO (AZO) single layer and AZO/Ag bi-layered films were deposited on the glass substrates by radio frequency and direct current magnetron sputtering and then the effect of Ag buffer layer on the electrical and optical properties of the films was investigated. The thicknesses of AZO upper layer was kept as 100 nm, while Ag buffer layer was varied from 5 to 15 nm. The observed results mean that opto-electrical properties of the AZO films is influenced with Ag buffer layer and AZO film with 10 nm thick Ag buffer layer show the higher opto-electrical performance than that of the AZO single layer film prepared in this study.

• 대한금속재료학회지
• /
• 제48권12호
• /
• pp.1109-1115
• /
• 2010

ZnO thin films were deposited on Si(100) substrates at low temperatures ($44^{\circ}C{\sim}210^{\circ}C$) by atomic layer deposition using DEZn (diethyl zinc) and water as precursors. The film thickness was measured by ellipsometry calibrated with cross-sectional TEM. The phase formation, microstructure evolution, UV-absorbance, and chemical composition changes were examined by XRD, SEM, AFM, TEM, UV-VIS-NIR, and AES, respectively. A uniform amorphous ZnO layer was formed even at $44^{\circ}C$ while stable crystallized ZnO films were deposited above $90^{\circ}C$. All the samples showed uniform surface roughness below 3 nm. Fully crystallized ZnO layers with a band-gap of 3.37 eV without carbon impurities can be formed at substrate temperatures of less than $90^{\circ}C$.

• 한국자기학회지
• /
• 제18권1호
• /
• pp.32-35
• /
• 2008

차세대 반도체 산업의 발전을 위하여 반도체 소자의 구조는 DRAM, FRAM, MRAM 등 여러 분야에서 다양한 연구가 진행되고 있다. 특히 이런 차세대 반도체 소자에서 금속 배선으로는 Cu가 사용되며, Cu 금속 배선을 위한 확산방지막에 대한 연구는 반드시 필요하다[1-3]. Cu 금속 배선을 위한 확산방지막에 대한 현재까지의 연구에서는 Tungsten(W)을 기반으로 Nitride(N)를 불순물로 첨가한 확산방지막에 대하여 연구되었다[4-7]. 이러한 W-N를 기반으로 본 연구에서는 물리적 기상 증착법(PVD) 방법인 RF Magnetron Sputter 방법으로 W-N 이외에 Carbon(C) 과 Boron(B)을 첨가하여 확산방지막의 특성을 확인하였고, 특히 Boron Target의 power를 변화하여 W-B-C-N 확산방지막의 Boron에 의한 특성과 열적 안정성을 연구하였다[8-10]. 실험은 다양한 Boron의 조성을 가지는 확산방지막을 증착하여 $\beta$-ray와 4-point probe를 사용하여 확산방지막의 특성을 확인하였고, 고온($700^{\circ}C{\sim}1000^{\circ}C$) 열처리한 후 X-ray Diffraction 분석을 하여 열적 안정성을 확인하였다.

• 한국수소및신에너지학회논문집
• /
• 제21권5호
• /
• pp.375-382
• /
• 2010

A layered perovskite photocatalysts, $SrBi_2Nb_2O_9$ (SBN), was synthesized by the conventional solid-state reaction method and characterized by X-ray diffraction (XRD) and UV-visble spectrophotometry. The results showed that the structure of $SrBi_2Nb_2O_9$ is orthorhombic. Diffuse reflectance spectra for calcined and attrition-milled SBN showed the main absorption edges were less 400 nm, that is ultraviolet region. SBN under micron-sized powder was deposited on the $Al_2O_3$ by room temperature powder spray in vacuum process, so called aerosol deposition (AD), and nano-grained $SrBi_2Nb_2O_9$ photocatalytic thick film was fabricated. AD-deposited SBN thick films were characterized by XRD, scanning electron microscopy (SEM) and UV-visable spectrophotometry, Moreover, it was found that several nano-sized SBN film by AD process can improve the photocatalytic activity under visable reflectance.